• Journal of Welding and Joining
• /
• v.15 no.5
• /
• pp.56-63
• /
• 1997

In The study, the bonding of WC-9%Co to SUJ2 steel using Ag-Cu-Zn-Cd insert metal has performed to investigate the bonding properties by heat-treatment. Bonding was brazed for 5-30min at 95$0^{\circ}C$, performed solution treatment for 5 min at 85$0^{\circ}C$ and sustained subsequently oil quenching. To investigate the effect of heat-treatment, tempering was executed at $600^{\circ}C$ for 30 min after oil quenching. Mechnical properties and chemical compositions on the brazed bonding interface were investigated by means of microstructural observation, 4-point bending test and EDS and XRD measurements. The results obtained were as follows. 1) The bonding strength of WC-9%Co/SUJ2 joints by Ag-Cu-Zn-Cd insert metal obtained about 78, 117 and 72MPa after brazing for 5, 20 and 30 min at 95$0^{\circ}C$. And the highest bonding strength obtained about 131MPa after brazing for10 min at 95$0^{\circ}C$ 2) Higher bonding strength of 288MPa was obtained in the joint that brazed for 10 min at 95$0^{\circ}C$, and carried out tempering for 30 min at $600^{\circ}C$ subsequently. 3) Fracture of joint brazed by Ag-Cu-Zn-Cd insert metal for 5, 10, 20 and 30 min created WC-9%Co/SUJ2 interface. The joint that brazed for 10 min at 95$0^{\circ}C$ and then tempered for 30 min at $600^{\circ}C$ was fractured at the site of WC-9%Co.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.161-164
• /
• 2008

In recent years, carbon fiber-reinforced polymer (CFRP) has been widely used for repairing and/or strengthening structural elements in concrete. Not enough test data, however, are available to predict the long-term performance of the repaired and improved structures exposed to weathering. The objective of this research is to study the effect of freeze-thaw cycling on the behavior of reinforced concrete (RC) beams strengthened in shear with carbon fiber sheet. Six small-scale RC beams (100mm${\times]$100mm${\times]$400mm) were strengthened with CFRP in shear, subjected to up to 400 cycles freeze-thawing from -17${\sim}4^{\circ}C$, and tested to failure in four-point bending. Test result, there was no significant damage to carbon fiber sheet strengthened concrete beams had been suffered 30 cycles of freeze-thawing, and more over 60 cycles of freezing-thawing brought about a reduction in resistance of only 25% of the initial level.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.25-35
• /
• 2011

Purpose: There are some advantages of the acrylic resin denture base ; appropriate strength, volume safety, simple processing apparatus, and low cost. But, it have a weakness for fracture by intense pressure or shock. However, the repairs for resin denture base are possible using various materials and techniques. There is a few studies in repairs for resin denture base, but not clinical researches. And there is no studies in absorbed saliva into the region of fracture and bond strength. This study is to observe re-bond strength of resin denture base after repairing under saliva absorption. Methods: The samples were made of heat curing resin and the rectangular parallelepiped specimens which were 50mm long, 10mm wide and 3mm high. The four different groups immersed in the artificial saliva for 2 weeks were prepared, 1) no repaired control samples, 2) immediately repaired samples, 3) repaired samples after 1 day dry, and 4) repaired samples after 3 days dry. The prepared samples were repaired by two different curing materials, self curing resin and heat curing resin method. Each groups composed of 10 specimens were experimented with the three point bending tests for bonding strength measuring Results: There were under condition absorbed in the artificial saliva and repaired by self curing resin method, repaired specimens after 1 day and 3 days dry groups had higher values of bonding strengths than control group, and bonding strengths of immediately repaired samples were similar to those of control samples (p<0.05). There were under condition immersed in the artificial saliva and repaired by heat curing resin method, immediately repaired samples showed similar values to bonding strengths of control groups, and repaired samples after 1 day and 3 days dry groups were lower than those of control group (p>0.05). Conclusion: In this study, the repairs for resin denture base were remarkably high values of bonding strengths than those of the past, and showed that have stable bonding strengths independent of saliva absorption of denture base, so present repairs for resin denture base can be performed, regardless of saliva conditions.

