• Journal of Digital Convergence
• /
• v.19 no.3
• /
• pp.245-251
• /
• 2021

This study was to investigate the effect of the new surface treatment method of zirconia on the shear bond strength with resin cement. The zirconia specimens were classified according to the surface treatment. CON: non-treatment, HF: 10 minutes exposure to 9% HF, ZS15: Apply 15% ZrO2 slurry, ZS30: Apply 30% ZrO2 slurry, ZS50: Apply 50% ZrO2 slurry. The resin cement was layered on the surface treated zirconia, and the shear bond strength between the zirconia and the resin cement was measured after thermo-cycling. The statistical methods for shear bond strength were Kruskal-Wallis test, Mann-Whitney U test, and Bonferroni correction(α=.05/10=.005). ZS15, ZS30, and ZS50 groups treated with zirconia slurry showed higher shear bond strength than CON and HF groups(p<.05/10=.005). Within the limits of this study, the surface treatment using zirconia slurry increased the shear bond strength with resin cement. The new surface treatment method complements and improves the limitations of the adhesion of zirconia, so that various clinical applications of zirconia can be expected.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1996.10a
• /
• pp.59-59
• /
• 1996

막분리에 의한 폐윤활유 재생공정을 개발하기 위한 기초 연구로써 폐윤활유 분리/재생용으로 적합한 복층(multilayer)세라믹 복합막의 제조와 합성막의 폐유 분리 효율등이 연구되었다. 결함이 없고 두께가 균일한 지르코니아 복합막 (기공크기 0.07 $\mu$m 이하)은 압출 성형법으로 제조한 튜브형 $\alpha$-알루미나 담체 (외경 7.8 mm, 두께 0.6 mm, 기공크기 0.7 $\mu$m)내부표면에 역침지 인상법(reverse dip-drawing technique)에 의하여 지르코니아 슬러리를 코팅 한 후 950$\circ$C에서 1시간 열처리하여 제조 되었다. 또한 지르코니아 복합막 위에 니타니아 졸-겔 코팅을 한 후 450$\circ$C에서 2시간 열처리하여 기공크기가 15 nm정도인 3층 복합막을 제조 하였다. SEM, Bubble Point Test, Mercury Porosimeter 그리고 분획 분자량 측정등에 의하여 복합막의 코팅층 두께, 결함유무 및 막의 기공크기등을 분석하였다.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.446-451
• /
• 2002

Zirconia/alumina mixture powder was spray-dried various degree of dispersion, type of dispersants and powder content in the slurry. The quality of the granule was determined by observation of the granule shapes after spray drying and fracture of intergranular boundaries during pressing. Defect-free granules were obtained from the powders that formed weak flocs in the slurry. The granules, spray-dried from the slurry containing 32.5 vol% powder mixture and PVP as binder, were fractured completely during shaping and the sintered specimens showed a density of 99.7% and a flexural strength of 850 MPa.

• Korean Journal of Materials Research
• /
• v.6 no.2
• /
• pp.166-174
• /
• 1996

경제적이고 단순성의 공정특성을 갖는 닥터 블레이드법을 이용하여 평판형 고체산화물 연료전지의 고체전해질용 이트리아 안정화 지르코니아 박막을 제조하였다. 슬러리의 최적 제조조건과 그린 필름의 최적 소성조건을 얻었으며, 이 제조 조건에서 제조된 전해질의 결정구조, 미세구조 그리고 전기적 성질을 각각 X-선 회절, 주사전자현미경 그리고 교류 임피던스 분석기를 이용하여 조사하였다. 동량의 8mol% 이트리아를 첨가한 경우, 닥터 블레이드법에 의해 제조된 이트리아 안정화 지르크니아 박막은 금형가압성형법에 의해 제조된 이트리아 안정화 지르코니아 펠렛과 거의 비슷한 전기전도도를 나타내었다. 닥터 블레이드법에 의해 제조된 이트리아 안정화 지르크니아 박막의 경우, 8mol%이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우 보다 993K 이상과 523K 8mol% 이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우 보다 993K이상과 523K이하의 온도에서는 더 높고, 523-933K사이의 온도구간에서는 낮게 나타났다. 게다가, 모든 시편에 있어서 전체 전도도에 대한 벌크 전도도의 기여도에 대한 기여도보다 더 크게 나타났다.

