• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 춘계학술대회 논문집
• /
• pp.151-154
• /
• 2002

In this paper, the effect of the crack growth length on the plastic zone size at the crack tip and the crack growth lives of the DENT specimen under constant amplitude cyclic loading were studied. The plastic zone size was calculated by nonlinear static method in commercial finite element analysis program, MSC/NASTRAN and the crack growth lives were also calculated by using compliance function considering geometric shape in MSC/FATIGUE. The calculated plastic zone size increased proportional to the crack length. And comparison of calculated plastic zone size and crack growth lives with the experimental results shows a good agreement.

• 한국기계가공학회지
• /
• 제18권5호
• /
• pp.9-16
• /
• 2019

Recent economic trends are worsening and becoming longer, and Korean shipbuilding is focused on high value added and high technology, especially for LNG carriers and large container ships. Both ship types increased in size in the 2010s but have requirements such as high strength, toughness at low temperatures and continuous weldability for preventing brittle fractures at service temperatures. In particular, as container ships become larger, the International Classification Society (IACS) has established a provision (IACS UR S33) that mandates the use of BCA (Brittle Crack Arrest) certified vessels for large container vessels contracted after 2014 to ensure safety. Therefore, studies on BCA 47Y.P are currently being undertaken, but BCA 40Y.P has not been actively studied yet. We will test BCA 40Y.P to verify why it can be applied to a large container ship and measure fatigue cracking.

• 한국기계가공학회지
• /
• 제20권3호
• /
• pp.24-32
• /
• 2021

The size of container ships is increasing to increase the cargo loading capacity. However, container ships are limited in terms of the hull longitudinal strength. To overcome this limitation, brittle crack arrest steel can be used. This study was aimed at examining the influence of the heat input on the welding procedures of flux cored arc welding and submerged arc welding. In the experiment, the crack tip opening displacement test, which pertains to a parameter of fracture mechanics, was performed, and a 3-point bending tester was adopted. Based on the results, the crack measurement method was presented, and the stress expansion coefficient value for the pre-fatigue crack length was derived according to the heat input after the pre-cracking length was measured. It was noted that the heat input affected the crack tip opening displacement of brittle crack arrest steel.

• 대한기계학회논문집A
• /
• 제39권7호
• /
• pp.713-720
• /
• 2015

저압터빈 최종단 블레이드는 발전설비의 대용량화에 따라 대형화 되고 있으며, 터빈을 구성하는 모든 블레이드 중 상대적으로 그 크기가 가장 크다. 그 결과 블레이드는 매우 높은 원심력과 낮은 고유 진동수 특성을 가지며 그에 따른 각종 손상이 발생하게 된다. 최근 국내에서 가동연수 증가와 잦은 기동정지에 따른 저압터빈 최종단 블레이드의 손상이 자주 보고되고 있어, 본 연구에서는 유한요소법을 이용하여 원심력에 의한 응력해석, 응력경화효과에 따른 고유진동수 해석 및 조화응답해석을 수행 하였다. 그 결과 예측된 블레이드의 에어포일 선단부 최대 피로응력의 위치와 실제 균열의 발생위치가 일치함으로써 피로손상에 의한 결과임을 확인하였고, 노치에 의한 등가피로한도가 노치피로한도에 접근하였다.

• 대한조선학회논문집
• /
• 제28권1호
• /
• pp.108-116
• /
• 1991

선용재료중(船用材料中)에는 정적하중(靜的荷重)에 의한 정적거동(靜的擧動)(응력-변형률관계)과 반복하중(反復荷重)에 의한 반복거동(反復擧動)(응력진폭-변형률진폭관계)이 상이(相異)하게 되는 경우가 많다. 특히 탄소성(彈塑性) 응력집중부(應力集中部)에서 진전(進展)하는 초기의 짧은 피로균열(疲勞龜裂)은 재료(材料)의 반복거동(反復擧動)에 크게 의존하여 성장하므로 재료(材料)의 정적(靜的) 및 반복거동(反復擧動)의 비교, 검토가 요구된다. 본 연구에서는 2종류의 철강재료(鐵鋼材料)(SS41, HT80)와 5종류의 Al합금(合金)(A5083-O, A6N01-T5, A7N01-T4, A7016-T6, A7178-T6)에 대하여 정적(靜的) 및 반복하중(反復荷重)에 의한 재료(材料)의 응력-변형율(應力-變形率) 관계(關係)를 비교, 검토하였고, 각(各) 재료상수(材料常數)를 구하였다. 또한 응력집중부(應力集中部)에 일정 진폭의 반복하중(反復荷重)이 작용(作用)하여 탄소성(彈塑性) 변형(變形)할 때 그 선단(先端)의 응력(應力)과 변형률(變形率) 진폭(振幅)의 변화(變化)에 미치는 재료(材料)의 반복(反復) 경화특성(硬化特性)의 영향에 대하여 Neuber법칙(法則)과 중앙(中央)노치재(材의) 실험(實驗)에 의하여 고찰(考察을 행하였다.