• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.171-179
• /
• 1991

The purpose of this study was to investigate the color stability of 3 porcelain repair composite resins Twenty specimens of each composite resin were made and ten specimens were polished at 10 minutes after polymerization, and the others were polished at 48 hours after polymerization. For 60 days, the color characteristics were measured by fiber-optic colorimeter (Model Tc-6FX, Tokyo Denshoku Co.). The obtained results were as follows: 1. The changes of $a^*$ value and $b^*$ value in composite resin polished at 10min. after polymerization were greater than those of composite resins polished at 48 hrs. after polymerization. 2. The $a^*$ values of all composite resins were increased and the $b^*$ values were decreased. 3. The $L^*$ values were decreased in composite resin manufactured by K & B Co., which were polished at 10min. after polymerization, but increased in composite resin manufactured by K & M Co., polished at 48 hrs. after polymerization.

• Journal of Technologic Dentistry
• /
• v.30 no.1
• /
• pp.65-71
• /
• 2008

The use of titanium in the field of dentistry has increased, due to their excellent biocompatibility, appropriate mechanical properties, corrosion-resistance and low price. However, many difficulties with the use of titanium for metal-ceramic crowns remain to be solved. The objective of this study was to evaluate the influence of surface modifications on the bonding characteristics of specific titanium porcelain bonded to cast titanium. The surfaces of Titanium were prepared with 4 test groups, i) sandblasted with particles of different size, ii) sandblasted after treated oxidization and oxidized after sandblast. We observed the bond strength and node aspect of titanium and ceramic, and respect to the methods of modifying surface of titanium by the test of mean roughness of surface, Scanning Electron Microscope, and 3-point flexural bend test. The results show that, 1. The specimens, which treated oxidization after process of sandblast with particles of 50um size, were the better for the bond strength in comparison with other specimen. 2. The specimen with process of sandblasting after oxidization treatment were the better for stability of the bond strength. 3. The wettability of titanium surface affect the bond strength.

• Journal of Technologic Dentistry
• /
• v.45 no.3
• /
• pp.55-60
• /
• 2023

Purpose: This study aimed to evaluate the effects of a special heat treatment on Pd-Au-Ag metal-ceramic alloy after degassing treatment and on changes in the hardness of the alloy during the firing process. Methods: Specimen alloys were cast and subjected to degassing at 900℃ for 10 minutes. These specimens were then subjected to a special heat treatment at 600℃ for 15 minutes in a dental porcelain furnace. Further, the specimens were subjected to simulated firing in the porcelain furnace. The resulting specimens were then tested for hardness, and changes in the microstructure were observed. Results: There was a decrease in the hardness of the alloy during the simulated firing of the cast alloy due to the coarsening of the particles. Meanwhile, additional heat treatment after degassing was found to play a crucial role in preventing a decrease in hardness. This treatment effectively suppressed the coarsening of the precipitates during repeated firing at high temperatures. Conclusion: Specific heat treatment of the Pd-Au-Ag metal-ceramic alloy prevented a decrease in its hardness and extended the lifespan of the metal-ceramic prosthesis.

• Restorative Dentistry and Endodontics
• /
• v.32 no.1
• /
• pp.19-27
• /
• 2007

The purpose of this study is to develope new dental color-space system. Twelve kinds of dental composites and one kind of dental porcelain were used in this study. Disk samples (15 mm in diameter, 4 mm in thickness) of used materials were made and sample's CIE $L^*a^*b^*$ value was measured by Spectrocolorimeter (MiniScan XE plus, Model 4000S, diffuse/$8^{\circ}$ viewing mode, 14.3 mm Port diameters, Hunter Lab USA) The range of measured color distribution was analyzed. All the data were applied in the form of T### which is expression unit in CNU Cons Dental Color Chart. The value of $L^*$ lies between 80.40 and 52.70. The value of $a^*$ are between 10.60 and 3.60 and $b^*$ are between 28.40 and 2.21. The average value of $L^*$ is 67.40, and median value is 67.30. The value of $a^*$ are 2.89 and 2.91 respectively. And for the $b^*$, 14.30 and 13.90 were obtained. The data were converted to T### that is the unit count system in CNU-Cons Dental Color Chart. The value of $L^*$ is converted in the first digit of the numbering system. Each unit is 2.0 measured values. The second digit is the value of $a^*$ and is converted new number by 1.0 measured value. For the third digit $b^*$ is replaced and it is 2.0 measured unit apart. T555 was set to the value of $L^*$ ranging from 66.0 to 68.0, value of $a^*$ ranging from 3 to 4 and $b^*$ value ranging from 14 to 16.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.24 no.2
• /
• pp.101-121
• /
• 2015

