• Journal of Sericultural and Entomological Science
• /
• v.28 no.1
• /
• pp.66-71
• /
• 1986

The studies were carried out to screen the optimum conditions for enzymatic degumming of raw silk yarn and silk fabric by use of Alkalase, a protease produced by Bacteria, comparing with Papain and Trypsin representing natural proteolytic enzymes. 1. The optimum temperature and acidity of degumming solution were 70$^{\circ}C$, pH 5-6 for Papain degumming, 40$^{\circ}C$, pH 8 for Trypsin and 50-60$^{\circ}C$ pH 8-9 for Alkalase. 2. By increasing the Alkalase concentration in the range of 0.6 to 1.0 gram per liter, the time for enzymatic degumming of silk yarn could be reduced by 40 minutes. 3. In degumming of silk yarn by Alkalase, the pretreatment of 95$^{\circ}C$, 10 minutes at 0.1% sodium bicarbonate solution or posttreatent of 80$^{\circ}C$, 20 minutes at 2% (o.w.f.) sodium silicate solution improved the efficiency of enzymatic degumming, as compared to that of nontreatment. 4. The breaking strength, elongation and Lousiness results of enzymatically degummed silk yarn were apt to be improved more than those of soap-degummed one. 5. When the pretreatment of alkaline solution was done with over 20% of degumming ratio, the enzymatic degumming efficiency of both Havutae and Crepe de chine could be reached to the same level with those of soap-soda degummed. 6. As the pretreated silk fabric with 20% of degumming ratio was under action of three proteases, respectively, the deumming efficiency of Havutae and Crepe de chine were completed by Alkalase more than by Papain or Trpysin. 7. The stiffness of enzymatically degummed Crepe de chine was not only reduced by 17% more than that of soap-soda degummed one but also the Drape coefficient was decreased in enzymatically degummed fabrics, which was closely related with the soft touch of degummed fabrics.

• Journal of Sericultural and Entomological Science
• /
• v.36 no.1
• /
• pp.44-52
• /
• 1994

Degumming with enzyme Degummase can be a viable alternative to the existing methods of degumming. Degumming, carried out with the conventional method of Marseille's soap 25%(owf) for 1.5h at boil gives a weight loss of about 24%. On Comparison, degumming with 10 enzyme at 5$0^{\circ}C$ for 60 min gives a weight loss of about 22%. Treatment with enzyme requires a much lower temperature and also the treatment time is shorter than the conventional process. Processing of silk at these conditions is likely to retain the lustre and softness of silk. To economise on the quantity of enzyme, conditions were optimised for a pad-store process. An enzyme concentration of 0.5% at 5$0^{\circ}C$ for a time period of 5~6h resulted in a weight loss of 22%. Though the concentration of the enzyme used was 20 times less than that used for long liquor method there was some strength loss. At 5$0^{\circ}C$ treatments carried out for 7~8 h resulted in some degradation. Strength loss occurs because enzyme in the absence of any stirring keeps acting at the place where it is deposited. Effect of temperature was more pronounced than time in degrading silk.

• Journal of Sericultural and Entomological Science
• /
• v.47 no.1
• /
• pp.36-40
• /
• 2005

This studies were carried out to develop the new silk degumming method by elelectrolyzed alkaline water on the silk degumming process. Using to this method, it could be collect pure sericin from the degumming water, because the degumming water by elelectrolyzed alkaline water was not contaminated by chemicals including soap. The range of elelectrolyzed alkaline water was pH 11.5 to 11.7 and maintained the first value for 8 days under the cool and closed conditions. The degumming ratio of silk was higher in elelectrolyzed alkaline water(pH 11.5~11.7)than that of soap and alkaline bath. When the pH value of elelectrolyzed alkaline water was adjusted at pH 11.0, the degumming ratio of silk was similar to that of soap and alkaline degumming. After degumming the pH value of degumming water decreased largely in the elelectrolyzed alkaline water compared to that of soap and alkaline bath. The tenacity and elongation of degummed silk by elelectrolyzed alkaline water was almost same those of soap and alkaline degumming for 90 min.

• Journal of Sericultural and Entomological Science
• /
• v.35 no.1
• /
• pp.43-47
• /
• 1993

Using the new scouring soap made from rapeseed oil, various scouring test was done souring effects of new scouring soap were estimated. In the effects of scouring soap on the degumming ratio, OS (the soap made from oleic acid) was the most excellent and the next was RS (the soap made from rapeseed oil). Both OS and RS were more excellent than MS (the soap on the market). In a buffer power of soap solution, OS and RS were good, but MS was poor. The uneven dyeing was not observed in the silk fabric degummed by OS and RS, but observed in silk fabric degummed by MS. The value of tenacity and elongation in the silk degummed by OS and RS was higher that degummed by MS. In the crease recovery, softness and whiteness, the order of value was OS, RS, MS.

