• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.735-742
• /
• 1996

Antimony-doped Tin oxide (ATO) thin films were deposited on soda-lime glass substrates by DC magnetron sputtering technique. Effects of DC power film thickness and post heat-treatment on electrical conductivity of ATO film were investigated. Other properties of ATO film such as optical anti-chemical and wear properties were also reported in this work. The obtained ATO films showed electrical resistivities ranging from 5$\times$10-3 $\Omega$cm to 3$\times$10-3 $\Omega$cm with the average optical transparency above 80% in visible wavelength range and excel-lent anti-chemical properties where the electrical resistivity was not changed even after soaking the films in 1M HCl or 1M NaOH solution for 10 days. These properties were found to be related to the crystallinity of ATO film and the films having higher crystallinity showed better properties.

• Korean Journal of Materials Research
• /
• v.25 no.4
• /
• pp.177-182
• /
• 2015

Sb-doped $SnO_2$(ATO) thin films were prepared using electrospinning. To investigate the optimum properties of the electrospun ATO thin films, the deposition numbers of the ATO nanofibers(NFs) were controlled to levels of 1, 2, 4, and 6. Together with the different levels of deposition number, the structural, chemical, morphological, electrical, and optical properties of the nanofibers were investigated. As the deposition number of the ATO NFs increased, the thickness of the ATO thin films increased and the film surfaces were gradually densified, which affected the electrical properties of the ATO thin films. 6 levels of the ATO thin film exhibited superior electrical properties due to the improved carrier concentration and Hall mobility resulting from the increased thickness and surface densification. Also, the thickness of the samples had an effect on the optical properties of the ATO thin films. The ATO thin films with 6 deposited levels displayed the lowest transmittance and highest haze. Therefore, the figure of merit(FOM) considering the electrical and optical properties showed the best value for ATO thin films with 4 deposited levels.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.241-246
• /
• 2003

The transparent conducting thin film of ATO (antimony-doped tin oxide) was successfully fabricated on$SiO_2$/glass substrate by a sol-gel dip coating method. The crystalline phase of the ATO thin film was identified as SnO$_2$ major phase and the film thickness was about 100 nm/layer at the withdrawal speed of 50 mm/minute. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin film which was annealed under nitrogen atmosphere were 84% and $5.0\times 10^{-3}\Omega \textrm{cm}$, respectively. It was found that the $SiO_2$ layer inhibited Na ion diffusion and the formation of impurities like $Na_2SnO_3$ or SnO while increasing Sb ion concentration and higher ratio of $Sb^{5+}/Sb^{3+}$in the film. Annealing at nitrogen atmosphere leads to the reduction of $Sn^{4+}$ as well as $Sb^{5+}$ resulting in decrease of the electrical resistivity of the film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.361-364
• /
• 2000

Antimony doped tin oxide (ATO) thin films were deposited at room temperature by reactive ion-beam sputter deposition (IBSD) technique in oxidizing atmosphere utilizing Sb and Sn metal targets. Effect of Sb doping concentration, film thickness and heat treatment on electrical and optical properties was investigated. The thickness of as-deposited films was controlled approximately to 1500 $\AA$ or 2000$\AA$, and Sb concentration to 10.8 and 14.9 wt%, as determined by SEM and XPS analyses. Heat treatment was performed at the temperature from 40$0^{\circ}C$ to 80$0^{\circ}C$ in flowing $O_2$or forming gas. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition, thickness and firing condition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.5
• /
• pp.230-234
• /
• 2013

IR cut-off thin films consisted of ATO nanoparticles were successfully fabricated by sol-gel method. The coating solution was synthesized with organic/inorganic hybrid binder and ATO colloidal solution and ATO thin films were coated on a slide glass with the withdrawal speed of 5~40 mm/s. As the withdrawal speed increased from 5 mm/s to 40 mm/s, the thickness of coating thin films also increased from $1.05{\mu}m$ to $4.25{\mu}m$ and the IR cut-off in wavelength of 780~2500 nm increased from 49.5 % to 66.7 %. In addition, the pencil hardness of ATO thin films dried at $80^{\circ}C$ was ca. 5H and the coating films were not removed after a cross cutter tape test because of the hybrid binder synthesized with tetraethylorthosilicate and methyltrimethoxysilane. The surface morphologies, optical properties and film thickness of prepared thin films with a different withdrawal speed were measured by field emission scanning electron microscope (FE-SEM), UV-Vis spectrophotometer, and Dektak.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.307-310
• /
• 2000

