• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.10
• /
• pp.1861-1868
• /
• 1992

Laser beam hardening of 12%-Cr steel has been evaluated by using a continuous wave 3kW co$_{2}$ laser with a hardening mirror set. Experiment was performed on the hardening condition with a laser power of 2.85kW and travel speed of 1.0 and 1.5m/min. Multi passes have been also tried to find the hardening characteristics of partly overlapped zone. The black paint to use at high temperature was adopted to increase the absorptivity of laser beam energy with the wavelength of 10.6.mu.m at the surface of base metal. The microstructure of the hardened layers was observed by using a light microscopy, SEM and TEM. A fine Lamellar martensite formed in the hardened zones exhibits very high Vickers microhardness of 600Hv, whereas the tempered martensite distributes in the base metal with Vickers microhardness of 240Hv.It has been found that laser hardening with multi passes showed no significant drop of the hardness between adjacent passes.

• Journal of Korea Ship Safrty Technology Authority
• /
• s.22
• /
• pp.34-53
• /
• 2007

In the case of hull material. large sized merchant ships are made of steel, on the other hand FRP or wood are used for small sized fishing boats. At present in Korea approximately 88,500 fishing boats are in operation of which 70% are made of FRP In the meantime, stainless steel is frequently used as shaft materials of the small-size FRP fishing boat. Namely, the kinds of shaft materials are STS 304(18Cr-8Ni), STS 316(18Cr-12Ni-2.5Mo steel) and STS 630(17Cr-Ni-Nb steel)etc. Among these things, STS 304 which is the cheapest and having ordinary corrosion resistance is most widely used as 2nd class shaft material. But, using STS 304 for shaft system material of the small-size FRP fishing boat on seawater environments entails a severe corrosion which causes shaft system troubles. Particularly, the corrosions tend to be concentrated of the stern and bow side, propeller shaft surface of inside of stern tube and the boat having no stern cooling pipe line system. As a solution for those problems, research on the ways to mitigate corrosion on the part of 2nd class stainless steel shaft have been undertaken. In the result, not only clarification for the reason of corrosion of the part of stainless steel shaft used mainly for the small-size FRP fishing boat was done, but also most optimal corrosion protection system was developed by experimenting shaft's protection simulation based of the electrochemical cathodic protection principle. In addition, verification through the field test on the optimal cathodic corrosion protection method by means of aluminum sacrificial anode was carried out. In this study, effective and economical shaft's protection system is suggested to the small-size FRP fishing boat operator by substantiating the results obtained from the research on the optimal cathodic protection.

• Korean Journal of Materials Research
• /
• v.25 no.12
• /
• pp.666-671
• /
• 2015

In this study, we investigated the effect of the residual carbides and tempered carbides precipitated by tempering treatment after quenching on the pitting corrosion of mod. 440A martensitic stainless steel. In quenched specimens and tempered specimens after quenching of mod. 440A martensitic stainless steel, the volume fraction of the residual carbides and total carbides decreased with the increase of the austenitizing temperature. Pitting resistance increased with the increase of austenitizing temperature. With the increase of the volume fraction of the residual and total carbides, the pitting resistance of mod. 440A martensitic stainless steel was decreased. The pitting resistance of mod. 0.5C-17Cr-0.5Ni 440A martensitic stainless steel had stronger affected by residual carbides than precipitated carbides produced by tempering.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.2
• /
• pp.49-56
• /
• 2006

In this study, the movable flame hardening process of 12Cr steel for a uniform hardness and desirable residual stress have been investigated. For this, the temperature cycles have been controlled accurately as a function of the three processing variables, the flame intensity $I_f$, the scanning velocity $V_s$, and the initial flame holding time $t_h$, where the standard surface temperature $T_{s,\;max}$, was maintained at $960^{\circ}C$. The optimized conditions were $V_s=0.68mn/s\;and\;t_h=67sec$ for the $C_3H_8:O_2\;=\;5:20l/min,\;V_s=0.80mm/s$ and $t_h=56sec$ for the $C_3H_8:O_2=6:24l/min,\;V_s=1.01mm/s\;and\;t_h=48sec$ for the $C_3H_8:O_2=7:28l/min,\;and\;V_s=1.15mm/s$ and $t_h=39sec$ for the $C_3H_8:O_2$=8:32 l/min. The optimally flame-hardened surface exhibited uniform distributions of the hardness and residual compressive stress over the treated area with moderate levels of $470{\sim}490HV_{0.2}$in hardness and $-300{\sim}-450MPa$ in residual stress, which were acceptable on the basis of the acceptance criteria of Siemens AG-KWU and GE Power Generation Engineering.

• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.621-630
• /
• 2006

Twelve beams made of lightweight high-strength concrete were tested to determine their diagonal cracking and ultimate shear capacities. A total of 12 beams without(4 beams) and with lightweight(8 beams) were tested in a stiff testing facility, and complete load-midspan deflection curves, including the maximum capacities portion, were obtained. The variables in the test program were concrete strength, which varied 35.4 MPa, 65.3 MPa; shear span-depth ratios a/d=1.5, 2.5, 3.5, 4.5; and tensile steel ratio between 0.57 and 2.3 percent. Also, we divided beam by diagonal tension crack and ultimate shearing strength to propose an equation. In addition, it analyzed comparison mutually applying existing proposal and guide. $V_{cr}$ was as result that AIK recommendations and Zsutty proposal decrease more than a/d=2.5, increased some in Mathey's proposal equation. $V_{cr,\exp}/V_{cr,cal}$ showed tendency of overestimation according to increase of tensile steel ratio and compressive strength of concrete. On the other hand, $V_{cr,\exp}/V_{cr,cal}$ is superior in conformability with an experiment result Zsutty's proposal among other equations. The proposal equation hew that expect $V_{cr}/V_u$, rationally about shearing strength. Therefore, shear strength an equation is considered to be utilized usefully evaluating capacity by change of the shear span depth ratio of lightweight concrete, tensile steel ratio, and compressive strength of the concrete in this research.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.12
• /
• pp.3088-3095
• /
• 2000

Creep-fatigue crack growth behavior was experimentally measured particularly when a crack was located in the heat affected region of lCr-5Mo steel. Load hold times of the tests for trapezoidal fatigue waveshapes were varied among 0, 30, 300 and 3,600 seconds. Time-dependent crack growth rates were characterized by the $C_r$parameter. It was found that the crack growth rates were the highest when the crack path was located along the fine-grained heat affected zone(FGHAZ). Cracks located in other heat affected regions had a tendency to change the crack path eventually to FGHAZ. Creep-fatigue crack growth law of the studied case is suggested in terms of (da/dt)$_{avg}$ vs. ($C_t$)$_{avg}$ for residual life assessment.

• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.4
• /
• pp.324-332
• /
• 1998

The grain growth characteristics of dual-phase (${\alpha}+{\gamma}$) containing high Cr-steel have investigate using ${\alpha}$-, ${\gamma}$-single phases and (${\alpha}+{\gamma}$)dual-phase of 12%Cr Steel. The heat treatment has performed at $1000-1200^{\circ}C$ for 1-100hr. The results are as follows : 1) The grain growth rate in (${\alpha}+{\gamma}$) dual phase was substantially slower than that of single grain. 2) The relation between mean grain radius $\bar{{\gamma}}$ and annealing time t is, in general, described as following equation : $$(\bar{{\gamma}})^n-(\bar{{\gamma}_o})^n=K_n{\cdot}t{\cdots}{\cdots}(1)$$ i) In the case of single phase of high Cr steel, Eq.(1) is described as $(\bar{{\gamma}})^2-(\bar{{\gamma}_o})^2=K_2{\cdot}t$ and the grain growth is controlled by boundary migration. ii) In dual phase, the grain growth needs diffusion of alloying elements because the chemical composition of ${\alpha}$- and ${\gamma}$- phases differs from each other. When the volume fraction of ${\alpha}$-, ${\gamma}$-phase was almost equal and ${\gamma}$-phase in the case of 80 and $90%{\gamma}$. Eq.(1) is described as $(\bar{{\gamma}})^3-(\bar{{\gamma}_o})^3=K_3{\cdot}t$ because the grain growth is controlled by volume diffusion iii) In the case of ${\gamma}$-rich phase (80 and $90%{\gamma}$), the grain growth of minor phase (10 and $20%{\alpha}$) is described as $(\bar{{\gamma}})^4-(\bar{{\gamma}_o})^4=K_4{\cdot}t$ because the boundary diffusion is predominent rather than volume diffusion.

• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.73-78
• /
• 2011

Weldability, especially HAZ cold cracking, weld metal solidification cracking, and HAZ liquation cracking susceptibilities, of ASTM A356 CA6NM martensitic stainless steel casting was investigated and compared with that of 9-12% Cr ferritic steel castings. Irrespective of the Cr and Ni content in the castings, the HAZ maximum hardness increased with an increase of carbon content. CA6NM steel, which has the lowest carbon content, had the lowest HAZ hardness and showed no cold cracking in y-slit cracking tests. CA6NM steel, meanwhile, showed the largest weld metal solidification cracking susceptibility in varestraint tests because of its higher amount of impurity elements, phosphorus, and sulfur. All castings investigated had good high temperature ductility in hot ductility tests and showed little difference in liquation cracking susceptibility.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.12
• /
• pp.4270-4274
• /
• 2011

A method is proposed for determining chromium content in the carbon steel pipes of a nuclear power plant (NPP) to evaluate wall thinning caused by flow-accelerated corrosion (FAC). A flat file was used to obtain filings samples. To assess sampling quality, a disk form of SRM 1227 was ground with the flat file, and the amount of Cr in the filings was determined by ICP-AES. The content of chromium in the filings of SRM 1227 was estimated as six times higher than the certified value due to the contamination of chromium in the file. To eliminate chromium contamination from the file, it was coated with WC-12Co using high-velocity oxygen-fuel (HVOF) spraying systems. After obtaining filings samples using the coated file, Cr content in four types of disk-form SRMs was determined by ICP-AES. The recoveries of Cr in the disk-form SRMs were in the range of 95.4-102.6%, with relative standard deviations from 0.43 to 3.0%. The Cr contents in the filings collected from the used outlet headers of the nuclear power plants using the flat file coated were in the range of 0.11-0.19%.