• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.655-660
• /
• 2002

Major deterioration in concrete structures are salt attack and carbonation. Especially severe problems due to carbonation occur in tile concrete structures of city, tunnel, underground structures. Cracks in concrete during service life including early age due to hydration heat and/or shrinkage accelerate the diffusion of concrete so that the deterioration is also accelerated. In this study, carbonation depths of both non-cracked concrete and cracked concrete are evaluated and weight change test and TGA are carried out. Through the tests, a relation between water-cement ratio and carbonation depth is derived and also carbonation increase rate is derived in the function of crack width.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.767-770
• /
• 1999

The carbonation process is affected both by the concrete material properties such as W/C ratio, types of cement and aggregated, admixture characteristics and the environmental factors such as CO2 concentration, temperature, humidity. Based on results of preliminary research on carbonation, this study is to propose a carbonation prediction model by taking into account of prediction model by taking into account of CO2 concentration and W/C ratio among major factors affecting the carbonation process.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.555-558
• /
• 2001

Carbonation of concrete decreases durability of RC structures due to failure of passive film of rebar. Therefore, expecting carbonation depth is a governing parameter of service life prediction for RC structures. This study attempt to estimate carbonation depth quantitatively by using equivalent effective diffusion coefficient of $CO_2$.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.773-778
• /
• 2002

The variance characteristics of the calcium carbonate contents along to the concrete cover depth takes the prediction method of remaining service life of concrete. Calcium carbonate contents were measured by the Thermo Gravimetric/Differential Thermal Analysis method at three point, depth of 0.25cm, 0.75cm, 1.25cm from the surface of concrete. This prediction method contain some assumption that the chemical protection conferred on steel is through a passive protective oxide film which forms on steel in an environment at or above a pH of 10.5$^{4)}$ .

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.189-195
• /
• 1996

This study was carried out ont the longterm aged reinforced concrete housings for the prediction of life expectancy and the suggestion of fundamental informations on the durable concrete. In this paper, the durability of concrete is compared with carbonation depth, and the measutrments fo carbonation depth and properties have been made on the number of cores taken from structures. And finally, the relationships between carbonation rate and such properties as strength, absorption ratio, density were examined.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문 발표회
• /
• pp.77-82
• /
• 2003

The purpose of this study is development of technique to use cementitious powder as recycle cement produced from deteriorated Concrete waste which has a large quantity of calcium carbonate. Therefore, after having theoretical consideration based on the properties of high-heated concrete and concerning about neutralization of Concrete, we analysis chemical properties of ingredients of cementitious powder. After making origin cement paste, then processing the accelarated carbonation, we consider the properties of hydration and chemical properties of cementitious powder under various temperature conditions. As a result of the thermal analysis, the CaCo3 content of cementitious powder would affect decision of heat temperature to recover its hydrated ability because CaCo3 content is increased when neutralization is progressed. And as a result of XRD analysis, in case of origin powder of non-neutralized paste, CaO peak is found at 700℃. but, heat temperature to generate CaO would increase when the content of neutralized ingredients is increased. Finally, recycle cement heated at 700℃ shows the best compressive strength when the content of neutralized ingredients in recycle cement is less then 50%. However, it would be quite difficult to manage quality of recycle cement according to recycling points of various concrete waste.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문발표회
• /
• pp.77-82
• /
• 2003

The purpose of this study is development of technique to use cementitious powder as recycle cement produced from deteriorated Concrete waste which has a large quantity of calcium carbonate. Therefore, after having theoretical consideration based on the properties of hish-heated concrete and concerning about neutralization of Concrete, we analysis chemical properties of ingredients of cementitious powder After making origin cement paste, then processing the accelerated carbonation, we consider the properties of hydration and chemical properties of cementitious powder under various temperature conditions As a result of the thermal analysis, the CacO3 content of cementitious powder would affect decision of heat temperature to recover its hydrated ability because CacO3 content is increased when neutraliTation is preBlessed. And as a result of XRD analysis. in case of origin powder of non-neutralized paste, CaO peak is found at $700^{\circ}C$. but, heat temperature to generate CaO would increase when the content of neutralized ingredients is increased. Finally, recycle cement heated at $700^{\circ}C$ shows the best compressive strength when the content of neutralized ingredients in recycle cement is less then 50%. However, it would be quite difficult to manage quality of recycle cement according to recycling points of various concrete waste.

