• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.11
• /
• pp.7910-7916
• /
• 2015

This paper examines the mechanical and autogenous shrinkage characteristics per curing condition of Ultra High Performance Concrete (UHPC) according to the change in the quantities of expansive admixture and shrinkage-reducing agent. In view of the mechanical properties according to the curing condition, all the UHPC specimens that experienced steam curing at $90^{\circ}C$ developed compressive strength higher than 190 MPa, and the specimens that experienced water curing at $20^{\circ}C$ developed compressive strength comparable to that developed at 91 days by the steam-cured specimens. The specimens steam-cured at $90^{\circ}C$ showed high tensile strength of 23.4 MPa whereas slight loss of the tensile strength was observed in those water-cured at 20. Besides, in view of the autogenous shrinkage according to the curing condition, no particular change could be found in the final shrinkage. The compressive strength developed by UHPC according to the use of expansive and shrinkage-reducing agents reached values higher than 190 MPa in case of steam curing at $90^{\circ}C$. Shrinkage reduced by about 45% when using both expansive and shrinkage-reducing agents without difference according to the curing condition.

• International Journal of Highway Engineering
• /
• v.20 no.3
• /
• pp.39-46
• /
• 2018

PURPOSES: This study is to estimate nondestructive strength equation based on probability for bridges using field test data. METHODS : In this study, a series of the field inspection and the test have been performed on 297 existing bridges, in order to evaluate the bridges, based on the test results of the in-depth inspection, and the estimated strengths by means of the nondestructive strength equations are analyzed and compared with results of the core specimen strengths. RESULTS : According to results of analyses, In case of standard design compressive strength of concrete is 18MPa, 21MPa, similar reliability of RILEM equation were 0.89~0.90, but in case of standard design compressive strength of concrete is 35MPa, 40MPa were 0.4~0.56. According to standard design compressive strength of concrete is 40MPa, similar reliability of ultrasonic pulse velocity method equation were 0.56. CONCLUSIONS :RILEM equation had high similar reliability than other equation in case of standard design compressive strength of concrete is 18MPa, 21MPa, but had low similar reliability than other equation in case of standard design compressive strength of concrete is 35MPa, 40MPa. and ultrasonic pulse velocity method equation had low similar reliability than other equation in case of standard design compressive strength of concrete is 40MPa.

• Journal of the Korean Magnetics Society
• /
• v.20 no.1
• /
• pp.8-12
• /
• 2010

The magnetostriction and stress of multilayer $NiFeCr/(Cu/Co_{90}Fe_{10}){\times}N/NiFeCr$ films were investigated. As the number of Cu $15{\AA}$/CoFe $15{\AA}$ bilayers was increased, the saturation magnetostriction decreased from $-5.6\times10^{-6}$ at 2 bilayers to $-8.5\times10^{-6}$ at 20 bilayers. A change of CoFe thickness from 10 to $20{\AA}$ caused a decrease in the magnitude of tensile stress from 980MPa to 590MPa as the number of Cu $15{\AA}$/CoFe $15{\AA}$ bilayers increased from 2 to 20. The maximum magnetostrictive anisotropy field that could be developed due to nonzero magnetostriction and stress is calculated to be 135.7 Oe when the number of Cu $15{\AA}$/CoFe $15{\AA}$ bilayers is 10.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.39 no.1
• /
• pp.90-95
• /
• 2011

A Kick Motor, KSLV-I second stage propulsion system, utilizes a flexible seal for pitch and yaw axis controls during combustion. A flexible seal consists of the alternate laminate of rubber and composite reinforcement between forward and aft rings. A Kick Motor nozzle is rotated by the shear deformation of rubber layers. Consequently, the development of rubber, which is appropriate to the usage condition of flexible seal, is very important. A tensile test, QLS test (shear modulus and failure shear stress), and aging test have been carried out to confirm the performance of rubber developed. Test results show that the shear modulus of rubber are 0.4310 ~ 0.4997MPa and the failure shear stress is more than 2.5MPa.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2004.11a
• /
• pp.98-99
• /
• 2004

(1) Using high-frequency induction heating sintering and spark plasma sintering method, the densification of WC-Ni hard materials was accomplished using ultra fine power of Ni and WC. (2) Nearly fully dense WC-Ni could be obtained within 1 min. (3) Relative density and mechanical properties of WC-Ni obtained by HFIHS were high than those obtained by SPS. And WC grain size made by HFIHS was smaller than that made by SPS. (4) The fracture toughness and hardness values of WC-8Ni, WC-10Ni, and WC-12Ni made by HFIHS were $13MPa{\cdot}m^{1/2}\;and\;1950kg/mm^2,\;13.5Mpa{\cdot}m^{1/2}\;and\;1810kg/mm^2,\;14.4MPa{\cdot}m^{1/2}\;and\;1690kg/mm^2$, respectively for 60MPa and an induced current for 90% output of total capacity, 15KW. (5) The fracture toughness and hardness values of WC-8Ni, WC-10Ni, and WC-12Ni made by SPS were $12.2MPa{\cdot}m^{1/2}\;and\;1796kg/mm^2,\;12.9MPa{\cdot}m^{1/2}\;and\;1725kg/mm^2,\;13.6MPa{\cdot}m^{1/2}\;and\;1597kg/mm^2$, respectively for 60MPa and the electric current of 2500 A

