• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.157-158
• /
• 2007

AISI316L강의 내식성과 표면경도를 동시에 향상시키기 위한방법으로 저온 플라즈마 침탄과 저온 플라즈마 질화를 동일한 로 내에서 연속적으로 실시하였다. 여러 가지 공정인자 중 저온 플라즈마 질화 시 $N_2$가스가 표면에 미치는 영향을 조사 하였다. 모든 시편의 표면에 N에 의해 확장된 오스테나이트 (${\gamma}_N$)가 형성되었으며, 형성된 ${\gamma}_N$로 인하여 표면경도가 약 $3{\sim}4$배 증가하였다. $N_2$가스가 증가할수록 ${\gamma}_N$층의 두께가 증가 하였다.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.18 no.5
• /
• pp.381-388
• /
• 1998

The ultrasonic method, which is well known as non-destructive test method, is widely used to evaluate the material damage caused by degradation practically. However, this method is just used for measuring the crack size and the thickness loss of tube. The purpose of this study is to investigate the applicability of the ultrasonic technique for the evaluation of carburized material and to suggest the correlations between the ultrasonic characteristics and carburized degradation. The miniaturized specimens($40{\times}20{\times}6.3mm$) are adopted from the HK-40 (25Cr-20Ni-0.4C) centrifugal cast tube after carburization treatment. Carburization was carried at $1200^{\circ}C$ by the pack method. The results of ultrasonic test present that the longitudinal wave velocity increased with the increase of carburized depth. The correlation between the longitudinal wave velocity and carburization was changed with the density and Young's modulus. Therefore, the average velocity in the materials carburized for 336 hours and the unused one were 5,840 m/s and 5,755 m/s at 5 MHz, respectively. With the obtained results from this study, it can be recognized that the technique using the ultrasonic velocity property is very useful method to evaluate the degree of carburized material non-destructively.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.125-125
• /
• 2013

기계부품 및 자동차부품 등의 내마모나 내피로성의 향상을 위한 표면처리로서 고주파처리, 침탄처리, 질화처리 등이 사용되고 있다. 최근에는 변형을 최소화 함으로써 후가공을 생략할 수 있는 질화처리가 주목받고 있다. 질화처리종류로는 염욕질화나 가스질화법이 사용되고 있으나, 이들에 비해 환경오염 및 공해가 적고 인체에 무해한 플라즈마 연질화법이 사용되고 있다. 플라즈마 연질화 기술은 IT기기의 제품에 적용되는 표면경화의 공정개발은 미비한 실정이다. 마이크로 구동 요소 부품중의 하나인 Leadscrew는 이송장치를 구성하는 핵심 부품으로 IT기기의 정밀 이송 및 구동제어에 사용되는 핵심 부품으로 사용되고 있으며, 리드스크류의 소재인 SWCH1018A(냉간압조용강선)은 표면 경도가 낮고 변형이 쉽기 때문에 표면 경화를 위한 플라즈마 연질화 기술을 이용하고자 했다. 본 연구는 플라즈마 연질화 공정을 적용한 시편의 표면경도를 높혀주고 변형을 최소화 할 수 있는 공정을 확인하는 것이다. 공정변수를 변화 시키면서 얻어진 시편의 표면미세 구조를 미소경도측정, XRD, SEM분석을 통하여 확인하였으며, 이를 통해 시편 표면경도를 높여주는 공정 조건을 도출하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.29-29
• /
• 2014

