• Journal of the korean Society of Automotive Engineers
• /
• v.18 no.3
• /
• pp.17-22
• /
• 1996

티타늄합금을 사용하여 흡기밸브, 배기밸브, 밸브스프링 리테이너를 시제작하였다. FEM 구조해석결과와 모터링 내구실험결과를 통해 이들 부품들이 신뢰성을 가지는 것으로 판명되었다. 엔진성능실험을 통해서 고속영역에서 엔진출력 및 토오크가 3-4% 향상되었다. 단 향후 엔진내구실험을 통하여 충분한 내구성검증이 필요하다고 판단된다.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.04a
• /
• pp.32-32
• /
• 2005

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.4
• /
• pp.245-251
• /
• 2013

Purpose: This study was conducted to compare in vivo biofilm formation on titanium surface and zirconia surface. Materials and methods: For biofilm formation on titanium and zirconia in oral cavity, after producing oral appliances using acrylic resin and orthodontic wire tailored to 9 subjects, we made titanium and zirconia specimens ($6mm{\times}6mm{\times}2mm$), fixed them on oral appliances and maintained them in oral cavity of test subjects for 24 and 72 hours. Test subjects who have equipped two pairs of specimens maintained oral hygiene not by using toothpaste but only by tooth brushing. After 24 and 72 hours, we removed and observed specimens through scanning electron microscopy (SEM). Results: Biofilm formation showed large deviation depending on individuals. For formation comparison between titanium and zirconia for 24 hours, zirconia showed less biofilm formation than titanium. Biofilm formation showed large deviation depending on individuals. As for formation comparison between zirconia and titanium, the degree of biofilm formation in zirconia was less than it was in titanium after a lapse of 24 hours. The result of biofilm formation in 72 hours trial show that zirconia has an inclination to formate less biofilm than it was in titanium. Conclusion: Based on the above results, we can conclude that early biofilm formation in oral cavity was influenced by difference of abutment materials.

• Analytical Science and Technology
• /
• v.16 no.4
• /
• pp.261-268
• /
• 2003

To investigate the matrix effect of sample for hydrogen analysis by inert gas fusion-thermal conductivity detection, calibration factor for the hydrogen analyser of the inert gas fusion-thermal conductivity detection method was measured with hydrogen standard materials in Ti, Zr-2.5Nb and by hydrogen gas dosing method. Also the hydrogen extraction efficiency for the different sample matrix, Ti and Zr-2.5Nb, was evaluated without adding tin flux. The calibration factor of the hydrogen analyser which was calibrated by hydrogen standard material in Zr-2.5Nb and Ti was 2~3% and 14% higher than that by hydrogen gas dosing method, respectively. Based on the results of calibration factor measurement, it could be concluded that the hydrogen extraction efficiency of the Ti matrix sample will be 12% lower than that of the Zr-2.5Nb. And according to the experimental results of hydrogen recovery test by no tin flux, the hydrogen recovery percentage of the Ti and Zr-2.5Nb matrix sample was about 70% but the recovery rate of Ti matrix sample was slightly lower than that of Zr-2.5Nb.

• The korean journal of orthodontics
• /
• v.37 no.6
• /
• pp.432-439
• /
• 2007

The purpose of this study was to evaluate the influence of intraoral temperature changes on the orthodontic force level of a superelastic nickel-titanium alloy wire. Methods: Nickel-titanium archwires of $0.016"{\times}0.022"$ thickness were tested with a three point bending test setup, and temperature changes were applied. The force level changes according to temperature changes were measured at a 1.5 mm deflection during the loading phase and a 1.5 mm deflection during the unloading phase from a deflection to 3.1mm. Ten cycles of thermal cycling from baseline $(37^{\circ}C)$ to cold $(20^{\circ}C)$ or hot $(50^{\circ}C)$temperature were applied. Results: Alter thermal cycling, the force level during the loading phase decreased and the force level during the unloading phase increased even after the temperature was changed to the initial $37^{\circ}C$. Conclusions: The results suggest that the orthodontic force level can not return to the initial force level after temperature changes. When applying superelastic nickel-titanium archwires, we must consider that a lighter force than the loading force and a heavier force than the unloading force will be applied after intraoral temperature changes caused by eating and drinking.

• Journal of Korean Ophthalmic Optics Society
• /
• v.14 no.4
• /
• pp.33-37
• /
• 2009

Purpose: To examine the coloring condition of titanium spectacle frames with various colors by using anodization method. Methods: We made an anodization coater. Platinum plate with $3{\times}3cm^2$ was used for a cathode and titanium spectacle frame specimens was mounted on an anode in an electrolyte. An electric source device were designed to supply steady state current. The color of the coated spectacle frame specimens were measured by a spectrophotometer equipped with an integrating sphere. We use CIE $L^*a^*b$ color system as chromaticity coordinates. Results: The thickness of $TiO_2$ of titanium spectacle frame specimens was varied as controlling current flow time for electrodes. The specimens with various kinds of color as a walnut, a yellow brown, a navy blue, a blue, a light blue, a mung bean, a yellowish green, a light purple, a purple, a flower pink, a bluish green, an emerald, and a green color etc. were obtained. The values of CIE $L^*a^*b^*$ for these specimens were measured and analyzed to be changed clockwise in chromaticity coordinates as the thickness of $TiO_2$ increases. Conclusions: We identified the coloring mechanism by anodization method in titanium spectacle frame specimens.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.1
• /
• pp.65-72
• /
• 2011

