• 대한기계학회논문집A
• /
• 제28권6호
• /
• pp.807-815
• /
• 2004

In order to evaluate the static stability of hybrid carbody structures of Korean Tilting Train eXpress(TTX) caused by degradation of composites under ground environments, T300/AD6005 graphite/epoxy composite specimens were exposed to accelerated environmental conditions including ultraviolet radiation, temperature and moisture fer 2000 hours. It was found that the stiffness and strength of composites after aging were lower than those of unexposed specimens, and decreased as the aging time increases. The values of the degraded properties were used in the static analysis to check the static stability of hybrid carbody structures caused by environmental degradation of composites. The results shown that the structural stability of hybrid carbody structures was affected by the degradation of composites after exposure to accelerated aging environments.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2000년도 춘계학술대회 논문집
• /
• pp.57-62
• /
• 2000

This paper describes the need for a ductile Fiber Reinforced Plastic(FRP) reinforcement for concrete structures. Using the material hybrid and geometric hybrid. it is demonstrated that the pseudo-ductility characteristic can be generated in FRP rebar. Ductile hybrid FRP bars were successfully fabricated at 4mm and 10mm nominal diameters using an hand lay up method. Tensile specimens from these bars were tested and compared with behavior of FRP rebar and steel bar

• 비파괴검사학회지
• /
• 제28권1호
• /
• pp.46-53
• /
• 2008

복합재료의 내부 결함 평가를 위해 일반적으로 적용되어온 초음파 C-스캔 기법은 섬유자동 배열을 통한 정밀 성형 공정에 적용하기에는 많은 어려움이 있다. 따라서 본 연구는 복합재료의 정밀 성형 공정 중에 발생되는 각종 내부 결함들을 비파괴적, 비접촉으로 평가하기 위한 새로운 하이브리드 초음파 평가 기법을 확립하는데 목적이 있다. 이를 위하여 본 연구에서는 초음파 산란 반사(scattering reflection) 방식을 토대로 한 새로운 이중 피치-캐치(dual pitch-catch) 기법을 확립하여 기존의 결함평가를 위해 시험편의 스캔에 소요되는 시간을 줄이면서 우수한 결함 영상을 얻을 수 있는 새로운 하이브리드 기법을 개발하였다. 즉 두 가지 종류의 열경화성 및 열가소성 복합재료(carbon/epoxy, carbon/PPS) 적층판의 내부 박리(delamination) 결함의 영상화를 위하여 레이저를 이용한 유도 초음파의 발생 및 이중 피치-캐치(pitch-catch)방식을 토대로 한 비접촉식 공기 정합 트랜스듀서(air-coupled transducer)를 이용하여 결함 영상을 얻기 위한 핵심 알고리즘을 확립하였다.

• 수산해양기술연구
• /
• 제40권4호
• /
• pp.328-336
• /
• 2004

하이브리드 복합재료(Hybrid composites) 의 층간 파괴 인성치에 영향을 주는 인자 중 적층순서, 하중점변위율, 초기크랙길이를 변화 시켰을 때의 실험 결과는 다음과 같다. (1) CF/CF, CF/GF. GF/GF로 적층하였을 경우 층간파괴인성치값은 서로 같은 계면을 성형한 것보다 서로 다른 계면을 적층한 CF/GF의 경우가 강도면에서 가장 높게 나타나는 것을 알 수 있었다. (2) 하중점변위율은 미세한 변동은 있었으나, 하중점변위율의 영향은 거의 받기 않는 것을 알 수 있었다. (3) 초기크랙을 변화시켰을 때, 초기크랙길이의 영향은 일정하지 않았다. CF/CF인 경우는 초기크랙이 짧은 경우, CF/GF. GF/GF인 경우는 초기크랙이 긴 경우에 높은 값을 나타났다. 이것은 GF 섬유가 직조형태의 프리프레그로 되어 있어 크랙의 진전에 따라 섬유부스러기 등의 생성에 따른 영향이라고 생각된다. (4) 적층순서에 따라 파면의 섬유 분포 형태가 달랐으며 CF/GF인 경우가 섬유의 파손형태가 가장 복잡하게 나타났으며, 이것이 높은 층간파괴인성치를 나타내는 원인이라고 판단된다.

