• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.383-388
• /
• 2006

The varistor properties and DC accelerated aging characteristics of $ZnO-Pr_{6}O_{11}-CoO-Cr_{2}O_{3}$-based varistors were investigated at different $La_{2}O_3$ contents in the range of $0{\sim}2.0mol%$. The varistors doped with 0.5 mol% $La_{2}O_3$ exhibited good nonlinearity, with 81.6 in nonlinear coefficient. Increasing the $La_{2}O_3$ content further to 2.0 mol% caused the sintered density to increase, and the breakdown voltage and nonlinearity to decrease abruptly. The varistors with 0.5 mol% $La_{2}O_3$ exhibited the high electrical stability, with -1.14% in variation rate of breakdown voltage, -3.7% in variation rate of nonlinear coefficient, and +100% in variation rate of leakage current for specified DC accelerated aging stress condition (95% of breakdown voltage/$150^{\circ}C$/24 h).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.383-386
• /
• 2004

DC accelerated aging characteristics of Zn-Pr-Co-Cr-La oxides-based varistors were investigated with various sintering temperatures. The varistors sintered at $1240^{\circ}C$ exhibited the highest nonlinearity, with a nonlinear exponent of 79.3 and a leakage current of $0.3\;{\mu}A$, whereas completely degraded because of thermal runaway owing to low sintered density. The varistors sintered at $1250^{\circ}C$ exhibited not only a high nonlinearity with the nonlinear exponent 61.4 and the leakage current 0.7 ${\mu}A$, but also a high stability with the variation rates of varistor voltage and nonlinear exponent are -1.01% and -10.67%, respectively, under DC stress condition such as $(0.85\;V_{1mA}/115^{\circ}C/24\;h)+(0.90\;V_{1mA}/120^{\circ}C/24\;h)+(0.95\;V_{1mA}/125^{\circ}C/24\;h)+(0.95\;V_{1mA}/150^{\circ}C/24\;h)$.

• Journal of Sensor Science and Technology
• /
• v.22 no.1
• /
• pp.76-83
• /
• 2013

A real-time wireless monitoring and analysis methods using the wearable PPG sensor to estimate cardiovascular condition is studied for ubiquitous healthcare service. A small size and low-power consuming wearable photoplethysmogram (PPG) sensor is designed as a wrist type device and connected with the IP node assigned its own IPv6 address. The measured PPG waveform in the IP node is collected and transferred to a central server PC through the IP-enabled wireless network for storage and analysis purposes. A monitoring and analysis program is designed to process the accelerated plethysmogram (APG) waveform by applying the second order derivatives to analyze systolic waves as well as heart rate variability analysis from the measured PPG waveform. From our results, the features of cardiovascular condition from individual's PPG waveform and estimation of vascular compliance by the comparison of APG-aging index (AI) and ratio of LF/HF are demonstrated.

• Journal of Korea Foundry Society
• /
• v.28 no.6
• /
• pp.268-272
• /
• 2008

Interfacial characteristics of aluminum borate whisker reinforced AS52 matrix composite was investigated. Peak hardness of AS52 composite was obtained aging at $170^{\circ}C$ for 15h and the aging process was accelerated by the presence of the aluminium borate whisker. The MgO layer, which was the interfacial reaction product between the reinforcement and the Mg matrix, was produced with 20 nm thickness in as-cast condition. As the aging time increased, the thickness of the interfacial reaction layer increased to 50 nm in peak aged condition. The nano-indentation test results indicated that the strength of interface was improved by the aging but over-aging degraded the reinforcement and decreased the interfacial strength which resulted in the decrease of overall composite strength.

