• Journal of Korean Society of Steel Construction
• /
• v.11 no.4 s.41
• /
• pp.409-416
• /
• 1999

The fatigue crack growth analysis based on the fracture mechanics is useful to the estimation of the fatigue life on welded structures under cyclic loading. The analysis procedure in fatigue crack growth under uniform axial loading is applicable to bending fatigue problem as well. The intent of the present study is to show the procedure for calculating the fatigue crack propagation lifetimes of deckplates under bending stress and to explain the crack growth rates for the two dimensional crack problems. It is shown that the fatigue crack grows at a decreasing rate and the fatigue life depends on the initial crack length and the crack shape. The numerically predicted crack growth agree with the experimental data.

• Journal of Korean Society of Steel Construction
• /
• v.22 no.6
• /
• pp.589-597
• /
• 2010

Steel structures have a higher probability of being damaged by fatigue than by other causes of deterioration. As such, their maintenance to prevent fatigue damage is essential to sustain their safety and performance during their service period. In their maintenance, the current state of their fatigue cracks must be assessed to determine appropriate reinforcement methods and the suitable time intervals of periodic inspections when fatigue cracks are detected. Determining the crack growth rate is a successful method of predicting fractures, but it requires technical knowledge on fracture mechanics and experience in numerical methods and software for finite element analysis. In this study, a fatigue crack growth test on through-thickness cracked steel plates was conducted to assess the crack growth rate without superior technical knowledge and experience. The relationship between the Crack Opening Displacement (COD) and the crack growth rate was found in relatively long fatigue cracks.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.2
• /
• pp.179-188
• /
• 2011

Steel structures have been allowed to have fatigue damage tolerance in fact. If it would be assessed whether fatigue crack is growing or not and How fast fatigue crack is propagating, we should make a rational decision on methods and a period of reinforcement in the maintenance. In this study, fatigue crack growth tests on two kinds of through-thickness cracked steel plates and a out-of-plane gusset welded joint were conducted to evaluate fatigue crack growth rate using the COD(Crack Opening Displacement), and COD measurement using strain gauges was examined to offer a practical method. As a result, we proposed a reasonable assessing method for fatigue crack growth rate using the COD and it was experimentally proved practical to estimate the COD through measuring strains.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.6
• /
• pp.1568-1575
• /
• 1990

Fatigue crack growth behavior was investigated in the center cracked plate of KS SB41 steel and the relation between the crack growth rate and various mechanical parameters was studied at small scale yielding, large scale yielding and full scale yielding. The crack opening ratio U was about 0.6-0.8 and had the larger value in the case of load control than that of strain control. Effective stress intensity factor range, .DELTA.K$_{eff}$ and J integral range, .DELTA.J were obtained from the notion of crack opening, and the crack growth rate was expressed with these values. The value of J integral range increased rapidly at stress ratio, R=0 in full scale yielding of load control test. COD value also increased rapidly with the increase of ligament net stress at large scale yielding of load control test.t.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.3
• /
• pp.916-923
• /
• 1991

본 연구에서는 표면 균열이 있는 평판의 탄소성 피로하중 상태에서 성장하는 균열 형태의 변화와, 작용하는 응력의 크기에 따른 균열 개페구 특성의 변화를 연구하 였다.또, 유효 응력 확대계수 범위, .DELTA.K$_{eff}$와 J적분범위, .DELTA.J가 탄소성 응력 상태에서의 표면 피로균열 진전속도를 나타내는 역학양으로 사용되는데 따른 적합성등 을 검토하였다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.5
• /
• pp.938-946
• /
• 1989

