• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.22-27
• /
• 2014

In the past, cold crack was commonly observed in the HAZ(heat affected zone) of high-strength steels. Applying to TMCP(thermo-mechanical controlled process) and HSLA(high strength low alloy) steels, cold crack tends to increase the occurrence in the weld metal. It is generally understood that cold crack occurs when the following factors are present simultaneously : diffusible hydrogen in the weld metal, a susceptible microstructure and residual stress. In particular, many studies investigated the microstructural effect on the cold crack in HAZ and the cold crack in weld metals starts to receive the special attendance in modern times. The purpose of the study is to review the effect of weld microstructures (grain boundary ferrite, Widm$\ddot{a}$nstatten ferrite, acicular ferrite, bainite and martensite) on cold crack in the weld metals. Among various microstructures of weld metals, acicular ferrite produced the greatest resistance to the cold crack due to the fine interlocking nature and high-angle grain boundary of the microstructure.

• Journal of Welding and Joining
• /
• v.34 no.2
• /
• pp.67-72
• /
• 2016

Aluminum alloy is one of light weight material and it is used to make LNG tank and ship. However, in order to weld aluminum alloy high density heat source is needed. In this paper, I-butt welding of Al 5083 with 6mm thickness using Plasma-MIG welding was carried out. The experiment was performed to investigate the influence of plasma-MIG welding parameters such as plasma current, wire feeding rate, MIG-welding voltage and welding speed on the tensile strength of weld. In addition we suggested 3 strength estimation models which are second order polynomial regression model, multiple nonlinear regression model and neural network model. The estimation performance of 3 models was evaluated in terms of average error rate (AER) and their values were 0.125, 0.238, and 0.021 respectively. Neural network model which has training concept and reflects non -linearity was best estimation performance.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.61-65
• /
• 2014

The purpose of this study is to evaluate the applicability of the element stress to establish S-N design curve for the welded lap joint with thin plates below 2mm thickness. In order to do it, the extensive fatigue tests of the welded lap joints with INVAR alloy were performed. With the results, the deign S-N curves for the lap-weld were established by using the reference stresses such as the nominal stress range at the weld throat area, hot spot stress range and element stress range, and compared with regard to the standard deviation. The standard deviation of S-N curves with element stress range was less than that of S-N curves with other reference stresses. In addition, FEA results show the amount of the element stress is less sensitive to mesh size. Based on the results, it can be concluded that the element stress is to be used as the reference stress for the design S-N curves of the welded lap joint.

• Journal of Welding and Joining
• /
• v.31 no.4
• /
• pp.73-79
• /
• 2013

Burr grinding, Tungsten Inert Gas (TIG) dressing, ultrasonic impact treatment, and peening are used to improve fatigue life in steel structures. These methods improve the fatigue life of weld joints by hardening the weld toe, by improving the bead shape, and by creating the compressive residual stress. In this study, a new post-weld treatment method improving the weld bead shape and metal structure at the welding zone using Friction Stir Processing (FSP), a welding process, is proposed to enhance fatigue life. For that, a pin-shaped tool and processing condition employing Friction Stir Processing (FSP) is established through experiments. Experimental results revealed that fatigue life is improved by around 50% compared to as-welded fatigue specimens by reducing the stress concentration at the weld toe and by generating a metal structure finer than that of flux-cored arc welding (FCAW).

• Journal of the Korean Society of Safety
• /
• v.29 no.3
• /
• pp.1-7
• /
• 2014

In this study, for the evaluation of the static and fatigue joining strength of the joint, the geometry of the cross-tension specimen was adopted. The specimens were produced with optimal joining force and fatigue life of the clinch joint specimens was evaluated. The material selected for use in this study was cold rolled mild steel (SPCC) with a thickness of 0.8 mm. The maximum tensile load was 708 N for the specimen with single point. The fatigue endurance limit (=42.6 N) per point approached to 6% of the maximum tensile strength at a load ratio of 0.1, suggesting that the joints are vulnerable to cross-tension loading during fatigue. Compared to equivalent stress and maximum principal stress, the SWT fatigue parameter and equivalent strain can properly predict the current experimental fatigue life. The SWT parameter can be expressed as $SWT=2497.5N^{-0.552)_f$.