Purpose: The purpose of this study was to evaluate the level of electro-chemical corrosion and surface roughness change for the cases of Ti abutment connected to restoration made of base metal alloys. Materials and methods: It was hypothesized that Ni-Cr alloys in different compositions possess different corrosion resistances, and thus the specimens ($13{\times}13{\times}1.5\;mm$) in this study were fabricated with 3 different types of metal alloys, commonly used for metal ceramic restorations. The electrochemical characteristics were evaluated with potentiostat (Parstat 2273A) and the level of surface roughness change was observed with surface roughness tester. Paired t-test was used to compare mean average surface roughness (Ra) changes of each specimen group. Results: All specimens made of nickel-chromium based alloys, average surface roughness was increased significantly (P < .05). Among them, the Ni-Cr-Be alloy ($0.016{\pm}.007\;{\mu}m$) had the largest change of roughness followed by Ni-Cr ($0.012{\pm}.003\;{\mu}m$) and Ni-Cr-Ti ($0.012{\pm}.002\;{\mu}m$) alloy. There was no significant changes in surface roughness between each metal alloys after corrosion. Conclusion: In the case of galvanic couples of Ti in contact with all specimens made of nickel-chromium based alloys, average surface roughness was increased.

• The korean journal of orthodontics
• /
• v.39 no.5
• /
• pp.310-319
• /
• 2009

Objective: NiTi closed coil springs were reported to have relatively constant unloading forces. However, the characteristics of NiTi closed coil springs from various manufacturers have not been elucidated. The purpose of this study was to compare load-deflection characteristics of various NiTi closed coil springs and to find out the optimal range of extension. Methods: Seven kinds of NiTi closed coil springs from five manufacturers were tested. Load deflection curves were obtained at extension ranges from 2 mm to 30 mm. Also, springs were kept extended during a 4 week period, and then load deflection curves were obtained again. Results: Sentalloy (Tomy) and Jinsung blue (Jinsung) showed superelasticity in every extension ranges tested and showed plastic deformation of less than 1 mm. Ni-Ti (Ormco) showed superelasticity only after the springs were extended at or more than 10 mm, thereby meaning that clinicians should extend these springs at or more than 10 mm to utilize the superelasticity. Orthonol (RMO) and Nitanium (Ortho Organizers) did not show superelasticity. After 4 weeks of extension, all springs showed plastic deformation less than 1 mm when the extension was at or under 25 mm. Conclusions: The superelastic behavior of NiTi closed springs were different among various NiTi spring products, and some NiTi closed springs failed to show superelasticity.

• The korean journal of orthodontics
• /
• v.30 no.4 s.81
• /
• pp.453-465
• /
• 2000

The purpose of this study was to investigate the change of mechanical properties, surface topography and frictional force of various nickel titanium wires after recycling. Three types of nickel-titanium wires and one type of stainless steel wire were divided to three groups: as-received condition(T0:control group), treated in artificial saliva for four weeks(T1) and autoclaved after being treated in artificial saliva(T2). Some changes were observed for the selected mechanical properties in tensile test, surface topography by means of SEM and 3D profilogram, and frictional coefficient. The findings suggest that: 1. Nickel-titanium wires demonstrated no statistically significant differences in maximum tensile strength, elongation rate and modulus of elasticity, but stainless steel wire demonstrated statistically significant differences in maximum tensile strength, elongation rate and modulus of elasticity between the groups(p<0.05). 2. NiTi, Optimalloy, Stainless Steel wires demonstrated increased pitting and corrosion in SEM finding. 3. Recycled NiTi, Optimalloy and stainless steel wires demonstrated significantly greater surface roughness(Ra and Rq) through 3D profilogram when compared with the control wires(p<0.05), but Sentalloy didn't demonstrate significant difference. 4. Recycled NiTi, Optimalloy and stainless steel wires demonstrated significantly greater maximum frictional coefficient when compared with the control wires(p<0.05), but Sentalloy didn't demonstrate significant difference The changes of surface roughness and frictional coefficient in NiTi and Optimalloy had no clinical implication. Consequently recycled nickel titanium wires demonstrated no clinical problem in tensile properties, surface topography and frictional coefficient.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.3
• /
• pp.9-15
• /
• 2021

Miniaturization of semiconductor devices has recently faced a physical limitation. To overcome this, 3D packaging in which semiconductor devices are vertically stacked has been actively developed. 3D packaging requires three unit processes of TSV, wafer grinding, and bonding, and among these, copper bonding is becoming very important for high performance and fine-pitch in 3D packaging. In this study, the effects of Ti nanolayer on the antioxidation of copper surface and low-temperature Cu bonding was investigated. The diffusion rate of Ti into Cu is faster than Cu into Ti in the temperature ranging from room temperature to 200℃, which shows that the titanium nanolayer can be effective for low-temperature copper bonding. The 12nm-thick titanium layer was uniformly deposited on the copper surface, and the surface roughness (R_q) was lowered from 4.1 nm to 3.2 nm. Cu bonding using Ti nanolayer was carried out at 200℃ for 1 hour, and then annealing at the same temperature and time. The average shear strength measured after bonding was 13.2 MPa.