• Journal of Dental Rehabilitation and Applied Science
• /
• v.34 no.2
• /
• pp.72-79
• /
• 2018

Purpose: The purpose of this study was to compare flexural strength and elastic modulus of several splinting materials dependent on water absorption. Materials and Methods: Three different materials; LightFix, G-FIX, G-aenial Universal Flo; were used in this study. Thirty rectangular bar specimens ($25{\times}2{\times}2mm$) of each materials were prepared. Fifteen specimens of each materials were stored in 100% relative humidity atmosphere, $37^{\circ}C$ for 24 hours. The other specimens were stored in distilled water, $37^{\circ}C$ for 30 days. Flexural strength and elastic modulus were calculated using Universal testing machine. One-way ANOVA and Scheffe's post hoc test at 95% level of significance were used on all test results. Results: In LightFix, flexural strength and elastic modulus were significantly decreased after aging. In G-FIX, there was no significant change in flexural strength and elastic modulus after aging. In G-aenial Universal Flo, flexural strength was significantly decreased, but elastic modulus did not change significantly. Statistical analysis reveals that flexural strength and elastic modulus increased in the order of LightFix, G-FIX, G-aenial Flo in both 24 hours and 30 days. Conclusion: It could be deduced from this study that flexural strength and elastic modulus of some resins could be changed when it aged in oral environment. Thus this should be considered when choosing a resin to perform a resin-bonded splint.

• Restorative Dentistry and Endodontics
• /
• v.36 no.3
• /
• pp.203-210
• /
• 2011

Objectives: The purpose of this study was to evaluate the effect of various application methods of one-step self-etch adhesives to microtensile resin-dentin bond strength. Materials and Methods: Thirty-six extracted human molars were used. The teeth were assigned randomly to twelve groups (n = 15), according to the three different adhesive systems (Clearfil Tri-S Bond, Adper Prompt L-Pop, G-Bond) and application methods. The adhesive systems were applied on the dentin as follows: 1) The single coating, 2) The double coating, 3) Manual agitation, 4) Ultrasonic agitation. Following the adhesive application, light-cure composite resin was constructed. The restored teeth were stored in distilled water at room temperature for 24 hours, and prepared 15 specimens per groups. Then microtensile bond strength was measured and the failure mode was examined. Results: Manual agitation and ultrasonic agitation of adhesive significantly increased the microtensile bond strength than single coating and double coating did. Double coating of adhesive significantly increased the microtensile bond strength than single coating did and there was no significant difference between the manual agitation and ultrasonic agitation group. There was significant difference in microtensile bonding strength among all adhesives and Clearfil Tri-S Bond showed the highest bond strength. Conclusions: In one-step self-etching adhesives, there was significant difference according to application methods and type of adhesives. No matter of the material, the manual or ultrasonic agitation of the adhesive showed significantly higher microtensile bond strength.

• Progress in Medical Physics
• /
• v.20 no.2
• /
• pp.80-87
• /
• 2009

Phase transformation, superelastic characteristics and variation of surface residual stress were studied for Nitinol shape memory alloy through application of UNSM technology, and life extension methods of stent were also studied by using elastic resilience and corrosion resistance. Nitinol wire of ${\phi}1.778$ mm showed similar surface roughness before and after UNSM treatment, but drawing traces and micro defects were all removed by UNSM treatment. It also changed the surface residual stress from tensile to compressive values, and XRD result showed less intensive austenite peak and clear martensite and additional R-phase peaks after UNSM treatment. Fatigue resistance could be greatly improved through removal of surface defects and rearrangement of surface residual stress from tensile to compressive state, and development of surface modification system to improve not only bio-compatability but also resistance to corrosion and wear will make it possible to develop vascular stent which can be used for circulating system diseases which run first cause of death of recent Koreans.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.526-536
• /
• 2008

The purpose of this study was to compare the effect of various dentin bonding systems on microtensile bond strength of immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Eighteen extracted permanent molars were used in this study. The teeth for DDS group were restored with a provisional restorations, and immersed in saline solution for 1 week, and divided into 3 subgroups according to various dentin bonding adhesives; SB subgroup (3 step total-etch adhesive), SE subgroup (2 step self-etch adhesive), XE subgroup (1 step self-etch adhesive). In IDS group, the teeth were divided into 3 subgroups, and applied with bonding adhesives as in DDS group. The teeth were restored with provisional restorations, and immersed in saline solution for 1 week. Indirect composite disc was cemented with resin cement, and all specimens were subjected to microtensile bond strength. The data were statistically analyzed with oneway ANOVA and Student t-test. The results were as follows: 1. The IDS group showed significantly higher ${\mu}TBS$ than DDS group in 3 step total-etch and 2 step selfetch adhesive (p < 0.05). 2. In IDS and DDS group, 3 step total-etch adhesive showed the highest ${\mu}TBS$ value, followed by 2 step self-etch, and 1 step self-etch adhesive. In IDS group, the ${\mu}TBS$ value for 1 step self-etch adhesive was significantly different from those of the other subgroups (p < 0.05), and in DDS group, there were statistical differences in all subgroup (p < 0.05). 3. Failure modes of tested dentin bonding adhesives were mostly mixed failure and only 1 step self-etch adhesive showed adhesive failure.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.545-552
• /
• 2008