• International Journal of Concrete Structures and Materials
• /
• v.11 no.2
• /
• pp.215-228
• /
• 2017

A new approach for measuring the specific fracture energy of concrete denoted modified disk-shaped compact tension (MDCT) test is presented. The procedure is based on previous ideas regarding the use of compact tension specimens for studying the fracture behavior of concrete but implies significant modifications of the specimen morphology in order to avoid premature failures (such as the breakage of concrete around the pulling load holes). The manufacturing and test performance is improved and simplified, enhancing the reliability of the material characterization. MDCT specimens are particularly suitable when fracture properties of already casted concrete structures are required. To evaluate the applicability of the MDCT test to estimate the size-independent specific fracture energy of concrete ($G_F$),the interaction between the fracture process zone of concrete andthe boundary of theMDCTspecimens at the end of the test is properly analyzed. Further, the experimental results of $G_F$ obtained by MDCT tests for normal- and high-strength self-compacting concrete mixes are compared with those obtained using the well-established three-point bending test. The procedure proposed furnishes promising results, and the $G_F$ values obtained are reliable enough for the specimen size range studied in this work.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.2
• /
• pp.133-139
• /
• 2013

PURPOSE. This study was to evaluate the effect of the solution temperature on the mechanical properties of dualcure resin cements. MATERIALS AND METHODS. For the study, five dual-cure resin cements were chosen and light cured. To evaluate the effect of temperature on the specimens, the light-cured specimens were immersed in deionized water at three different temperatures (4, 37 and $60^{\circ}C$) for 7 days. The control specimens were aged in a $37^{\circ}C$ dry and dark chamber for 24 hours. The mechanical properties of the light-cured specimens were evaluated using the Vickers hardness test, three-point bending test, and compression test, respectively. Both flexural and compressive properties were evaluated using a universal testing machine. The data were analyzed using a two way ANOVA with Tukey test to perform multiple comparisons (${\alpha}$=0.05). RESULTS. After immersion, the specimens showed significantly different microhardness, flexural, and compressive properties compared to the control case regardless of solution temperatures. Depending on the resin brand, the microhardness difference between the top and bottom surfaces ranged approximately 3.3-12.2%. Among the specimens, BisCem and Calibra showed the highest and lowest decrease of flexural strength, respectively. Also, Calibra and Multilink Automix showed the highest and lowest decrease of compressive strength, respectively compared to the control case. CONCLUSION. The examined dual-cure resin cements had compatible flexural and compressive properties with most methacrylate-based composite resins and the underlying dentin regardless of solution temperature. However, the effect of the solution temperature on the mechanical properties was not consistent and depended more on the resin brand.

• Journal of the Korean Ceramic Society
• /
• v.44 no.7
• /
• pp.343-348
• /
• 2007

Alumina/silver nanocomposites were fabricated using a soaking method through a sol-gel route to construct an intra-type nanostructure. The pulse electric-current sintering (PECS) technique was used to sinter the nanocomposites. Several specimens were annealed after sintering. The microstructure, mechanical properties, critical frontal process zone (FPZ) size, and thermo-mechanical properties of the nanocomposites were estimated. The relative densities of the specimens sintered at 1350 and $1450^{\circ}C$ were 95% and 99%, respectively. The maximum value of the three-point bending strength was found to be 780 MPa for the $2{\times}2{\times}10 mm$ specimen sintered at $1350^{\circ}C$. The fracture toughness of the specimen sintered at $1350^{\circ}C$ was measured to be $3.60 MPa{\cdot}m^{1/2}$ using the single-edge V-notched beam (SEVNB) technique. The fracture mode of the nanocomposites was transgranular, in contrast to the intergranular mode of monolithic alumina. The fracture morphology suggested that dislocations were generated around the silver nanoparticles dispersed within the alumina matrix. The specimens sintered at $1350^{\circ}C$ were annealed at $800^{\circ}C$ for 5 min, following which the maximum fracture strength became 810 MPa and the fracture toughness improved to $4.21 MPam^{1/2}$. The critical FPZ size was the largest for the specimen annealed at $800^{\circ}C$ for 5 min. Thermal conductivity of the alumina/silver nanocomposites sintered at $1350^{\circ}C$ was 38 W/mK at room temperature, which was higher than the value obtained with the law of mixture.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• v.1
• /
• pp.379-384
• /
• 2006

