• 공업화학
• /
• 제25권3호
• /
• pp.312-317
• /
• 2014

공침전법으로 제조된 CuO-$CeO_2$ 혼합산화물 촉매에서 벤젠의 촉매연소 반응에 대해 연구하였다. CuO-$CeO_2$ 혼합산화물 촉매들은 침전제 및 CuO 전구체를 달리하여 제조하였고, XRD, BET, XPS 및 $H_2-TPR$에 의해 특성분석을 하였다. 침전제의 종류에 상관없이 CuO 피크가 $2{\Theta}=35.5^{\circ}$와 $38.5^{\circ}$에서 뚜렷하게 나타났다. $NH_4OH$를 침전제로 사용하여 제조한 Cu/(Cu+Ce)의 몰비율이 0.35인 촉매가 가장 높은 활성을 보여주었다. 또한, 수소로 전처리하면 벤젠 연소반응의 활성이 증가하였고, $400^{\circ}C$에서 수소로 전처리한 촉매가 가장 높은 활성을 보여주었다.

• 대한치과교정학회지
• /
• 제48권4호
• /
• pp.224-235
• /
• 2018

Objective: The purpose of this study was to compare the skeletal, dental, and soft-tissue treatment effects of nonextraction therapy using the modified C-palatal plate (MCPP) to those of premolar extraction (PE) treatment in adult patients with Class II malocclusion. Methods: Pretreatment and posttreatment lateral cephalographs of 40 adult patients with Class II malocclusion were retrospectively analyzed. The MCPP group comprised 20 patients treated with total arch distalization of the maxillary arch while the PE group comprised 20 patients treated with four PE. Fifty-eight linear and angular measurements were analyzed to assess the changes before and after treatment. Descriptive statistics, paired t-test, and multivariate analysis of variance were performed to evaluate the treatment effects within and between the two groups. Results: The MCPP group presented 3.4 mm of retraction, 1.0 mm of extrusion, and $7.3^{\circ}$ lingual inclination of the maxillary central incisor. In comparison, the PE group displayed greater amount of maxillary central incisor retraction and retroclination, mandibular incisor retraction, and upper lip retraction (5.3 mm, $14.8^{\circ}$, 5.1 mm, and 2.0 mm, respectively; p < 0.001 for all). In addition, the MCPP group showed 4.0 mm of distalization and 1.3 mm of intrusion with $2.9^{\circ}$ distal tipping of the maxillary first molars. Conclusions: These findings suggest the MCPP is an effective distalization appliance in the maxillary arch. The amount of incisor retraction, however, was significantly higher in the PE group. Therefore, four PE may be recommended when greater improvement of incisor position and soft-tissue profile is required.

• 펄프종이기술
• /
• 제31권5호
• /
• pp.86-94
• /
• 1999

Alkaline peroxide bleaching of chemi-mechanical pulp is a very complicated system where various process factors affect the bleacing performance and pulp properties. Traditional onefactor-at a time method is ineffective and costly infinding the optimal bleaching conditions. In this study, statistical experimental design and multiple regression method wre used to investigated the interactions among various bleaching factors and to find out the possbile maximal brightness development during one stage alkaline peroxide bleacing of TMP. The TMP was made from 10% Korean red pine and 90% Korean spruce and had an initial brightness of 54.5% ISO. the TMP was pretreated with EDTA(0.5% on O.D. pulp, 3% pulp consistency, 30$^{\circ}C$ for 60 minutes) and bleached in a 2 L Mark V Quantum Reactor at 750 rmp, 7.5% of bleaching consistency and with 0.05% magnesium sulfate addition. The ranges of chemical factors studied , based on oven-ried pulp, were 1-5% for hydrogen peroxide, 1-4% for sodium hydroxide and 1-4% for sodium silicate. The rages of reaction temperature and time were 50-90$^{\circ}C$ and 40-180minutes respectively. Interactions of hydrogen peroxide with alkali , time with temperature ature, alkali with time and silicate with temperature were found to be significant which means that hydrogen peroxide bleaching will be favored at stable concentration of perhydroxyl ion, relatively short time and low temperature, and high level of silicate. Mathematical model which has good predictability for target brightness in one stage peroxide bleaching can also be established easily. Base ion the model, maximal brightness of 70% ISO was found to at 50$^{\circ}C$ and 50 minutes by chemical additions of 5% for hydrogen peroxide, 3.2-3.4% for sodium hydroxide and 4% for silicate based on O.D. pulp. However, this result might not be suitable for situation where furnishes are different from ours, or different pretreatment is used, or bleaching carried out at different pulp consistency. In these cases it will be good to re-investigate the process by a similar methodology as was used in this study.

