• E2M - 전기 전자와 첨단 소재
• /
• 제5권1호
• /
• pp.111-121
• /
• 1992

본 연구는 Pb( $Co_{1}$3/Nb$_{2}$3/) $O_{3}$-PbTi $O_{3}$-PbZr $O_{3}$계 압전세라믹스의 조성에 따른 착화소자특성과 기계적응력 인가시의 압전열화현상에 대하여 조사하였다. 그 결과 상경계 조성에서 소결밀도, $K_{33}$ 및 출력전압이 최고치를 나타내었으며 능방정계조성에서는 조성의 변화에 따른 소결 및 전기적특성의 변화는 정방정계조성에 비하여 작았다. 기계적 응력 인가시의 압전퇴화현상은 분역의 재배열로 설명할 수 있었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권1호
• /
• pp.1-8
• /
• 1996

We investigated the effects of doping elements on the Bi-Sr-Ca-Cu-O ceramics. The doping elements can be classified into four groups depending on their supeconducting characteristics in the Bi-Sr-Ca-Cu-O structure. The first group of doping elements(Co, Fe, Ni and Zn) substitute into the copper site and can reduce the critical temperatures of the 2223 and 2212 phases. The second group of doping elements(Y and La) substitute into the Ca site and cause the disappearance of the 2223 phase and increase the critical temperatures in the 2212 phase. The third group of doping elements(P and K) have a tendency to decompose the superconducting phase and reduce the optimal sintering temperature. The fourth group of doping elements(B, Si, Sn and Ba) almost unaffected the superconductivity of the 2223 and 2212 phase.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.43-43
• /
• 2007

LTCC는 최근의 이동 통신 환경의 급격한 발전 속에 그 응용 및 특성 요구가 증폭되고 있다. 이러한 LTCC 소재는 주로 테이프 캐스팅에 의한 후막 공정으로 제품이 만들어지게 되는데, 캐스팅을 위해 제조되는 슬러리는 일반적으로 유변학적 의사가소성 거동을 하는 것으로 알려져 있다. 그러나, 슬러리 제조 조건에 따라 유변학적 거동이 다르게 나타나는 것이 관찰되었다. 이에, 슬러리 제조 조건을 다양하게 변화시키며, 유변학적 거동을 살며 보고 이렇게 변화된 유변학적 거동과 캐스팅된 시트 특성과의 관계를 검토해 보려 한다. LTCC 재료의 주 구성 요소인 glass와 세라믹 분말의 초기 조건 및 각각의 rheology 특성과 혼합 슬러리에서의 관계성 등을 고찰하려 한다.

• E2M - 전기 전자와 첨단 소재
• /
• 제5권1호
• /
• pp.28-42
• /
• 1992

본 논문에서는 ZnO 바리스터의 유전특성에 대해 검토하였다. 25~75[.deg.C]의 온도에서 1[kHz]~13[MHz]의 부파수 범위에서 LCR meter와 computer로 구성된 측정장치를 사용하여 정전용량-주파수, 및 손실계수-주파수의 관계를 측정하였다. 수학적 해석 방법에 의해 복소유전율의 실험결과로 부터 3-4개의 Debye 피크를 추출할 수 있었다. 각 피크를 .alpha., .betha., .gamma. 및 .delta.라 할 때 활성화에너지는 각각 0.35-0.48, 0.62-0.99, 0.48 및 0.33-0.41[eV]이었고, 각 피크 중 .gamma.는 공핍층에 형성된 도너준위, .alpha. 및 .delta.는 결정립 계면준위, .betha.피크는 도너이온에 의한 것으로 추정된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.330-330
• /
• 2010