• Clean Technology
• /
• v.17 no.2
• /
• pp.110-116
• /
• 2011

The dyeing of polyester fiber with two different disperse dyes (Disperse Red 60 and Disperse Yellow 54) was carried out using supercritical carbon dioxide ($SCCO_2$) as a dyeing medium at temperatures ranging from $50^{\circ}C$ to $90^{\circ}C$ and at pressures from 15 MPa to 30 MPa. The dye uptake of Disperse Red 60 on polyester fiber was found to increase with temperature at constant pressure and $SCCO_2$ density (700 kg/$m^3$). At $90^{\circ}C$ and 30 MPa, the dye uptake on polyester fiber increased with dyeing time and the saturation concentration of Red 60 was attained within 240 min, while a longer dyeing time was required for Yellow 54 to reach its saturation concentration. When dyestuff mixtures with mixing ratios of 0.01 to 9.0 (Red 60/Yellow 54) were used, the uptake ratio of the two dyes was found to be proportional to 0.26 power of their mixing ratio. Dyed fibers showed an orange color and the depth of the color depended upon the mixing ratio of the dyestuffs.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.231-236
• /
• 1988

In order to investigate the effect of second phase on $Al_2O_3$ matrix, SiC particles were dispersed in $Al_2O_3$ matrix as a second phase over the content range of 5 vol.% to 20 vol.%. To this mixture, $Y_2O_3$ or $TiO_2$ powders were added as a sintering additive before isostatically pressing and pressurelessly sintering at 180$0^{\circ}C$ for 90 min in $N_2$ atmosphere. With increasing SiC content, relative densities of composites were decreased but mechanical properties of composites were improvjed. In the case of adding $Y_2O_3$ as a sintering additive, maximum values of flexural strength, hardness and fracture toughness were 525 MPa, 17.1 GPa, 4.1 MPa.m1/2 respectively. In the case of adding X$TiO_2$ as a sintering additive, maximum values of flexural strength, hardness were 285 MPa, 12.1 GPa respectively. Improved mechanical properties were found to be the results of grain growth control of $Al_2O_3$ matrix and crack deflection by the second phase SiC particles.

• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.278-282
• /
• 2001

The recombination motion of Partial dislocations on basal slip (0001) 1/3<1120> in sapphire ($\alpha$-Al$_2$$O_3$) single crystals was investigated using the four-point bending test with the prism plane (1120) samples. These bending experiments were carried but in the temperature range from $1200^{\circ}C$ to $1400^{\circ}C$ at various engineering stresses 90MPa, 120MPa, and 150MPa. During these tests it was shown that an incubation time was needed for basal slip to be activated. The activation energy for the incubation time was 5.6-6.0eV in the temperature range from $1200^{\circ}C$ to $1400^{\circ}C$. The incubation time is believed to be related to recombination of climb dissociated partial dislocations via self-climb. In addition, these activation energies are nearly same as those for oxygen self-diffusion in $Al_2$$O_3$ (approximately 6.3 eV). Thus, the recombination of the two partial dislocations would be possibly controlled by oxygen diffusion on the stacking fault between the partials.

• Korean Journal of Materials Research
• /
• v.11 no.3
• /
• pp.221-226
• /
• 2001

The basal slip (0001)1/3<1120 > dislocation velocity in sapphire ($\alpha$-$Al_2$$O_3$) single crystals was measured by four-point bending test. The bending experiment was carried out in the temperature range from 120$0^{\circ}C$ to $1400^{\circ}C$ at various engineering stresses 90MPa, 120MPa, and 150MPa. The velocity of such dislocations was estimated from the bending displacement rate of the four-point bend sample. The dependence of temperature and stress in dislocation velocity was investigated. The activation energy for dislocation velocity was determined to be about 2.2$\pm$0.4eV. In addition, the stress exponent (m) describing the stress dependence of dislocation velocities was in the range of 2.0$\pm$0.2.

• The Journal of the Korea Contents Association
• /
• v.21 no.3
• /
• pp.602-608
• /
• 2021

For the comparison of bond strength between the Co-Cr alloy and ceramic, which are clinically used, test samples made with a traditional casting method as a control group), and Milling and SLM(3d printing group) samples were made as an experimental group. The metal-ceramic bond strength was measured with a universal testing machine. For the measurement, a three-point bending test was conducted. After the bond strength was measured, metal-ceramic interface was observed. According to the test result, casting group had 53.59 MPa, milling group had 45.90 MPa, and 3d printing group had 58.34 MPa. There was no statistical significance. With regard to failure pattern, most of the samples in two groups, showed mixed failure. This study showed a clinically applicable value when measuring the bond strength of alloy-ceramic material with an alloy produced by 3D printing.