• Journal of the Korean Applied Science and Technology
• /
• v.34 no.4
• /
• pp.851-856
• /
• 2017

The mechanical properties of coating resin on stainless steel were measured by SEM, FT-IR spectra, tensile properties, mole ％ of [NCO/OH], and particle size analyzer. Growing concerns in the environment-friendly coating resin, we have synthesized the solvent-free coating resin to be coating on metals such as stainless steel. The properties of the synthesized coating resin to be contained polyols, MDI, silicone surfactant, fillers and vegetable oil(castor oil), that they have highly stronger in intensity and longer durability than general coating resin of polyurethane resin on stainless steel. The rigid segments of polyurethane in mechanical properties of coatings were due to unsaturated vegetable oil and the increase mole % of [NCO/OH]. In conclusion, the coating microstructure with castor oil can be good material for coatings of anticorrosion of metal substrates such as stainless steel.

• Journal of Conservation Science
• /
• v.31 no.4
• /
• pp.499-506
• /
• 2015

The artifacts of Admiral Yi Sun-sin (Treasure No.326) consist of six items with two long swords, a jade decoration, a belt and two peach-shaped cups. In commemoration of the opening of Chungmugong Yi sun-sin Memorial Museum (April 28, 2011), there were conservation treatments for those artifacts at the beginning of 2011. At that time, from the result of non-destructive surface analysis on pigments in blood-colored grooves of the two long swords, it was presumed to be synthetic resin paints. This study shows the accurate identification on pigments which was presumed as synthetic resin paints and its removal. To identify pigments in blood-colored grooves, the optical microscope, scanning electron microscope, Micro-XRF, XRD and FT-IR were used for the analysis. The results turned out that the thickness of $10{\sim}90{\mu}m$ in a single layer was measured. And major components containing Pb and Cr and lead chromium molybdenum oxide were identified and to identify components of adhesives from the analysis by FT-IR, it turned out to be alkyd resin, which can be presumed that they were recently colored with synthetic paints. The synthetic paints easily react with most of the organic solvents. And it is so easy to handle without the effect on metal that it was removed with acetone. While removing synthetic paints, all of paints on it were collected for identifying whether there is traditional pigment but nothing was identified.

• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.349-358
• /
• 2001

Silyl group-containing acrylic resins were synthesized to prepare weather resistant coatings. Acrylic copolymer was synthesized by the addition copolymerization of n-butyl methacrylate, methyl methacrylate, n-butyl acrylate and 3-methacryloxypropyl trimethoxysilane (MPTS). Acrylic copolymer were synthesized such that their $T_g$'s were adjusted to $20^{\circ}C$ and their MPTS contents were varied to 10, 20 and 30 wt%. As the content of MPTS increased, viscosity of coatings increased and thermal stability at the high temperature was improved. Coatings was prepared by blending the synthesized resins with a white pigment. The adhesion performance of coatings was superior with various substrates and their other properties were on the whole suitable. Weatherability was tested by outdoor exposure test, WOM test and QUV test. It was proved that resin with 30 wt% MPTS was suitable as the binder for weather resistant coatings.

• Applied Chemistry for Engineering
• /
• v.24 no.2
• /
• pp.171-176
• /
• 2013

The need of volatile organic compound (VOC) free coating material has been increased to solve environmental problems such as the global warming. Nowadays, about 70~80% of coating materials used in the worldwide are a liquid type. Therefore, the development of non-solvent coating material that can minimize VOCs emissions is necessary to solve the global warming problem. In this study, acrylic monomers were added to develop non-solvent paints in order to improve disadvantages of the poor adhesion of a conventional phenolic resin caused by acidification. As a result, the blend resins of 2.818 Mpa phenol- formaldehyde resin/poly methyl methacrylate (PE/PMMA) has the best properties and performances for the adhesives.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.2
• /
• pp.476-487
• /
• 2021

To prepare acrylic resin coatings containing 70% of solids, we used n-butyl methacrylate(BMA), methyl methacrylate(MMA), 2-hydroxyethyl methacrylate(2-HEMA), and acetoacetoxyethyl acrylate(AAEA), caprolactone acrylate(CLA) as raw materials, the glass transition temperature(T_g) of acrylic copolymer was adjusted around 50 ℃. The viscosity and molecular weight of the acrylic resins was increased with increasing OH values. Di-tert-amyl peroxide was found to be the suitable initiator to get high-solids acrylic resins. The optimum reaction conditions found in the study are 5 wt% of initiator, 4 wt% of chain transfer agent, 4 hrs of dropping time, and 140 ℃ of reaction temperature. The structure of the synthesized resins were characterized by FT-IR and ¹H-NMR spectroscopy. Number average molecular weight of 1900~2600 and molecular wight distribution of 1.4~2.1 were obtained. Crosslinked acrylic urethane clear coatings were obtained by curing reaction between the synthesized acrylic resins and hexamethylene diisocyanate trimer(Desmodur N-3300), the equivalent ratio of NCO/OH was 1.2/1.0. The physical properties from the following studies were carried out: viscosity(Zahn cup #2), adhesion, drying time, pot-life, pensil hardness, and 60° specular gloss. Various properties of the acrylic urethane clear coatings were also evaluated on the coating specimens. Adhesion property to a substrate, drying time, pot-life, pencil hardness, and 60° specular gloss of prepared paint showed quite good properties. Futhermore, prepared paint containing 10% of CLA showed quite good properties for adhesion, low viscosity and high hardness.