이동통신 시스템의 소형화, 경량화, 다기능화 추세에 따라 이동통신 부품도 단위 부피당 소자의 집적도를 증가시키기 위하여 고집적화 추세로 급진전되고 있다. 이에 따라 세라믹 공정 기술도 고집적 추세로 다층화 되고 있어 수동소자의 내장화에 대한 필요성이 증대되고 있다. 이를 위하여 다양한 유전율 대역의 이종소재간 접합을 시도하지만 de-lamination, 내부 crack 등의 결함들이 발생하므로 열팽창계수 조절이 용이한 동종의 글라스를 사용하는 것이 유용하다. 본 연구에서는 공통의 글라스를 개발한 후 다양한 필러들을 혼합하여 mm파 대역에서 다양한 유전율을 갖는 LTCC 소재를 개발함으로써, 수동소자의 내장화에 따른 이종접합시의 매칭성을 극대화하고자 하였다. 이를 위하여 CaO-$Al_2O_3-SiO_2-B_2O_3$계 공통글라스에 $CaZrO_3$, $1.3MgTiO_3$, $2La_2O_3TiO_2$ 필러를 혼합하여 소결체의 미세구조, 유전특성 및 열기계적 특성을 고찰하였다. 이때 유전율 6에서 20에 이르는 저손실 소재를 개발할 수 있었다.

• 한국정보전자통신기술학회논문지
• /
• 제9권6호
• /
• pp.604-608
• /
• 2016

최근 난방장치에 대한 에너지의 효율적 사용측면에서 경제성과 안정성을 높이기위한 지속적인 연구 개발이 이루어지고 있다. 특히 고성능 및 신기능 소재에 대한 기술개발이 활발히 이루어지고 있다. 본 논문은 에너지 전달특성이 우수한 발열제품 개발에 관한 것으로 침구류나 매트리스 등에 사용되는 발열체는 전열선을 사용하는 것으로서 전열선이 가늘기 때문에 열의 분포가 전열선 주변에서만 집중되어 전열선에서 떨어진 부분과 온도 편차가 심하게 발생되는 단점이 있다. 또한 전자기가 유도되어 인체에 유해하고 에너지 소비도 많다. 따라서 원적외선, 음이온 등이 방사되어 인체에 이로우면서도 무해할 뿐 아니라 열전도가 우수하여 에너지 효율을 높일 수 있는 SiC계 세라믹을 이용한 면상발열판넬을 개발하고자 한다.

• 방사선산업학회지
• /
• 제3권1호
• /
• pp.7-11
• /
• 2009

Hard magnet was usually used by coating $SiO_2$ ceramic thick films followed by the thermal annealing process. In this work, the alternative annealing process for NdFeB magnets using e-beam sources (1~2 MeV, 50~400 kGy) was investigated. NdFeB magnets was coated with ceramic thick films using the spray method. The optimal annealing parameter for e-beam source reveals to be 1 MeV and 300 kGy. The sample prepared at 1 MeV and 300 kGy was characterized by the analysis of the surface morphology, film hardness, adhesion and chemical stability. The mechanical property of thick film, especially film hardness, is better than that of thermal annealed samples at $180^{\circ}C$. As a result, e-beam annealing process will be one of candidate and attractive heat treatment process. In future, manufacturing process will be carried out in cooperation with the magnet company.

• 한국세라믹학회지
• /
• 제40권1호
• /
• pp.31-36
• /
• 2003

본 연구에서는 칩 인덕터용 코어 소재로 사용되는 NiCuZn-ferrite를 공침법을 이용하여 나노크기의 초미세 분말로 합성하고, 합성된 NiCuZn-ferrite의 하소 온도에 따른 저온소결 특성 및 전자기적 특성에 관하여 고찰하였다. 조성은 (N $i_{0.4-X}$C $u_{x}$Z $n_{0.6}$)$_{1+w}$(F $e_2$ $O_4$)$_{1-w}$에서 x 값을 0.2, w 값은 0.03으로 고정하였고, 하소는 30$0^{\circ}C$에서 7$50^{\circ}C$의 온도범위에서 진행하였다. 하소 후 90$0^{\circ}C$에서 소결한 시편의 특성을 측정한 결과, 공침법으로 합성한 NiCuZn-ferrite는 90$0^{\circ}C$의 저온에서 소결밀도 4.90g/㎤, 초기투자율 164, Q-factor 72임을 확인하였다. 또한, NiCuZn-ferrite의 미세구조는 하소온도가 증가함에 따라 입자가 커지고 불균일한 상태가 되며, 초기투자율 등의 ferrites의 전자기적 특성이 저하되었다.되었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제3권3호
• /
• pp.233-241
• /
• 1990