• 수산해양기술연구
• /
• 제39권4호
• /
• pp.262-268
• /
• 2003

하이브리드 복합재료(Hybrid composite)의 모드 I 층간파괴인성치에 영영향 주는 인자 중 적층순서, 하중점변위율, 초기크랙길이를 변화 시켰을 때의 실험 결과는 다음과 같다. (1) CF/CF, CF/GF, GF/GF로 적층하였을 경우 층간파괴인성치값은 서로 같은 계면을 성형한 것보다 서로 다른 계면을 적층한 CF/GF 의 경우가 강도면에서 가장 높게 나타나는 것을 알 수 있다. (2) 하중점변위율을 0.2, 2, 20mm/min로 변화하였을 때, 미세한 변동은 있었으나, 허중점변위율의 영향은 거의 받지 않는 것을 알 수 있었다. (3) 초기크랙을 25, 30, 35, 40, 50mm로 변화시켰을 때 초기크랙길이의 영향은 일정하지 않았다. CF/CF인 경우는 초기크랙이 짧은 경우, CF/GF, GF/GF인 경우는 초기크랙이 긴 경우에 높은 값을 나타냈다. 이것은 GF 섬유가 직조형태의 프리프레그로 되어 있어 크랙의 진전에 따라 섬유부스러기 등의 생성에 따른 영향이라고 생각된다. (4) 적층순서에 따라 파면의 섬유 분포 형태가 달랐으며, CF/GF인 경우가 섬유의 파손형태가 가장 복잡하게 나타났으며, 이것이 높은 층간파괴인성치를 나타내는 원인이라고 판단된다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2005년도 춘계학술발표대회 논문집
• /
• pp.94-97
• /
• 2005

The strength of aluminum 7075 and carbon composite hybrid joints was studied for adhesive, bolt, and the adhesive-bolt combined joints. Several hybrid joint specimens were tested to get the failure load and modes for three types of the joints. Adhesive Cytec EA9394S was used for aluminum and carbon bonding. Failure load of the adhesive-bolt combined joint was 94 % of the sum of the failure load of the separately bonded and bolted joints. Hybrid joint also showed more stable failure behavior than the simple adhesive or bolted joint.

• Composites Research
• /
• 제17권1호
• /
• pp.18-28
• /
• 2004

섬유강화 적층 복합재 차체 구조물의 강도를 평가하기 위해 전체 적층판 접근방법의 적용을 제시하였다. 180km/h급의 한국형 틸팅열차의 하이브리드 복합재 자체 기본설계를 검증하기 위해서 구조해석을 수행하였으며 또한 복합재 적층판의 강도를 구하기 위해 기계적 물성시험을 수행하였다. 결과적으로, 한국형 틸팅열차의 복합재 자체 구조물에서 발생하는 응력값들은 모두 파손영역의 안전한 범위 내에 존재하였으며 전체 적층판 접근방법은 초기 기본석계 단계에서 하이브리드 복합재 자체 구조물의 파손을 예측하는데 매우 유용함을 증명하였다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 춘계학술발표대회 논문집
• /
• pp.48-52
• /
• 2002

This paper describes the need for a ductile Fiber Reinforced Plastic(FRP) reinforcement for Concrete Structures. Using the material hybrid and geometric hybrid, it is demonstrated that the pseudo-ductility Characteristic can be generated in FRP rebar. Ductile hybrid FRP bars were successfully fabricated at Ø3mm and Ø10mm nominal diameters using the braidtrusion process. Tensile and bending specimens from these bars were tested and compared with behavior of stress-strain of steel bar and GFRP rebar

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 추계학술발표대회 논문집
• /
• pp.29-32
• /
• 2001

The objective of this work was to optimize processing parameters of hybrid thermoplastic composites in compression molding. The mechanical properties of the composites manufactured with various forming conditions were measured to characterize processing parameters. Polypropylene(PP) composites containing randomly oriented long carbon fiber and carbon black were used in this work. The composite materials contained 5%, 10%, 15%, and 20% carbon fiber and 5%, 10%, 15%, 20%, and 25% carbon black by weight. Compression molding was conducted at various mold temperatures. The temperature of the material in the mid-plain was monitored during the forming. Crystallinity was also measured by using XRD. The tensile modulus of the composites increase, with increasing the mold temperature. However, the impact strength of the composites decreases as mold temperature increases.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 추계학술발표대회 논문집
• /
• pp.195-198
• /
• 2001

To improve the properties of FRP composite materials, the hybrid prepreg with non-woven tissue (NWT) is developed. The hybrid prepreg consists of undirectional prepreg and NWT prepreg. The NWT prepreg is made by compounding the NWT and polymer resin, which is similar to the production method of FRP prepreg. The NWT has short fibers which are discretely distributed with in-plane random orientation. The stiffness and strength of NWT composites are lower than those of continuously fibrous composites. The strengthening technique and fabricating technique for the hybrid prepreg are described in this work. The mechanical characteristics of hybrid composites with NWT are discussed and compared with those of the FRP composites.