• Journal of the Korean Society for Precision Engineering
• /
• v.23 no.4 s.181
• /
• pp.109-115
• /
• 2006

This paper is designed to estimate friction and powdering characteristic of coating layer on galvannealed sheet steel with different annealing temperature, which is 465, 505, 515 and $540^{\circ}C$, Estimations of powdering and friction were done using a $60^{\circ}$ bending test and one side friction test, respectively. In order to obviously understand the effect of coatings on friction cross-section of coatings before and after friction test was also observed by SEM. The results show that powdering of coatings is increased with increasing of annealing temperature and that friction characteristic greatly depends on powdering which leads to increase of real contact area between tools and coatings.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.1012-1015
• /
• 2005

This paper is designed to estimate friction and powdering characteristic of coating layer on galvannealed sheet steel with different annealing temperature, which is 465, 505, 515 and $540^{\circ}C$. Estimations of powdering and friction were done using a $60^{\circ}$ bending test and one side friction test, respectively. In order to obviously understand the effect of coatings on friction cross-section of coatings before and after friction test was also observed by SEM. The results show that powdering of coatings is increased with increasing of annealing temperature and that friction characteristic greatly depends on powdering which leads to increase of real contact area between tools and coatings.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.12
• /
• pp.1107-1114
• /
• 2008

This paper is aimed to understand the effect of different galvannealing temperatures on the frictional properties and Fe-Zn intermetallic phases of the galvannealed (GA) coatings on steel sheets. Their galvannealing treatments were conducted at 465, 505, 515 and $540^{\circ}C$ for about 10s in the additional heating furnace of an industrial continuous hot-dip galvanizing line. The mechanical and the frictional properties of the coatings were estimated using nanoindentation, nanoscratch, micro vickers hardness tests and flat friction tests, which were performed at contact pressures of 4, 20 and 80MPa. Also, the correlation between the microstructure and the frictional properties of the GA coatings were investigated by SEM observation for the cross-section of the GA coating after and before flat friction tests. The results showed that the mechanical and the frictional properties of the coatings are strongly dependent on their phase distributions and microstructure. Especially, in low contact pressure of 4MPa the frictional properties of the coatings were dependent on the surface phases and morphology, while in high contact pressure of 80MPa it was influenced by their mechanical properties based on the dominant phase distributions.