Zirconia polycrystalline (Y-TZP) showed better mechanical properties and superior resistance to fracture than other conventional dental ceramics. Zirconia-based ceramics have been successfully introduced into the clinic to fabricate fixed dental prostheses (FDPs), along with a dental computer-aided/computer-aided manufacturing (CAD/CAM) system. It has been clinically available as an alternative to the metal framework for fixed dental prostheses (FDPs). The most frequent clinical complication with zirconia-based FDPs was chipping of the veneering porcelain that was affected by many factors. Another option was full-contour zirconia FDPs using high translucent zirconia. Full-contour zirconia FDPs has many clinical advantages but it caused concern about the wear of antagonist enamel, because the hardness of Y-TZP was over double that of porcelain. However, many articles demonstrates that highly polished zirconia yielded lower antagonist wear compared with porcelains. In this article (1) advantages of full zirconia restorations, (2) clinical applications of zirconia restorations, (3) abutment preparation, (4) surface finish of zirconia restoration and antagonist enamel wear, (5) bond of zirconia with resin-based luting agents, (6) communication in clinical & lab.procedures for full zirconia restorations are reviewed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.31 no.4
• /
• pp.482-505
• /
• 1993

The purpose of this study was to evaluate the fracture characteristics and the effect of resin bonding of laminate porcelain. In order to characterize the indentation-induced crack, Young's moduli and characteristic indentation dimensions were measured. The fatigue life under three point flexure test was measured using the electro-dynamic type fatigue machine, and the crack propagation with thermocycling was investigated on the condition of 15 second dwell time each in $5^{\circ}C\;and\;55^{\circ}C$ bath. The Vickers indentation pattern and the fracture surface were examined by an optical microscope and a scanning electron microscope (SEM). The results obtained were summarized as follows ; 1. Young's moduli(E) of the laminate porcelain and the resin cement used in this experiment were $62.56{\pm}3.79GPa$ and $15.01{\pm}0.12GPa$, respectively. 2. The initial crack size of the laminate porcelain was $69.19{\pm}5.94{\mu}m$ when an indentation load of 9.8N was applied, and the fracture toughness was $1.065{\pm}0.156MPa\;m^{1/2}$. 3. The fatigue life of laminate porcelain showed the constant fracture range at the stress level 27.46-35.30MPa. 4. When a cyclic flexure load was applied, the fatigue life of resin-bonded laminate porcelain was more decreased than that of laminate porcelain. 5. When a thermocycling was conducted, the crack growth rate of resin-bonded laminate porcelain was more increased than that of laminate porcelain. 6. Fracture surface showed the radial crack, the lateral crack, and the macroscopic crack branching region beneath the plastic deformation region when an indentation load of 9.8N was applied.

• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.2
• /
• pp.309-319
• /
• 1996

This study was performed to evaluate the fracture toughness of seven commercially available dental ceramics by indentation fracture method. All specimens were fabricated to the final dimensions of approximately 12mm in diameter 2mm in thickness. The characte-ristic indentation dimensions of Vickers or Knoop indentation were measured to calculate the fracture toughness values and Young’s moduli. The results obtained were summarized as follows; 1. Young’s modulus and Vickers hardness of Vita In-Ceram showed the maximum values of $154.4{\pm}49.2$ Gpa and $12.60{\pm}0.71$Gpa, respectively. Results of Scheff test exhibited the significant difference between Vita In-Ceram group and others(p<0.01). 2. Maximum fracture toughness of $2.562{\pm}0.37 MPam^{1/2}$ for Vita In-Ceram and the maxi-mum one of $0.908{\pm}0.132MPam^{1/2}$ for Vitadur-N were calculated. Results of Scheff test showed the significant difference between Vita In-Ceram group and Vita Hi-Ceram(p<0.05) : also between Vita In-Ceram or Vita Hi-Ceram and others(p<0.01). 3. The alumina-based core ceramics showed the aspect of Palmqvist crack for the indentation load of 49.0N, but others showed the median/lateral crack for the indentation load of 9.8N.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.5
• /
• pp.656-673
• /
• 2003

