• Transactions of the Korean hydrogen and new energy society
• /
• v.29 no.3
• /
• pp.274-279
• /
• 2018

Sc-substituted $La_{0.6}Sr_{0.4}FeO_{3-{\delta}}$(LSFSc) has synthesized for ceramic interconnector of tubular solid oxide cells (SOCs). For improving the redox stability and electric conductivity of LSFSc, the compositions of Sc, pH value of mixed precursors, calcination temperature and times were optimizing. The electrochemical performances of $La_{0.6}Sr_{0.4}Fe_{1-x}Sc_xO_{3-{\delta}}$ powders were measured as depending on Sc composition. The electric conductivity and redox stability of $La_{0.6}Sr_{0.4}Fe_{1-x}Sc_xO_{3-{\delta}}$ was determined by Sc concentration. $La_{0.6}Sr_{0.4}Fe_{0.9}Sc_{0.1}O_{3-{\delta}}$ powders can be one of the stable composition for ceramic interconnector of tubular-SOCs.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.83-88
• /
• 2019

LiBaPO₄:Eu²⁺ phosphors with stoichiometric and nonstoichiometric compositions were prepared using a solid state reaction followed by heat treatment in reduced atmosphere, and the crystal structures and photoluminescence(PL) properties of the powders were investigated by x-ray powder diffraction and luminescence spectrometer. At 900℃, the Ba₃(PO₄)₂ phase as the intermediate phase was observed with the LiBaPO₄ phase as the main crystalline phase. Samples with a low europium concentration at 1,000℃ belonged to the trigonal structure, whereas samples with Eu²⁺ content more than 4 mol% showed monoclinic structure. In the nonstoichiometric compositions of 4 mol% Eu²⁺ and above, a single phase of Eu²⁺-doped LiBaPO₄, showing bluish green emission, was formed.

• Resources Recycling
• /
• v.25 no.3
• /
• pp.49-54
• /
• 2016

In this study, zircon sand is separated into zirconia and silica by using the Ar-$H_2$ arc plasma refining. And then silica is removed from it by the microwave leaching method to produce a high pure zirconia. Plasma melting consist of two sequential processes; reduction process with Ar gas only followed by refining process with Ar-$H_2$ gas. After cooling in chamber. The solid phase obtained at $240^{\circ}C$ were found to be composed of 20% sulfuric acid solution. The solution was used as a leaching solution with microwave irradiation to obtain a high purity zirconia.

• Journal of Korean Society of Environmental Engineers
• /
• v.32 no.10
• /
• pp.928-935
• /
• 2010

A bag filter system was partially burnt down during a trial run of waste wood incineration boiler. This brought about unburned hydrocarbon which caused a rapid deactivation of low temperature SCR catalyst set up in two stage after the bag filter. The deactivated catalyst was investigated in order to trace the origin by several characterization methods such as XRD, EDX, BET, TGA, SEM. The deactivated catalyst was regenerated by different methods such as acid washing, water washing in ultrasonication, and calcination treatment under air condition. It is found the calcination treatment under air condition at $450^{\circ}C$ for 2 hours to be the best regeneration method. The catalytic activity was measured in the form of 2 cm ${\times}$ 2 cm ${\times}$ 10 cm (catalyst weight 10 g) honeycomb type. A deNOx efficiency of the regenerated catalyst showed 100% at $180^{\circ}C$ which is the same level of fresh one.

• Resources Recycling
• /
• v.1 no.1
• /
• pp.44-50
• /
• 1992

The $\alpha$-FeOOH powders were prepared by allkaline and acidic method on the small scale plant from the waste pickling liquor of iron. $\alpha$-FeOOH, $\alpha-Fe_2O_3$, $Fe_3O_4$ and ${\gamma}-Fe_2O_3$ powders were examined by TEM, SEM, TG-DTA, X-ray diffraction, VSM and chemical analysis. The results obtained from the experiment could be summerized as follows : the reaction time for the preparation of $\alpha$-FeOOH was observed to be smaller in the case of alkaline method and the products was acicular with the size of about $0.5\mu\textrm{m}$. The color of $\alpha-FeOOH and $\alpha-Fe_2O_3$was lovely yellow and red, respectively. The magnetic properties of $Fe_3O_4$ obtained by the reduction of $\alpha-Fe_2O_3$in the $H_2$ atomosphere at $370^{\circ}C$ for 1 hour showed 367(Oe) and 82.7(emu/g).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.288-288
• /
• 2007

본 연구에서 내환원성 $BaTiO_3$의 PTCR(Positive Temperation Coefficient Resistance) 특성 및 미세구조에 대한 분쇄 및 출발 원료들의 하소 조건의 영향을 연구하였다. $BaCO_3$, $TiO_2$, $CeO_2$를 Attrition milling 하여 1차 혼합 및 분쇄한 후 건조하여 혼합분말을 얻었으며, $(Ba_{1-x}Ce_x)TiO_3$를 합성하기 위하여 $1000^{\circ}C{\sim}1200^{\circ}C$ 공기중에서 하소하였다. 각 하소온도에서 제조한 $(Ba_{1-x}Ce_x)TiO_3$에 첨가제를 2차 혼합하고 초미분쇄하여 분말을 제조하였다. 직경 5mm 의 시편을 제조하여 환원 및 재산화 분위기에서 소결을 한 후 상온저항값 및 R-T특성을 측정하였고 SEM 을 통해 미세구조를 관찰하였다. 또한 하소 후 온도에 따른 상분석을 XRD를 통하여 분석하였다. 그 결과 하소온도가 증가함에 따라 상온저항값은 감소하는 경황을 보였으며 PTC특성은 감소하다가 증가하는 경향을 보였다. 초미분쇄에 따른 입자크기는 $1{\mu}m$이하로 작아졌으며 미립화가 됨에 따라 하소/소결온도에 앙향을 줄 것으로 사료된다.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.200-204
• /
• 2011