Using the CT specimen of carbon steel(SM45C), we estimated the fatigue crack propagation behavior in stable crack propagation range. Furthermore the fatigue crack propagation rate, Acoustic Emission(AE) count rate, and fractography characteristics were also compared among others. The following results were confirmed by experimental observation. Near-threshold stress intensity factor range(.DELTA. $K_{th}$) is influenced by stress ratio but not at the upper limit of stable crack propagation range. As stress intensity factor range(.DELTA.K) and(or) stress amplitude increase (s), both crack propagation rate(da/dN) and AE count rate(dn/dN) increase. Effective stress intensity factor range(.DELTA. $K_{off}$) determined from the crack closure point measurement by AE method is useful for the evaluation of fatigue crack propagation rate. Fractography in stable crack propagation range showed striation, and agreed with the crack propagation rate obtained either by experiment of by the results of microscopic measurements.s.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.36-41
• /
• 1997

액체금속로는 고온 하중 효과(피로, 크립, 크립-피로)를 고려한 내열응력설계가 중요하다. 최근에는 액금로 후보재료로서 종래의 스테인레스강에 질소를 첨가하여 고온강도를 계량한 316LN 스테인레스강이 개발되었다. 본 연구에서는 액체금속로 재료의 가장 지배적인 손상 기구로 인식되고 있는 피로-크립 파손에 대한 설계자료를 확보하기 위해 DCPD(Direct Current Potential Drop)법에 의한 고온피로균열 측정 시스템을 개발하고 316L 및 스테인레스강인 316LN 스테인레스강에 대한 고온 피로균열진전시험을 수행하였다. 본 연구에 의해 개발된 피로균열진전속도 측정 시스템에 의하면 25$\mu\textrm{m}$ 이하의 분해능으로 균열길이를 측정할 수 있다. 한편 316L 스테인레스강에 질소를 적당량 첨가하면 상온에서 $600^{\circ}C$사이의 온도에서 피로균열진전에 대한저항성이 증가하는 것을 확인하였다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.5
• /
• pp.921-927
• /
• 1989

One of the most important problems in recent life prediction is to introduce the degradation effects into life prediction procedure. In the present paper, the effect of the material degradation on the fatigue surface crack growth and fatigue life prediction in a 2 1/4 Cr-1Mo steel were investigated. The 2 1/4 Cr-1Mo steel has been used in a plant having operated for over 60000hours and subjected to material degradation due to temper-embitterment. A Monte-Carlo simulation was made on the basis of the data obtained in the experiment in order to determine the P-S-N diagrams of surface crack growth for the degraded and recovered steels.

• The Journal of the Convergence on Culture Technology
• /
• v.10 no.1
• /
• pp.363-368
• /
• 2024

Steel structures used in marine environments, such as ships, offshore structures or sub-structures in wind power generation facilities are prone to corrosion. In this study, the corrosion fatigue crack propagation characteristics due to the environmental load are examined by experiment at -1050 mV vs. SCE, which is equivalent to the anti-corrosion potential of zinc anodes that are widely used as sacrificial anodes. In this study, for this purpose, an experimental study is conducted on the effect of cathodic protection on the propagation of fatigue cracks in the seawater environment under the condition of -1050 mV vs. SCE, considering the wave period in synthetic seawater. Cathodic protection prevents corrosion; however, excessive protection generates hydrogen through chemical reactions as well as calcareous deposits. The fatigue crack propagation rate appeared to be faster than the rate in a seawater corrosion environment at the early stages of the experiment. As the crack length and stress intensity factor K increased, the crack propagation rate became slower than the fatigue crack propagation rate in seawater. However, the crack growth rate was faster than that in the atmosphere.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.20 no.2
• /
• pp.11-17
• /
• 2016

Powder metallurgy nickel based superalloy has been used in a high temperature part of turbine engine for airplane. The fatigue crack growth behavior was investigated using CT specimens for the materials at room temperature(R.T.), $600^{\circ}C$ and $700^{\circ}C$. The direct current potential drop(DCPD) method suggested by ASTM E647 was used to measure the crack length during fatigue crack growth at various stress ratios. The fatigue crack growth rate at R=0.5 was faster than that at R=0.1 for all temperature conditions and increased with the increase of stress ratio and temperature. Fractography was conducted for analysis of fracture mechanism.