• Journal of the Korean Society of Safety
• /
• v.31 no.3
• /
• pp.1-7
• /
• 2016

In this study, static and fatigue tests on the self-piercing riveted (SPR) joint were conducted using cross-shaped specimens with aluminum alloy (Al-5052) sheets. Mixed mode loading was achieved by changing the loading angles of 0, 45, and 90 degrees using a special fixture to evaluate the static and fatigue strengths of the SPR joints under mixed mode loading conditions. Simulations of the specimens at three loading angles were carried out using the finite element code ABAQUS. The fatigue specimens failed in an interfacial mode where a crack initiated at the upper sheet and propagated along the longitudinal direction and finally fractured Maximum principal stress, von-Mises effective stress failed to correlate the fatigue lifetimes at three loading angles. However, the equivalent stress intensity factor was found to be appropriate to correlate the fatigue lifetimes at three loading angles.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.11a
• /
• pp.16-16
• /
• 2011

기존의 얇고 가벼운 기능성 투습방수 film은 각종 등산복이나 육해공군전투복, 경찰복, 소방복 등에 폭넓게 이용되고 있다. 그러나 현재의 이런 제품들은 뛰어난 투습방수성을 나타내지만 눈, 비, 이슬 등과 같은 수분과 만날 경우 필름 고분자 구조의 Swelling으로 표면의 불규칙한 요철현상이 생기며, 이는 제품의 불량으로 문제시 되고 있다. Swelling이 생기지 않는 친수성 Urethane film이 스키복으로 많이 상용되고 있기는 하지만 두께가 두껍고 무거워서 움직임이 불편한 단점이 있다. 본 연구에서는 이러한 문제점들을 보완하여 얇고 가벼운 기능성 비팽윤 투습 방수 필름을 제조하였다. 제조된 비팽윤 투습 방수 필름제품은 기존의 투습 방수 필름과도 다른 독특한 Bead concrete 구조를 형성하고 있으며, 미세입자들이 서로 접합하여 우수한 투습성을 발현하며, 기저층의 모노리스 멤브레인(Monolithic film)의 적층구조로서 형성되어 있어 강도 및 투습도 등의 성능이 제어되고, 수분 흡수에 따른 팽윤현상이 발생하지 않는다.

• Journal of the Korean Society of Safety
• /
• v.26 no.4
• /
• pp.1-6
• /
• 2011

New methods for joining sheet of metal are being sought. One of the most promising methods is MPJ (mechanical press joining). It has been used in thin metal work because of its simple process and relative advantages over other methods, as it requires no fasteners such as bolts or rivets, consumes less energy than welding, and produces less ecological problems than adhesive methods. In this study, the joining process and static behavior of single overlap joints has been investigated. During fixed die type joining process for SPCC plates, the optimal applied punching force was found. The maximum tensile-shear strength of the specimen produced at the optimal punching force was 1.75 kN. The FEM analysis result on the tensile-shear specimen showed the maximum von-Mises stress of 373 MPa under the applied load of 1.7 kN, which is very close to the maximum tensile strength of the SPCC sheet(= 382 MPa). This suggests that the FEM analysis is capable of predicting the maximum tensile load of the joint.

• Proceedings of the Korean Society for Quality Management Conference
• /
• 2006.04a
• /
• pp.375-380
• /
• 2006

Recently European Council(EU) published the RoHS(restriction of the use of certain hazardous substances in electrical and electronic equipment) which is prohibit the use of Pb, Hg, Cd, $Cr^{+6}$, PBB or PBDE in the electrical and electronic equipments. So EU member States shall ensure that, from 1 July 2006, new electrical and electronic equipment put on the market does not contain 6 hazardous substances. So many kinds of projects is proceeding to ensure the reliability of Pb-free electronics in the worlds. Especially it is necessary to evaluate of Pb-free solder joints in electronics. Therefore, on this paper, we compared with solder joint strength of chip components, respectively SnPb, Pb-free solder as follows reliability test methods. We also measured the shear strength of solder joint and also compared the effects of environmental test methods. In this results, we analyzed and compared the shear strength variation as follows solder materials and reliability test conditions.

• Journal of Welding and Joining
• /
• v.7 no.3
• /
• pp.28-35
• /
• 1989

It was reported that the toughness for welded region was influenced by various factors such as the gradient for prior austenite grain size, the variation of microhardness and the characteristic microstructure depending on distance from the fusion boundary. Therefore, in order to evaluate the fracture strength of the weldment in which the microstructures change continuously, it is important to assess the peculiar strength of each microstructure in welded region. It was known that the small punch(SP) test technique which was originally developed to study the irradiation damage effect for the structures of nuclear power plant was also useful to investigate the strength evaluating of nonhomogeneous materials. In this paper, by means of a small punch test technique the possibility of evaluating strength of parent and welded region in SS41 and SM53B steels was investigated. The obtained results are summerized as follows: 1) The small punch test which showed markedly the ductile-brittle transition behavior in this experiment may be applied to evaluation for the fracture strength of welded region. 2) It was shown that the ductile-brittle regime lied in Region III(plastic membrane stretching region) of the flow characteristics observed in SP test. 3) The SP test technique which shows a more precipitous energy change transition behavior than the other test technique is able to estimate the more precise transition temperature. 4) It could be seen that in comparision with the structure of parent the structure of weld HAZ in SS41 steel was improved while it in SM53B steel was deteriorated.