• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.

• Journal of the KSME
• /
• v.52 no.12
• /
• pp.49-53
• /
• 2012

이 글에서는 조직공학에 사용되는 재료들의 기계적 특성에 대해 간략하게 정리하였다. 당연하게도, 각각의 재료들은 그 기계적/화학적 특성에 맞는 제작방법이 필요하며, 이러한 기계적/화학적 특성들은 타겟 장기/조직이 필요로 하는 그것과 유사해야 한다.

• Proceedings of the KSEEG Conference
• /
• 1999.04a
• /
• pp.21-23
• /
• 1999

• Proceedings of the Korea Water Resources Association Conference
• /
• 2007.05a
• /
• pp.581-585
• /
• 2007

본 연구는 시화호 표층에 분포하는 점착성 퇴적물의 침식특성을 정량적으로 산정하고 산정된 침식특성의 지엽적 변화 및 타 지역 침식특성 결과와의 비교/분석을 통한 공간적 변화 해석을 목적으로 환형수조를 이용한 침식 실험을 수행하였다. 또한 퇴적물 자체의 물리 화학적 특성 및 해수 특성이 침식특성에 미치는 영향을 파악하기 위하여 시화호 점착성 퇴적물에 대한 물리 화학적 특성 및 해수 특성에 대한 분석이 수행되었다. 침식실험은 균일저면 조건에서 3개 지점에 대해 지점별로 $5{\sim}7$회씩 총 17회의 실험이 수행되었으며, 본 연구를 통하여 도출되어지는 시화호 점착성 퇴적물의 침식특성 매개변수들은 시화호 해역에서의 수층 탁도 분포 및 세굴/퇴적량 산정 등을 위한 수치모형실험 시에 기초 입력 자료로 크게 활용될 수 있을 것이다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.177-179
• /
• 1997

본 연구에서는 최근 그 사용이 급증하고 있는 옥외용 절연재료에 대한 열화특성을 평가하기 위하여 펄렛상태의 EPDM 원 시료를 Hot plate를 이용하여 씨트로 제작하였다. 기후조건에 대응하는 열 싸이클에 의해 절연재료에 일어나는 화학적, 전기적 특성변화를 조사하기 위하여 주기적인 열싸이클을 가하면서 일정 기간별로 유전특성과 표면누설전류 및 표면의 화학적 변화에 대하여 측정하였다. 또한 접촉각 측정을 통하여 EPDM의 전기적 화학적 열화 또는 성질 변화에 대하여 검토하였다. 측정 결과 EPDM은 비교적 단기간의 열싸이클에 대해서 전기적 화학적 특성변화는 그다지 나타나지 않는 것으로 나타났다.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2008.05a
• /
• pp.2166-2169
• /
• 2008

한강 하구 점착성 퇴적물의 침강속도를 정량적으로 산정하고, 산정된 침강속도의 계절적 변화 해석을 목적으로 침강수주를 이용한 침강 실험이 수행되었다. 침강실험은 1개 정점에서 3계절에 채취된 퇴적물 표본 시료에 대해 계절별로 $5{\sim}6$회씩 총 16회의 실험이 수행되었으며, 또한 퇴적물 자체의 물리 화학적 특성 및 해수 특성에 따른 침강속도의 정성적 변화 특성을 파악하기 위하여 한강 하구 점착성 퇴적물에 대한 물리 화학적 특성 및 해수 특성에 대한 분석이 수행되었다. 본 연구를 통하여 도출되는 한강 하구 점착성 퇴적물 침강속도의 정량적 결과는 향후 한강 하구에 대한 체계적 관리 및 기능 회복을 위한 기술 개발시에 크게 활용될 수 있을 뿐만 아니라, 저면의 침식과 퇴적에 따른 하상변동 해석, 수질 및 퇴적물 오염 절감을 위한 대책 방안 수립 등 다양한 목적으로 크게 활용될 수 있을 것이다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.71-71
• /
• 2010

최근 나노선의 우수한 전기적, 광학적 특성을 다양한 종류의 전자소자, 광소자, 그리고 센서에 응용하는 연구가 활발히 진행되고 있다. 그 중 $SnO_2$ 나노선은 n-type의 전기특성과 우수한 광 특성을 보이며, 전자소자, 광소자 뿐 아니라 다양한 종류의 가스 센서 제작에 널리 사용되고 있다. 본 연구에서는 화학기상증착법 (Chemical Vapor Deposition)으로 $SnO_2$ 나노선을 성장하여 전계방출효과 트랜지스터 (field effect transistor: FET)를 제작하여 전기적 특성을 측정하였다. 나노선의 성장 조건 (온도와 산소 유량) 에 따른 나노선의 구조, 화학조성, 전기적 특성을 체계적으로 조사하였다. 산소의 유량이 낮을 때는 온도에 따라 나노선의 크기와 전기 특성에 변화가 없었으나, 산소의 유량을 높이면 온도에 따라 나노선의 두께와 전기적 특성이 크게 변화하였다. 본 연구에서는 특히, FET 구조에서 on/off current ratio 가 $10^5$ 이상으로 매우 높은 나노선 제작이 가능하였다. 전기적 특성과 나노선의 결정구조, 화학적 조성을 함께 비교하여 성장 메커니즘을 이해하고자 한다.

