• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.1A
• /
• pp.219-228
• /
• 2006

Because of the advantage of light weight, lightweight concrete is frequently applied to long-span bridges and high-rise buildings. In the country, there is not enough experience for the long-span bridges using lightweight concrete. This paper presents results of an experimental study on the punching shear strength of high-strength lightweight concrete slabs. Four test slabs are fabricated using high-strength lightweight concrete and normalweight concrete and at the center of the test slabs, simulated wheel load is applied until failure. The compressive strengths of lightweight concrete and normalweight concrete are 47MPa and 32MPa, respectively. The test results show the failure mode of all specimens are punching shear and the behaviors of high-strength lightweight concrete slabs are very similar to that of normalweight concrete slabs. Based on the test results, it is discussed the safety and serviceability of high-strength lightweight concrete bridge decks.

• 한국방재학회:학술대회논문집
• /
• 2011.02a
• /
• pp.160-160
• /
• 2011

현대의 건설기술은 자원절약과 환경보전이라는 시대적 흐름 속에, 자원순환과 지속 가능한 친환경 건설기술 개발은 차세대 연구분야로써, 연구가 시급한 분야가 되었다. 최근에는 골재 수급불균형 문제를 해결하고 동시에 자원순환을 위한 방안으로서 건설폐기물로부터 생산된 순환골재를 콘크리트용 천연골재의 대체재로 활용하기 위한 연구개발이 이루어지고 있다. 지속가능형 건설기술을 국내 독자 기술로 확립하고 건설현장에서 발생하는 폐기물의 순환시스템을 확고하게 구축하여 순환자원에 의한 국가경쟁력 강화를 기대할 수 있다. 본 연구의 목적은 순환골재 콘크리트의 역학적 특성을 개선하기 위해 순환골재 콘크리트 공시체를 제작하여 강도 및 강성을 검증하는 것이다. 실험방법으로 순환굵은골재의 치환 비율을 0%에서 100%까지 변화시킨 공시체를 제작하고 각 공시체의 정적 극한강도 거동을 비교 분석하였다. 하중은 공시체가 파괴가 발생 할 때까지 변위제어 방식으로 재하 하였으며 이 때 공시체의 파괴거동은 설치된 계측센서들을 이용하여 계측 및 분석하였다. 실험결과 공시체의 압축강도는 순환굵은골재 치환률이 25% 미만일 경우 일반 콘크리트 압축강도의 95% 이상의 구조성능을 갖지만, 순환굵은골재 치환률이 100%인 경우, 일반콘크리트 압축강도의 85% 수준의 구조성능을 나타냈다. 강성은 FRP 부재의 순환골재 치환률에 따라 최대 14%의 강성차이를 보였다. 이를 통해 순환골재 치환률이 높을수록 순환골재 표면의 폐모르타르와 이물질의 영향으로 재료간의 부착강도가 감소되어 강도와 강성이 저하되었음을 확인하였다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.49-52
• /
• 2008

The tensile and bond performance of GFRP rebar are different from those of conventional steel reinforcement. It requires some studies on concrete members reinforced with GFRP reinforcing bars to apply it to concrete structures. GFRP has some advantages such as high specific strength, low weight, non-corrosive nature, and disadvantage of larger deflection due to the lower modulus of elasticity than that of steel. Bridge deck is a preferred structure to apply FRP rebars due to the increase of flexural capacity by arching action. This paper focuses on the behavior of concrete bridge deck reinforced with newly developed GFRP rebar. A total of three real size bridge deck specimens were made and tested. Main variable was reinforcement ratio of GFRP rebar. Static test was performed with the load of DB-24 level until failure. Test results were compared and analyzed with ultimate load, deflection behavior.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2011.04a
• /
• pp.340-343
• /
• 2011

장대 케이블 교량의 풍응답을 계측할 수 있는 무선센서네트워크 기반의 풍응답 계측시스템을 개발하고, 이를 사용하여 인천대교의 시공단계별로 고유진동수, Mode Shape과 같은 Modal Parameters의 변화를 추정하고 보강형에서의 풍압분포와 보강형, 주탑, 케이블의 가속도를 계측하여 내풍 성능을 분석하였다. 개발된 계측 시스템은 인천대교 사장교의 전체 거동을 계측할 수 있도록, 1.5km 범위에 넓게 분포된 최대 55 Nodes에서 최대 1kHz의 동기화된 계측을 수행할 수 있으며, 각 Node별로 3축가속도나 풍압을 측정할 수 있다. 전체 Node에서 가속도를 계측하는 경우에는 최대 165 Channel을 1kHz로 측정할 수 있다. Modal 해석의 경우에, 고가교, 접속교, 사장교 주탑, 보강형, 케이블의 시공 단계별 동특성의 변화를 추정하였으며, 고가교에서는 모드해석을 통해 역추정한 구조계수를 정적재하실험 및 실험실에서의 Mold 시험결과와 비교하였으며 사장교 케이블에서는 케이블 댐퍼의 성능을 분석하였다. 또한 인천대교 보강형에서의 풍압분포를 계측하였으며, 풍압의 공간상관관계를 분석하였고, 풍하중 및 풍진동 특성을 분석하여 가속도 계측 결과와 비교하였다. 계측 및 분석 결과를 바탕으로 장대교량의 내풍성능을 확보하고 향상시키는데 활용할 수 있을 것으로 기대한다.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.1A
• /
• pp.55-64
• /
• 2012