• Journal of Applied Reliability
• /
• v.4 no.2
• /
• pp.73-90
• /
• 2004

We performed the heat aging test to predict the useful lifetime of Elastomeric Bearing Chloroprene Rubber (CR) used for supporting bridge. During the test, we measured elongation that are influenced by temperature and aging time. The failure of a test piece is defined as the point at which the elongation reaches to 75% of the initial value. This failure criterion is based on KS F 4420: 1998 (Elastomeric Bearing for bridge). Through the accelerated heat aging test, we found that the Arrhenius relationship and the Weibull lifetime distribution are appropriate as the life-temperature relationship and lifetime distribution of the CR, respectively. Using the Arrhenius -Weibull model, the parameters of the model are estimated and the lifetime of the CR at use condition is predicted.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.38 no.3 s.116
• /
• pp.66-71
• /
• 2006

The objective of this study was to find in what color Hanji(Korean hand-made paper) is dyed when it is dyed with a pigment extracted from clove tree using different kinds of mordant, and how the paper is discolored and variety of strength under the condition of accelerated aging test. The results of this experiment are as follows. The Hanji dyed with aluminum acetate mordant was colored yellowish brown at pH 4.82, discoloration after aging was as much as a slight difference of color was recognized, and the decrease of strength after aging test was small. Thus, the method using aluminum acetate mordant was usable in coloring Hanji. The second most useful Hanji dyeing moth of was using distilled water and ferrous sulfate mordant, which dyed Hanji light brown at pH 6.03. However, when pigment was extracted using distilled water and copper sulfate mordant was used, discoloration was satisfactory but strength decreased too much and pale brown was obtained. Thus, this method was not usable.

• Proceedings of the KIEE Conference
• /
• 2005.07e
• /
• pp.82-84
• /
• 2005

In a transformer, thermal stress is the most influential parameter affecting the aging behavior of insulation system. The aging behavior of insulation system in transformer is determined mainly by the thermal conditions inside the transformer. The thermal stress on the insulation system may occur from operation in a high temperature caused by overloading or local overheating. Thus, this paper investigated the condition monitoring of insulation condition in thermally accelerated aged transformer oils by in-situ sensor. The condition of aged samples was investigated by measurements of relative permittivity i.e. capacitance change by capacitive sensor. Results from the experiments are presented in this paper.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.35 no.1
• /
• pp.48-53
• /
• 2003

The objective of this study was to find in what color Korean handmade paper(Hanji) is dyed when it is dyed with a pigment extracted from waste onion peelings using different kinds of mordant, and how the paper is discolored and variety of strength under the condition of accelerated aging test. The results of this experiment are as follows. 1. Korean handmade paper was dyed in different colors according to the kinds of mordant. Mainly it was dyed in orange-brown, and sometimes in gold or khaki. 2. Korean handmade paper dyed was not discolored much, which suggests that the pigment is strong under the condition of aging. 3. As for durability, Korean handmade paper dyed in gold was strongest. Korean handmade paper, to which aluminum sulfate, iron sulfate or sodium dichromate was applied as mordant, had poor durability. Thus, these were not suitable as mordant.

• Korean Journal of Materials Research
• /
• v.16 no.7
• /
• pp.416-421
• /
• 2006

The varistor properties of ZPCCL-based ceramics were investigated at different $La_2O_3$ contents in the range of $0{\sim}2.0$ mol%. As $La_2O_3$ content increased, the ceramic density greatly increased in the range of $4.71{\sim}5.77\;g/cm^3$ and the varistor voltage greatly decreased in the range of $503.5{\sim}9.4$ V. The varistor with 0.5 mol% $La_2O_3$ exhibited good nonlinearity, in which the nonlinear exponent is 81.6 and the leakage current is 0.2 ${\mu}A$. Furthermore, the varistors exhibited the high electrical stability, with $%{\Delta}V_{1mA}=-1.1%,%{\Delta}{\alpha}=-3.7%$, and $%{\Delta}I_L=+100%$ for DC accelerated aging stress condition of 0.95 $V_{1mA}/150^{\circ}C/24$ h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.199-202
• /
• 1998

In examining application of polymer as electrical insulators, it is very important to perform accelerated aging test substituted the process which polymer insulator is degraded for long-time by the process of short-time. The purpose of this paper is to examine the properties of water degradation which affect on the efficiency of epoxy insulator. To do this, the surface properties on epoxy insulating material have been investigated after long-time accelerated degradation in boiling water condition. The experimental results showed the contact angle and surface resistivity after treatment to decrease the sample of water treatment. In dielectric properties, dielectric constant was increased by the aging development with water treatments.