• Fire Science and Engineering
• /
• v.23 no.6
• /
• pp.126-134
• /
• 2009

In an attempt to control the spalling in high strength concrete, spalling reducer was mixed to identify the effect and thermal characteristics of concrete beam member at high temperature. The member was manufactured in such as way of adding 40~60MPa of high strength concrete into spalling reducer, and then fire resistance performance were monitored under the ISO standard fire load condition in accordance with KS F 2257. As a result of test, fore rate performance of 40MPa beam without spalling reducer was 180minutes, 50MPa was 174minutes and 60MPa was 152minutes, indicating that 50MPa and 60MPa beam appeared 6~28minutes short to become a 3-hour rate. However, 50 and 60MPa beam mixed with spalling reducer appeared to have satisfied the requirements for 180minutes. A spalling was occurred in surface of 50 and 60MPa beam mixed without spalling reducer, while no spalling or surface failure was occurred with 50 and 60MPa beam mixed with spalling reducer. Thus polypropylene fiber mixed with the concrete proved to be effective, but viewing that the surface of 60MPa was peeled off partially, the steel fiber mixed appeared not to be effective for the beam more than 60MPa.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.5
• /
• pp.86-94
• /
• 2020

When the Superabsorbent Polymer (SAP) is added into concrete, the slump decreases rapidly, deteriorating the workability, the internal curing effect can be obtained through the water absorption and discharge process, and the internal voids of the concrete are increased. In this study, the effects of internal curing and voids were evaluated by evaluating the compressive strength, freeze-thaw resistance, and chloride penetration resistance of SAP-adding concrete that secured workability using a water reducing agent. Also, the internal curing effect of SAP was evaluated by dividing the curing conditions of concrete into water curing and sealed curing. From the result, as the SAP adding ratio increased, the amount of water reducing agent increased, and as for the compressive strength, the SAP adding ratio of 1.5% showed the greatest compressive strength. In particular, in the case of sealed curing showed higher compressive strength than the water curing. It is considered that the compressive strength increased due to the reduction of the effective water-cement ratio and the internal curing effect. Adding 1.0~1.5% of SAP improved the freeze-thaw resistance similar to the case of adding the AE agent, and the addition of more than 1.0% of SAP improved the chloride penetration resistance. The optimal adding ratio of SAP is 1.5%, and the adding ratio of 2.0% or more adversely affects the compressive strength and freeze-thaw resistance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.919-922
• /
• 2008

This paper reports the physical and shrinkage properties of concrete using expansive additive(E) and three shrinkage reducing admixtures(SRA1, 2, 3) in order to reduce shrinkage of concrete. For the properties of fresh concrete, the use of SRA1, 2, 3 results in a increase in fluidity and decrease in the dosage of super plasticizer as much as 0.05$\sim$0.1%. And For the properties of hardened concrete, the use of SRA1, 2, 3 results in a decrease in compressive, tensile and flexural strength slightly. For drying shrinkage properties, the use of SRA3 is the most effective for reduction of shrinkage, and the next best way to reduce shrinkage is combination with expansive additive(E) and shrinkage reducing admixture(SRA) or the using of expansive additive(E).

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.885-888
• /
• 2008

In recent years, the terminology "High-Performance Concrete(HPC)" has been introduced into the construction industry. Most high-performance concretes have a high cementitious content and a low water-cementitious material ratio. The proportions of the individual constituents vary depending on local preferences and local materials. Therefore, many trial batches are usually necessary before a successful mix is developed. The objective of this experiments is to investigate the fundamental properties of high performance concrete based binary cimentitious materials such as ordinary portland cement and ground granulated blast furnace slag. The results from the study will be utilized as the basic data and guideline in making standard mixproportions and the manufacture, construction work and quality control of HPC

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.12 no.4
• /
• pp.95-106
• /
• 1992

This paper presents a comparative evaluation of five different types of steel fibers used as reinforcing material in concrete beams. Two types of plain and RC beams were prepared to compare the relative flexural behavior. The fibers used were dog bone (paddled), both ends hooked. コ-type straight. crimped and wavy type with aspect ratio of 43 to 75. Fiber volume fraction of 1 to 2% were used while shear span to depth ratio (aid) and steel ratio p were fixed. Fiber reinforcement effect index Ef and effective toughness index Te were adopted to evaluate fiber reinforcing effects. The effect of fiber reinforcement on flexural strength is higher in plain beams than in RC beams. Hooked and dog bone type fibers were found to be more effective than the other type ones in enhancing the flexural strength and post-peak energy absorption capacity of concrete beams.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.813-816
• /
• 2008