• 한국식품영양과학회지
• /
• 제40권2호
• /
• pp.149-155
• /
• 2011

산수유 5 g에 100 mL의 증류수를 가하고 항온수조를 이용하여 $25^{\circ}C$, $50^{\circ}C$, $90^{\circ}C$에서 추출한 다음 농축하여 각각 온도별 추출물을 얻었다. 각 온도별 추출물을 이용하여 산수유의 항산화 활성 조사 결과, 총 페놀함량은 가장 높은 온도($90^{\circ}C$)에서 추출한 추출물이 5.5 g/100 g GAE으로 가장 높았고, 그 다음으로 $50^{\circ}C$, $25^{\circ}C$ 추출물 순으로 페놀 함량이 많았다. DPPH 라디칼 소거능 측정에서는 각 시료의 농도가 증가할수록 DPPH 라디칼 소거능이 유의하게 증가하였다. 그러나 라디칼의 50%를 저해하는 농도인 $SC_{50}$은 추출 온도에 따른 유의적 차이는 나타나지 않았다. SOD 유사활성에서도 역시 각 시료의 농도가 증가할수록 활성이 높았으며, $SC_{50}$은 다른 온도에 비해 $25^{\circ}C$에서 유의하게 낮았는데 이는 $25^{\circ}C$에서 SOD 유사활성이 가장 좋음을 나타낸다. 또한 ORAC assay를 이용한 peroxyl 라디칼 소거능은 저농도에서는 각 온도에 따라 유의적은 차이를 보이지 않았으나, 고농도에서는 $50^{\circ}C$에서 유의하게 높았다. 한편 산수유 추출물의 산화적 스트레스에 의한 DNA 손상 억제 효과를 보기 위해 1, 10, $50\;{\mu}g$/mL의 농도로 백혈구에 처리한 후 $200\;{\mu}M$ $H_2O_2$로 DNA 손상을 유도한 결과, $50\;{\mu}g$/mL 농도에서 손상된 DNA tail 부분의 DNA 함량을 측정한 % tail DNA inhibition이 $25^{\circ}C$에서 28.5%, $50^{\circ}C$에서 37.5% 그리고 $90^{\circ}C$에서는 38.5%로 나타났다. 이상의 결과에서 산수유를 물로 추출할 경우 추출 온도가 높을수록 총 페놀함량은 증가한 것으로 나타났지만 항산화 활성과 항유전독성 효과는 추출 온도와는 상관 없이 우수한 것으로 나타났다. 이는 산수유가 일반적으로 고온에서 열수 추출하는 한약재로서 뿐만 아니라 비교적 낮은 온도에서 우려내는 식용 음료로서도 사용이 가능하다는 것을 제시한다.