• Polymer(Korea)
• /
• v.29 no.1
• /
• pp.91-95
• /
• 2005

The PVA hydrogels were prepared by the chemical and irradiation method to improve the heat resistance of these hydrogels at the high temperature. The physical properties such as the gel content, the degree of swelling and the gel strength for the synthesized hydrogels were examined. Gel content increased as the chemical reaction time and the irradiation dose increased, and gel content of the hydrogels were higher when the two-steps of chemical and irradiation method were used rather than only the chemical method. Gel strength increased as the chemical reaction time increased, and as the irradiation dose decreased. The hydrogels prepared by the chemical reaction for 5 hours and the two-steps had the heat resistance at the high temperature.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.116.1-116.1
• /
• 2017

본 연구는 PVD와 CVD를 동시에 사용한 하이브리드 공정시스템을 이용하여 Ti를 도핑한 Diamond-like carbon(DLC) 코팅 전극의 특성 분석에 대한 내용을 다루고 있다. DLC는 높은 경도, 낮은 마찰 계수, 화학적 안정성 등의 좋은 기계적 물성을 가지고 있어 주로 내마모성이 요구되는 분야에 주로 적용되어 왔다. 또한 DLC는 넓은 전위창 및 낮은 백그라운드 전류 등의 전기화학적 특성을 가지고 있어 최근 전극용으로 전도유망한 소재로 주목받고 있지만, 높은 비저항과 낮은 접착력은 여전히 극복해야할 문제로 남아있다. 본 연구에서는 Plasma enhanced chemical vapor deposition (PECVD) 법과 High power impulse magnetron sputtering (HiPIMS) 기법을 동시에 사용하여 Ti/TiC 하지층과 그 위에 Ti-DLC 막을 증착하였고, Ti 함량에 따른 DLC 박막의 특성변화를 살펴보았다. PVD/CVD 하이브리드 증착법에 의한 하지층은 DLC막과 기판사이의 밀착력을 향상시켰고, 기존 PECVD법과 비교하였을 때 하이브리드 증착법은 DLC 박막의 증착률을 크게 증가시켰다. DLC 박막에 소량의 Ti가 들어가면 C-C $sp^2$ 구조가 증가하여 전기적, 전기화학적 특성이 향상되었고, Ti의 함량이 일정 이상 증가하면 TiC의 영향을 받아 전기적, 전기화학적 특성이 나빠지는 것을 알 수 있었다. 본 연구에서는 DLC를 전극으로 활용하기 위해 전기적 및 전기화학적 특성을 향상시키는 연구에 집중하였지만, 산업에 활용하기 위해서 기계적 물성향상과 수명에 관한 추가적인 연구가 이루어 진다면 DLC 전극 분야 발전에 많은 기여를 할 수 있을 것이라 생각한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.448-448
• /
• 2012

최근에 pH 감지막의 감지감도특성을 평가하기 위해 electrolyte insulator semiconductor (EIS) 구조가 유용하게 이용되고 있다. EIS는 간단한 구조와 pH 용액에 빠른 응답속도, 낮은 단가 및 집적이 용이하다는 장점이 있다. EIS 구조에서 화학적 용액에 대한 감지감도 평가 중 가장 중요하게 작용하는 부분이 감지막이다. 이 감지막은 감지 대상 물질과 물리적으로 직접 접촉되는 부분으로서 일반적으로 기계적/화학적 강도가 우수한 실리콘 산화막($SiO_2$)이 많이 사용되어져 왔다. 최근에는 기존의 $SiO_2$ 보다 성능이 향상된 감지막을 개발하기 위하여 $Al_2O_3$, $HfO_2$, $ZrO_2$, 그리고 $Ta_2O_5$와 같은 고유전 상수(high-k)를 가지는 물질들을 EIS 센서의 감지막으로 이용하는 연구가 활발하게 진행되고 있다. High-k 물질 중 $Al_2O_3$는 산성에서 알칼리성 영역까지의 넓은 화학안정성을 가지며 화학용액에 대해 내구성이 우수한 특성을 가진다. $HfO_2$은 내식성이 뛰어나며 출력특성이 높은 장점을 가진 물질이다. 본 실험에서는 특성이 다른 두 물질을 EIS의 감지막으로 각각 사용하여 두께에 따른 의존성을 평가하였다. 제작한 EIS 구조의 pH 센서를 바이오 센서에 적용하였을 때 신호대 잡음비(SNR: signal to noise)가 여전히 취약하다는 문제점이 있었다. 이런 문제점을 보완하기 위하여 감지막의 물리적 두께는 점점 얇아지게 되었고 그 결과 높은 출력 특성을 얻게 되었지만, 감지막이 얇아짐에 따라서 화학 용액 중의 이온 침투로 인한 감지막 자체의 손상 또한 심각한 문제로 대두되었다. 이로 인해 최적화 된 감지막의 두께를 얻을 필요가 있다. 결론적으로 $Al_2O_3$, $HfO_2$ 두 감지막 모두 두께가 23 nm일 때 가장 우수한 특성을 보였으며, $Al_2O_3$를 감지막으로 사용하였을 경우 화학적 용액에 대해 내구성이 뛰어났고, $HfO_2$을 사용하였을 때에는 화학적 용액에 대한 안정성 보다는 pH 용액변화에 따른 향상된 감지감도특성을 보였다.