• Restorative Dentistry and Endodontics
• /
• v.29 no.2
• /
• pp.177-184
• /
• 2004

Objectives : This study investigated the hypothesis that increasing light-curing time would leave the oxygen-inhibited layer (OIL) of the adhesive thinner, and in turn, result in lower shear bond strength (SBS) than those obtained by the routine curing procedures. Methods：120 human extracted posterior teeth were randomly divided into three groups for bonding with three adhesives：All Bond 2/sup (R)/, One Step/sup (R)/, and Adper Prompt/sup (R)/. They were subsequently divided into four subgourps with different light-curing time (10, 20, 30 and 60s). The assigned adhesives were applied on superficial occlusal dentin according to the manufacturer's instructions and cured with one of the four curing times. Composite resin cylinder, 2.35㎜ in diameter, were built on the cured adhesive and light-cured for 40s. SBS were measured after 24h from the bonding using a universal testing machine (crosshead speed 1.0 ㎜/min). The relative thickness of the OIL and the degree of conversion (DC) were determined from the adhesive on a slide glass using FT-NIR in an absorbance mode. Data were analysed with One-way ANOVA and Duncan's multiple test (p〈0.05), Results：With increasing cure time, although there were no significant difference in th SBS of One-step and Adper Prompt (p〉0.05), those of All Bond 2 decreased significantly (p〈0.05). The relative thicknesses of the OIL on each adhesive were not affected by the cure time (p〉0.05). Although the DC of All-Bond 2 were statistically not different with increasing cure time (p〉0.05), those of One-Step and Adper Prompt showed an increasing trends with increasing cure time (p〈0.05). Conclusions：Increasing light-curing time did not affect on the relative thickness of the OIL of the adhesives, and in turn, on the SBS to dentin.

• Restorative Dentistry and Endodontics
• /
• v.34 no.3
• /
• pp.177-183
• /
• 2009

The aim of this study was to evaluate the marginal and internal gaps in CEREC3 CAD/CAM inlays of three different preparation designs. CEREC3 Inlays of three different preparation designs (n=10) were fabricated according to Group I-conventional functional cusp capping/shoulder preparation, Group II-horizontal reduction of cusps and Group III-complete reduction of cusps/shoulder preparation. After cementation of inlays. the bucco-lingual cross section was performed through the center of tooth. Cross section images of 20 magnifications were obtained through the stereomicroscope. The gaps were measured using the Leica application suite software at each reference point. Statistical analysis was performed using one-way ANOVA and Tukey's test (${\alpha}<0.05$). The marginal gaps ranged from 80.0 to $97.8{\mu}m$ for Group I, 42.0 to $194.8{\mu}m$ for Group II, 51.0 to $80.2{\mu}m$ for Group III. The internal gaps ranged from 90.5 to $304.1{\mu}m$ for Group I, 80.0 to $274.8{\mu}m$ for Group II, 79.7 to $296.7{\mu}m$ for Group III. The gaps of each group were the smallest on the margin and the largest on the horizontal wall. For the CEREC3 CAD/CAM inlays, the simplified designs (groups II and III) did not demonstrate superior results compared to the traditional cusp capping design (group I).

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.450-459
• /
• 2009

The aim of this study was to measure the initial dynamic modulus changes of light cured composites using a custom made rheometer. The custom made rheometer consisted of 3 parts: (1) a measurement unit of parallel plates made of glass rods, (2) an oscillating shear strain generator with a DC motor and a crank mechanism, (3) a stress measurement device using an electromagnetic torque sensor. This instrument could measure a maximum torque of 2Ncm, and the switch of the light-curing unit was synchronized with the rheometer. Six commercial composite resins [Z-100 (Z1), Z-250 (Z2), Z-350 (Z3), DenFil (DF), Tetric Ceram (TC), and Clearfil AP-X (CF)] were investigated. A dynamic oscillating shear test was undertaken with the rheometer. A certain volume ($14.2\;mm^3$) of composite was loaded between the parallel plates, which were made of glass rods (3 mm in diameter). An oscillating shear strain with a frequency of 6 Hz and amplitude of 0.00579 rad was applied to the specimen and the resultant stress was measured. Data acquisition started simultaneously with light curing, and the changes in visco-elasticity of composites were recorded for 10 seconds. The measurements were repeated 5 times for each composite at $25{\pm}0.5^{\circ}C$. Complex shear modulus G*, storage shear modulus G', loss shear modulus G" were calculated from the measured strain-stress curves. Time to reach the complex modulus G* of 10 MPa was determined. The G* and time to reach the G* of 10 MPa of composites were analyzed with One-way ANOVA and Tukey's test ($\alpha$ = 0.05). The results were as follows. 1. The custom made rheometer in this study reliably measured the initial visco-elastic modulus changes of composites during 10 seconds of light curing. 2. In all composites, the development of complex shear modulus G* had a latent period for $1{\sim}2$ seconds immediately after the start of light curing, and then increased rapidly during 10 seconds. 3. In all composites, the storage shear modulus G" increased steeper than the loss shear modulus G" during 10 seconds of light curing. 4. The complex shear modulus of Z1 was the highest, followed by CF, Z2, Z3, TC and DF the lowest. 5. Z1 was the fastest and DF was the slowest in the time to reach the complex shear modulus of 10 MPa.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.424-429
• /
• 2009