Antimony doped tin oxide (ATO) thin films were deposited at room temperature by ion-beam sputter deposition (IBSD) technique in oxidizing atmosphere utilizing Sb and Sn metal targets. Effect of Sb doping concentration, film thickness and heat treatment on electrical and optical properties was investigated. The thickness of as-deposited films was controlled approximately to $1500{\AA}$ or $2000{\AA}$, and Sb concentration to 10.8 and 14.9 wt%, as determined by SEM and XPS analyses. Heat treatment was performed at the temperature from $400^{\circ}C$ to $600^{\circ}C$ in flowing $O_2$ or forming gas. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition, thickness and firing condition.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1025-1032
• /
• 2000

산화분위기에서의 반응성 이온빔 스퍼터링법으로 Sn과 Sb 금속 타겟을 사용하여 실온에서 ATO 박막을 증착하였다. Sb 첨가량, 박막의 두께 및 열처리가 ATO 박막의 전기적 특성과 광학적 특성에 미치는 효과를 연구하고자 하였다. 제조된 ATO 박막의 두께는 약 1500$\AA$과 1000$\AA$으로 조절하였으며, Sb 농도는 10.8wt% 또는 14.9wt%임이 XPS 분석에 의하여 확인되었다. 증착한 박막의 열처리는 40$0^{\circ}C$~$600^{\circ}C$의 온도범위에서 산소 또는 forming gas(10% H$_2$-90% Ar) 분위기에서 30분간 수행하였다. 이렇게 제조된 ATO 박막은 Sb의 첨가량, 두께 및 열처리 조건에 따라 다양한 전기 비저항 값과 가시광선 대역에서의 광투과도를 나타내었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.256-261
• /
• 2009

Hydrophilic and transparent $TiO_2$ thin film was fabricated by sol-gel method and the properties of contact angle, surface morphology, and transmittance were measured. In addition, surfactant Tween 80 was used for increasing the hydrophilic property of thin film. When the contents of Tween 80 in $TiO_2$ solution was 0, 10, 30, 50wt%, the contact angles of $TiO_2$ thin film were $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$, respectively. Fabricated $TiO_2$ thin film showed the photocatalytic property that decomposed methylene blue and decreased the absorbance of solution after UV irradiation. $TiO_2$ thin films fabricated with the solution of 30 wt% Tween 80 were deposited on glass (bare), antimony tin oxide (ATO), fluorine tin oxide (FTO), indium tin oxide (ITO) coated glass substrates, and the contact angle and transmittance of thin film was measured. The contact angles of thin films deposited on four substrates were $16.2\sim27.1^{\circ}$ and was decreased to the range of $13.2\sim17.6^{\circ}$ after UV irradiation, Especially, the thin films coated on ATO and FTO glass substrate showed high transmittance of 74.6% in visible range, respectively, and low transmittance of 54.2% and 40.4% in infrared range, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.192-195
• /
• 2000

Antimony doped tin oxyde thin films have been deposited by sol-gel method using non-alkoxide precursor SnCl$_2$$.$2H$_2$O as host and SbC1$_3$ as dopant material. Using spin coating method, thin films of thickness up to 200nm have been uniformly deposited on Corning 1737F non-alkali glass substrates. Effect of Sb doping concentration and heat treatment on electrical and optical properties was investigated. Heat treatment was performed at the temperature from 350$^{\circ}C$ to 650$^{\circ}C$ in flowing O$_2$. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition and firing condition.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.5
• /
• pp.241-244
• /
• 2012

Antimony doped tin oxide (ATO) thin films on glass substrate were prepared by the chemical solution deposition (CSD) method, using sol-gel solution synthesized by non-alkoxide precursors and the sol-gel route. The crystallinity and electrical properties of ATO thin films were investigated as a function of the annealing condition (both annealing environments and temperatures), and antimony (Sb) doping concentration. Electrical resistivity, carrier concentration, Hall mobility and optical transmittance of ATO thin films were improved by Sb doping up to 5~8 mol% and annealing in a low vacuum atmosphere, compared to the undoped tin oxide counterpart. 5 mol% Sb doped ATO film annealed at $550^{\circ}C$ in a low vacuum atmosphere showed the highest electrical properties, with electrical resistivity of about $8{\sim}10{\times}10^{-3}{\Omega}{\cdot}cm$, and optical transmittance of ~85% in the visible range. Our research demonstrates the feasibility of low-cost solution-processed transparent conductive oxide thin films, by controlling the appropriate doping concentration and annealing conditions.