• Journal of Sensor Science and Technology
• /
• v.9 no.3
• /
• pp.242-247
• /
• 2000

$Pb_{0.99}[(Zr_{0.6}Sn_{0.4})_{0.9}Ti_{0.1}]_{0.98}Nb_{0.02}O_3(PNZST)$ thin films were deposited by RF magnetron sputtering on $(La_{0.5}Sr_{0.5})CoO_3(LSCO)/Pt/Ti/SiO_2/Si$ substrate using a PNZST target with excess PbO of 10 mole%. The thin films deposited at substrate temperature of $500^{\circ}C$, and at RF power of 80W were crystallized to a perovskite phase after rapid thermal annealing(RTA). The thin films annealed at $650^{\circ}C$ for 10 seconds in air exhibited the good structures and electrical properties. The fabricated PNZST capacitor had a remanent polarization value of about $20\;{\mu}C/cm^2$ and coercive field of about 50 kV/cm. The reduction of the polarization after $2.2{\times}10^9$ switching cycles was less than 10%.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.69-74
• /
• 2007

[ $0.6Pb(Sc_{1/2}Ta_{1/2})O_3-0.4PbTiO_3$ ] (hereafter PSTT) ceramics were prepared by the molten salt synthesis (MSS) method using KCI as a flux. Formation of perovskite phase was investigated by a differential thermal analysis (DTA) and X-ray diffraction (XRD) analysis in the temperature range from $600^{\circ}C$ to $850^{\circ}C$. A 92% perovskite phase was synthesized at $750^{\circ}C$ for 2 hrs using the MSS method, while 82% perovskite phase was synthesized at $850^{\circ}C$ for 4ks using the calcining of mixed oxide (CMO) method. This result could be due to the improvement in reactivity of $Sc_2O_3$ by melting of KCI. The MSS specimen sintered at $1,100^{\circ}C$ for 4hrs showed a dielectric constant of 11,200, a remnant polarization of $13.5{\mu}C/cm^2$ and a coercive field of 10.198 kV/cm, which was discussed in view of the microstructure.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.202-208
• /
• 1997

Bi-layered SrBi2Ta2O9(SBT) films were deposited on Pt/Ti/SiO2/Si sibstrates by rf magnetron sputt-ering at room temperature and then were annealed at 75$0^{\circ}C$, 80$0^{\circ}C$ and 85$0^{\circ}C$ for 1 hour in oxygen at-mosphere. The film composition of SrBi2Ta2O9 was obtained after depositing at room temperature and annealing at 80$0^{\circ}C$. Excess 20mole% Bi2O3 and 30 mole% SrCO3 were added to the target to compensate for the lack of Bi and Sr in SBT film. 200 nm thick SBT film exhibited and dense microstructure, adielectric constant of 210, and a dissipation factor of 0.05 at 1 MHz frequency. The films exhibited Curie temperature of 32$0^{\circ}C$ and a dielectric constant of 314 at that temperature under 100 kHz frequency. The remanent polarization(2Pr) and the coercive field(2Ec) of the SBT films were 9.1 $\mu$C/$\textrm{cm}^2$ and 85 kV/cm at an applied voltage of 3V, resspectively and the SBT film showed a fatigue-free characteristics up to 1010 cy-cles under 5V bipolar pulse. The leakage current density of the SBT film was about 7$\times$10-7A/$\textrm{cm}^2$ at 150 kV/cm. Fatigue-free SBT films prepared by rf magnetron sputtering can be suitable for application to non-volatile memory device.

