• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.1
• /
• pp.56-63
• /
• 2016

This experiment was compared and analyzed between the original surface paint through chloride penetration, neutralization, freeze-thaw and chemical corrosion resistance measuring internal structure and volume of voids in order to evaluate the effect of increase in durability of the newly modeled nano synthesized polymer paint painted on concrete surface which results improvement on air permeability to increase the durability of concrete structures. The test result of measuring volume of void and inner structure, concrete, spreaded with nano synthesized polymer paint, showed decreasing trend of pore volume in the range of less than $0.1{\mu}m$ and more than $0.3{\mu}m$. Also, using an electron microscope inside showed tightness of hydration texture. Chloride penetration depth of concrete, painted with nano synthesized polymer paint, was decreased more than 92% compared to non-painted concrete and 70% with water-based epoxy painted concrete. Especially, chemical corrosion resistance test set with aqueous solution of 5% sulfuric acid, non-painted concrete and water-based epoxy painted concrete showed weight loss of 4% after dipping for 12 days. On the other hand, concrete painted with nano synthesized polymer paint showed 1.7% weight loss under the same condition. Also, it showed great result of appearance under the criteria of Tsivilis et al.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.193-194
• /
• 2010

Developed is a chloride penetration analysis program that can consider a concrete surface coating. The effect of concrete surface coating on the service life is simulated by the developed finite element program. It was revealed that the coating at the earlier age is the more effective way to extend the service life.

• Proceedings of the Korean Fiber Society Conference
• /
• 2001.10a
• /
• pp.51-54
• /
• 2001

Mercerization은 대부분의 면제품에 널리 적용되고 있는 가공방법이나 일반적으로 이루어지고 있는 상온에서의 NaOH에 의한 mercerization은 용액의 표면장력과 점도 때문에 알칼리가 섬유내부까지 깊숙이 침투하지 못하고 이로 인해 섬유의 표면에만 Mercerization이 진행되어 태가 뻣뻣해지는 단점이 있다. 이러한 jamming effect에 의한 표면(skin)과 내부(core)간의 머서화차이를 제거하기 위하여 고온 머서화가공에 대한 연구가 진행된 바 있으나 에너지의 과다소비라는 측면에서 상업화되기에는 문제가 있는 실정이다. (중략)

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.5
• /
• pp.157-163
• /
• 2006

This study is on the evaluation of double surface protection method using water repellent primer and final top coat to protect concrete. Water repellent agent has been applied on the final top coat to protect concrete. However, to make up for the weakness to the ultraviolet of the water repellent, the work procedure of these protectors is done vice versa. This combination of protectors was compared with existing ones in this study. Even though the final top coat was applied on the water repellent primer, its adhesive strength met to KS F 4936-' 03 with other protectors used in this study. All surface protectors used in this study were excellent in protecting concrete. Especially, in case of applying with final top coat in conjunction with water repellent primer, the resistance against chloride ion penetration and neutralization by $CO_2$ was more efficient than other surface protectors used in this study under this given condition.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2001.11a
• /
• pp.45-45
• /
• 2001

종이 표변에 전분 사이징을 하는 목적은 종이가 액체에 대하여 침투저항성을 부여하 여 종이의 인쇄적성을 향상시키며 아울랴 종이의 표면적성과 종이강도 등의 물리적 특 성을 향상시키기 위해서 사용된다. 표면 사이징은 기본적으로 종이 표면에 전분을 이용 한 필름을 형성하여 종이 표면의 공극크기를 줄여 인쇄잉크 등과 같은 액체의 침투속 도를 늦여준다. 현재 국내에서 널리 사용되는 표면 사이징용 전분으로는 산화전분과 자 가변성용 일반전분이 있다. 자가변성용 전분은 효소나 APS로 전분의 chain 길이를 적 당한 점도로 잘라주는 것으로 전분 호액의 노화가 쉽게 일어나는 경향이 있다. 산화전 분은 전분회사에서 산화제를 이용하여 전분의 점도를 사용자의 요구에 따라 조절한 것 으로 water holdout이 개선되고 자가변성용 전분보다는 노화 안정성이 개선되지만 종 이 내부로의 칩투가 많이 일어나 전분 필름 강도가 약해지며 표면 강도 향상 효과가 적고 종이의 광학적 특성을 저하시키는 단점을 지니고 있다. 또한 약 10 ~ 20% 정도 사 용되는 파지의 재활용시 펄프 섬유에 흡착되지 않는 전분으로 인해 백수 내의 COD 및 B BOD를 증가시키는 원인이 된다.따라서 본 연구에서는 펄프 섬유와 친화력이 높아 지료 내첨용 지력증강제로 널리 사용되고 있는 양성 전분의 양이온 치환도 및 점도를 사이즈 프레스에 적합하게 조절 하여 백상지 제조업체의 라언에 적용하였다. 결과분석 항목으로는 파지 재활용에 따른 백수내 COD, 칼숨 이온함량 등의 백수 시스템의 변화와 종이의 물리적, 광학적 특성 및 ink jet 용지의 인쇄적성 등을 측정하여 산화전분과 비교하였다. 그 결과 약 20%의 C COD 감소 효과와 10%정도의 OPR 향상 효과를 얻을 수 있었다. 종이 물성의 경우 인 장강도와 뺏뺏이(stiffness) 및 지분 등을 측정한 결과 산화전분 보다 향상되었다. 특히 지분의 경우, 참여한 회사의 지분관련 complain이 약 80% 정도 감소하는 결과를 나타 내었다. 또한 백상지의 경우 ink jet 프린터에 많이 사용됨으로 ink jet 프린터의 인쇄 적성을 image analyzer로 측정한 결과 산화전분 보다 향상된 결과를 나타내었다.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2009.10a
• /
• pp.221-228
• /
• 2009

