• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.04a
• /
• pp.141-143
• /
• 2008

극한의 추위를 견디기 위한 내한성 코팅 직물의 개발은 활발히 진행되었으나, 항균성에 대해서는 활발한 개발이 이루어지지 않고 있다. 본 연구는 내한성 코팅 직물에 천연항균제를 처리하여 물성의 변화를 알아보고자 한다. 현재 시판되고 있는 내한성 코팅 수지에 해조류에서 추출한 천연항균제를 처리하여 상용성을 알아보았다. 내한성 코팅수지에 천연항균제를 처리하면, 내한성 코팅 수지의 고유 물성은 유지되면서 항균성이 나타나는 것을 알 수 있었다.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1678-1686
• /
• 2021

In this study, we prepared phosphorous flame-retarding coating solutions by mixing triphosphate (3 phosphonate), phytic acid (6 phosphonate), or ammonium polyphosphate (10 phosphonate) with boric acid as a crosslinking agent and acryl resin binder. Prepared phosphorous flame-retarding coating solutions were coated onto non-woven fabrics, respectively, to obtain high flame-retarding effects. These prepared flame-retardant non-woven fabrics were evaluated using smoke density standard test (ASTM E662), limit oxygen index standard test (ISO E622), and vertical burning standard test (UL 94). Their flame-retarding effects were affected by the number of phosphonate groups. Regardless of natural or synthetic binder resins, their effects showed the following order: ammonium polyphosphate > phytic acid > triphosphate. Natural hydrocarbon compounds were also examined to determine the possible retardancy of binder resins. Results showed that natural hydrocarbon binder resins could be used for preparing fire-retardant nonwoven fabrics.

• Journal of Adhesion and Interface
• /
• v.8 no.2
• /
• pp.15-21
• /
• 2007

To prepare a natural rubber-based pressure-sensitive adhesive (PSA) for protection film of opto- functionalized sheet, natural rubber (NR) was blended with a DCPD type tackifier and three types of aliphatic hydrocarbon resins, respectively. Also, to supply low cohesion strength of NR, in the fixed ratio of tackifier, synthetic rubber, styrene-isoprene-styrene (SIS) block copolymer was blended with NR as a function of SIS contents. PSA performance of prepared PSAs was evaluated using probe tack and peel strength. Probe tack of NR/tackifier blends was increased with increasing tackifier contents, and showed maximum peak. In addition, probe tack of NR/tackifier blends slightly increased with increasing softening point of aliphatic hydrocarbon resins. Their peel strength increased up to 50 wt% of tackifier contents, but in the over contents of tackifier, they showed stick-slip failure mode. Finally, probe tack of NR/SIS/tackifier blends showed the maximum values at 20~40 wt% of tackifier contents, but at 20 wt% of tackifier contents, they showed fibrillation. For this reason, peel strength showed maximum values at 40 wt% of tackifier contents.

• Korean Journal of Heritage: History & Science
• /
• v.56 no.3
• /
• pp.158-171
• /
• 2023

Pottery filled with organic materials was excavated from the G-2 building site of Yongjangseong Fortress, Jingo, a relic of the Goryeo Dynasty. In this study, the characteristics of organic material were confirmed by a scientific analysis of organic material in pottery found at the palace in Yongjangseong, Jindo. In addition, it was intended to review the analysis method to identify the natural resin and to secure characteristic components(biomarkers) for each natural resin and use them as basic data in the future. The organic materials in the pottery were analyzed using attenuated total reflectance Fourier-transformed infrared spectroscopy(ATR-FTIR) and gas chromatography mass spectrometry(GC-MS). The infrared spectral characteristics were estimated to be natural resin, and biomarkers of organic materials were identified as sesquiterpene-based compounds(C₁₅H₂₄, MW 204) and derivatives. The lacquer(T.vemicifluum) is composed mainly of alkenes, alkanes, and catechol. Pine resin(P.densiflora), on the other hand, is primarily composed of diterpenoid(abietic acid, pimaric acid) and Whangchil(yellow lacquer) is identified to have sesquiterpenes(such as selinene, muurolene, calamenene) as its main components. So, the organic material in the pottery can be identified as Whangchil by comparing their compounds with modern resin materials from Dendropanax. morbifera that correspond with the results. Whangchil, which is exuded from the Dendropanax. morbifera, has been used as a natural coating materials since ancient times, and it has been confirmed that the characteristic components are well preserved even 700 years later. It can be assumed that the interior Whangchil was stored not for use as a coating, but rather for ritual purposes when the building was constructed, because the pottery was found near the cornerstone. Furthermore, based on simplified sample preparation using pyrolysis-gas chromatography mass spectrometry(Py-GC-MS), the thermal decomposition products were found to be similar to the characteristic components, suggesting that this method can be applied to the identification of natural resins used in historic artifacts.

