• Journal of Korean Society of Steel Construction
• /
• v.14 no.6
• /
• pp.773-782
• /
• 2002

In this study, a series of fatigue tests are performed in order to estimate quantitatively the characteristics of fatigue crack growth rate according to the base metal, heat affected zone(HAZ) and weld metal, and the welding method and grade of strength of object steels, and the influence on fatigue crack growth rate according to the direction of welded line for high strength steels of SM570, POSTEN60, and POSTEN80 steels. From the fatigue test results, the retardations of fatigue crack growth rate are remarkable in case that the direction of notch is parallel to welded line than in case that the direction of notch is perpendicular to welded line because of compresive residual stress in weld metal & HAZ. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range. Meanwhile, fatigue safety is guaranteed sufficiently in the object steels because the fatigue crack growth rate in the range of fatigue crack propagation has a similar tendency to the test results & existing results.

• Polymer(Korea)
• /
• v.32 no.3
• /
• pp.270-275
• /
• 2008

Crack growth characteristics of elastomeric materials are an important factor determining the strength and durability. In this study, the fatigue crack growth characteristic of filled EPDM compounds with different reinforcing fillers, such as silica and carbon black, was investigated using a newly designed tester. Frequency and test temperature had significant effects on the fatigue crack growth. The crack growth rate decreased with increasing frequency and the rate increased with increasing temperature. A power law relationship between the tearing energy and crack growth was observed for filled EPDM compounds. The crack growth rate reduced with increasing filler contents. Silica filled EPDM showed a better fatigue resistance than carbon black filled EPDM. The crack growth rate of silica filled EPDM decreased up to 30 phr and increased again at 50 phr. The formation of microductile type pits was observed on the fatigue-failure surface of unfilled EPDM, and relatively coarse surface with randomly distributed tear lines was observed on the failure surface of silica filled EPDM.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.4
• /
• pp.375-381
• /
• 2011

The primary aim of this study is to investigate the probabilistic characteristics of the fatigue parameters that describe the fatigue crack growth behavior in magnesium alloy. Statistical fatigue crack propagation experiments have been performed on rolled AZ31 magnesium alloy CT specimens with different specimen thickness, load ratio, and maximum load at ambient temperature in a laboratory. Using the statistical fatigue data obtained from these experiments, the goodness-of-fit of the probability distribution of the fatigue behavior parameters is evaluated in this study by performing statistical analyses. The crack growth rate coefficient is a fatigue parameter having a very large COV(Coefficient of Variation), but the variation of a crack growth rate exponent is not substantial. It is considered that a crack growth rate exponent can be a material constant. It is also found that the best fit probability distribution of the parameters such as the crack growth rate coefficient and crack growth rate exponent for a magnesium alloy is a three-parameter Weibull distribution, and two-parameter Weibull distribution is a good distribution only for the crack growth rate coefficient.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.124-129
• /
• 1998

고온고압 수화학 분위기를 모사한 조건에서 피로균열성장 거동에 관한 연구를 수행하였다. 고온고압분위기 모사를 위해 Load machaine, Autoclave, Water loop, 균열측정장치(Reversing DCPD) 그리고 전기화학변수 측정장치 등을 설치하였다. 우선 공기분위기 및 상온수화학 분위기에서의 시험을 통해 안정성을 확인하였으며, 안정한 조건에서 고온수화학분위기에서 실험을 수행하였다. 수화학 분위기에서 용존산소에 상관없이 취성파면이 관찰되었다. 용존산소의 양이 적을 경우(10ppb이하) 발견된 취성파면의 양은 연성파면에 비해 훨씬 적었으며, 용존산소가 높을 경우(8000ppb) 취성파면의 양이 많이 발견되었다. 산소포화된 고온수화학 분위기 피로시험결과는 피로균열성장이 주로 취성파면에 의해 이루어졌으며, 균열성장속도 또한 크게 증가하였다.