This study aimed to assess the influence of different cross-sectional area on the cyclic fatigue fracture of Ni-Ti rotary files using a fatigue tester incorporating cyclical axial movement. Six brands of Ni-Ti rotary files (ISO 30 size with. 04 taper) of 10 each were tested: Alpha system (KOMET), HeroShaper (MicroMega), K3 (SybronEndo), Mtwo (VDW), NRT (Mani), and ProFile (Dentsply). A fatigue-tester (Denbotix) was designed to allow cyclic tension and compressive stress on the tip of the instrument. Each file was mounted on a torque controlled motor (Aseptico) using a 1:20 reduction contra-angle and was rotated at 300 rpm with a continuous, 6 mm axial oscillating motion inside an artificial steel canal. The canal had a $60^{\circ}$ angle and a 5 mm radius of curvature. Instrument fracture was visually detected and the time until fracture was recorded by a digital stop watch. The data were analyzed statistically. Fractographic analysis of all fractured surfaces was performed to determine the fracture modes using a scanning electron microscope. Cross-sectional area at 3 mm from the tip of 3 unused Ni-Ti instruments for each group was calculated using Image-Pro Plus (Imagej 1.34n, NIH). Results showed that NRT and ProFile had significantly longer time to fracture compared to the other groups (p < .05). The cross-sectional area was not significantly associated with fatigue resistance. Fractographycally, all fractured surfaces demonstrated a combination of ductile and brittle fracture. In conclusion, there was no significant relationship between fatigue resistance and the cross-sectional area of Ni-Ti instruments under experimental conditions.

• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.88-95
• /
• 2010

The purpose of this study was to compare the root canal shaping ability of 4 rotary NiTi instruments in simulated root canals. For the preparation of thirty two curved root canals, Mtwo instruments using "single length"technique, and Profile, ProTaper Universal, and K3 using crown-down technique (N = 8) were used. All canal samples were prepared by reaching an apical canal size of #30. Pre- and post-instrumentation digital images were recorded and an assessment of canal shape was determined using a computer image analysis program SigmaScan Pro (Systat Software Inc., San Jose, CA, USA). The changes of the dimension of inner walls of canals, (2) the changes of the dimension of outer walls of canals, and (3) the centering ratio were measured at 7 measuring points, and then data were statistically analyzed using one-way ANOVA and Duncan's test. The results were as below; 1. The root canal shaping ability of Profile was significantly faster than that of other rotary NiTi instruments (p < 0.05). 2. The deformation and fracture of all instruments used for this study were not experienced. 3. In the degree of changes of the dimension of inner walls of canals, Profile demonstrated the lowest changes of the dimension of inner walls of canals except at the measuring points of the 1 and 2 mm (p < 0.05). However, the ProTaper Universal showed the highest changes of the dimension of inner walls of canals at all measuring points (p < 0.05). 4. In the degree of changes of the dimension of outer walls of canals, Mtwo demonstrated the lowest changse of the dimension of outer walls of canals except at the measuring point of the 1 mm (p < 0.05). However, Profile exhibited the highest changes of the dimension of outer walls of canals at the measuring points of 3 and 4 mm and ProTaper Universal and K3 showed the largest changes of the dimension of outer walls of canals at the measuring points of 1, 2, 6, and 7 mm (p < 0.05). 5. In degree of centering ratio, Profile demonstrated the least centering ratio comparing with the centering ratio shown by other NiTi instruments at the measuring points of 1, 4, 5, and 6 mm. Results suggest that in the coronal part of canal preparation, active cutting files such as ProTaper Universal may efficiently flare the canal orifice and form a better taper, and in the apical part of the canal, files which have a better centering ability such as Profile may maintain the original canal curvature and reduce the shaping time.

• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.69-79
• /
• 2010

The purpose of this study was to evaluate the effect of film thickness of various resin cements on bonding efficiency in indirect composite restoration by measurement of microtensile bond strength, polymerization shrinkage, flexural strength and modulus, fractographic FE-SEM analysis. Experimental groups were divided according to film thickness (< $50\;{\mu}m$-control, $50\;{\mu}m$-T50, $100\;{\mu}m$-T100, $150\;{\mu}m$-T150) using composite- based resin cements (Variolink II, Duo-Link) and adhesive-based resin cements (Panavia F, Rely X Unicem). The data was analyzed using ANOVA and Duncan's multiple comparison test (p < 0.05). The results were as follows ; 1. Variolink II showed higher microtensile bond strength than that of adhesive-based resin cements in all film thickness (p < 0.05) but Duo-Link did not show significant difference except control group (p > 0.05). 2. Microtensile bond strength of composite-based resin cements were decreased significantly according to increasing film thickness (p < 0.05) but adhesive-based resin cements did not show significant difference among film thickness (p > 0.05). 3. Panavia F showed significantly lower polymerization shrinkage than other resin cements (p < 0.05). 4. Composite-based resin cements showed significantly higher flexural strength and modulus than adhesive-based resin cements (p < 0.05). 5. FE-SEM examination showed uniform adhesive layer and well developed resin tags in composite-based resin cements but unclear adhesive layer and poorly developed resin tags in adhesive-based resin cements. In debonded surface examination, composite-based resin cements showed mixed failures but adhesive-based resin cements showed adhesive failures.

• Restorative Dentistry and Endodontics
• /
• v.30 no.1
• /
• pp.1-6
• /
• 2005

In order to examine the immunoresponse of host cells to Enterococcus faecalis, this in vitro study monitored the production of Interleukin-2 (IL-2), Interleukin-4 (IL-4) and Transforming growth factor-$\beta1\;(TGF-\beta1)$ in human lymphocytes. Lymphocytes were activated with PHA in the presence or abscence of sonicated extracts of E. Faecalis (SEF) and further incubated for 72 hours. The level of each cytokine was measured by ELISA. Data were analyzed with Kruskal-Wallis test and Mann-Whitney U test (P < 0.05). PHA-activated group did exhibit higher level of IL-2 and IL-4 than untreated control group. The levels of expression of both cytokines were significantly decreased following the treatment of high (25 ${\mu}g/ml$) and medium concentration (12.5 ${\mu}g/ml$)) of SEF (P > 0.05) than those of PHA activated group. But low concentration (5 ${\mu}g/ml$)) of SEF showed th similar level of IL-2 and IL-4 production as those of PHA activated group. $TGF-\beta1$ was unaffected by SEF treatment. These results suggested that E. faecalis may suppress IL-2 and IL-4 production by lymphocytes and this could be one of possible factors why E. faecalis are found frequently in the teeth with failed endodontic treatment.

• Restorative Dentistry and Endodontics
• /
• v.31 no.3
• /
• pp.147-152
• /
• 2006

The purpose of this study was to evaluate the influence of the AH-26 root canal sealer on the shear bond strength of composite resin to dentin. One hundred and forty four (144) extracted, sound human molars were used. After embedding in a cylindrical mold, the occlusal part of the anatomical crown was cut away and trimmed in order to create a flat dentin surface. The teeth were randomly divided into three groups; the AH-26 sealer was applied to the AH-26 group, and zinc-oxide eugenol (ZOE) paste was applied to the ZOE group. The dentin surface of the control group did not receive any sealer. A mount jig was placed against the surface of the teeth and the One-step dentin bonding agent was applied after acid etching. Charisma composite resin was packed into the mold and light cured. After polymerization, the alignment tube and mold were removed and the specimens were placed in distilled water at $37^{\circ}C$ for twenty four hours. The shear bond strength was measured by an Instron testing machine. The data for each group were subjected to one-way ANOVA and Tukey's studentized rank test so as to make comparisons between the groups. The AH-26 group and the control group showed significantly higher shear bond strength than the ZOE group (p<0.05). There were no significant differences between the AH-26 group and the control one (p>0.05). Under the conditions of this study, the AH-26 root canal sealer did not seem to affect the shear bond strength of the composite resin to dentin while the ZOE sealer did. Therefore, there may be no decrease in bond strength when the composite resin core is built up immediately after a canal filling with AH-26 as a root canal sealer.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.54-67
• /
• 1998