• Proceedings of the Korean Vacuum Society Conference
• /
• 2003.08a
• /
• pp.83-83
• /
• 2003

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.16-23
• /
• 2018

In this study, Polydimethylsiloxane (PDMS) was applied to Strain Hardening Cement Composites (SHCC) for penetrating water repellency. The penetration depth of PDMS, strength of SHCC, and chloride ion penetration resistance of SHCC were investigated. As a result of measuring penetration depth of PDMS when applying different application method, it was confirmed that all methods satisfied the requirements of KS F 4930. Although the immersion method showed the largest penetration depth, the spray method was considered to be more appropriate considering the ease of field application. Compressive strength tests showed that the penetration depth of PDMS decreased as the compressive strength of SHCC increased. The compressive strength of M4-A and M4-B specimens with large PDMS penetration depths decreased by 9.6% and 8.0%, respectively, compared with those of M4 specimens produced without PDMS. Compressive strengths of the M1-A and M1-B specimens with small PDMS penetration depths were reduced by 4% and 2.2%, respectively, compared with the M1 specimen. As a result, it can be seen that the strength reduction rate of SHCC increases as the penetration depth of PDMS increases. The chlorine ion penetration tests showed that the chlorine ion penetration resistance increases with the penetration depth of PDMS.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2020.06a
• /
• pp.331-331
• /
• 2020

급격한 산업화와 도시화로 인한 도시유역의 불투수면의 증가와 이에 따른 배수능력의 저하로 인해 도시 물순환의 왜곡이 발생하였다. 따라서 과거 도시 물관리 기법의 한계가 나타났으며 이를 위해 저영향개발 기법 등과 같은 도시 물관리 기법의 패러다임이 변화하였다. 본 연구에서는 저영향개발 기법에서 도시유역 내 활용이 유용한 침투형 시설 중 투수블럭에 대한 물순환 성능평가를 실외실험을 통해 분석하였다. 성능평가 실험은 부산대학교 양산캠퍼스 한국 GI&LID 센터 내 투수블록 뿐만 아니라 블록 하부 골재층까지 설치가 가능하도록 되어있어 실제 현장과 유사한 환경을 구축이 가능한 2.4×10.9×0.4 (m) 규모의 주차장형 LID 실증시험시설을 활용하였다. 인공강우 분사를 위한 실외 인공강우모사 장치 크기는 2×2(m)으로 본 시험을 위하여 5개의 인공강우모사 장치를 연결하여 활용하였으며, 본 시험장치는 강우를 공급하기 위한 수조와 펌프, 일정한 유량을 유입하기 위한 유량계, 강우를 분사하기 위한 노즐, 인공강우가 실제 강우와 같이 자유낙하 하도록 구현하기 위한 오실레이터 등으로 구성되었다. 시험대상인 틈새투수블록은 석재블록 규격 400×600×100 mm이며 재질은 받침안정층(흙), 투수블록(화강석)으로 구성되어 있다. 실험의 시나리오는 시험체에 강우강도 30mm/hr, 50mm/hr, 100mm/hr에 해당하는 양을 1시간 동안 유입하여 시험 시작 후, 강우지속시간, 표면유출지속시간, 표면유출량을 1분 단위로 측정. 시험체에 유공관이 설치된 경우에는 침투유출지속시간, 침투유출량도 함께 1분 단위로 측정하였으며 각 강우강도별로 측정하고, 1회 측정 후, 각 시험별 시험 대상체의 조건을 같게 하기 위한(하부 지반의 건조) 약 3일 이후(상황에 따라 변동 가능) 시험하였다. 본 실험의 결과, 강우강도가 30 mm/hr와 50 mm/hr인 경우에는 화강석 틈새투수블록포장에서 지표 유출이 발생하지 않았으며, 강우강도 100 mm/hr의 경우 260 L의 지표 유출이 발생하여, 불투수표면 대비 84%의 지표유출 저감률을 보여줌으로서 투수블럭에 물순환 성능에 대한 효과를 분석하였다.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.6
• /
• pp.47-52
• /
• 2008

Deicer has been generally used for prevention of a road freezing in winter, and the usage amount is increasing every year. However, deicer may induce the decrease of bond strength, surface scaling, and environmental pollution. In this study, the field test was performed to investigate the deterioration of concrete road structures used for 17 years. And, the corrosion resistance characteristics were compared for the existing deicer and eco-friendly deicer. According to the field test results, the penetration depth of limit chloride amount was about 40mm, and the average concentration of chloride was $3.45kg/m^3$ at the surface of structures. On the contrary, the carbonation depth was slight. The penetration depth of eco-friendly deicer was less than the existing deicer, and the corrosion resistance of eco-friendly deicer was higher.