• Nuclear Engineering and Technology
• /
• v.27 no.6
• /
• pp.825-832
• /
• 1995

The effect of loading variables and temperature on fatigue crack growth rate in SA508 Cl.3 nuclear pressure vessel steel was investigated in air environment Crack growth rate tests on compact tension specimen of thickness 12mm were conducted by using sinusoidal waveform. The crack length was monitored by compliance method. Test conditions were at 0.1 and 0.5 of load ratio, at 1 and 10 Hz of loading frequency, and at room temperature to 40$0^{\circ}C$. At the lower temperatures, the fatigue crack propagation was not affected by the frequency and temperature, while at the higher temperatures above 12$0^{\circ}C$, fatigue crack growth rate increased with decreasing loading frequency and increasing temperature. This accelerated fatigue crack propagation was associated with the increase of oxidation rate at the ahead of crack tip. Fatigue crack growth rate increased with in-creasing the load ratio. The effect of load ratio was more significant at the lower temperature, while the dependence on load ratio decreased with increasing temperature. The sensitivity of load ratio to temperature can be explained by crack closure with the oxidation process.

• Journal of the Korean Society for Precision Engineering
• /
• v.4 no.3
• /
• pp.19-27
• /
• 1987

부재가 피로하중을 받을 경우에는 피로하중의 변동과 균열의 성장에 인한 균열크기의 변동때문에 각순간에서의 응력확대계수가 변화하게 된다. 피로균열성장을 모델링할때 응력확대계수를 이용할 수 있는 타당성은 균열성장속도가 매우 느리므로 순간순간에서의 형상계수의 변화가 거의 무시할 수 있다는 사실에 근거하고 있다. 즉 균열의 길이는 순간순간에 일정하다고 생각하는 즉 준-정적인 문제로 귀착되며, 이 경우 에는 순간순간에 대응하는 단지 변동하는 하중에 대한 응력확대계수의 변동양상을 검토하면 되는 것이다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.42.1-42.1
• /
• 2009

오스테나이트 스테인리스강은 우수한 내식성 및 기계적 특성으로 인해 구조용 재료로 널리 사용되고 있다. 표준원전 경수로의 경우 가압기 밀림관소재로 Nb 안정화 오스테나이트 스테인리스강인 type 347 스테인리스강이 사용되고 있다. 그러나 원전배관에서는 운전중 배관내 온도편차에 의한 열응역과 하중변화에 의한 기계적하중에 의해 피로손상을 받는다. 일반적으로 범용 오스테나이트 스테인리스강(AISI 304, 316)의 피로균열 성장거동에 대한 연구결과는 국내외적으로 다수 축적되어 있으나 type 347 탄소, 질소 함량에 따른 기계적 특성 및 피로균열성장 연구는 매우 미비하다. 따라서 본 연구에서는 탄소와 질소의 함량에 따른 기계적거동을 평가하고, 이에 따른 피로균열전파속도를 관찰하여 스테인리스강의 정확한 피로균열전파속도 곡선을 제시하고자 한다. 실험에 사용된 시편은 두께 5mm, 폭 25.4mm CT시편을 사용하였으며, 1mm의 예비균열을 주었다. 그리고 실험온도는 상온과 원전가동온도인 $316^{\circ}C$에서 실시하였으며, 주파수는 10Hz를 주었다. 실험결과 각 함량에 따른 type 347의 미세조직 관찰결과 기지내에 압연방향을 따라 조대한 석출물의 흐름이 관찰되었으며, 크기나 분포가 큰 차이를 보였다. C+N 함량이 낮은 시편은 주로 $0.1\;{\mu}m$ 이하의 미세한 입자들이 오스테나이트 기지조직의 입내와 입계에 고르게 분포되어 있었다. 그러나 C+N 함량이 높은 시편의 경우에는 $0.1\;{\mu}m$ 이하의 미세한 입자들과 함께 국부적으로 $1\sim10\;{\mu}m$의 조대한 입자들이 분포하고 있는 것이 관찰되었다. 그리고 질소의 함량이 높아짐에 따라 인장강도는 증가하였으며, 피로시험결과 고온에서 실험한 피로균열성장률 곡선이 상온보다 높게 나타남을 확인할 수 있었다. 그리고 질소가 적게 첨가되고 탄소의 함량이 많을수록 피로균열성장률은 ASME 곡선보다 낮게 나타났다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.39.1-39.1
• /
• 2011