• Membrane Journal
• /
• v.3 no.1
• /
• pp.12-21
• /
• 1993

세라믹 분리막은 알루미나($Al_2O_3$), 지르코니아($ZrO_2$), Carbon, 실리콘 카바이드, 스테인레스 등의 무기재료를 이용하여 제조된 분리막이다. 압출성형공정으로 제조된 지지체는 1700$^{\circ}C$ 이상의 소결공정을 거치므로 지지체 상단에 슬러리 코팅공정으로 형성된 얇은 막에게 안정된 분리기능을 수행할 수 있도록 커다란 물리적 강도를 제공한다. 따라서, 세라믹 분리막은 다공성 세라믹 구조를 갖는 특징적인 두 개 또는 세 개의 균일한 층으로 구성된 복합막이라 할 수 있다.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.791-798
• /
• 1999

The preparation method of yttria-stabilized zirconia(YSZ) thin film for an anode support type solid oxide fuel cell(SOFC) by electrophoretic deposition(EPD) and dip-coating was studied. And the difference in both preparation method was investigated through basic understanding of processing parameters which may significantly affect weight microstruxcture and defect of film. In dip-coating the thickness of film increased with time until 30 s and then the weight of film decreased with time due to particle falling off from the coagulated film. In EPD although the weight of film increased with time and applied constant-current sagging of the film was observed when the applied current was less that 0.035 mA/$cm^2$ and more than 120 s. Since YSZ thin film by EPD on porous substrate was dense smooth and homogeneous it was expected to be suitable for the electrolyte of an anode support type SOFC.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.2
• /
• pp.204-211
• /
• 2006

The electrolyte in the solid oxide fuel cell must be dense enough to avoid gas leakage and thin enough to reduce the ohmic resistance. In order to manufacture the thin and dense electrolyte layer, 8 mol% $Y_2O_3$ stabilized-$ZrO_2$ (8YSZ) electrolyte layers were coated on the porous tubular substrate by the novel vacuum slurry dip-coating process. The effects of the slurry concentration, presintering temperature, and vacuum pressure on the thickness and the gas permeability of the coated electrolyte layers have been examined in the vacuum slurry coating process. The vacuum-coated electrolyte layers showed very low gas permeabilities and had thin thicknesses. The single cell with the vacuum-coated electrolyte layer indicated a good performance of $495\;mW/cm^2$, 0.7 V at $700^{\circ}C$. The experimental results show that the vacuum dip-coating process is an effective method to fabricate dense thin film on the porous tubular substrate.

• Korean Journal of Materials Research
• /
• v.11 no.6
• /
• pp.519-526
• /
• 2001

The effects of methyl isobutyl ketone(MIBK)/ethanol(EtOH) solvent mixtures on the dispension, particle size distribution and rheology of $Al_2$O$_3$/ZrO$_2$ nonaqueous suspensions were investigated by measuring sedimentation density and viscosity. The sedimentation density of $Al_2$O$_3$ and ZrO$_2$ particles increased in MIBK-rich($\geq$60 vol%) solvents with 'Hypermer' KD-1 as a dispersant. The ball-milled suspensions in 80MIBK/20EtOH(vol%) solvent exhibited the narrow and unimodal particle size distribution. Although all Suspensions exhibited the Pseduo-Plastic flow(Shear thinning) the shear thinning behavior was somewhat different depending on the mixture ratio of $Al_2$O$_3$/ZrO$_2$ and MIBK/EtOH. Under a given shear rate( <300 s$^{-1}$ for $Al_2$O$_3$; <3000 s$^{-1}$ for ZrO$_2$) the strongest shear thinning appeared in the $Al_2$O$_3$ and ZrO$_2$ suspensions with pure MIBK solvent. The shear thinning was nearly independable on the mixture ratio of $Al_2$O$_3$/ZrO$_2$ in case of using the identical solvent(80MIBK/20EtOH, vol%).