• Polymer(Korea)
• /
• v.26 no.5
• /
• pp.615-622
• /
• 2002

Weather-resistant coatings were prepared by mixing a synthesized mill-base and let-down silicone/acrylic resin in weight ratios of 4 : 6, 3 : 7, and 2 : 8. The weatherability of the prepared coatings was tested. The thermal stability, general physical properties, and weatherability of the films of the coatings were improved with silicone content. Among the three mixing ratios mentioned, the ratio of 2 : 8 was the most suitable for the preparation of weather-resistant Coatings. The coatings containing 30 wt% of silicone proved to be a high weather-resistant coating.

• Journal of the Korean Applied Science and Technology
• /
• v.29 no.2
• /
• pp.317-322
• /
• 2012

The microstructures were examined by SEM, FT-IR spectra, tensible properties mole % of [NCO/OH], and particle size analyzer. Growing concerns in the environment-friendly industries have led to the development of solvent-free formulations that can be cured. We had synthesized the polyurethane resin having the ability to protect stainless steel against corrosion. Compared with general packing materials and coatings, this resin is highly stronger in intensity and longer durability. Polyurethane resins were composed of polyols, IPDI, silicone surfactant, catalyst and crosslink agent. Moreover, thermal fillers such as $Al_2O_3$, fume silica and $ZrO_2$ not only accelerated the curing rate but also improved the physical property as thermal barriers. The rigid segments of polyurethane in mechanical properties were due to crosslink agent and the increase of [NCO/OH]. In conclusion, the polyurethane microstructure with crosslink agent can be good material for themoset coating of metal substrates such as stainless steel.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.4
• /
• pp.1358-1364
• /
• 2019

The mechanical properties of Heavy duty resin of synthetic polyurethane-epoxy resin for stainless steel were measured by SEM, FT-IR, tensile properties, and specific mass loss by EIS analysis, etc. As interest in eco-friendly medium coatings increased, the Heavy duty coatings were synthesized for various metals such as stainless steel composed of Polyol, MDI, water bored Epoxy resin, filling agent, silicon surfactant, catalyst etc. The coatings of synthetic Heavy duty resin were increased tensile strength due to various temperature change, and the low-Specific Mass Loss was measured in a highly electrolytic solution. In conclusion, the Heavy Duty coatings composed of polyurethane and waterbored Epoxy resin were synthetic microstructure with cross linkage can be good material for coating of anticorrosion of metal substrates such as stainless steel.

• Korean Chemical Engineering Research
• /
• v.55 no.5
• /
• pp.586-592
• /
• 2017

In this study, acrylic resins with solids content of 75% were prepared by addition polymerization of n-butyl acrylate (BA), methyl methacrylate (MMA), 2-hydroxypropyl methacrylate (HPMA) and acetoacetoxyethyl methacrylate (AAEM) monomers. At this time, the glass transition temperature ($T_g$) of the acrylic resin was changed to 20, 30 and $40^{\circ}C$, and the hydroxyl value (OH value) was changed to 60, 90 and 120. As a result, the viscosity of acrylic resin increased with increasing $T_g$ and hydroxyl (OH) value. The synthesized acrylic resin was designed to have a high cross-link density to maintain high elasticity and high durability. The crosslinked acrylic resin was used to prepare an acrylic urethane clear coating by curing reaction with a block isocyanate (Desmodur BL-3175). The physical properties of the clear paints were analyzed by measuring viscosity, adhesion, pencil hardness and $60^{\circ}$ specular gloss. Acrylic urethane clear coatings were prepared as specimens and evaluated for various properties to be applied as top coatings for coil coating. The prepared coatings were excellent in adhesion, excellent in $60^{\circ}$ specular gloss and pencil hardness, and eco-friendly.

• Korean Chemical Engineering Research
• /
• v.55 no.5
• /
• pp.579-585
• /
• 2017

Acrylic resins containing tertiary amine were synthesized by a radical polymerization of monomers including n-butyl acrylate (BA), methyl methacrylate (MMA), n-butyl methacrylate (BMA) and dimethylaminoethyl methacrylate (DMAEMA), and diethylaminoethyl methacrylate (DEAEMA) containing tertiary amine. Synthesized acrylic resins were applied to develope coatings of acrylic resins containing tertiary amine. And ${\gamma}$-glycidoxypropyl trimethoxysilane (GPTMS) or ${\gamma}$-glycidoxypropyl triethoxysilane (GPTES) was used as hardener. Developed coatings were white colored ones to use titanium dioxide and were hardened with hardener for measuring their physical properties. Measured physical properties were basic properties, adhesivity and weatherability. As a result, developed acrylic resins coatings containing tertiary amine showed excellent adhesivity on various substrates and also showed the same result on weatherability on dry weather condition.