Statement of problem : Long-term exposure of dental porcelain to saliva during temporary cementation of a porcelain-fused to metal (PFM) restoration could affect mechanical strength of dental porcelain if the restoration is refired. Purpose : This work was performed to verify the effect of water on the mechanical strength in aged dental porcelain. Material and method : 63 specimens(Vintage Metalbond opaque and opal powder) were distributed to three experimental groups ; non-water immersed control, immersed and pedried, and immersed and non-predired groups. The changes in flexural strength and fracture toughness after specimen refiring related to Fourier Transform Infrared (FT-IR) spectroscopy. Results : 1. The FT-IR reflectances assigned to molecular bonds of $H_2O$ were noted as significantly different between the first-fired group and three refired groups and between two water-immersed groups and control group after refiring(p<0.05). They were also significantly different between predried group and non-predried group after refiring(p<0.05) 2. For opal specimens, FT-IR absorbances for hydrogen bond of $H_2O$ and silanols were significantly higher in non-predried group than in predreid group(p<0.05). 3 Predried opal group showed the highest mean flexural strength(p<0.05). Non-predried group indicated higher mean flexural strength than control group(p<0.05). 4. The mean fracture toughness for predired group was higher than non-predried group(p<0.05). 5. The difference of leucite crystal size is noted between control group and water-immersed, predried group in scanning electron microscopic study(${\times}10000$).

• Journal of Technologic Dentistry
• /
• v.38 no.3
• /
• pp.175-183
• /
• 2016

Purpose: Observation of Oxide Film Formation and Bonding Strength according to surface treatment of Co-Cr Alloy for porcelain fused to Metal. Methods: metal specimens $0.5mm{\times}25mm{\times}4mm$ in size were made using Co-Cr alloys for porcelain fused to metal crown (Heraenium P, Tae jung Medis). Dental porcelain $0.5mm{\times}25mm{\times}4mm$ in size was sintered on the metal specimens after changing the etching time, sandblasting condition, and heat treatment temperature. Subsequently, the bonding strength was compared by the three-point flexural strength test using a universal testing machine (UTM) to observe the fracture surface and oxidized layers. Results: With regard to the experimental group treated with acid-etching, Specimen 1 treated for 25 minutes (B-3) showed the highest bonding strength, and Specimen 2 treated only with sandblasting showed the most excellent bonding force at 3.5 bar (C-3). With regard to the experimental group treated with sandblasting at 3.5 bar after acid-etching for 25 minutes, Specimen 3 with heat treatment at $980^{\circ}C$ (D-3) showed the highest bonding strength. Conclusion: The specimen which went through both sandblasting and etching, showed an excellent ceramicmetal bond strength.

• Journal of Technologic Dentistry
• /
• v.39 no.1
• /
• pp.43-52
• /
• 2017

Purpose: Physical and chemical properties of gold is most suitable to be restored of teeth to its original state. Recently zirconia was used instead of gold because of esthetical and intimacy of human body. Because of high strength and high abrasion resistance of zirconia, all zirconia artificial tooth lead to wear the original tooth of opposite site. To preserve this original tooth, zirconia artificial tooth covered with dental ceramic glass was used. When joining the zirconia core and dental ceramic glass, difference of their thermal expansion coefficient and wetting ability is generated the residual stress at interface lead to crack. In order to solve this problem, intermediate layer what is called zir-liner was imported to decrease the residual stress and increase the bonding strength. Methods: In this study, to identify the optimum conditions for manufacturing process, various methods to rough the surface of zirconia core were adopted, and vary the thickness of interlayer, and analyzed bond strength. Results: Bond strength of sanding specimens group showed higher than that of non-sanding specimens group, and once applied intermediate layer with sanding specimens showed highest bond strength with 28 MPa. SEM photomicrographs of zirconia cores fired at $1500^{\circ}C$ showed parallel straight lines in sanding and pockmarked surface in blasting surfaces as abrasion traces. Observation of the destruction section after shear test by SEM were carried out. Liner applied non-sanding group and non-liner applied sanding group all showed interfacial crack. Sandblasting group with non-liner showed remained dental ceramic glass on the surface of zirconia. Sandblasting group with once applied liner showed partially remained liner and dental ceramic glass on the surface of zirconia. XRD analysis revealed that sandblasting group showed higher monoclinic peaks than other specimens group and this result was due to the high collision energy for stress induced phase transformation. Conclusions: A study on the improvement of bonding strength between zirconia and dental ceramic glass steadily carried out for the future to practical use.