Chloride attack, one of the major deterioration phenomena in RC(Reinforced Concrete) structure, causes corrosion of reinforcement, and this leads degradation of serviceability and structural problems. The application of silicate based impregnant to concrete surface are known for excellent constructability and cost-benefit for the maintenance of RC structure. In the work, the compressive strength and resistance of chloride diffusion for concrete were evaluated after improving property of concrete surface through two types of silicate based impregnant. Furthermore, based on the previous research and the result from the work, service life analysis was performed. After impregnating of silicate, strength and resistance of chloride diffusion were remarkably improved, and the service life increase to 159% for silicate A impregnation and 304% for silicate B impregnation, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.31-36
• /
• 2019

Concrete is a material generally used to build structures and it is exposed to various environment conditions. In particular, a medium such as water lets noxious factors flow into concrete, causing a lot of damage. Therefore, different kinds of materials are being developed to increase the durability of concrete. Among such materials, silane and siloxane compound are known to have a high utilization as an absorption inhibitor. However, if aged or deteriorated reinforced concrete is treated with those compounds, they easily come off the concrete and lose their function since the basic material is weak. This study conducted an experiment to provide concrete with both an absorption-inhibiting effect and surface strengthening by using melamine-formaldehyde resins that are surface-treated with siloxane compound. In addition, a study on the porosity and surface hardness characteristics of a concrete was conducted to check the absorption-inhibiting effect and surface strengthening.

• The Journal of the Convergence on Culture Technology
• /
• v.8 no.6
• /
• pp.727-732
• /
• 2022

Applying the calculated cross-sectional reduction due to the corroded rebar investigated in the field to the numerical analysis model, the damage pattern and delamination of concrete in the field showed a tendency relatively similar to the numerical analysis results. It was analyzed that when the expansion pressure due to corrosion of the reinforcing bar is greater than the tensile stress of the concrete, cracks are generated and the concrete cover can be fracture. As a result of this study, the correlation between the corrosion rate of reinforcing bars and the crack occurrence of the concrete cover of the subway box structure was verified based on the numerical analysis and field test results. To prevent rebar corrosion, the corrosion rate can be reduced by applying rust prevention to the reinforcing bar and changing the material. In the case of exposed to a corrosive environment, the tensile strength of the concrete is improved by adjusting the concrete compressive strength to secure durability against the expansion pressure caused by the corroded rebar.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.30 no.3A
• /
• pp.221-228
• /
• 2010

External bonding of carbon fiber reinforced polymer (CFRP) sheets has been widely accepted as a popular method for strengthening of deteriorated RC structures. The long-term behavior of CFRP-strengthened RC structure is often affected by that of the interface between CFRP sheets and concrete. This study aims at applying a viscoelastic model to describe the creep behaviour of the adhesive layer bonding CFRP sheet to concrete, the CFRP-concrete interface. Reviews of available models on concrete creep behavior have been first carried out and then new FE analysis model is proposed. The proposed FE analysis model based on the maxwell model has been verified by previous experimental results. It is shown that the creep effect of interfacial adhesive layer is very important on the long-term behavior of concrete structures strengthened with CFRP.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.11 no.1
• /
• pp.97-105
• /
• 2009

This paper studied the cause of the deterioration of the four 3-Arch tunnels built in mid-1990. The common deteriorations of the four 3-Arch tunnels were longitudinal cracks, leakage and efflorescence at the same parts of lining concrete. Three fourths of 3-Arch tunnels, there was high percentage longitudinal cracks and a quarter was low frequency about longitudinal cracks. So the material reviewed to find out the differences between two groups in construction process and analysis was conducted such as non-destructive testing, precise visual survey and safety evaluation of one tunnel which had bad ground condition As the result, the tunnels were safety condition and the primary deterioration occurred during the construction process, namely, problems arrangement of rebar and the effects of the blast at middle tunnel.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.771-776
• /
• 2001

Test results on the deterioration process of concrete under single and combined attacks of chloride penetration have been obtained. After test period of 52 weeks, it is found that the internally penetrated chloride ion contents are less in the single attacks of chloride than the combined attacks of chloride and sulfate. Both the diffusion coefficients and surface chloride concentration derived form the chloride profiles showed a time dependence. Also the performance of fly ash-blended cements was observed to be better than plain cements in retarding chloride attack. However it should be needed that improved chloride diffusion model for the combined deterioration process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.627-630
• /
• 2005

This paper examines degradation properties of alkali-activated alumino-silicate composite body by NAS solution exposed to high temperature. Activators include sodium hydroxides and sodium silicate solution. In the result of experiment, flexural and compressive strength of AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than alumina cement base mortar. Particularly, In case of compressive strength, alumina cement base mortar was decreased by about $60\~70\%$. While, AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than that curing by room temperature. The above results showed that AAS base inorganic binder has a good mechanical properties exposed to high temperature($400\~600$).

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.313-316
• /
• 2006

The most serious cause of deterioration in the concrete structures is reinforcing corrosion due to the chloride attack and carbonation. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. The object of this study is to develop a preventing aging technology. The work involves the development of silicate type penetration reinforcing agent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.515-516
• /
• 2009

Recently, A lot of roads, railroads and tunnels are constructed for development of industrialization and efficient use of national land. So, we have focused on to figure out the best combination between Slag powder and Mortars with Accelerator to repair of tunnel structure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.134-138
• /
• 1995

The reinforced concrcte structure were once belicved to have permanent durability. However, it is now spoiled by durability failure caused by the corrosion of embeded steel reingorcement carbonation. alkali-aggregate reaction and salt attack Recently. salt damage has been also spreading. Salt damage is found in concrete structures built using seasands or certain admixtures containing calcium chlorides and in coastal structures frequently caught in seawater spray or blown by seawind It is the aim of this study to investigate the performance and application of new repair system for the exterior wall according to the durability improvement in the RC structures.