• 한국식품과학회지
• /
• 제28권6호
• /
• pp.1071-1077
• /
• 1996

직접 설계한 냉각조, 침지조 및 살수조를 갖춘 냉수냉각 시스템에서 수냉각에 의한 냉각특성시험을 하므로써 향후 시스템 제작에 필요한 기초자료를 제공함과 아울러 본 시스템에 의한 농산물의 선도유지 및 저장효과를 살펴보기 위해 유자를 시료로 수확 후의 저장기간별 품질변화를 조사하였다. 냉수냉각에 있어 냉각시간에 대해 무차원화한 온도를 semi-log로 plotting한 결과, 유자 중심부의 냉각속도계수는 $-0.012{\sim}-0.017\;min^4\;(R^2=0.97{\sim}0.99)$, 표면에서는 $-0.033{\sim}-0.075\;min^4\;(R^2=0.89{\sim}0.93)$로 나타났다. 저장온도에 따른 처리구별 저장시험에서 처리조건에 따른 중량감소율은 모든 시료에서 저장온도 $15^{\circ}C$에서 저장 7주 후까지는 선형적으로 서서히 증가하여 약 $22{\sim}23%$ 수준을, 저장온도 $5^{\circ}C$에서는 저장 8주후에 $10{\sim}11$의 중량감소율로 저장온도에 따른 중량감소의 차는 확실히 나타나지만 수냉처리의 효과는 그다지 크게 나타나지 않았으며, 수분함량 변화는 무처리구(시료A)에서 $5^{\circ}C$저장, 1주후 3% 이상의 수분감소를 보였으나 수냉처리구(시료C)에서는 저장 7주 까지도 약 $1{\sim}2%$ 정도로 거의 변화가 없는 것으로 나타났다. 그리고 저장 초리 pH 및 산도는 무처리구의 경우, 저장온도에 따라 타 처리구에 비해 미미한 변화를 보였으나 큰 차는 볼 수 없었고, 가용성고형분 함량의 변화는 $5^{\circ}C$ 저장에서는 처리조건에 관계없이 약간의 증가를 보였으나 $15^{\circ}C$ 저장에 있어서는 무처리 시료가 저장 7주 후 $12.4^{\circ}Bx$로 증가한 반면에 수냉처리한 시료와 예건처리한 시료는 저장 7주 후 $11.6^{\circ}Bx$로 다소 적게 증가하였다. 색택변화도 수냉처리한 유자는 무처리한 유자에 비해 저장기간의 경과에 따라 증감속도가 다소 느리게 나타났으며, $15^{\circ}C$ 저장시 수냉처리한 유자의 호흡량은 무처리한 유자에 비해 약 1/2 정도 낮은 $103.63{\;}mg{\cdot}CO_2/kg{\cdot}hr$로 나타났다.

• 대한치과교정학회지
• /
• 제22권1호
• /
• pp.43-65
• /
• 1992

Bonding orthodontic adhesive resins to glazed porcelain surface is not attainable. The aim of this investigation was to examine, in vitro, the effect of three methods of porcelain surface pretreatment on the shear bond strength of orthodontic adhesives, and to compare the shear strength of orthodontic bracket bonding to porcelain surface by the best results that to human enamel. Porcelain disks ($Ceramco^{(TM)}$ and $Vita^{(TM)}$) baked in the laboratory were roughened by sandpapers, #320, #600, #800, #1000 and #1200, and were pretreated with silane and dried at the various temperatures, room temperature, $50^{\circ}C$, $70^{\circ}C$ and $90^{\circ}C$, and were etched by 3% hydrofluoric acid solution for 1, 3, 5, 7, and 9 minutes, orthodontic adhesives (System $1+^{(TM)}$ and $Unite^{(TM)}$) were applied on them, and shear bond strengths were measured by Instron. The best results of pretreatment of each method were determined by the shear bond strengths. Again, porcelain disks were pretreated by the determined best results and human enamel were etched by 37% hydrofluoric acid solution, orthodontic brackets were bonded on them by the orthodontic adhesives, and the shear bond strengths were measured and compared between them. 1. Roughening porcelain surfaces with coarse sandpaper (#300) showed higher shear bond strength than that with finer sandpapers, but it $(22.44Kgf/cm^2)$ was distinguishably low compared to that from etched human enamel $(144.11Kgf/cm^2)$. 2. There were disparities in shear bond strengths upon the orthodontic resins, which was presumably related to the contents of fillers in orthodontic adhesive resins. Also there were disparities in shear bond strength upon the porcelains which had different composition. 3. Silane enhanced the shear bond strength of orthodontic resins to porcelain surfaces ($25.20Kgf/cm^2$ at $50^{\circ}C$), which was markedly low compared to that from etched human enamel. 4. Etched porcelain surface with 3% hydrofluoric acid solution for 1 to 9 minutes showed no difference in shear bonding strength of orthodontic adhesive resins. Shear bond strength from etched porcelain $(97.43-120.72Kgf/cm^2)$ were as high as clinically available, but low compared to that from etched human enamel. 5. Roughening with #300 sandpaper and etching by 3% hydrofluoric acid followed silane application on porcelain surface showed lower shear bond strength than etched human enamel, but were as high as clinically useful. 6. The results suggest that etching porcelain surface by 3% hydrofluoric acid solution might provide comparatively high shear bond strength as much as clinically favorable.

