• Korean Chemical Engineering Research
• /
• v.50 no.2
• /
• pp.191-197
• /
• 2012

Acrylic terminated polyurethane prepolymers were synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate (IPDI), polycarbonate diol (PCD) and dimethylol propionic acid (DMPA), with pentaerythritol triacrylate (PETA). Subsequently, silylated acrylic terminated prepolymers were prepared by capping the NCO groups of acrylic terminated polyurethane prepolymers with different types of silane coupling agents, glycidoxypropyl trimethoxysilane (GPTMS) or aminopropyl triethoxysilane (APS). The average particle size of pure waterborne polyurethane solution, measured by the dynamic light scattering method, was increased from 14.3 nm to 208.6 nm by adding PETA and APS. Also, the coating film of silylated acrylic terminated waterborne polyurethane showed better abrasion resistance and pencil hardness than that of pure waterborne polyurethane.

• Korean Chemical Engineering Research
• /
• v.49 no.4
• /
• pp.411-416
• /
• 2011

NCO terminated polyurethane prepolymers were synthesized from isophorone diisocyanate(IPDI), polycarbonate diol(PCD) and dimethylol propionic acid(DMPA). Subsequently, acrylic terminated prepolymers were prepared by capping the NCO groups of polyurethane prepolymers with different moles of pentaerythritol triacrylate (0~0.024 moles) as a acrylate monomer. The average particle size of the acrylic terminated polyurethane solutions was increased with increasing PETA contents. Also, the prepared coating films showed better abrasion resistance and pencil hardness than pure waterborne polyurethane.

• Korean Chemical Engineering Research
• /
• v.49 no.5
• /
• pp.548-553
• /
• 2011

NCO terminated polyurethane prepolymers were synthesized from isophorone diisocyanate(IPDI), polycarbonate diol(PCD) and dimethylol propionic acid(DMPA). Subsequently, acrylic terminated polyurethanes were prepared by capping the NCO groups of polyurethane prepolymers with different types of acrylate monomers, such as 2-hydroxyethyl methacrylate(HEMA), 2-hydroxyethyl acrylate(HEA) and pentaerythritol triacrylate(PETA). The average particle sizes of the acrylic terminated polyurethane solutions were increased by capping acrylate monomers. Also, the prepared coating films showed better abrasion resistance and pencil hardness than those of pure waterborne polyurethanes. The coating film with PETA exhibited the best abrasion resistance and pencil hardness of coating films prepared with three acrylate monomers.

• Clean Technology
• /
• v.23 no.2
• /
• pp.148-157
• /
• 2017

To prepare UV-curable polyurethane-acrylate oligomer, NCO-terminated urethane prepolymers with trimethylolpropane, [TMP; 0 (0), 0.1 (0.021) and 0.2 (0.043) mole (mole fraction)] as crosslinkable tri-functional chain extender were end-capped with pentaerythritol triacrylate [PETA; 2.0 (0.400), 1.7 (0.354) and 1.4 (0.304) mole (mole fraction)] with one hydroxyl group/three vinyl functionalities. The stable as-formulated UV-curable polyurethane-acrylates [stable mixtures of PETA-capped oligomer/reactive acrylic monomer diluents without/with heptadecafluorodecyl methacrylate (PFA; 0, 6 and 9 wt%)] were formed up to 0.2 (0.043) mole (mole fraction) of TMP content in the prepolymer, while homogeneous-mixing failed at 0.3 (0.068) mole (mole fraction), in which the crosslink density in NCO-terminated urethane prepolymer was too high to enable the formation of stable mixture. This study examined the effect of TMP/PETA molar ratio and heptadecafluorodecyl methacrylate (PFA) content (wt%) on the properties of UV-cured polyurethane-acrylates as marine antifouling coating materials. The properties of UV-cured polyurethane-acrylate were found to be significantly dependent on the crosslinkable TMP/PETA ratio and PFA content. With the increasing of the TMP and PFA contents, the contact angles increased, and consequently the surface tension decreased. The adhesion of algae/barnacles to PFA contained film samples were found to be sufficiently weak to allow their easy removal. These results suggest that the UV-cured samples containing PFA have strong potential as coating materials for antifouling applications.