• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.267-267
• /
• 2012

$TiO_2$-Ni inverse catalysts were prepared using atomic layer deposition (ALD) process and catalytic $CO_2$ reforming of methane (CRM) reaction over catalysts (either bare Ni or $TiO_2$ coated-Ni particles) were performed using a continuous flow reactor at $800^{\circ}C$. $TiO_2$-Ni inverse catalyst showed higher catalytic reactivity at initial stage of CRM reactions at $800^{\circ}C$ comparing to bare Ni catalysts. Moreover, catalytic activity of $TiO_2$/Ni catalyst was kept high during 13 hrs of the CRM reactions at $800^{\circ}C$, whereas deactivation of bare Ni surface was started within 1hr under same conditions. The results of surface analysis using SEM, XPS, and Raman showed that deposition of graphitic carbon was effectively suppressed in a presence of $TiO_2$ nanoparticles on Ni surface, thereby improving catalytic reactivity and stability of $TiO_2$/Ni catalytic systems. We suggest that utilizing decoration effect of metal catalyst with oxide nanoaprticles is of great potential to develop metal-based catalysts with high stability and reactivity.

• Textile Coloration and Finishing
• /
• v.15 no.3
• /
• pp.161-167
• /
• 2003

The preparations of deodorizing fibers using $TiO_2$ have been investigated. The fibers were coated with $TiO_2$ for the purpose of deodorizing by dipping fibers into the $TiO_2$ sol solutions and calcined at $450^\circ{C}$, $500^\circ{C}$ and $750^\circ{C}$ for 1 h after coating. The surface structure of the coated fibers was studied with XRD on the different preparation conditions of calcination temperatures. The deodorizing function of the prepared fibers was studied by the determination of the decomposing capability for $NH_3,\;CH_3SH\;and\;CH_3CHO$. The deodorant activity(D.A.) of these deodoriBing fibers was measured by chromogenic gas detector tubes. The deodorizing effect of the prepared fibers were shown to be similar for the three model compounds; 5wt% $TiO_2$ sol solution calcined at $450^\circ{C}$ < 5 wt% $TiO_2$ sol solution calcined at $500^\circ{C}$< 5 wt% TiO$_2$ sol solution calcined at $750^\circ{C}$.

• Journal of the Semiconductor & Display Technology
• /
• v.23 no.1
• /
• pp.1-6
• /
• 2024

Recently, artificial neural networks have been playing a crucial role and advancing across various fields. Artificial neural networks are typically categorized into feedforward neural networks and recurrent neural networks. However, feedforward neural networks are primarily used for processing static spatial patterns such as image recognition and object detection. They are not suitable for handling temporal signals. Recurrent neural networks, on the other hand, face the challenges of complex training procedures and requiring significant computational power. In this paper, we propose memristors suitable for an advanced form of recurrent neural networks called reservoir computing systems, utilizing a mask processor. Using the characteristic equations of Ti/TiOx/TaOy/Pt, Pt/TiOx/Pt, and Ag/ZnO-NW/Pt memristors, we generated current-voltage curves to verify their memristive behavior through the confirmation of hysteresis. Subsequently, we trained and inferred reservoir computing systems using these memristors with the NIST TI-46 database. Among these systems, the accuracy of the reservoir computing system based on Ti/TiOx/TaOy/Pt memristors reached 99%, confirming the Ti/TiOx/TaOy/Pt memristor structure's suitability for inferring speech recognition tasks.

• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.270-276
• /
• 1999

Ti-Ni-Cu alloy powders were fabricated by ball milling, and the properties of these powders were characterized. Mixed 50Ti-(50-x)Ni-xCu powders of 5 to 10at.%Cu composition were milled for 100 hours using SUS 1/4" balls in argon atmosphere. Ball to powder ratio was 20:1 and rotating speed was 100 rpm. Tensile strength, microstructure and phase transformation of ball milled Ti-(50-x)Ni-xCu powders were studied. After 100 hours milling, Ti, Ni and Cu elements were alloyed completely and an amorphous phase was formed. Amorphous phase was crystallized to martensite(B 19') and austenite(B2) after heat treatment for 1 hour at $850^{\circ}C$. As the Cu contents were increased, tensile strength of extruded 6061Al/TiNiCu was decreased, and B19'martensite phases In the TiNi particles were the causes of high tensile stress of extruded 6061Al/TiNiCu.NiCu.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.122-127
• /
• 2003

Ti - Si - N hard films were deposited on SKD11 steel substrates by a hybrid deposition system, where TiN was deposited by AIP method while Si was incorporated by sputtering one. The microstructure of Ti-Si-N films was revealed to be a composite of TiN crystallites and amorphous Si3N4 by instrumental analyses. The highest hardness value of about 45 Gpa was obtained at the Si content of around 7.7 at.%. With increase of Si content, the size of TiN crystallites was reduced and their distribution was changed from aligned to randomly orientated states. Surface roughness of Ti-Si-N film also decreased with increase of Si content.