• Journal of Chest Surgery
• /
• 제42권2호
• /
• pp.157-164
• /
• 2009

배경: 폐동맥 판막 협착 혹은 형성 부전을 동반한 여러 선천성 심장기형의 수술적 치료를 위하여, 다양한 종류의 우심실-폐동맥간 도관이 사용되었다. 장기 성적이 우수한 냉동동종 이식편(cryopreserved homograft)의 공급의 제한으로 이를 대체할 이종 조직 이식편의 석회화 방지를 위한 효과적인 기법의 확립이 필요하다. 본 연구에서는 L-lysine을 이용한 diamine bridge의 항석회화 효과를 Ethanol과 비교하여 알아보고자 하였다. 대상 및 방법: 0.625% glutaraldehyde ($4^{\circ}C$에서 2일, 상온에서 7일간) 고정한 돼지 심낭을 80% Ethanol (상온에서 1일), 혹은 0.1M L-lysine ($37^{\circ}C$에서 2일)로 처리 한 후 각각의 두께(thickness)와 장력(tensile strength)을 측정하였다. 각각의 항석회화 처리한 돼지 심낭을 생후 3주된 쥐의 피하조직에 이식하고 8주 뒤 칼슘을 정량하고 조직학적 소견을 관찰하였다. 결과: 0.625% glutaraldehyde 고정만 시행한 군$(51.2{\pm}8.5ug/mg)$과 비교하여 0.625% glutaraldehyde 고정 후에 80% Ethanol 처리한 군($13.6{\pm}10.0ug/mg$, p=0.008)과, 0.625% glutaraldehyde 고정 후에 L-lysine 처리한 군($15.3{\pm}1.0ug/mg$, p=0.002), 그리고 0.625% glutaraldehyde 고정 후에 80% Ethanol과 L-lysine 처리한 군($16.1{\pm}11.1ug/mg$, p=0.012)은 통계적으로 의미 있게 칼슘의 침착량이 적었다. 0.625% glutaraldehyde 고정 후에 80% Ethanol 처리한 군의 두께와 장력은 각각 $0.18{\pm}0.02mm,\;1.20{\pm}0.30kg$중/5mm로 0.625% glutaraldehyde 고정 후에 L-lysine 처리한 군의 $0.13{\pm}0.03mm$, $0.85{\pm}0.36$ 1.0kg 중/5mm 보다 증가되어 있었다(p<0.01, p=0.035). 결론: L-lysine을 이용한 diamine bridge는 Ethanol과 비교하여 비슷한 항석회화 효과를 보여 주었으며 Cross-link를 증가시켜 이종 이식편의 두께와 장력을 증가시켜 주는 효과가 있었다.