The purpose of this study was to evaluate the influence of sodium ascorbate on microtensile bond strengths of total-etching adhesive system to pulp chamber dentin treated with NaOCl. Pulp chambers of extracted human non-caries permanent molars were treated as follows: group 1, with 0.9% NaCl; group 2, with 5.25% NaOCl; group 3, with 5.25% NaOCl and 10% sodium ascorbate for 1min; group 4, with 5.25% NaOCl and 10% sodium ascorbate for 1 min and 10ml of water; group 5, with 5.25% NaOCl and 10% sodium ascorbate for 5 min; group 6, with 5.25% NaOCl and 10% sodium ascorbate for 5 min and 10ml of water; group 7, with 5.25% NaOCl and 10% sodium ascorbate for 10 min; group 8, with 5.25% NaOCl and 10% sodium ascorbate for 10 min and 10ml of water. Treated specimens were dried, bonded with a total-etching adhesive system (Single bond), restored with a composite resin(Z250) and kept for 24h at 100% humidity to measure the microtensile bond strength. NaOCl-treated group (group 2) demonstrated significantly lower strength than the other groups. No significant difference in microtensile bond strengths was found between NaCl-treated group (group 1) and sodium ascorbatetreated groups (group 3-8). The results of this study indicated that dentin treated with NaOCl reduced the microtensile bond strength of Single bond. Application of 10% sodium ascorbate restored the bond strength of Single bond on NaOCl-treated dentin. Application time of sodium ascorbate did not have a significant effect.

• Korean Journal of Materials Research
• /
• v.2 no.6
• /
• pp.408-416
• /
• 1992

Stable TiS$i_2$was formed by RTA on single-Si and on poly-Si. Subsequently, an Al-1% Si layer with 600-nm thick was deposited on top of the TiS$i_2$, Finally, the specimens were annealed for 30min at 400-60$0^{\circ}C$in $N_2$ambient. The thermal stability of Al-1% Si/TiS$i_2$bilayer and interfacial reaction were investigated by measuring sheet resistance, Auger electron spectroscopy (AES), and scanning electron microscopy (SEM). The composition and phase of precipitates formed by the reaction of Al-1% Si with Ti-silicide were studied by energy dispersive spectroscopy (EDS), X-ray diffraction (XRD). In the case of single-Si substrate the reaction of Al-1% Si layer with TiS$i_2$layer resulted in precipitates, consuming all TiS$i_2$layer at 55$0^{\circ}C$. On the other hand, the disappearance of TiS$i_2$on poly-Si occurred at 50$0^{\circ}C$ and more precipitates were formed by the reaction of Al-1% Si/TiS$i_2$on potty-Si substrate than those of the reaction on single-Si substrate. This phenomenon resulted from the fact that Ti-silicide formed on poly-Si was more unstable than on single-Si by the effect of grain boundary. By EDS analysis the precipitates were found tobe composed of Ti, Al, and Si. X-ray diffraction showed the phase of precipitates to be theT$i_7$A$l_5$S$i_12$ternary compound.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.4
• /
• pp.619-627
• /
• 2008

The objective of this study was to compare the microleakage of five adhesive systems in the enamel and dentin of permanent teeth. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were prepared on both buccal and lingual surfaces of 25 extracted human molar teeth. The tested adhesives were: Adper Scotchbond Multi-purpose Plus Adhesive (SM), Adper Single bond 2 (SB), Clearfil SE Bond (SE), Adper Prompt L-Pop (PL) and G-Bond (GB). The results were as follows: 1. At the enamel margins, PL showed the highest leakage value(0.85), and others showed values of SB(0.55), GB(0.50), SM(0.35) and SE(0.25) in decreasing order. There were statistically significant differences in PL vs. SM and PL vs. SE(p<0.05). 2. At the dentin margins, GB showed the highest leakage value(2.10), and others showed values of SE(1.45), PL(1.40), SB(1.05), SM(0.70) in decreasing order. There were statistically significant differences in GB vs. SB and GB vs. SM(p<0.05). 3. Dentin margins showed high dye penetration rate than enamel margins in all material tested groups and there were statistically significant differences for SE, PL and GB.