This study is an experimental study on the properties and efficiency of mold-prevention mortar and the results are summarized as following. The flow, compressive stress, and the drying shrinkage ratio of mold-prevention mortar was similar with plain, so it was shown that the mold-prevention does not influence physical effect specially. However, the mold-prevention mortar which even mixed with few mold, the mold-prevention capacity greatly increased. Also, the mold-prevention capacity of 1:4 ratio mortar was better than 1:2 ratio mortar.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.225-233
• /
• 2011

The volume change in concrete takes place with changes in temperature and water content immediately after concrete casting. In the early age stage, the thermal and drying shrinkages can cause cracks that are very crucial to the durability of concrete. It was reported that when the cement with lightly-burnt MgO powder was used, the shrinkage of concrete can be reduced. This study investigates fundamental properties of cement composites with lightly burnt MgO powder by performing various experiments. The stability test results verified that MgO powder in cement composites does not cause any abnormal expansion. Also, the hydrate product analysis results obtained from MgO cement paste showed that MgO powder reduces the shrinkage at the longterm ages. In addition, the cement composites containing the proper amount of MgO powder could improve compressive strength. Finally, the shrinkage reduction from using MgO powder can be optimized by increasing MgO replacement level and curing temperature.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.6
• /
• pp.485-494
• /
• 2019

This study is to evaluate the effect of admixtures such as blast-furnace slag and fly ash on adhesion in flexure and tension of polymer cement mortar(PCM) using SAE emulsion. The test specimens are prepared with five polymer-cement ratios and five admixture contents, and tested for flexural strength, adhesion in flexure, tensile strength and adhesion in tension. Based on the test results, no improvement of flexural strength and adhesion in flexure caused by admixtures in PCM can be indicated, but the tensile strength and adhesion in tension is improved due to mixing of the admixtures. In particular, the maximum of adhesion in tension of PCM with P/C 20% and BF content of 10% is 3.35MPa which is about 2.36 times higher than that of ordinary cement mortar, and 1.32 times that of PCM that does not contain any admixture. The average ratio of adhesion in tension to tensile strength of PCM was 48.7%. It is apparent that admixture contents of 5% or 10% could be proposed for improvement of tensile strength and adhesion in tension of PCM.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.90-99
• /
• 2015

This study examined dynamic and characteristics and chloride penetration of concrete mixed with large amount of FA and BFS, which are considered for positive application to construction fields with purpose of long-tern durability of concrete structures. As a result of strength test on FA and BFS, FA concrete showed higher increase of strength compared to OPC, when FA4000 and FA5000 were mixed 30%, respectively. For BFS concrete, those mixed with 30% and 50% of BFS8000, respectively, showed higher or equivalent strength compare to OPC. As a result of test of chloride penetration on FA and BFS, diffusion coefficients of concrete mixed with 30% FA4000 and FA5000, respectively, showed to restrain average 6.5% of diffusion coefficient compared to OPC. And in case of BFS concrete, those mixed with BFS6000 and BFS8000, restrained diffusion of chloride ions 253% and 336%, respectively, compared to OPC. Therefore, Mixing 50% of BFS was most efficient in order to maximize restraint of chloride penetration according to metathesis of large amount. For relation between compression strength and diffusion coefficient of FA and BFS concrete, as strength increased, diffusion coefficient decreased. In this study, when mixing FA and BFS to concrete for long-run durability and restraint against chloride penetration, for FA, mixing it to concrete with less or equivalent 30% of replacement rate was most efficient. And for BFS, as fineness was higher and mixing it to concrete with less or equivalent 50% of replacement rate, there were results of higher strength compared to OPC and more efficient restraint of chloride ions.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.357-363
• /
• 2016

To solve the exhaustion problem of natural aggregate which were create the high value in construction and environmental industry, recycled aggregates have considerable benefits than other materials. However, even though many researches have been conducted with recycled aggregates, building structures with recycled aggregated are rarely constructed because it has lower quality than natural aggregates have. In this study, mechanical and strain properties of recycled aggregates concrete containing steel fibers have been reviewed in order to complement performance of recycled aggregates concrete. As results, recycled aggregates concrete showed lower compressive strength and elastic modulus than plain concrete. But, recycled aggregates concrete containing steel fibers showed equivalent performance with plain concrete. In review of drying shrinkage and creep coefficient, recycled aggregates concrete containing steel fibers showed similar behavior with plain concrete in the range of 0.5 Vol.% fiber content rate by internal restraint effect, moisture transport restraint effect and strength enhancement effect of steel fiber. Therefore, it is considered that mixing steel fibers with concrete is the effective method as a active application plan for recycled aggregates.