• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.7
• /
• pp.1147-1154
• /
• 2001

One of major problems in analyzing failure mechanism of real components is the accurate measurement of crack size and shape. The DCPD(Direct Current Potential Drop) method has been widely used for the crack measurement of a structure and finite element analysis has been used for the derivation of calibration equations, which relates the potential drop with the crack depth. In this paper, finite element analyses were performed for semi-elliptical surface cracks with various crack shapes(a/c) and crack depths(a/t). As a result, a calibration equation has been derived for the measurement of a semi-elliptical surface crack in wide plates. Analytical results are compared with experimental results to evaluate the validity and the applicability of the derived equation. The proposed method is expected to provide efficient and accurate measurement of a surface crack during crack growth.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.12
• /
• pp.1375-1382
• /
• 2009

The objective of this paper is to apply the load ratio method to the measurement of the crack length of the real scale pipe specimen. The load ratio method was modified and finite element analyses were performed to derive the relationship between the normalized compliance and the normalized crack length for the pipe specimen. In order to measure the crack length, the direct current potential drop method and the modified load ratio method were applied to the pipe test. The applicability of the modified load ratio method was confirmed by comparing the calculated crack length with the measured crack length from the pipe experiment.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.48-53
• /
• 1998

원자력 발전소 배관계통에 파단전 누설 (LBB) 설계개념의 적용을 위해서는 원자로 가동온도에서의 재료의 파괴저항성 평가가 필수적이다. 본 연구에서는 국내 원자로의 1차 냉각계통배관의 엘보우 소재로 사용되는 SA516-Gr.70 강의 파괴저항성에 미치는 DSA (Dynamic Strain Aging, 동적변형시효) 영향을 고찰하였다. 파괴저항성 평가를 위해 원자로 가동온도를 포함한 상온~50$0^{\circ}C$ 온도영역에서 준정적 하중에서부터 지진 하중 정도의 동적 하중까지 하중속도를 달리하여 직류전위차법 (DCPD) 이용하여 J-R 시험을 행하였다. J-R 시험결과, SA516-Gr.70 강은 특정한 온도와 하중속도의 조합에서 파괴저항성이 크게 떨어지는 양상을 보였으며, 낮은 파괴저항성을 나타내는 온도는 하중속도가 증가함에 따라 높은 온도쪽으로 이동하는 전형적인 DSA 감수성을 보였다. 인장시험을 통해서도 큰 폭의 serration 이 관찰되었으며 SA516-Gr.70 강에서 파괴저항성의 변화와 DSA 현상과의 연관성을 고찰하였다.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.61-66
• /
• 2000

The fatigue crack initiation life is studied on automotive spot weldment made from cold rolled carbon steel(SPC) sheet by using DCPDM and local strain approach. It can be found that the fatigue crack initiation behavior in spot weldment can be definitely detected by DCPDM system. The local stresses and strains are estimated by elastic-plastic FEM analysis and the alternative approximate method based on Neuber's rule were applied to predict the fatigue life of spot weldment. A satisfactory correlation between the predicted life and experimental life can be found in spot weldment within a factor of 4.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.328-332
• /
• 2000

Following the method described in ASTM E1737, J resistance curves are measured for Cr-Mo steel SA387, and Cr steel A240 which are used as piping materials in nuclear industry. Crack driving force diagrams are generated in order to find out instability points in crack growth. The $J_{appl}$ curves, which are used in the crack driving force diagram, are obtained from EPRI J estimation method and the finite element analysis. Crack growth instability points are plotted in load-crack length plane and the results are discussed.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.78-83
• /
• 2004

Environmental fatigue crack propagation of CF8M and CF8A steels used in the domestic PWR were investigated on the simulated PWR condition(Temperature: $316^{\circ}C$, Pressure: 15MPa). The test equipment for environmental fatigue(high temperature-high pressure loop, autoclave, load frame, measurement system) were designed. As-received and 60-year aged specimens were used in the test. To compare with environmental fatigue test, another test was performed in the air condition. The fracture surface of specimens were difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, more particles covered fracture surface were peeled.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.262-267
• /
• 2004

The unloading compliance method is the most commonly used method to evaluate the fracture resistance characteristics of a material. In dynamic loading condition, the direct current potential drop(DCPD) method has been used because the unloading compliance method can not be applied due to the discontinuity of loading. However, even in the dynamic test using DCPD method, there is a problem that the voltage drops sharply on the initiation of crack. For the reason metioned above, the normalization method was suggested on ASTM E 1820 which is revised recently, as a new method to evaluate the dynamic fracture resistance characteristic. The nomalization method can be used to obtain a fracture resistance curve directly from a load-load line displacement. In this study, we obtained two fracture resistance curves from static test of welding part of nuclear piping both by unloading compliance and nomalization method. The two curves were almost same each other, so the adaptability of the nomalization method has been proved. We conducted a dynamic fracture resistance test for the same material. The fracture resistance curve from the dynamic test was obtained by normalization method and compared to that of the static test result.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.8
• /
• pp.751-758
• /
• 2017

The behavior of fatigue crack growth of nickel-based powder metallurgy superalloy that could be used in aircraft turbine disc is investigated at room temperature, and $650^{\circ}C$ considering real operating conditions. The direct current potential drop(DCPD) method was used to measure the crack length of material in real time according to ASTM E647. Tests were performed with various stress ratios (0.1 and 0.5). Experimental results show that stress ratio, and temperature all affect the behavior of fatigue crack growth. As the stress ratio and temperature increase, the fatigue crack growth rate of nickel-based powder metallurgy superalloy also increases. Results were compared and reviewed with fatigue crack growth rates of other nickel-based superalloy materials (Inconel-100) that were studied in previous papers. Fractography analysis of the fractured specimens was performed using as SEM.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.4 s.247
• /
• pp.420-427
• /
• 2006

The structural and leakage integrity of steam generator tubes should be sustained against all postulated loads even if a crack is present. During the past three decades, most of the efforts with respect to integrity evaluation of steam generator tubes have been focused on limit load solutions but, recently, the applicability of elastic-plastic fracture mechanics was examined cautiously due to its effectiveness. The purpose of this paper is to introduce a testing method to estimate fracture resistance characteristics of steam generator tubes with a through-wall crack. Due to limited thickness and diameter, inevitably, the steam generator tubes themselves were tested instead of standard specimen or alternative ones. Also, a series of three dimensional elastic-plastic finite element analyses were carried out to derive closed-form estimation equations with respect to J-integral and crack extension for direct current potential drop method. Since the effectiveness of $J_{IC}$ as well as J-R curves was proven through comparison with those of standard specimens taken from pipes, it is believed that the proposed scheme can be utilized as an efficient tool for integrity evaluation of cracked steam generator tubes.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.11
• /
• pp.2860-2870
• /
• 1994

When crack are detected in aged turbine rotors of power plants, information on fracture resistance of the aged material at operating temperature is needed for determination of critical loading condition and residual life of the turbine. In this study, fracture toughness (J$_lc$) and tearing modulus(T$_mat$) of virgin and thermally degraded 1Cr-1Mo-0.25V steel, which is one of the most widely used rotor steels, were measured at 538.deg. C according to ASTM E813 and ASTM E1152, respectively. Five kinds of specimen with different degradation levels were prepared by isothermal aging heat treatment at $630^{\circ}C.$ It was observed that J$_lc$ and T$_mat$ value decreased as the degradation level increased. Analysis of microstructures using a scanning electron microscope showed that the decrement of J$_lc$ is related to segregation of impurities at grain boundaries. It was also verified that the DC electric potential drop method is accurate and reliable for crack length monitoring at elevated temperature.