• Journal of Powder Materials
• /
• v.28 no.2
• /
• pp.110-119
• /
• 2021

In this study, the high-temperature oxidation properties of austenitic 316L stainless steel manufactured by laser powder bed fusion (LPBF) is investigated and compared with conventional 316L manufactured by hot rolling (HR). The initial microstructure of LPBF-SS316L exhibits a molten pool ~100 ㎛ in size and grains grown along the building direction. Isotropic grains (~35 ㎛) are detected in the HR-SS316L. In high-temperature oxidation tests performed at 700℃ and 900℃, LPBF-SS316L demonstrates slightly superior high-temperature oxidation resistance compared to HR-SS316L. After the initial oxidation at 700℃, shown as an increase in weight, almost no further oxidation is observed for both materials. At 900℃, the oxidation weight displays a parabolic trend and both materials exhibit similar behavior. However, at 1100℃, LPBF-SS316L oxidizes in a parabolic manner, but HR-SS316L shows a breakaway oxidation behavior. The oxide layers of LPBF-SS316L and HR-SS316L are mainly composed of Cr₂O₃, Fe-based oxides, and spinel phases. In LPBF-SS316L, a uniform Cr depletion region is observed, whereas a Cr depletion region appears at the grain boundary in HR-SS316L. It is evident from the results that the microstructure and the high-temperature oxidation characteristics and behavior are related.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.6
• /
• pp.1193-1202
• /
• 1989

본 논문에서는 발전소의 소재로 많이 쓰이고 있는 304 스테인리스강(앞으로는 304SS로 표기함)과 316스테인리스강(앞으로는 316SS로 표기함)의 크립 균열 발생 거동 을 각각 600.deg. C와 625.deg. C에서 조사한다. 이 온도는 발전소의 반응기(reactor)에 사용 되는 304SS와 316SS이 받는 온도이다. 즉 304SS와 316SS의 크립 균열 발생을 지배 하는 파괴 매개변수가 무엇인지가 크립 파괴 실험을 통하여 조사된다. 실험 결과는 이미 제안되어 있는 크립 균열 발생 모델에서 예측된 결과와 비교된다. 특히 304SS 와 316SS은 고온에서의 연성도가 변형률 속도에 따라 변하는 것으로 알려져 있다. 본 연구에서는 '변형률 속도에 따른 재료의 연성도의 변화에 근거한 균열 발생 모델' 을 제안하고, 그 모델에서 예측된 크립 발생 거동을 실험 결과와 비교한다.

• Nuclear Engineering and Technology
• /
• v.51 no.2
• /
• pp.479-489
• /
• 2019

Low-cycle fatigue (LCF) tests were performed for Alloy 690 and 316 SS in a simulated pressurized water reactor (PWR) environment. Alloy 690 showed about twice longer LCF life than 316 SS at the test condition of 0.4% amplitude at strain rate of 0.004%/s. Observation of the oxide layers formed on the fatigue crack surface showed that Cr and Ni rich oxide was formed for Alloy 690, while Fe and Cr rich oxide for 316 SS as an inner layer. Electrochemical analysis revealed that the oxide layers formed on the LCF crack surface of Alloy 690 had higher impedance and less defect density than those of 316 SS, which resulted in longer LCF life of Alloy 690 than 316 SS in a simulated PWR environment.

• Journal of the Society of Naval Architects of Korea
• /
• v.34 no.3
• /
• pp.61-69
• /
• 1997

A simple and relatively new experimental method is proposed to estimate the plane stress fracture toughness by using compact tension (CT) specimen. The anti-buckling plates (fabricated to prevent the buckling caused by the 45 plastic yielding around crack tip under the plane stress condition) help to determine the relatively accurate plane stress fracture toughness of two stainless steels (SS304 and SS316). The fatigue crack propagation behavior of two stainless steels under two different loading conditions such as 10Hz and 5Hz frequency fatigue loadings was investigated by using image analysis technique (IAT) which renders several technical advantages over various conventional measuring methods. It was found that the IAT could be used to estimate fatigue crack lengths more effectively. Furthermore, it was suggested that we might control the measuring time interval for fatigue crack propagation by nearly automatically controlled technical process with the help of IAT.

• Proceedings of the KOSOMBE Conference
• /
• v.1994 no.12
• /
• pp.175-177
• /
• 1994

The wear corrosion behaviour of a nitrogen ion implanted super stainless steel (S.S.S, 22Cr - 20Ni - 6Mo - 0.25N) was compared with those of S.S.S, 316L SS and TiN coated 316L SS. The Cr and Ni amounts won out from the materials were investigated using an electrothermal atomic absorption spectrometry. We observed that the Cr dissolution rate of the S.S.S was similar to that of 316L SS, however, the Ni release of the S.S.S was feater than 316L SS. The metal ions released from the nitrogen ion implanted S.S.S surface were significantly reduced. The wear corrosion behaviour of the stainless steels was not correlated with the results shown by a static metal ion release test.