• 자원환경지질
• /
• 제51권4호
• /
• pp.359-370
• /
• 2018

기존 연구에서 초임계$CO_2$($scCO_2$)-물-순활골재 반응을 이용한 폐콘크리트 순환골재의 중성화(pH 저감) 처리에서 가장 문제시되었던 오랜 처리시간의 한계(최대 50일)를 최소 3시간까지 단축하는 배치실험과 칼럼실험을 수행하였다. 모르타르(골재를 포함하지 않은 시멘트+모래 혼합체)와 모르타르에 골재를 포함하는 2 종류의 순환골재를 실험에 사용하였다. 입자 크기별로 분류한 세 종류의 폐모르타르 시료에 대하여 $scCO_2$-물-폐모르타르 반응 시간을 1시간부터 24시간까지 다하게 설정하여 반응시킨 후, 폐모르타르의 pH가 지속적으로 9.8 이하로 낮게 유지되는 최소 반응시간을 결정하는 용출 배치실험을 실시하였다. 실제 현장에서 다량의 순환골재를 중성화 처리하는 경우 비평형상태에서 용출이 발생하는데, 이러한 kinetic 효과를 고려한 순환골재의 실제 pH 저감 효율을 측정하고자 대형 칼럼 연속 용출 실험을 실시하였다. 배치실험의 경우, 고압셀 내부에서 3차 증류수 70 mL와 순환골재 시료 35 g을 혼합한 후 100 bar, $50^{\circ}C$ 조건에서 1시간 ~ 24시간 동안 반응시켜 중성화 처리하였다. 처리 후 건조시킨 폐모르타르 시료 10 g + 증류수 50 ml의 비율(1:5 비율)로 혼합하여 10분 동안 150 rpm으로 교반한 후 정치시키고, 총 15일 동안 용출시간 별로 용출수의 pH를 측정하였다. 중성화 처리 후 순환골재의 광물학적 변화를 확인하기 위하여 처리 전/후 XRD, TG/DTA 등의 분석을 실시하였다. 대형 칼럼(직경 16 cm, 높이 1 m) 용출실험을 위해 순환골재 2 종류를 대상으로 3시간 동안 중성화 처리한 순환골재와 처리하지 않은 순환골재로 칼럼을 충진한 후, 증류수를 칼럼 상부에 설치된 스프링클러를 통하여 일정하게 총 220 L를 주입하였다. 칼럼에 충진된 순환골재를 통과하여 하부로부터 유출되는 유출수의 pH와 $Ca^{2+}$ 농도를 시간별로 측정하였다. 배치실험 결과 폐모르타르 시료(직경 10 ~ 13 mm)의 경우 3시간의 중성화 처리에 의해 용출액의 pH가 법적 허용기준인 9.8이하를 유지하는 것으로 나타났다. $scCO_2$ 반응 후 골재의 XRD, TG/DTA 분석 결과, 중성화 처리에 의해 시멘트 모르타르의 주성분인 포틀랜다이트($Ca(OH)_2$) 성분이 감소한 반면 방해석($CaCO_3$)이 2차 광물로 생성됨을 알 수 있었다. 칼럼 실험 결과 중성화 처리한 순환골재의 용출수는 kinetic 효과를 고려한 경우에도 굵은골재와 잔골재 모두 용출수의 pH가 9.8 이하로 유지되어, $scCO_2$를 이용한 순환골재의 3시간 중성화 처리에 의해 건설현장에서 재활용이 가능한 것으로 밝혀졌다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제19권3호
• /
• pp.22-29
• /
• 2015

본 연구에서는 압축강도 24MPa 이상 열전도율이 기존 콘크리트보다 2배 감소된 구조용 단열성능 향상 콘크리트를 개발하고 현장적용하기 위한 실험을 진행하였다. 슬럼프 및 공기량 시험결과 Plain과 규조토 미분말을 사용한 배합은 경과시간에 따라 슬럼프와 공기량 저하가 나타났으며, 마이크로기포제를 사용한 배합은 슬럼프와 공기량 저하가 나타나지 않았다. 또한 단열성능 향상 재료를 사용한 배합의 단위용적질량은 Plain 대비 감소하였다. 압축강도는 단열성능 향상 콘크리트가 Plain보다 감소한 결과를 나타내었으나 목표강도 24MPa를 만족하였으며, 열전도율은 Plain보다 감소하는 경향을 보였다. 단열성능 향상 콘크리트의 동결융해 저항성은 Plain과 유사하였고, 중성화 저항성은 규조토 미분말을 사용한 배합이 재령 4주에 Plain과 유사했으며, 마이크로기포제를 사용한 배합은 Plain보다 중성화 저항성이 저하되었고, 길이변화율은 Plain보다 전체적으로 증가되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1995년도 가을 학술발표회 논문집
• /
• pp.30-34
• /
• 1995

There are carbonatiion, salt attack, freezing & thawing and alkali-aggregate reactions as the cautions of durability lowering of concret structure. Generally, these cautions complicatedly lower the durability of structure and among these cautions the most serious problem is salt attack and carbonation. This study is intending to get the carbonation phenominon, that among cement calcium hydroxides change into calcium carbonate by responding to carbon mitrogen in the air.