Experimental investigation on the structural behavior of steel fiber-reinforced ultra high performance concrete (UHPC) beams subjected to shear are presented. Six tests carried out on simply supported I-beams under concentrated loads are presented. The parameters varied were the volume fraction of the fibers (1.0, 1.5 and 2.0%) and shear span-effective depth ratio (2.5, 3.4). The test results indicated that ultimate shear strength increased with increasing fiber volume, and that ultimate shear strength decreased with increasing shear span-effective depth ratio. In addition, applicability of predictive equations for evaluating the ultimate shear strength of steel fiber-reinforced UHPC beams are estimated based on the test results. The comparison between computed values and the experimentally observed values are shown to validate the proposed theoretical equations. It is found that predictions by using AFGC and JSCE recommendations provide the most accurate estimates of shear strength of steel fiber-reinforced UHPC beams.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.3
• /
• pp.91-99
• /
• 2010

In order to strengthen RC structures, various strengthening methods have been used. Particularly, external tendon strengthening method is very popular method to strengthen damaged structures in terms of efficiency, ease, economics. In this study, improved anchorage elements using the lifting hole were proposed to strengthen PSC or RC girder without any damage. Two types of anchorage elements were proposed and these elements were applied on six RC beams. Also, three types of existing anchorage elements were applied on three RC beams. Otherwise, any anchorage element was not applied on one RC beam to used as a control beam. To analyse behavior of these elements, static load tests were carried out. Test variables were anchorage shapes, prestressing level on the steel bar and tendon profiles. Deflections, strains and modes of failure were recorded to examine the strengthening effects of the beams. Ductility index and tendon stress were analyzed by comparing cracking load, yielding load and ultimate load. As a result, proposed anchorage elements using lifting hole were superior to existing anchorage elements in terms of strengthening effect and furthermore, they showed ductile behavior based on energy method.

• Tunnel and Underground Space
• /
• v.22 no.2
• /
• pp.77-85
• /
• 2012

In a material, micro-cracks can be progressively occurred, propagated and finally lead to failure when it is subjected to cyclic or periodic loading less than its ultimate strength. This phenomenon, fatigue, is usually considered in a metal, alloy and structures under repeated loading conditions. In underground structures, a static creep behavior rather than a dynamic fatigue behavior is mostly considered. However, when compressed air is stored in a rock cavern, an inner pressure is periodically changed due to repeated in- and-out process of compressed air. Therefore mechanical properties of surrounding rock mass and an inner lining system under cyclic loading/unloading conditions should be investigated. In this study, considering an underground lined rock cavern for compressed air energy storage (CAES), the mechanical properties of a lining system, that is, concrete lining and plug under periodic loading/unloading conditions were characterized through cyclic bending tests and shear tests. From these tests, the stability of the plug was evaluated and the S-N line of the concrete lining was obtained.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.309-312
• /
• 2008

This paper describes ultimate load tests which were performed to show the effects of prestress loss and tendon corrosion on the flexural strength of post-tensioned concrete beams and the occurrence of wire fracture. Five test specimens were fabricated in laboratory with the variations of the prestress of tendons and the loss of tendon area. For two specimens, small area of tendon at the center of the beam was exposed by using diameter 25mm drill and the exposed tendon was corroded using accelerated corrosion equipment. During the tests, deflections, crack width, and strain changes were measured and acoustic events were monitored with two acoustic sensors. Tests results show that the ultimate flexural strength of test specimens with corroded tendons is smaller than the predicted flexural strength which is calculated considering the loss of tendon area. It is considered that estimation of flexural strength of PSC beams with corroded tendons is very complicated just based on the loss of tendon area obtained by one-side visual inspection.

• Journal of Korean Society of Steel Construction
• /
• v.27 no.3
• /
• pp.347-357
• /
• 2015

In this study, an experimental study was performed to evaluate the concrete breakout strength of unreinforced cast-in-place anchors by seismic qualification test under shear loading. The CIP anchors tested herein were 30mm in diameter with an edge distance of 150mm and an embedment depth of 240mm in uncracked and cracked concrete. The cracked specimen consisted of orthogonal and parallel crack to the loading direction, respectively. The dynamic loading sequence during the seismic qualification test was determined based on CSA N287.2, ACI 355.2 and ETAG 001 codes. After the dynamic loading, the static loading was applied until failure occurs. The shear resistance by seismic qualification tests showed almost the same strength as that obtained from the static tests in uncrcaked and cracked concrete, respectively. Meanwhile, the breakout depth did not reach $8d_0$, therefore the modified strength equation of ACI 318-11 could estimate properly the concrete breakout strength, which does not consider effective bearing length.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.10 no.1 s.47
• /
• pp.41-49
• /
• 2006

Through the 1982 Urahawa-ohi and the 1995 Kobe earthquakes, a number of bridge columns were observed to develop a flexural-shear failure due to the bond slip as a consequence of premature termination of the column longitudinal reinforcement. Because the seismic behavior of RC bridge piers is largely dependent on the performance of the plastic hinge legion of RC bridge piers, it is desirable that the seismic capacity of RC bridge pier is to evaluate as a curvature ductility. The provision for the lap splice of longitudinal steel was not specified in KHBDS(Korea Highway Bridge Design Specification) before the implementation of 1992 seismic design code, but the lap splice of not more than 50%, longitudinal reinforcement was newly allowed in the 2005 version of the KHBDS. The objective of this research is to investigate the distribution and ductility of the curvature of RC bridge column with the lap splice of longitudinal reinforcement in the plastic hinge legion. Six (6) specimens were made in 600 mm diameter with an aspect ratio of 2.5 or 3.5. These piers were cyclically subjected to the quasi-static loads with the uniform axial load of $P=0.1f_{ck}A_g$. According to the slip failure of longitudinal steels of the lap spliced specimen by cyclic loads, the curvatures of the lower and upper parts of the lap spliced region were bigger and smaller than the corresponding paris of the specimen without a lap splice, respectively. Therefore, the damage of the lap spliced test column was concentrated almost on the lower part of the lap spliced region, that appeared io be failed in flexure.