가압경수로의 압력경계기기는 약 $300^{\circ}C$, 150기압의 고온고압수환경에서 가동되고 있다. 특히 가압기 밀림관은 고온수와, 저온수가 교차하는 부분으로 열성층 형성으로 열적, 기계적 피로 및 수화학환경이 더해진 부식피로 등에 의하여 손상을 받는다. PWR 원전에서 수화학환경은 대표적으로 용존산소(DO) 5ppb, pH 6~8, 용존수소(DH) <30 cc/kg, 온도 $316^{\circ}C$의 환경을 유지하게 된다. 가압기 밀림관에는 오스테나이트계 스테인리스강이 사용되는데, 오스테나이트계 스테인리스강은 고온 수화학환경에 민감한 것으로 알려져 있다. 따라서 오스테나이트계 스테인리강을 공기중에서의 기계적특성 및 피로특성을 향상시키기 위하여 질소를 첨가한 스테인리스강을 제조하여 PWR 원전환경에서의 피로균열성장특성을 평가하였다. 실험에 사용된 재료는 PWR 원전 가압기 밀림관 소재인 Type 347 스테인리스강에 0.0005 wt%가 첨가된 상용재와 0.11 wt% 질소가 첨가된 재료이다. 사용된 시편형상은 두께 5 mm, 폭 25.4 mm의 CT 시편이다. 수화학환경은 150기압, 온도 $316^{\circ}C$, 용존산소(DO) 5ppb, 용존수소(DH) 30 cc/Kg, pH는 약 7로 유지 하였으며, 응력비 0.1, 하중 반복속도 10Hz의 기계적 조건에서 하중제어로 시험을 진행하였다. 균열길이는 직류전위차법(Direct Current Potential Drop: DCPD)을 이용하여 측정하였다. 질소함량이 증가할수록 동일 사이클에서 균열길이가 늦게 성장하였고, 피로균열성장속도도 약간 늦어지는 것으로 나타났다. 각 스테인리스강의 피로파면 관찰결과 상용재는 약 1 ${\mu}m$의 산화물들이 생성되는 반면 질소첨가 스테인리스강은 약 0.1 ${\mu}m$정도 산화물이 생성되었다. 산화막의 두께도 질소가 첨가됨으로써 상용재에 비해 얇게 생성되었다. 따라서 질소가 첨가됨으로써 부식환경에서 내산화성이 향상되었으며, 이는 피로균열성장특성에 영향을 미치는 것으로 판단된다.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.127-135
• /
• 1997

In this study, the wedge splitting tcst (WST) was carried out for the fatigue wack growth behavior of concrete. Selected test variables were concrete compressive strength of 28, 60 and 118 MI%, and stress ratio with 2 levels (6. 13%). In oder to make the designed stress ratio, the maximum and thr minimum fatigue loading level were 75-85% and 5- 10% of ultimate static load, respectively. Fatigue testing was preceded by crack mout.h opening displacement (CMOI)) compliance calibration tcst, and then the fatigue crack growth was computed by crack lcngth vs. (lMOI) compliance relations acquisited by the CMOD compliance calibration technique. To evaluate thc validity of CMOD compliancc calibration techniquc, the crack length p~mlicted by this method was cornpard with the crack length by linear elastic fracture mechanics(LEFIbl) and dyeing test. On the basis of the experimental results, a LRFhl-based c.mpirica1 model for f'at,igue crack growth rate(da/dN-AKI relationships) was presented. The fat,igut. crack growth ratc increased with the strength of concwtc. It appcars that t.he da/tiN-AKI relationships was influenced by stress ratio, however, the effect is diminished with an increase of strength. The comparisons between CblOl) compliance calibration technique anti the other. methods gave the validity of' ('MOD compliance calibration technique for the LZXT.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.3
• /
• pp.916-923
• /
• 1991

본 연구에서는 표면 균열이 있는 평판의 탄소성 피로하중 상태에서 성장하는 균열 형태의 변화와, 작용하는 응력의 크기에 따른 균열 개페구 특성의 변화를 연구하 였다.또, 유효 응력 확대계수 범위, .DELTA.K$_{eff}$와 J적분범위, .DELTA.J가 탄소성 응력 상태에서의 표면 피로균열 진전속도를 나타내는 역학양으로 사용되는데 따른 적합성등 을 검토하였다.