• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.340-340
• /
• 2016

We have prepared alumina (Al2O3) doped zinc oxide (AZO) films by DC magnetron sputtering (MS) technique and obtained higher self surface texturing at a high target angle (f). We have characterized the films and applied it as a front electrode of a single junction amorphous silicon solar cell. At a lower f the deposited films show higher values of optical gap (Eg), charge carriers mobility & concentration, crystallite grain size and wider wavelength range of transmission. At higher target angle the sheet resistance, surface roughness, haze factor etc for the films increase. For f=72.5o the haze factor for diffused transmission becomes 6.46% at 540 nm wavelength. At f=72.5o the material shows a reduction in crystallinity and evolution of a hemispherical-type sub-micron surface textures. A Monte Carlo method (MCM) of simulation of the AZO film deposition shows that such an enhanced self-surface texturing of the films at higher f is possible.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.587-591
• /
• 1998

AZO transparent conducting thin film were fabricated by DC magnetron sputtering using the Zn: Al (2% aluminu contained ) alloy target with inducing microwave to the plasma, and the effect of microwave was studied. The optical transmittance, the resistivity and dynamic deposition rate at the applied voltage to target of 420 V was 50~70%, $ 5.5{\times}10^{-3}{\Omega}$cm and 6,000 $\AA\textrm{mm}^2$/J, respectively. After annealing AZO coated glass at $400^{\circ}C$ for 30 minutes, the light transmittance was increased to 80% and electrical conductivity was also increased two times, reached to resistivity of $2.0{\times}10^{-3}{\Omega}$cm.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.294-294
• /
• 2015

대향타겟식 스퍼터링법을 이용해 유연한 기판에 증착시켜 고주파 마그네트론 스퍼터링보다 덜 손상이 입히도록 증착 시켰으며, 플라즈마 주파수를 다양하게 하여 밴딩테스트 후 나빠지는 전기적, 광학적 특성을 개선하고, 그 원인을 분석하였다.

• Korean Journal of Materials Research
• /
• v.19 no.5
• /
• pp.259-264
• /
• 2009

In this study we investigated the effect of the multi-step texturing process on the electrical and optical properties of hydrogenated Al-doped zinc oxide (HAZO) thin films deposited by rf magnetron sputtering. AZO films on glass were prepared by changing the $H_2/(Ar+H_2)$ ratio at a low temperature of $150^{\circ}C$. The prepared HAZO films showed lower resistivity and higher carrier concentration and mobility than those of non-hydrogenated AZO films. After deposition, the surface of the HAZO films was multi-step textured in diluted HCl (0.5%) for the investigation of the change in the optical properties and the surface morphology due to etching. As a result, the HAZO film fabricated under the type III condition showed excellent optical properties with a haze value of 52.3%.

• Korean Journal of Metals and Materials
• /
• v.46 no.4
• /
• pp.249-256
• /
• 2008

0.5 wt% Al doped ZnO thin films (AZO) were prepared on glass substrates using RF magnetron sputtering method. Thin films were grown at substrate temperature of $250^{\circ}C$, RF power of 75W, working pressure of 10 mTorr, by changing the $O_2/Ar$ pressure ratio from 0% to 16.7%. The effects of oxygen partial pressure during the deposition process on structural and optical properties of the films were investigated using XRD, SEM, AFM, EPMA and UV-visible spectroscopy. All the AZO thin films were grown as hexagonal wurtzite phase with the c-axis preferred out-of-plane orientation. The surface roughness and grain size of AZO films decreased with increasing oxygen ratio from 10.6 nm to 3.2 nm and 94.9 nm to 30.9 nm, respectively. On the other hand, the transmittance and band gap energy of the AZO films increased from 84.7% to 92.6% and 3.24 eV to 3.28 eV, respectively with increasing the $O_2/Ar$ pressure ratio.