Since the monolithic ceramic substrate was introduced for automotive catalytic converters, the durability of the substrate has been a continuing requirement to reduce the emission gas of vehicle. The substrate can occupy a volume as small as 82 $cm^3$ and as large as 8200 $cm^3$ to provide the required substrate for catalytic activity. The long-term durability varies with the size of the substrate from manufacture's point of view. Therefore This study presents that the response surface model using central composite design can explain size effect on the modulus of rupture in a cordierite ceramic monolithic substrate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.381-382
• /
• 2007

IZO/Ag/IZO (IAI) anode films for flexible organic light emitting diodes (OLEDs) were grown on PC (polycarbonate) substrate using DC sputter (IZO) and thermal evaporator (Ag) systems as a function of Ag thickness. To investigate electrical and optical properties of IAI stacked films, 4-point probe and UV/Vis spectrometer were used, respectively. From a IAI stacked film with 12nm-thick Ag, sheet resistance of $6.9\;{\Omega}/{\square}$ and transmittance of above 82 % at a range of 500-550 nm wavelength were obtained. In addition, structural and surface properties of IAI stacked films were analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscopy), respectively. Moreover, IAI stacked films showed dramatically improved mechanical properties when subjected to bending both as a function of number of cycles to a fixed radius. Finally, OLEDs fabricated on both flexible IAI stacked anode and conventional ITO/Glass were fabricated and, J-V-L characteristics of those OLEDs were compared by Keithley 2400.

• Korean Journal of Materials Research
• /
• v.30 no.5
• /
• pp.231-238
• /
• 2020

The composition of martensite transformation in NiAl alloy is determined using pure nickel and aluminum powder by vacuum hot press powder metallurgy, which is a composition of martensitic transformation, and the characteristics of martensitic transformation and microstructure of sintered NiAl alloys are investigated. The produced sintered alloys are presintered and hot pressed in vacuum; after homogenizing heat treatment at 1,273 K for 86.4 ks, they are water-cooled to produce NiAl sintered alloys having relative density of 99 % or more. As a result of observations of the microstructure of the sintered NiAl alloy specimens quenched in ice water after homogenization treatment at 1,273 K, it is found that specimens of all compositions consisted of two phases and voids. In addition, it is found that martensite transformation did not occur because surface fluctuation shapes did not appear inside the crystal grains with quenching at 1,273 K. As a result of examining the relationship between the density and composition after martensitic transformation of the sintered alloys, the density after transformation is found to have increased by about 1 % compared to before the transformation. As a result of examining the relationship between the hardness (Hv) at room temperature and the composition of the matrix phase and the martensite phase, the hardness of the martensite phase is found to be smaller than that of the matrix phase. As a result of examining the relationship between the temperature at which the shape recovery is completed by heating and the composition, the shape recovery temperature is found to decrease almost linearly as the Al concentration increases, and the gradient is about -160 K/at% Al. After quenching the sintered NiAl alloys of the 37 at%Al into martensite, specimens fractured by three-point bending at room temperature are observed by SEM and, as a result, some grain boundary fractures are observed on the fracture surface, and mainly intergranular cleavage fractures.

• Journal of Welding and Joining
• /
• v.30 no.3
• /
• pp.26-31
• /
• 2012

Three-dimensional integrated circuit (3D IC) technology has become increasingly important due to the demand for high system performance and functionality. We have evaluated the effect of Buffered oxide etch (BOE) on the interfacial bonding strength of Cu-Cu pattern direct bonding. X-ray photoelectron spectroscopy (XPS) analysis of Cu surface revealed that Cu surface oxide layer was partially removed by BOE 2min. Two 8-inch Cu pattern wafers were bonded at $400^{\circ}C$ via the thermo-compression method. The interfacial adhesion energy of Cu-Cu bonding was quantitatively measured by the four-point bending method. After BOE 2min wet etching, the measured interfacial adhesion energies of pattern density for 0.06, 0.09, and 0.23 were $4.52J/m^2$, $5.06J/m^2$ and $3.42J/m^2$, respectively, which were lower than $5J/m^2$. Therefore, the effective removal of Cu surface oxide is critical to have reliable bonding quality of Cu pattern direct bonds.