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.375-380
• /
• 2004

Pb(Ni$\_$1/3/Nb$\_$2/3/)O$_3$-PbZrO$_3$-PbTiO$_3$ thick films were screen-printed on platinized alumina substrates and fired at 800-1000$^{\circ}C$. Two kinds of powders with different particle size were prepared by attrition and ball milling methods. Effects of particle size of starting material on the microstructure and electrical properties of the thick films were investigated. Average particle size of attrition milled-powder (0.44 ${\mu}$m) was much smaller than that of ball milled-powder (2.87 ${\mu}$m). Average grain size of the thick film prepared from attrition-milled powder was smaller than that of the thick film prepared from ball-milled powder at the sintering temperature of 800$^{\circ}C$. However, the difference in average particle size became smaller with increasing the sintering temperature. Thick films prepared from attrition-milled powders showed more uniform and denser microstructures at all firing temperatures. Thick films prepared from attrition-milled powders had better electrical properties at the firing temperature above 900$^{\circ}C$ than thick films prepared from ball-milled powders. Dielectric constant, remanent polarization and coercive field of the thick film prepared from attrition-milled powders and fired at 900$^{\circ}C$ were 559, 16.3 ${\mu}$C/cm$^2$, and 51.3 kV/cm, respectively.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.40 no.9
• /
• pp.631-637
• /
• 2003

We have evaluated structural and electric, ferroelectric properties of PZT(30/70) thick film prepared by using 1,3-propanediol based sol-gel method on Pt/Ti/SiO$_2$/Si substrates. Rapid thermal annealing (RTA) is used to reduce the thermal stress and final furnace annealing is processed at $650^{\circ}C$. As the results of SEM analysis, we find that we get 350 nm in thickness for one coating and 1 $\mu$m for three times of coating. In the results of C-D analysis at 1 kHz, dielectric constant ($\varepsilon$$_{r}$) and dissipation factor were 886 and 0.03, respectively. C-V curve is shaped as a symmetrical butterfly. Leakage current density at 200 kV/cm is 1.23${\times}$10$^{-5}$ A/cm$^2$ and in the results of hysteresis loops measured at 150 kV/cm, the remnant polarization (P$_{r}$) and the coercive field (E$_{c}$) are 33.8 $\mu$C/cm$^2$ and 56.9 kV/cm, respectively. PZT(30/70) thick film exhibits relatively good ferroelectric, electric properties.s..

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.9 no.3
• /
• pp.609-615
• /
• 2005

The effects of Zr/Ti concentration ratio in PLZT (10/y/z) thin films prepared by sol-gel method are investigated for the NVFRAM application. As Ti amount of Zr/Ti concentration ratio increases, the dielectric constants at 10 kHz decrease from 550 to 400, while the loss tangents increase from 0.028 to 0.053 and the leakage current densities at 170 kV/cm decrease from $1.64\times10^{-6}$ to $1.26\times10^{-7}\;A/cm^2$. In the results of hysteresis loops measured at $\pm170kV/cm$, the remanent polarization and the coercive field increase from 6.62 to $12.86{\mu}C/cm^2$ and from 32.15 to 56.45 kV/cm, respectively, according to the change from 40/60 to 0/100 in Zr/Ti concentration ratio. Fatigue and retention properties also improve much as the Zr/Ti concentration ratio change from 40/60 to 0/100. After applying $10^9$ square pulses with $\pm5V$, the remanent polarization of the PLZT (10/40/60) thin film decreases $50\%$ from the initial state while that of the PLZT (10/0/100) thin film decreases $28\%$. In the results of retention measurements of 10s s, the remanent polarization of the PLZT (10/0/100) thin film dec.eases only $10\%$ from the initial state, while that of the PLZT (10/40/60) thin film decreases $40\%$.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.9 no.5
• /
• pp.1066-1072
• /
• 2005

The effects of La concentration in PLZT (z/30/70) thin film prepared by sol-gel method are investigated for the NVFRAM application. As the La concentration increases, the dielectric constants at 10 kHz increase from 450 to 600, while the loss tangent and the leakage current density at 100 kV/cm decrease from 0.075 to 0.025 and from $5.83{\times}10^{-7}\;to\;1.38{\times}10^{-7}\;A/cm^2,$ respectively. In the results of hysteresis loops measured at 175 kV/cm, the remanent polarization and the coercive field decrease from 20.8 to $10.5{\mu}C/cm^2$ and from 54.48 to 32.12 kV/cm, respectively, with the increase of La concentration from 0 to $10mol\%.$ After applying for $10^9$ cycles of square pulses with ${\pm}5V$ height, the remanent polarization of the PLZT (10/30/70) thin film decreases $40\%$ from the initial state, while that of the PLZT (10/30/70) thin film decreases $64\%.$.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.28-33
• /
• 2008