• Journal of the Korean Vacuum Society
• /
• v.18 no.5
• /
• pp.377-383
• /
• 2009

Aluminum-doped zinc oxide (AZO) thin films were deposited on sapphire substrate by using radio-frequency magnetron sputtering and were performed in the temperature range of $600-900^{\circ}C$ by rapid thermal annealing (RTA). The crystallographic structure and the surface morphology were investigated by using X-ray diffraction and scanning electron microscopy, respectively. The crystallinity of the films was improved with increasing the annealing temperature and the average size of crystalline grains was found to be 50 nm. All the thin films showed an average transmittance of 92% in the wavelength range of 400-1100 nm. As the annealing temperature was increased, the bandgap energy was decreased and the violet photoluminescence (PL) signal at 400 nm replaced the ultraviolet PL signal. The electrical properties of the thin films showed a significant dependence on the annealing temperature.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.107-107
• /
• 2011

오늘 날 transparent conductive oxide는 다양한 분야에서 활용되고 있다. 최근에는 태양전지 분야에서도 많이 활용되고 있으며, 초기에는 transmittance 및 낮은 sheet resistance 특성을 가지는 ITO가 많이 활용되었지만 thin film solar cell와 같이 hydrogenation 공정에 약한 ITO보다는 Al-doped ZnO가 사용되기 시작하면서 많은 연구가 진행되고 있다. 본 연구에서는 thin film solar cell 및 silicon heterojunction solar cell에 적용 가능한 Al-doped ZnO에 관한 연구로써 a-Si:H의 Si-H bonds에 영향을 주지 않는 낮은 영역의 substrate temperature와 power로 Al-doped ZnO를 형성하고 상기 parameter에 따른 Al-doped ZnO의 특성 변화에 대해서 분석하였다. 특히 substrate temperature가 변화할수록 carrier concentration 및 sheet resistance가 많은 변화를 보였으며 이로 인하여 transmittance 특성이 온도에 따라 좋아지다가 너무 높은 온도에서는 오히려 좋지 않게 되었다. 이는 너무 높은 carrier concentration은 free carrier absorption에 의해 transmittance 특성을 오히려 좋지 않게 한다. 우리는 본 연구를 통해 92.677% (450 nm), 90.309% (545 nm), 94.333% (800 nm)의 transmittance를 얻을 수 있었다.

• Current Photovoltaic Research
• /
• v.11 no.1
• /
• pp.13-17
• /
• 2023

Functional transparent electrode was achieved by metal oxide-metal-Metal oxide (OMO) structure. Tailoring of metal oxide and metal layers, optically transparent and electrically excellent OMO films were investigated. Silver (Ag) is adopted for the metal layer and Ag oxide (AgO) is reactively formed by flowing O₂ gas during the sputtering process. This spontaneous AgO formation from Ag simultaneously provides the good electrical interface with high transparency. Due to the feature of transparent electrode of OMO, it endows the shielding effect (SE) function of electromagnetic interference. Optically transparent and electrically conductive OMO electrode shows the high transmittance (83.7%) and low sheet resistance (6.5 Ω/☐) with SE of 29.54 dB.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.60-61
• /
• 2007

IAZO (indium aluminium zinc oxide) anode films were co-sputtered on glass substrate using a dual target DC magnetron sputtering system. For preparation of IATO films, at constant DC power of IZO (indium zinc oxide) target of 100 W, the DC power of AZO (Aluminum zinc oxide) target was varied from 0 to 100 W. To analyze electrical and optical properties of IAZO anode, Hall measurement examination and UV/V is spectrometer were performed, respectively. In addition, structure of IAZO anode film was examined by X-ray diffraction (XRD) method. Surface smoothness was investigated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). From co-sputtered IAZO anode, good conductivity($2.32{\times}10^{-4}{\Omega}.cm$) and high transparency(approximately 80%) in the visible range were obtained even at low temperature deposition. Finally, J-V-L characteristics of phosphorescent OLED with IAZO anode were studied by Keithley 2400 and compared with phosphorescent OLED with conventional ITO anode.

• Journal of the Optical Society of Korea
• /
• v.19 no.5
• /
• pp.508-513
• /
• 2015

A capacitive-type touch screen panel (TSP) composed of silver nanowire (AgNW) crossing electrodes and transparent bridge structures was fabricated on a polycarbonate film. The transparent bridge structure was formed with a stack of Al-doped ZnO (AZO) electrodes and SU-8 insulator. The stable and robust continuity of the bridge electrode over the bridge insulator was achieved by making the side-wall slope of the bridge insulator low and depositing the conformal AZO film with atomic layer deposition. With an extended exposure time of photolithography, the lower part of the SU-8 layer around the region uncovered by the photomask can be exposed enough to the UV light scattered from the substrate. This leads to the low side-wall slope of the bridge insulator. The fabricated TSP sample showed a large capacitance change of 22.71% between with and without touching. Our work supplies the technological clue for ensuring long-term reliability to the highly flexible and transparent TSP made by using conventional fabrication processes.