• Journal of Sericultural and Entomological Science
• /
• v.29 no.2
• /
• pp.58-66
• /
• 1987

This study was investigated on the effect of degumming of cocoon shell, raw silk yarn and grey silk crepe by use of Papain, comparing with soap, soda and soap-soda. The obtained results may be summarized as follows : 1. Degumming loss, when the pretreatment was done, was completed by Papain more than by alkali. 2. Lousiness result of Papain degummed silk yarn was apt to be improved more than that of alkali degummed one. 3. As a result of tensile property test, elasticity and resilience of Papain degummed crepe were good compared to those of alkali degummed one. 4. Not only bending rigidity of Papain degummed crepe was reduced more than that of alkali degummed one but also hysteresis of bending moment was decreased in papain degummed crepe. 5. Handle of Papain degummed crepe was superior to that of alkali degummed one.

• Journal of Sericultural and Entomological Science
• /
• v.35 no.2
• /
• pp.114-119
• /
• 1993

The weight loss for the mixture(raw-silk/PET) was tested to investigate the effects of weight loss accelerator on the degumming and weight loss. The degumming loss of raw-silk was decreased while the weight loss polyester(PET) was increased depending on the increase of accelerator concentration. The difference of the weight loss was not significant in raw-silk but the weight loss of PET was increased with the increase of the alkali concentration. The proper degumming of raw-silk was obtained and simultaneously the weight loss of PET was high for the raw-silk/PET "A" and "B" type. The proper degumming of raw-silk was obtained but the weight loss of PET was low for the raw-silk/PET "D" and "E" type. It showed that the typical degumming curve in raw-silk part and the weight loss of PET was increased depending on the treatment time in the weight loss for the fabric composed of raw-silk and PET.

• Journal of Sericultural and Entomological Science
• /
• v.29 no.2
• /
• pp.67-72
• /
• 1987

This study was carried out for the optimum predegumming in the protease degumming process of silk fabrics by ocmparing the physical properties of silk fabrics degummed with different weight losses of predegumming. 1. In twill habutai, the stiffness of fabric was reduced and the smoothness was improved with increasing weight loss of predegmming, however, the soft feeling value which means the total handle value of medium fabric for lady, was maximum at 20% of predegumming weight loss. 2. In the case of crepe de chine representing thin fabric for lady, the anti-drape stiffness was relatively increased with 22% weight loss of predegumming. However, the other physical properties, such as the flexibility with soft feeling were less related to the degrees of predegumming.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.13 no.1
• /
• pp.11-19
• /
• 2015

The production of nuclear fuel cladding tube is expected to increase with the nuclear power plant expansion. Zirconium(Zr) scrap that is generated during manufacturing is also expected to increase. Zr electrorefining experiment was carried out in the fluoride salt of LiF-KF-ZrF₄ using multiple electrode for scale up and improving throughput Zr electrorefiner develop-ment. The Zr reduction peak observed at-0.8 V(vs.Ni). Polarization behavior showed that the amount of applied current increases because of decreasing cell resistance as the number of cathode increases. Experimental results showed the highest recovery rate about 98% at lowest current density of 25.64 mA/cm² using 6 electrodes. XRD and TG analysis result show that pure Zr was recovered 99.92% and ICP analysis shows that lower impurity content than conventional impurity content of the Anode(97.8%). Electrorefining consumes energy about 7.15 kWh/kg less than 39.7% compared to the Kroll process using 6 electrode width of 20 mm and height of 65 mm. Because of increasing cell efficiency and recovery rate, using multiple cathode is determined as an efficient technique for scale up electrorefining Zr scrap.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.13 no.4
• /
• pp.315-319
• /
• 2015

A high-throughput electrorefiner has been developed for commercialization use by enhancing the uranium recovery from the reduced metal which is produced from the oxide reduction process. It is necessary to scrap and effectively collect uranium dendrites from the surface of the solid cathode for high yield. When a steel electrode is used as the cathode in the electrorefining process, uranium is deposited and regularly stuck to the steel cathode during electrorefining. The sticking coefficient of a steel cathode is very high. In order to decrease the sticking coefficient of the steel cathode effectively, vibration mode was applied to the electrode in this study. Uranium dendrites were scraped and fell apart from the steel cathode by a vibration force. The vibrational scraping of the steel cathode was compared to the self-scraping of the graphite cathode. Effects of the applied current density and the vibration stroke on the scraping of the uranium dendrites were also investigated.

• Resources Recycling
• /
• v.20 no.1
• /
• pp.61-68
• /
• 2011

Impurity removal from metallurgical grade silicon by acid washing at $50^{\circ}C$ was investigated by employing sulfuric, nitric acid and the mixture of hydrochloric and hydrofluoric acid. Acid washing treatment had no effect on the removal of boron and the concentration of this clement after treatment was rather increased. In our experimental range, the removal percentage of phosphorus was 60%. In the acid washing with sulfuric and nitric acid, the removal percentage of major impurities was below 50%, which indicates that refining effect was not great with these acids. Acid washing with the mixture of hydrochloric and hydrofluoric acid led to removal percentage of higher than 90%. Data on the purity of silicon after acid washing at various conditions are reported.