• Korean Journal of Heritage: History & Science
• /
• v.54 no.4
• /
• pp.78-89
• /
• 2021

Organic residues analysis is an analysis method that reveals the types of organic material samples by using the characteristic that main components constituting substances are different depending on the species of animals and plants. In this study, scientific analysis of the organic residues attached to wood coffins in the Joseon Dynasty Hoemyo excavated from the site of Singok-dong, Uijeongbu was used to identify the types of remnants and to use them as information to restore the uses of organic materials and the way they lived in the past. As a result of FT-IR analysis of the residue attached to the inside of the wood, it was estimated to be a natural plant resin material. In addition, as a result of analysis by GC-MS to confirm the characteristic factors of natural resins, diterpenoids (abietane) and pimaran (pimarane), such as dehydroabietic acid and pimaric acid (diterpenoid) compounds, and saturated and unsaturated fatty acid components were detected together. Diterpenoid compounds are components mainly found in Pinaceae resins. It is confirmed in the literature that rosin, a representative material of Pinaceae resin, was used as an adhesive material. Considering the situation where an organic material remained at the joint of the wood, the organic material attached to the wood is judged to be an adhesive material made of Pinaceae resin. In addition, the fatty acid component detected together is a component derived from plant oil, and it is presumed to be made by mixing rosin and oil as recorded in previous studies. This study confirms that organic residues remain in the burial environment without losing their characteristics. It is expected that scientific analysis of organic residues will be conducted in the future to accumulate information necessary for the interpretation of past living culture.

• Korean Chemical Engineering Research
• /
• v.47 no.3
• /
• pp.303-309
• /
• 2009

The effects of zeolite type catalysts addition on the thermal decomposition of low density polyethylene(LDPE) and ethylene vinyl acetate(EVA) resin have been studied in a thermal analyzer(TGA, DSC) and a small batch reactor. The zeolite type catalysts tested were natural zeolite, FCC catalyst, used FCC catalyst, and catalyst A. As the results of TGA experiments, addition of antifogging-agent decreased the pyrolysis point to $250^{\circ}C$, but addition of longevity-agent and clay reduced the pyrolysis rate in EVA resin. Addition of the zeolite type catalysts in the LDPE resin increased the pyrolysis rate in the order of catalyst A > used FCC catalyst > natural zeolite > LDPE resin. Addition of the zeolite type catalysts in the EVA resin increased the pyrolysis rate in the order of used FCC catalyst > natural zeolite > catalyst A > EVA resin. In the DSC experiments for LDPE resin, addition of zeolite type catalysts decreased the melting point and the heat of pyrolysis reaction in the order of catalyst A > used FCC catalyst > natural zeolite> LDPE resin. In the batch system experiments, the mixing of natural zeolite enhanced the yield of liquid fuel oil.

• Journal of Conservation Science
• /
• v.27 no.1
• /
• pp.49-59
• /
• 2011

The damaged ceramics were repaired and restored thru various methods with various materials. The history of Ceramic repair and restoration has developed widening its areas from traditional stage utilizing applicable living material to the specified field that introduces new materials, new process methods and material analysis. Through investigations over the documents, artifacts and analysis, the period could be divided into natural material period in which uses the bonds extracted from the animals, plants and lime (prehistoric to Japanese domination period), Semi-artificial period in which mix natural material and synthetic resins such as "Jusabi"(Japanese domination period to 1970s.) and complete synthetic resin period in which introduces new materials and process methods in accordance with preservation standard (after 1980s).