In this paper, we deposited the tungsten carbon nitride (W-C-N; nitrogen gas flow of 2 sccm) and tungsten carbon (W-C) thin film on silicon substrate using rf magnetron sputter. Then the thin films annealed at $800^{\circ}C$ during 30 minute ($N_2$ gas ambient) for thermal damage. Nano-indenter was executed 16 points on thin film surface to measure the thermal stability, and we also propose the elastic modulus and the Weibull distribution, respectively. This nanotribology method provides statistically reliable information. From these results, the W-C-N thin film included nitrogen gas flow is more stable for film uniformities, physical properties and crystallinities than that of not included nitrogen gas flow.

• Clean Technology
• /
• v.16 no.1
• /
• pp.19-25
• /
• 2010

In this work, the conversion of crystalline cellulose into polyols in the presence of hydrogen was examined over noble metal (Pt, Ru, Ir, Rh, and Pd) catalysts supported on activated carbon. For comparison, Pt/${\gamma}-Al_2O_3$ and Pt/H-mordenite were also investigated. Several techniques: $N_2$ physisorption, X-ray diffraction(XRD), inductively-coupled plasma-atomic emission spectroscopy (ICP-AES), temperature-programmed reduction with $H_2$ ($H_2$-TPR) and CO chemisorption were employed to characterize the catalysts. The cellulose conversion was not strongly dependent on the types of the catalyst used. Pt/AC showed the highest yields to polyols among activated carbon-supported noble metal catalysts, viz. Pt/AC, Ru/AC, Ir/AC, Rh/AC and Pd/AC.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.79-86
• /
• 2019

Recently, the use of lithium ion battery(LIB) has increased. As a result, the price of lithium and the amount spent lithium on ion battery has increased. For this reason, research on recycling lithium in waste LIBs has been conducted1). In this study, the effect of roasting for the selective lithium leaching from the spent LIBs is studied. Chemical transformation is required for selective lithium leaching in NCM LiNi_xCo_yMn_zO₂) of the spent LIBs. The carbon in the waste EV cell powder reacts with the oxygen of the oxide at high temperature. After roasting at 550 ~ 850 ℃ in the Air/N₂ atmosphere, the chemical transformation is analysed by XRD. The heat treated powders are leached at a ratio of 1:10 in D.I water for ICP analysis. As a result of XRD analysis, Li₂CO₃ peak is observed at 700 ℃. After the heat treatment at 850 ℃, a peak of Li₂O was confirmed because Li₂CO₃ is decomposed into Li₂O and CO₂ over 723 ℃. The produced Li₂O reacted with Al at high temperature to form LiAlO₂, which does not leach in D.I water, leading to a decrease in lithium leaching ratio. As a result of lithium leaching in water after heat treatment, lithium leaching ratio was the highest after heat treatment at 700 ℃. After the solid-liquid separation, over 45 % of lithium leaching was confirmed by ICP analysis. After evaporation of the leached solution, peak of Li₂CO₃ was detected by XRD.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.1
• /
• pp.278-283
• /
• 2019

3 kinds of fine powder, Fe-2%Ni alloy powder(N Ltd.) and Fe+2%Ni mixed powder(B Ltd. and S Ltd.), were fabricated into sintered compacts of bending strength specimens and ring type specimens by metal injection molding, debinding and controlling sintering conditions (reduction and sintering atmospheres, sintering temperature, sintering time and cooling rates). Density and magnetic properties of the sintered compacts were evaluated with the following conclusions. (1) When each compact was hold at 1123K for 3.6ks in H2 and sintered at 1623K for 14.4ks in Ar, the density of N, B and S Ltd.'s sintered compacts were measured as 96, 99 and 99%, and oxygen/carbon contents were measured as 0.0041%O/0.0006%C, 0.0027%O/0.0022%C, and 0.160%O/0.0026%C, respectively. (2) Magnetic characteristics of B Ltd. compact in Ar with the best results showed $B_{25}=14.3KG$, $B_r=7.75KG$, and $H_c=2.1Oe$, but not enough as those made by melting process. (3) Magnetic properties of B Ltd. compact which were sintered at 1673K for 14.4ks in Ar gas, and cooled at $0.83Ks^{-1}$ to 1123K and then cooled at $0.083Ks^{-1}$ down to room temperature were measured as $B_{25}=14.8KG$, $B_r=8.3KG$, and $H_c=1.3Oe$, almost similar to those made by melting process. Objected soft magnetic materials properties were obtained through sintering process by controlling sintering conditions (reduction condition, sintering atmosphere, sintering temperature and sintering time) and cooling rates.