• Journal of the Korean Ceramic Society
• /
• v.29 no.3
• /
• pp.211-215
• /
• 1992

Crack free PbTiO3 ceramics were produced by sol-gel processing using alkoxide, which has not been reported to be successful. The PbTiO3 gels were prepared from Ti alkoxide and lead acetate without any dopants. They were calcined at $600^{\circ}C$ and miled to produce fine PbTiO3 powder. It was pressed into discs and they were sintered at 110$0^{\circ}C$ for a few hours. The sintered ceramics were relativley hard and dense as having about 96% of theoretical density of PbTiO3. Fabrication of pure PbTiO3 ceramics by sol-gel processing is possibly due to their small grain size and uniform distribution of residual stress created during cubic-tetragonal transition over large number of small grains in fine grain PbTiO3 ceramics.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.512-518
• /
• 1997

The high temperature oxidation behaviors of titanium nitride films prepared by PACVD technique were studied in the temperature range of from 50$0^{\circ}C$ to 80$0^{\circ}C$ under air atmosphere. Ti0.88Al0.12N film, which showed the excellent microhardness from the previous work, was investigated on its oxidation resistance compared with pure TiN film. Ti-Al-N film showed superior oxidation resistance up to $700^{\circ}C$, whereas TiN film was fast oxidized into rutile TiO2 crystallites from at 50$0^{\circ}C$. It was found that an amorphous layer having AlxTiyOz formula was formed on the surface region due to outward diffusion of Al ions at the initial stage of oxidation. The amorphous oxide layer played a role as a barrier against oxygen diffusion, protected the remained nitride layer from further oxidation, and thus, resulted in the high oxidation resistive characteristics of Ti-Al-N film.

• Journal of the Korean Ceramic Society
• /
• v.27 no.7
• /
• pp.916-924
• /
• 1990

The preparatin of the fine TiN powders by reduction-nitridation of TiCl3-Al-N2 system was attempted in the temperature range from 350$^{\circ}$to 100$0^{\circ}C$. The formation mechanism and kinetics of TiN were examined, and the resultant TiN powder was characterized by means of XRD, PSA and SEM-EPMA methods. TiN was formed at temperatrue higher than $600^{\circ}C$. As an intermediate phase, AlTi was obtained. The apparent activation energy for the formation of TiN was approximately 4.2kcal/mole(600$^{\circ}$~90$0^{\circ}C$). The crystallite size and lattice constnat of TiN powder obtained in the temperature range from 600$^{\circ}$to 100$0^{\circ}C$ for 2h at the Al/TiCl3 molar ratio of 1.0 were 160~255A and 4.231~4.239A, respectively. According to PSA measurement, the mean particle size ranged from 14.0 to 14.8${\mu}{\textrm}{m}$.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.345-356
• /
• 1995

본 연구에서는 TiAl 금속간 화합물을 자전 고온 반응법을 이용하여 제조시 반응과정을 열시차 분석 방법으로 분석하였다. 합금 조성은 Ti-45at% Al, 53at%Al, 알루미늄 분말 크기, 승온 속도, 성형 밀도 등을 변화시켜 이들이 반응 과정에 미치는 영향을 관찰하였다. 분말이 미세할수록, 승온속도가 느릴수록, 성형 밀도가 낮을수록 반응 점화 온도 및 연소 온도가 감소하였으며, 고상 Ti와 고상 Al간의 반응정도가 증가하는 것이 관찰되었다. 고상 Ti와 고상 Al간의 반응에서 생성되는 것은 XRD 분석 결과 Ti$Al_{3}$상으로 확인되었다. 이에 비하여 반응 점화 온도가 알루미늄의 용융 온도보가 높을 경우에는 생성되는 상이 $Ti_{3}$Al, TiAl상으로 확인되었다. 이러한 상의 생성 원인에 대하여 확산 계수 및 알루미늄의 용해도등의 요인으로 설명하였다.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.4
• /
• pp.193-198
• /
• 2002

Alloys of XD45 (Ti45A12Nb2Mn-0.8vol%TiB$_2$) and XD47 (Ti47A12Nb2Mn-0.8vol%TiB$_2$) were oxidized between 800 and $1000^{\circ}C$ in air, and their oxidation characteristics were studied. The oxide scales consisted primarily of an outer $TiO_2$ layer, an intermediate $Al_2$$O_3$-rich layer, and an inner mixed layer of ($TiO_2$+$Al_2$$O_3$). Nb tended to present at the lower part of the oxide scale, whereas Mn at the upper part of the oxide scale. The Pt marker tests indicated that the outer oxide layer grew primarily by the outward diffusion of Ti and Mn, and the inner mixed layer by the inward transport of oxygen.