• The Journal of Korean Academy of Prosthodontics
• /
• v.32 no.1
• /
• pp.1-8
• /
• 1994

The purpose of this study was to evaluate the effect of the canal filling sealer to resin cement When posts were cemented in the endodontically treated teeth, 86 incisors were used. The coronal portion of the teeth were removed at the cemento-enamel junction, every tooth was done treatment of canal. And the teeth was divided was into 12 groups. G : I a n : 7 Treatment : Z.P.C (1 day after Z.O.E. sealer) G : I b n : 7 Treatment : All-Bond (3 day after sealer) G : II a n : 8 Treatemt : Z.P.C (3 day after sealer) G : II b n : 7 Treatemt : All-Bond (3 day after sealer) G : III a n : 8 Treatemt : Z.P.C (7 day after sealer) G : III b n : 8 Treatemt : All-Bond (7 day after sealer) G : IV a n : 7 Treatemt : Z.P.C (1 day after Apexit sealer) G : IV b n : 7 Treatemt : All-Bond (1 day after sealer) G : V a n : 7 Treatemt : Z.P.C (3 day after sealer) G : V b n : 7 Treatemt : All-Bond (3 day after sealer) G : VI a n : 7 Treatemt : Z.P.C (7 day after sealer) G : VI a n : 7 Treatemt : All-Bond (7 day after sealer) Ready made stainless steel Para-post(PD-K-3) was cemented with Z.P.C. in subgroup a, and cemented with All-Bond & composite resin cement in subgroup b to depth 7mm. After 5 days at cementation of post, teeth with cemented posts were mounted on a retention jig and the failure loads of the specimens were measured by an Instron Universal Testing Machine. The results were as follows. 1. The results of failure loads were $15.5{\pm}7.1kg$ in group I b, $21.6{\pm}5.4kg$ in group II b and $20.1{\pm}18.1kg$ in group III b, and there was no statistically significant , difference between each group(p>0.05). 2. The results of failure loads were $19.0{\pm}6.7kg$ in group IV b, $17.3{\pm}6.5kg$ in group V b.and $18.9{\pm}7.9kg$ in group VI b and there was no significant difference between each other(p>0.05). 3. In same condition, the failure load of subgroup a was largely higher the subgroup b. But there was no significant difference between each other(p>0.05).

• Journal of Periodontal and Implant Science
• /
• v.25 no.3
• /
• pp.587-602
• /
• 1995

The purpose of this study was to compare the effects of citric acid and tetracycline HCI application to the root surfaces of periodontally diseased teeth on the proliferation and spreading of human periodontal ligament cells. The roots were prepared so that the comparison could be made among root planed, citric acid treated and tetracycline HCI treated surfaces. In the cell proliferation experiment, human periodontal ligament cells at a concentration of $1{\times}10^5$ cells/ml were seeded in each culture well with specimens and incubated for 6 hours. Then, the specimens were transferred to a fresh culture well and incubated for 24, 48, 72 hours respectively. The cell counting was done after trypsinization. In the cell spreading experiment, $1{\times}10^4$ cells/ml were seeded in each culture well and incubated for 30min, 6 hours and 24 hours at 37.5$^{\circ}C$ in a $CO_2$ incubator. Then, all specimens were fixed with phosphate buffered glutaraldehydes, postfixed with phosphate buffered osmium tetraoxide, stained with phosphate buffered tannic acid, dehydrated in ethanol, dried at a critical point, coated with gold and examined under a scanning electron microscope. The results were as follows:In the cell proliferation experiments, the number of attached cells increased more in the tetracycline treated group than in the other groups. In the initial attachment, the appearance of the tetracycline treated the groups was slightly more spread out than in the other groups. After 6 hours of incubation, it was observed in most of the cells that cell morphologic alteration went from ovoid shapes sto spindle shapes. After 24 hours of incubation, the cells of all groups had a fusiform appearance and were connected to each other by numerous cytoplasmic processes. The tetracycline and citric acid treated groups had a similar spreading appearance of periodontal ligament cells, but the tetracycline treated group was more effective in the cell proliferation than the citric acid group.

• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.3
• /
• pp.211-221
• /
• 2014

Purpose: The purpose of this study was to evaluate the surface characteristics and response of osteoblast-like cell at SLA surface treated with NaOH. Materials and methods: Three kinds of specimens were fabricated for the experiment groups. Control group was a machined surface, SLA group was a conventionally SLA treated surface, and SLA/NaOH gorup was SLA surface treated with NaOH. To evaluate the surface characteristics, the surface elemental composition (XPS), surface roughness and surface contact angle were evaluated in each group. And the cytotoxicity, cell adhesion, cell proliferation and ATP activity of osteoblast-like cells (MG-63 cells) were compared in each group for evaluatation of the cell responses. Statistical comparisons between groups were carried out via one-way ANOVA using the SPSS software (SPSS Inc., Chicago, USA), and then performed multiple comparisons. The differences were considered statistically significant at P<.05. Results: SLA surface treated with NaOH (SLA / NaOH group) was changed to hydrophilic surface. All groups did not show the cytotoxicity to the MG-63. In cell adhesion studies, SLA / NaOH group showed the higher degree of adhesion than anothers (P<.05), Up to 7 days of incubation, the proliferation was showed the increasing tendency in all groups but SLA / NaOH group showed the highest cell proliferation between the three groups (P<.05). At 7 days of incubation, there was no difference in ALP activities between the three groups, but at 14 days, SLA / NaOH group showed significant increase in ALP activities (P<.05). Conclusion: In this study, SLA surface treated with NaOH promoted cell adhesion, proliferation and differentiation. It means that SLA/NaOH group is possible to promote osseointegration of implants.