본 연구에서는 xPb(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$-yBa(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$-zPbTiO(0.50.leq.x.leq.0.60, 0.10.leq.y.leq.0.20, 0.20.leq.z.leq.0.40)세라믹을 1050.deg.C에서 2시간동안 유지시켜 일반소성법으로 제작하였다. 시편 제작시 조성은 조성변태 상경계부근을 선택하였으며 Ba(Zn$_{1}$3/ Nb$_{2}$3/)O$_{3}$ 고용량에 따른 purochlore상의 억제 및 그 영향을 조사하고 구조적, 유전적 및 압전적 특성을 측정하였다. X-선 회절분석 및 미세구조의 관찰 결과, Ba(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$의 고용량에 따라 pyrochlore상 및 미반응 물질등은 억제되어 0.20mol 고용된 시편에서는 균질한 perovskite상이 형성되었다. Ba(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$의 고용량이 증가함에 따라 유전상수는 증가하여 0.50PZN-0.20BZN-0.30PT시편의 경우 6880.9의 높은 값을 나타내었으며 정전용량의 온도계수는 감소하여 0.383[%/.deg.C]의 양호한 값을 나타내었다. 큐리온도는 PbTiO$_{3}$의 고용량이 0.20mol에서 0.40mol로 증가함에 따라 30.deg.C에서 170.deg.C로 증가하였다. 전기기계 결합계수 (K$_{p}$), 기계적 품질계수(Qm) 및 압전전하 계수 (d$_{33}$)는 조성변태 상경계 부근의 조성에서 크게 나타났으며 0.60PZN-0.15BZN-0.25PT 시편의 경우 각각 58.5%, 120.5, 150x$10^{-12}$[C/N]의 값을 나타내었다.다.다.

• E2M - 전기 전자와 첨단 소재
• /
• 제5권2호
• /
• pp.198-206
• /
• 1992

(P $b_{1-x}$L $a_{x}$)[(S $b_{1}$2/S $n_{1}$2/) $Ti_{y}$ Z $r_{1-y}$] $O_{3}$(0.leq.x.leq.0.04, 0.25.leq.y.leq.0.40) 세라믹을 1250[.deg.C]에서 2시간동안 유지시켜 일반 소성법으로 제작하였으며 조성 및 L $a_{2}$ $O_{3}$첨가량에 따른 구조적, 압전적 특성을 관찰하였다. L $a_{2}$ $O_{3}$의 첨가량이 3-4[mol%]인 경우 La-rich의 pyrochlore상이 형성되었다. 시편의 평균결정립 크기는 1-2[.mu.n]의 크기를 나타내었으며 PbTi $O_{3}$조성이 증가함에 따라 다소 감소하는 경향을 나타내었다. 각 조성의 시편에 대해 PbTi $O_{3}$ 및 L $a_{2}$ $O_{3}$의 첨가량이 증가할수록 유전상수는 증가하는 경향을 나타내었으며 상전이 온도인 큐리온도는 PbTi $O_{3}$조성이 감소할수록 L $a_{2}$ $O_{3}$첨가량이 증가할수록 감소하는 경향을 나타내었다. 압전 전하계수 및 전기기계 결합계수는 L $a_{2}$ $O_{3}$첨가량 및 PbTi $O_{3}$조성에 따라 증가하였으며 L $a_{2}$ $O_{3}$가 4[mol%]첨가된 0.10PSS-0.40PT-0.50PZ 시편에서 각각 250x$10^{-12}$[C/N], 29.7[%]의 최대값을 나타내었다. 기계적 품질계수는 L $a_{2}$ $O_{3}$첨가량 및 PbTi $O_{3}$조성이 증가할수록 감소하는 경향을 나타내었으며 0.10PSS-0.25PT-0.65PZ 시편에서 138의 최대값을 나타내었다.다.