최근 화석에너지 고갈 및 에너지 수요의 폭발적 팽창을 해결하기 위하여 경량화와 내마모 측면에서 고효율 시스템을 적용한 자동차 및 각종 성형 기기들이 개발되고 있다. 특히 장치의 고성능화라는 요구조건을 충족시키기 위해서는 금속가공산업에서 표면개질의 중요성이 부각되고 있다. 이러한 표면개질에는 일반적으로 표면의 성질을 개선하여 마모(abrasion) 및 국부 압력(local stress) 또는 피로(fatigue), 마식(wear and corrosion)에 견디게 하여 부품의 수명증대와 제품의 소형화에 기여하고 있다. 이러한 표면개질법에는 경질의 물질을 표면에 코팅시켜 재료표면의 특성을 향상시키는 방법과 금속의 표면에 다른 원소를 침투 및 확산시키는 방법으로 나눌 수 있다. 확산방법으로 침탄, 질화, 보로나이징, 크마이징 처리 방법 등이 있다. 상업적으로 가장 많이 사용되는 표면 개질법은 침탄기술로서, 고온에서 짧은 시간내에 물성 향상이 가능하지만, 강의 변태점 이상의 온도에서 진행됨으로서, 변형에 따른 문제가 발생되어 후처리를 필요로 하는 문제점을 가지고 있다. 반면, 질화법은 변태점 이하의 저온에서 철강 표면에 N을 침투시켜 강을 경화시키는 특징을 가진다. 변형이 적고 질소원자가 강내에 침투함으로 인해 내마모성, 내피로성, 내식성 등의 물리적 성질을 향상시키는 점에서 유리하여 각종 정밀 부품 및 자동차 부품, 금형 등에 많이 사용된다. 또한, 경도 향상 및 결정구조의 영향으로 코팅처리시 모재와 코팅 층의 밀착력 향상을 가져오면 이러한 이유로 코팅 층의 하지 층으로써 각광 받고 있다. 본 발표에서는 플라즈마 질화의 이해를 높이기 위해 관련 기술에 대한 전반적인 소개와 향후 플라즈마 질화 기술의 적용이 기대되는 침탄대체 적용 가능 부품, 침류질화 기술, PECVD 공정과의 접목 등 산업적은 응용 측면에서 응용 분야에 대한 소개를 진행하고자 한다.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.296-301
• /
• 2004

• Tribology and Lubricants
• /
• v.36 no.1
• /
• pp.18-26
• /
• 2020

The effects of the carburizing process on the sliding wear behavior of SCM420H steel have been investigated. In particular, the effects of grain boundary corrosion observed in the surface layer after gas carburizing and the effects of hardness of the carburized cases after heat-treatment on the sliding wear properties were examined. Pin specimens carburized by two methods (gas carburizing and vacuum carburizing) were tempered at two temperatures of 180℃ and 400℃ after oil-quenching, respectively. Sliding wear tests were carried out against heattreated SKH51 steel at several sliding speeds using a pin-on-disc type test machine. As results, it can be found that there is no difference in the wear behavior between the pins carburized using two methods. This implies that the grain boundary corrosion that formed in the surface layer after gas carburizing has no effect on the sliding wear behavior of carburized SCM420H steels. Additionally, there is no significant difference in the wear behavior between carburized pins tempered at 400℃ and at 180℃ after oil-quenching, regardless of the carburizing method. This is because carburized pins tempered at 400℃ have a troostite structure, which exhibits higher tribochemical reactivity even though its hardness is lower than that of martensite structure. In this respect, it can be considered that good wear resistance of carburized cases is maintained at least until the effective case depth.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.719-723
• /
• 1996

In this research, The statistical characteristics of non-heated and nitro-carburized specimens are investigated under two stress levels (1.15 .sigma. $_{w}$ .leq. .sigma.$_{\alpha}$ .leq. 1.25 .sigma. $_{w}$). Seven specimens of each stress level are tested by rotary bending fatigue machine. The cycles about each crack length and crack propagation rate are used as statistical variagle of weibull distribution. By using concept of reliability function, reliable S-N formula of Nitro-Carburized specimen are gotten.ten.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.5
• /
• pp.160-167
• /
• 2000

In this research, the fatigue behaviors of carbonitrided Cr-Mo(SCM415) steel are examined. From fatigue test results, we propose a modified fatigue strength evaluation model and modified formulae. That is, we develop improved models fur evaluating and predicting the fatigue strength of carbonitrided SCM415 by modifying specific terms in the Murakami and Endo's model which is the representative fatigue strength evaluation formulae fur high strength steel.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.04b
• /
• pp.39-44
• /
• 1995

The gas nitro-carburizing treatment with the merits of carburizing and nitriding treatment is recently applied to transmission gears. the shafls of an engine oil pump and steering shafls. For all that, the researches of the gas nitro-carburizing treatment are short of the fatigue behavior and the evaluation of fatigue life. In this paer, it is examined for the effect of inclusions and hole defects with fatigue limit and the evaluation of the fatigue strengthaccording tothe hardness and resifualstress with the specimen of a notro-carburizing treatment.

• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.8
• /
• pp.135-144
• /
• 1998

In this research, the fatigue behaviors of Cr-Mo(SCM415) steel and carbonitrided CrMo(SCM415) steel are examined. The description of experiments in detail as follows. For SCM415 and carbonitried Cr-Mo(SCM415) steel, smooth specimens and hole defected specimens are fabricated and tested under a rotary bending tester, respectively. By performing the rotary bending fatigue test for smooth and hole defected specimens, the characteristics of the fatigue strength are examined for parameters such as tensile strength, hardness at surface, and residual stresses.