Lanthanum modified lead zirconate titanate ($Pb_{1.1}La_{0.08}Zr_{0.65}Ti_{0.35}O_3$) thin films were fabricated on indium doped tin oxide (ITO)-coated glass substrate by R.F magnetron sputtering method. The thin films were deposited at $500^{\circ}C$ and post-annealed with various temperature ($550-750^{\circ}C$) by rapid thermal annealing technique. The structure and morphology of the films were characterized with X-ray diffraction (XRD) and atomic force microscopy (AFM) respectively. The hysteresis loops and fatigue properties of thin films were measured by precision material analyzer. As the annealing temperature was increased, the remnant polarization value was increased from $10.6{\mu}C/cm^2$ to $31.4{\mu}C/cm^2$, and coercive field was reduced from 79.9 kV/cm to 60.9 kV/cm. As a result of polarization endurance analysis, the remnant polarization of PLZT thin films annealed at $700^{\circ}C$ was decreased 15% after $10^9$ switching cycles using 1MHz square wave form at ${\pm}5V$.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.17-23
• /
• 1998

$Pb(Fe_{0.5}Nb_{0.5}O_3(PFN)$ thin films were prepared by rf magnetron co-sputtering method on $SiO_2/Si$, ITO/glass, and $Pt/Ti/SiO_2/Si$ substrates and post-annealed at the $N_2$ atmosphere by RTA(rapid thermal annerling). The degree of crystallinity of PFN films was identified on various substrates. Electrical properties of PFN films was characterized for $Pt/PFN/Pt/Ti/SiO_2/Si$ structure. The composition of PFN films was estimated by EPMA (electron probe micro analysis). PFN films would be crystallized better to perovskite phase on ITO/glass substrate than $SiO_2/Si$ substrate. This may be induced by the deformation of Pb deficient pyrochlore phase due to Pb diffusion into $SiO_2/Si$ substrate. PFN films on $Pt/Ti/SiO_2/Si$ substrate. PFN films with 5-10% Pb excess were crystallized to perovskite phase from $500^{\circ}C$ temperature. In summary, we show that Pb composition and annealing temperature were critically influenced on crystallinity to perovskite phase. When PFN film with 17% Pb excess was annealed at $600^{\circ}C$ at the $N_2$ atmosphere for 300kV/cm and 88. Its remnant polarization coercive field $2.0 MC/cm^2$ and 144kV/cm, respectively.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.143-151
• /
• 1994

On PT/Ti/Si substrates, PZT thln fllms are deposited at $300^{\circ}C$ by rf magnetron sputtering uslng a $(PbZr_{52}, Ti_{48})O_{3}$ composltc cerarnlc target. To abtaln, the stable phase, perovskltc structure, furnace annealmg techmque had been cmplo:~d In PbO amb~ent for the $550^{\circ}C$-$750^{\circ}C$ temperature ranges. On Pt(250$\AA$)/Ti(500$\AA$)/Si, Pt(1000)$\AA$/Ti(500$\AA$)/Si substrates, effects of Ti layer and Pt thickness are studled. Though thickness of the Pt layer 1s 1000$\AA$). oxygen diffusion is not prevented and accelerated by Ti layer actlng for oxygen sink sites durmg furnace annealing. The upper TI layer 1s transformed Into TIOX by oxyen dlffuslon and lower Ti layer Into silicide with in-diffused Pt. The formation of TiOx layer seems to affect the orlentatton of the PZT layer. Furnace annealed f~lm shows ferroelectr~c and electrical properties wth a remanent polarlzation of 3.3$\mu A /\textrm{cm}^2$, , coerclve fleld of 0.15MV/cm, a=571 (10kHz), leakage current 32.65$\mu A /\textrm{cm}^2$, , breakdown voltage of 0.4OMV/cm.