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.79-79
• /
• 2011

최근 플라스틱 제품의 사용후 폐기에서 발생 되는 환경적인 문제점들이 대두 되고 있는 가운데, 이러한 제품에 대한 친환경적인 재료 설계에 대한 요구가 거세지고 있는 실정으로 플라스틱 업계의 사활이 걸릴 정도의 중요한 문제로 부각되고 있다. 본 연구에서는 이러한 플라스틱 제품의 치명적인 환경적인 문제점을 극복하고자, Matrix 물질이 되는 플라스틱에서 부터 친 환경적인 생분해성 수지를 사용하면서, 물성의 강화제로써 천연물 유래의 여러 종류의 섬유를 사용하고자 하였다.가장 보편화된 생분해성 플라스틱인 지방족 폴리에스테르 계통의 생분해성 수지와 Polylactic acid에 대해 검토를 하였다. 지방족 폴리에스테르 의 경우는 기존 플라스틱 제품과 비교해서 유연하고, 신장율이 높고, PLA 대비 내열 사용한계 온도도 높아서 물성적인 측면에서 상당한 장점을 가지고는 있으나 가격이 매우 고가이므로, 기존 플라스틱을 대체하는 것에는 문제점이 있다. 반면 PLA의 경우 지방족 폴리에스테르 대비 절반 이하의 가격이고 기계적 강도 또한 매우 높기 때문에 기존의 플라스틱을 대체할 수 있는 가장 유력한 물질로 대두 되고 있으나, 사출물과 같은 충격이 요구되는 제품에 있어서는 PLA 고유의 약한 취성이 가장 큰 단점으로 지적되고 있다. 본 연구에서는 이러한 PLA를 기반으로 PLA의 장점이 기계적 강성을 유지하면서, 취성을 보완하기 위해 PBS를 혼합 할 수 있는 기술을 개발하였으며, 또한 원재료의 Cost를 줄이고, PBS 혼합에 따른 PLA의 기계적 강도 감소를 보완하기 위해 천연물 유래의 Wood fiber, Starch, Bamboo fiber, Cellulose fiber, Paper fiber 와 같은 각종 천연 Filler를 사용하여 기계적 기계적 강도 감소를 최소화 하였다.

• Journal of Adhesion and Interface
• /
• v.14 no.3
• /
• pp.128-134
• /
• 2013

This study investigated the natural adhesives for ceramics conservation that can be used as a substitution for synthetic resins. Samples were prepared by mixing lacquer with animal glue and the structure and adhesion properties of the samples were analyzed. The structure analysis with FT-IR showed that carbonyl (C=O), amine (N-H) and aromatic (C=C) bonds are increased by adding animal glue on lacquer. Comparing to the viscosity and tensile strength of the sample to the Paraloid B-72 and Araldite rapid type, these natural adhesives can be a substitution for the synthetic resins. Through methodical and intensive study, we expect practical uses of this eco-friendly natural adhesives for ceramics conservation.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.1
• /
• pp.80-87
• /
• 2004

This study was carried out to improve the properties of powdered tannin adhesive(PT) by adding liquid tannin resin(LT) to PT in the manufacture of particleboard. Mixing the LT to PT from 50% to 100% by weight did not show any difference in particleboard properties, but the higher the powdered tannin resin ratio, the lower the properties of the board. The proper ratio of PT to LT was 30:70 for the improvement of PT-particleboard, unless LT lower than 70%. Internal bonding strength was in proportional to the amount of LT. Mixing amino adhesives and PT did not show any improvements in mechanical and physical properties of the board but they only acted as scavenger for the free formaldehyde.Manufacturing particle board with the adhesive of 30:70 (PT:LT) and by using double blender resulted in high-performance products of E₀ level of formaldehyde emission with high water resistance (U type; below 12%, M type; below 25%), as well as saving chip drying energy.