• 한국전기화학회:학술대회논문집
• /
• 2001.06a
• /
• pp.237-242
• /
• 2001

용융탄산염 연료전지에서 분리판으로 사용되는 316L 스테인리스 스틸의 내식성을 향상시키기 위해 Ni과 Al을 전기도금법에 의해 코팅하였으며 열처리를 통해 스테인리스 스틸표면에 $Ni_2Al_3$, NiAl 등의 금속간화합물을 형성시켰다. $62mol\%Li_2CO_3-38mol\%K_2CO_3$ 전해질 내에서 100시간 동안 침지실험을 수행한 결과 Al의 도금두께가 $10{\mu}m$ 이상인 경우에는 내식성이 상당히 향상되었음을 확인하였다.

• Journal of Welding and Joining
• /
• v.20 no.2
• /
• pp.109-115
• /
• 2002

In the case of using high temperature by coating ceramic/metal, large stress was produced due to difference of thermal expansion coefficient between those. And then lead to delamination. In order to relaxation of the stress A1$_2$O$_3$/SS316 composite powders with $10wt.%Al_2O_3$ compositional gradient and $10wt.%Al_2O_3$ agglomerated powder were made by spray drying method. These powders were sintered to improve the strength and to be plasma sprayed in order to fabricate the FGC(functionally graded coating). The influence of gun power, working distance and Ar pressure on the microstructure of the coating layer was studied in order to optimize the plasma spray conditions. It was proven that the optimum conditions were 40kw gun power, 5cm working distance and $100ft^3/h$ Ar flow for both powders. FGC with 10 compositional steps was fabricated and the total thickness was 1.3mm. FGC was heat treated at $1100^{\circ}C$for 10hours to evaluate the heat resisting characteristics.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.295-298
• /
• 2005

A minimum commitment method (MCM) was applied to predict the creep rupture life of type 316LN SS. For this purpose, a number of the creep rupture data for the type 316LN SS were collected through literature survey and experimental data of KAERl, Using the short-term creep rupture data under 2000 hr, the long-term creep rupture life above $10^5$ hour was predicted by means of the MCM. An optimum value of A, P and G function, used in the MCM equation, was determined respectively, and the creep rupture life with the A values in different temperatures was compared with the experimental data and the predicted curves.

• Journal of the Korean Vacuum Society
• /
• v.15 no.3
• /
• pp.325-330
• /
• 2006

In order to verify the integrity of the first wall (FW) of the International Thermonuclear Experimental Reactor (ITER), the fabricated Cu/SS mock-up is tested in the JAEA Electron Beam Irradiation Test Stand (JEBIS). To fabricate the Cu/SS mock-up, CuCrZr and 316L authentic stainless steel (SS316L) are used for Cu alloy and steel, respectively The hot isostatic pressing (HIP) is used as a manufacturing method with a $1050^{\circ}C$ and 150 MPa. The high heat flux (HHF) test is performed using an electron beam with a heat flux of $5MW/m^2$ and a cycle of 15-sec on time and 30-sec off time. The temperature measurement in the HHF test shows good agreement with the results obtained from ANSYS code analysis, which is used for determining the HHF test conditions.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.2
• /
• pp.169-177
• /
• 2020

Here, the stability of stainless steel 316 (SS-316) was investigated to identify its applicability in the oxide reduction process, as a component in related equipment, to produce a complicated gas mixture composed of O₂ and Cl₂ under an argon (Ar) atmosphere. The effects of the mixed gas composition were investigated at flow rates of 30 mL/min O₂, 20 mL/min O₂ + 10 mL/min Cl₂, 10 mL/min O₂ + 20 mL/min Cl₂, and 30 mL/min Cl₂, each at 600℃, during a constant argon flow rate of 170 mL/min. It was found that the corrosion of SS-316 by the chlorine gas was suppressed by the presence of oxygen, while the reaction proceeded linearly with the reaction time regardless of gas composition. Surface observation results revealed an uneven surface with circular pits in the samples that were fed mixed gases. Thermodynamic calculations proposed the combination of Fe and Ni chlorination reactions as an explanation for this pit formation phenomenon. An exponential increase in the corrosion rate was observed with an increase in the reaction temperature in a range of 300 ~ 600℃ under a flow of 30 mL/min Cl₂ + 170 mL/min Ar.