Environmental Fatigue Crack Propagation Behavior of Aged Cast Stainless Steel

열화 주조 스테인리스강의 환경피로균열 진전 거동

Environmental fatigue crack propagation of CF8M and CF8A steels used in the domestic PWR were investigated on the simulated PWR condition(Temperature: $316^{\circ}C$, Pressure: 15MPa). The test equipment for environmental fatigue(high temperature-high pressure loop, autoclave, load frame, measurement system) were designed. As-received and 60-year aged specimens were used in the test. To compare with environmental fatigue test, another test was performed in the air condition. The fracture surface of specimens were difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, more particles covered fracture surface were peeled.