The purposes of this study were to evaluate the efficiency of dentin cutting and root-end cavity preparation, and to determine the incidence of tooth crack when root-end retrograde cavity preparation was done with. ultrasonic diamond instruments. To evaluate the efficiency of dentin cutting, ultrasonic diamond and stainless steel instruments were applied to 20 exposed bovine dentin surfaces perpendicularly or parallely at the low, and medium power settings for 1 minute ($Miniendo^{TM}$, EIE, CA, U.S.A.). The resultant cavity depth was measured. To evaluate the efficiency of cavity preparation and to investigate the incidence of tooth crack, 165 mesiobuccal, distobuccal and palatal root-ends of extracted human maxillary first molars were resected by 3 mm perpendicularly to the long axis of tooth using a slow speed diamond saw after root canal preparation and filling. Retrocavities were prepared using a ultrasonic diamond instrument or a stainless steel one of the low- or medium power settings of 2 or 6. Time consumed and the number of strokes used for the cavity preparation were measured and the incidence of tooth cracks was evaluated under a stereomicroscope. The results were as follows: Both at the low and medium power settings, and both with perpendicularly- and parallely applied tips to dentin, diamond instruments showed higher dentin cutting efficiency than stainless steel ones did (p<0.01). When tips were applied to dentin perpendicularly, both diamond instrument and stainless steel one showed higher cutting efficiency with medium power setting than with low power one (p<0.01). Both at the low- and medium power settings, both diamond instrument and stainless steel one showed higher cutting efficiency when tips were applied perpendicularly to dentin surface than applied parallely (p<0.01). At the medium power setting, the number of stroke and time consumed were less with diamond instrument than with stainless steel one (p<0.05) for the retrograde cavity preparation. At the low power setting, diamond instrument induced less tooth cracks than stainless steel one did (p<0.01).

• Restorative Dentistry and Endodontics
• /
• v.34 no.4
• /
• pp.350-355
• /
• 2009

Bond strength depends on characteristics of bonding surface and restorative technique. The majority of studies dealing with dentin bond strength were carried out on flat bonding surface, therefore, difference of bond strength between axial wall and pulpal wall is not clear yet. This study evaluated bonding difference between cavity walls in class I composite resin restoration with different filling techniques. Twenty extracted caries-free human third molars were used. Cavities were prepared in 6 ${\times}$4 ${\times}$3 mm box-type and divided into four groups according to filling technique and bonding surface: Group I; bulk filling - pulpal wall, Group II; bulk filling - axial wall, Group III; incremental filling - pulpal wall, Group IV; incremental filling - axial wall. Cavities were filled with Filtek $Z250^{(R)}$(3M/ESPE., USA) and Clearfill SE $bond^{(R)}$(Kuraray, Japan). After 24 hour-storage in $37^{\circ}C$water, the resin bonded teeth were sectioned bucco-lingualy at the center of cavity. Specimens were vertically sectioned into 1.0 ${\times}$1.0 mm thick serial sticks perpendicular to the bond surface using a low-speed diamond saw (Accutom 50, Struers, Copenhagen, Denmark) under water cooling. The trimmed specimens were then attached to the testing device and in turn, was placed in a universal testing machine (EZ test, Shimadzu Co., Kyoto, Japan) for micro-tensile testing at a cross-head speed of 1 mm/min. The results obtained were statistically analyzed using 2-way ANOVA and t-test at a significance level of 95%. The results were as follows: 1. There was no significant difference between bulk filling and incremental filling. 2. There was no significant difference between pulpal wall and axial wall, either. Within the limit of this study, it was concluded that microtensile bond strength was not affected by the filling technique and the site of cavity walls.