• Journal of Plant Biology
• /
• 제37권3호
• /
• pp.387-394
• /
• 1994

보리수나무(Elaeagus umbellata Thunb.) 유식물의 생육과정에서 근류 형성 및 질소고정 활성에 대한 중요 요인으로서 광도, 온도, 질소화합물, 수분 스트레스 등의 영향을 정량적으로 분석하였다. 유식물의 상대생장률과 T/R비는 각각 초기의 $1.60%{\cdot}d^{-1}$와 1.12에서 근류 형성이 촉진된 후기에는 $3.75%{\cdot}d^{-1}$와 2.31로 증가하였다. 질소고정의 비활성은 근류 형성 초기에 $72.5\;\mu\textrm{M}\;C_2H_4{\cdot}g\;fr\;wt\;nodule^{-1}{\cdot}h^{-1}$로서 최대치를 나타낸 후 점차 감소하였다. 상대조도 20-25. 10-15 및 4-6% 처리구의 질소고정 활성은 대조구에 대해 각각 41, 54 및 71%의 감소를 보였다. 근류를 15, 20, 25 및 $30^{\circ}C$에서 배양할 때 활성은 각각 5.4, 24.7, 51.6 및 $58.5\;\mu\textrm{M}\;C_2H_4{\cdot}g\;fr\;wt\;nodule^{-1}{\cdot}h^{-1}$로 변하였다. 저온($15^{\circ}C$)의 전처리 후 $30^{\circ}C$로 옮겼을 때 근류 활성($66.5\;\mu\textrm{M}\;C_2H_4{\cdot}g\;fr\;wt\;nodule^{-1}{\cdot}h^{-1}$)은 고온($35^{\circ}C$) 전처리에 비해 촉진되었다. 근류의 활성은 산소분압에 비례하여 16 kPa 이상에서 포화되었고, 근류를 뿌리에서 떼어내거나 절단하면 92%와 43%로 활성이 억제되었다. pH 5.5, 6.5 및 8.0에서 생육된 초기 근류의 상대활성은 각각 89, 100 및 40%였으며, 1 및 3 mM의 $NO_3\;-N와\;{NH_4}^{+}-N$에서 생육된 초기 근류는 각각 6.1%와 68.50%의 상대활성을 보였다. 수분 공급량 20, 50 및 100mL에 의한 근류의 형성과 비활성은 각각 35, 120 및 8 mg.plant-1와 33.6, 58.4 및 $8.4\;\mu\textrm{M}\;C_2H_4{\cdot}g\;fr\;wt\;nodule^{-1}{\cdot}h^{-1}$였다. 식물체에 수분공급을 중단하였을 때 5일 후에 일시 위조가 나타났으며, 식물체의 함수량 및 증산량은 각각 90 및 53% 감소되었으나, 근류 활성은 완전히 소실되었다.

• 한국자원식물학회지
• /
• 제26권3호
• /
• pp.383-388
• /
• 2013

The research concerned of the regeneration of plants from embryos obtained from anther cultures of ginseng (Panax ginseng C. A. Meyer). The aim was to determine the influence of the regeneration medium on the efficiency of the regeneration process. We conducted to determine the optimum conditions such as cold pretreatment, plant growth regulators and carbon sources on anther culture of P. ginseng. Highest callus formation rate was obtained when flower buds pretreated at $4^{\circ}C$ for 1 day. Among the treated growth regulators with various degrees of concentration in Murashige and Skoog's (MS) medium, 4.53 ${\mu}M$ of 2.4-dichlorophenoxyacetic acid and 4.44 ${\mu}M$ of 6-benzylaminopurine gives the most responsive callus with the frequency of 73.89% and 129.53 g of fresh weight. When we used 3-9% of sucrose and maltose among the different kinds and various concentrations of carbohydrates, callus was formed highest 67.29% in the medium with 3% of sucrose. Shoots induced from callus supplemented with 28.9 ${\mu}M$ of gibberellic acid and rooted in Gamborg's B5 medium supplemented with 14.7 ${\mu}M$ of indole-3-butyric acid.

• 미생물학회지
• /
• 제38권1호
• /
• pp.45-49
• /
• 2002

Bradyrhizobium japonicum 은 콩과 식물의 뿌리에 감염하여 뿌리흑을 형성 질소를 고정하는 독특한 능력을 갖는 토양 세균이며 미생물 비료제로 사용되고 있다. 본 연구에서는 저온에서 전처리한 B . japonicum 균주를 여러 가지 환경스트레스 조건에 노출하였을 때 생균수의 변화를 확인하였다. 저온 전처리는 16시간 동안 $4^{\circ}C$의 조건을 유지했다. 다양한 스트레스(알콜, 과산화수소, 고온, 건조)에 노출하였을 때, 저온 전처리한 것이 그렇지 않는 것보다 10~1,000배 정도 높은 생균수를 유지하였다. 이러한 내성중진 현상에 전처리 동안 새로운 단백질 합성이 수반되는 것을 단백질 합성 저해제 인 chloramphenicol을 전처리 과정에 포함하여 확인하였다. 저온 스트레스 내성에 관여하는 유전자를 B. japonicum genome 으로부터 중폭하였고 염기서열 분석을 실시하였다. 실험에서 확인된 B . japonicum의 CSP (Cold shock protein) 단백질의 부분적 아미노산 서열은 이미 확인된 다른 균주의 Csp 단백질과 유사함을 확인하였다.