• Journal of Ocean Engineering and Technology
• /
• v.20 no.5 s.72
• /
• pp.82-88
• /
• 2006

This assessment is concerned with the fatigue strength of the tendon porch found in TLP. Lorge-scale fatigue tests with models constructed at 30% the size of the real structures have been carried out to investigate the fatigue behavior of the API 2W Grade 50 steel recently produced by POSCO. The fatigue life for the present test models was obtained based on the concept of nominal stress. A comparison of the present test results with those obtained by a numerical approach based on the structural analysis results has showngood agreement. The present results were also compared with the design curves in DnV RP-C203.

• Journal of the Korea Safety Management & Science
• /
• v.6 no.4
• /
• pp.239-248
• /
• 2004

Likelihood of failure for the external corrosion of carbon and low alloy steels, which affect to a risk of facilities, was analyzed quantitatively through the risk based inspection using API-581 BRD. We found that the technical module subfactor (TMSF) decreased as the inspection number increased and it increased as the Inspection effectiveness and the used year increased. In this condition, the TMSF showed high value for the case of the marine/cooling tower drift area as a corrosion driver, poor quality of coating, no insulation, and low insulation condition.

• Journal of Korean Society of Steel Construction
• /
• v.28 no.3
• /
• pp.195-202
• /
• 2016

In this study, it is carried out to analyze the international design standards such as Eurocode 8, API 650, NZSEE and etc for the seismic design of steel liquid storage tanks. From the comparison and analysis, the data for the required parameters and factors are provided for the establishment of Korean seismic design standard for steel liquid storage tanks. The simplified mechanical models have been presented for the seismic design of steel liquid storage tanks in all design standards and the parameters of mechanical models in design standards have similar values. Although the models for the seismic design of steel liquid storage tanks are similar in design standards, design approaches are given differently in accordance with the design methods, allowable stress design or limit state design. Therefore it is not easy to compare seismic forces presented in design standards directly. After comparison of design standards, it is concluded that establishment of Korean design standard for the seismic design of steel liquid storage tanks is necessary.

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.146-149
• /
• 2001

• Corrosion Science and Technology
• /
• v.17 no.3
• /
• pp.109-115
• /
• 2018

Electrical Resistance Welding (ERW) on a longitudinal seam-welded pipe has been extensively used in oil and gas pipelines. It is well known that the weld zone commonly suffers from grooving corrosion in ERW pipes. In this paper, the grooving corrosion performances of API X65 grade non-sour service (steel-A) and API X70 grade sour gas resistant (steel-B) steel electrical resistance welding pipelines were evaluated. The microstructure of the bondline is composed of coarse polygonal ferrite grains and several elongated pearlites. The elongated pattern is mainly concentrated in the center of the welded area. The grooving corrosion test and electrochemical polarization test were conducted to study the corrosion behavior of the given materials. A V-shaped corrosion groove was found at the center of the fusion zone in both the steel-A and steel-B ERW pipes, as the corrosion rate of the bondlines is higher than that of the base metal. Furthermore, the higher volume fraction of pearlite at the bondline was responsible for the higher corrosion rate at the bondline of both types of steel.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.401-407
• /
• 2004

This study is on the constant-current stress corrosion test related to the load stress in welded zone and non-welded zone of high tensile strength steel for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed global corrosion and narrow pitting, and the pitting was increased by increasing the load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel for natural gas transmission specimens was decreased suddenly, and the average relative electrode potential was higher and the average relative current was lower in welded zone than base metal. and the average relative electrode potential was decreased by increasing the load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone than base metal, and the corrosion rate was decreased by increasing the load stress.

• International Journal of Ocean System Engineering
• /
• v.2 no.3
• /
• pp.160-169
• /
• 2012

Flux Cored Arc Welding (FCAW) is a common practice to join thick plates such as the structural members of large scale offshore structures and very large container ships. The objective of this study was to investigate the mechanical properties and variability of the fatigue crack initiation life in the flux cored arc welded API 2W Gr.50 steel joints typically applied to offshore structures with a focus on the effect of the materials in fatigue crack growth life from the notch root of a compact tension specimen. Offshore structural steel (API 2W Gr.50) plates (60-mm thick) were used to fabricate multi-path flux core arc welded butt welded joints to clearly consider fatigue fractures at the weld zone from the notch. Fatigue tests were performed under a constant amplitude cyclic loading of R = 0.4. The mean fatigue crack initiation life of the HAZ specimen was the highest among the base metal (BM), weld metal (WM), and heat affected zone (HAZ). In addition, the coefficient of variation was the highest in the WMl specimen. The variability of the short fatigue crack growth rates from the notch tips in the WM and HAZ specimens was higher than in BM.

• Journal of Ocean Engineering and Technology
• /
• v.18 no.5
• /
• pp.50-56
• /
• 2004

This study is on the constant-current stress corrosion test, related to the load stress, in both the welded and non-welded zones of high tensile strength steel that is used for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed general corrosion and narrow pitting, and the pitting was increased with load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel, used for natural gas transmission specimens, were decreased rapidly, and the average relative electrode potential was higher and the average relative current was lower in welded zone, compared to base metal. The average relative electrode potential was decreased with load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone, compared to base metal, and the corrosion rate was decreased by increasing the load stress.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.766-773
• /
• 2011

In this study, three kinds of linepipe steels were processed by changing the amount of Mo and Nb to investigate the effects on microstructures, tensile and Charpy impact properties. All the specimens consisted of acicular ferrite, granular bainite and secondary phases such as martensite and austenite constituents (MA). The increase in Mo raised the volume fractions of the granular bainite and MA, and raised the number of fine precipitates, which increased the yield and tensile strengths and decreased the upper self energy and energy transition temperatures. In the steel having less Mo and more Nb, the volume fractions of the granular bainite and MA decreased, and a finer microstructure was observed. This microstructure suppressed the formation of separation during Charpy impact testing and led to a higher upper shelf energy and lower energy transition temperature, while the yield and tensile strengths were lower than those of the steels with more Mo and less Nb.

• Korean Journal of Materials Research
• /
• v.33 no.6
• /
• pp.251-256
• /
• 2023

This study aims to examine the correlation between microstructures and the mechanical properties of two high-strength API X70 linepipe steels with different specimen directions and Moaddition. The microstructure of the Mo-added steel has an irregularly shaped AF, GB matrix with pearlite because of the relatively large deformation in the non-recrystallization temperature region, while that of the Mo-free steel shows a PF matrix with bainitic microstructure. In the Mo-added steel, the M/A (martensite-austenite) in granular bainite (GB) and pearlite act as crack initiation sites with decreased upper shelf energy and an increased ductile to brittle transition temperature (DBTT). Regardless of Mo addition, all of the steels demonstrate higher strength and lower elongation in the T direction than in the L direction because of the short dislocation glide path and ease of pile-up at grain boundaries. In addition, the impact test specimens with T-L direction had a lower impact absorbed energy and higher DBTT than those with the L-T direction because the former exhibit shorter unit crack path compared to the latter.