• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.6
• /
• pp.272-278
• /
• 2003

$Bi_4Ti_3O_{12}$ (BIT) and $(Bi_{3.25}La_{0.75})(Ti_{2.97}V_{0.03})O_{12}$ (BLTV) thin films were deposited on ITO/glass substrates by metal organic chemical vapor deposition (MOCVD) using ultrasonic spraying. After deposition of the films in oxygen atmosphere for 30 min, the films were heated by rapid thermal annealing (RTA) method, especially direct insertion, at various temperatures. The films were investigated on phase formation temperature, microstructure and electrical properties. From x-ray diffraction (XRD) patterns, the perovskite phase formation temperature of BLTV thin film was about $600^{\circ}C$ which was lower than that of BIT, $650^{\circ}C$. The leakage current of the BLTV thin film was measured to be $1.52\times 10^{-9}$A/$cm^2$ at an applied voltage of 1 V. The remanent polarization (Pr) and coercive field (Ec) values of the BLTV film deposited at $650^{\circ}C$ were $5.6\muC/cm^2$ and 96.5 kV/cm, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.184-189
• /
• 2002

The electrical and optical properties of $(Pb_{0.91}La_{0.09})(Zr_{0.65}Ti_{0.35})O_3$(PLZT) thin films by MOCVD using ultrasonic spraying were investigated. To compensate the Pb loss by evaporation, 5 and 10 wt% of excess Pb was added to 0.2 M precursor. After deposition of films on ITO-coated glasses in oxygen atmosphere for 30 min, films were heated by in-situ RTA (rapid thermal annealing) method. When the films were heat treated at $600^{\circ}C$, perovskite single phase was obtained. The optical property of the film with 10 wt% excess Pb was excellent showing about 84 % of transmittance near 520 nm. The dielectric constant of the film was about 308 and the leakage current of the film was lower than the Pb excess 0, 5 wt% PLZT thin films.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.95-95
• /
• 2018

강재의 방식법 중 도장은 부식을 억제하는데 효과적이고 편리한 방법으로 선박 및 해양 강 구조물의 방식법으로 사용되고 있다. 한편, 강 구조물의 효율적인 유지관리를 위해서는 방식 도장의 도막 열화도를 평가하고 잔존 수명을 예측하여 최적 시기에 보수도장 혹은 재도장하는 것이 필요하다. 일반적으로 선박 및 해양구조물에 적용되는 도막의 방식 성능 평가 방법으로 해수 침지 시험, 염수 분무 시험, 옥외 폭로 시험 등이 있다. 그러나 이러한 시험들은 그 시험 방법에 따라서 정량적인 평가에 한계가 있음은 물론 장기간 소요되는 등 곤란한 문제점이 있다. 그러므로 선박 및 해양구조물을 비롯하여 교량, 각종 강 구조물의 도장 방식에 사용되는 방식용 도료의 성능을 단기간에 적절하게 평가할 수 있는 가속시험법이 제시되며 연구-사용되고 있다. 그 중 도막 방식 성능을 보다 효율적, 비파괴적, 정량적으로 평가할 수 있는 임피던스 분광법(EIS)과 같은 전기화학적 방법은 상대적으로 시험 기간을 크게 단축시킬 수 있고, 대상 방식 도장의 미세한 성능 차이도 분별 가능하다는 장점이 있다[1]. 따라서 본 연구에서는 선박 및 해양구조물 등 가혹한 부식환경에서 강력한 내구성을 가질 수 있도록 다양한 종류의 표면처리 도장 시편을 제작하여 자외선 조사-염수분무-침지환경 등의 열악한 환경조건 하에서 부식-열화 촉진 시험을 실시하였다. 그리고 그 촉진 열화 과정에서 도막의 외관 상태를 관찰 분석함은 물론 전기화학적 임피던스 분광법을 병행 측정하며 그 표면막의 부식 및 도막 열화도를 비교-종합 평가하였다.본 연구에 사용된 시편은 Al 및 Zn 도금 강판에 에폭시, 에폭시-실리콘 우레탄, 에폭시-우레탄 도장 시편으로 Scribe, No Scribe 및 비교재 Al 및 Zn 도금 시편으로 분류하여 각각 실험을 진행하였다. 즉, 도막 열화 시험은 복합 노화 시험법으로 UV 조사 36 시간(ASTM G53), 염수분무 32 시간(ISO 7253), 수분 응축 10 시간을 1 Cycle로 100 Cycle(7800 시간) 동안 실험을 진행하였다. 이때 도막 열화도 평가는 전기화학적 임피던스 분광법을 이용하여 각 실험 조건별로 주파수에 따른 임피던스(Z) 값을 평가하였다. 즉, 상온 $25^{\circ}C$의 3.5% NaCl 100 ml 수용액에 작동 전극(Working Electrode)과 구리 도선을 통해 연결하였고, 노출 면적은 $1cm^2$로 일정하게 유지 하였으며, 상대 전극(Counter Electrode)은 탄소봉, 기준 전극(Reference Electrode)으로 포화카로멜전극(Saturated Calomel Electrode)을 사용하여 측정하였다. No Scribe 시편의 경우에는 Al 기판 에폭시-실리콘 우레탄 도장 시편이 우수한 도막 저항성을 나타내었으며, 에폭시-우레탄 도장시편은 23사이클 이후의 저항값이 가장 낮게 나타났다. Zn 기판의 경우는 에폭시, 에폭시-실리콘 우레탄, 에폭시-우레탄 도장 시편 모두 저항 값이 유사하였으며, Al 및 Zn 도금 시편은 도장 처리된 시편에 비해 훨씬 낮은 저항 값을 보였다. 또한 Scribe 시편의 경우에는 Al 기판 에폭시-실리콘 우레탄 도장 시편에서 높은 초기 저항 값을 보였으며, 23 사이클 후의 저항 값은 세 종류의 도막에서 약 1~0.1 Gohm 으로 나타났다. 그리고 Zn 기판 에폭시-실리콘 우레탄 도장 시편에서 가장 낮은 도막 저항 값이 나타났다. 이상의 실험을 통해서 본 연구 내용은 실내촉진시험으로 선박 및 해양 강 구조물에 사용되는 다양한 종류의 도막의 열화도를 평가하는 기초 설계 지침으로 응용될 수 있을 것으로 사료된다. 한편, 도막은 노출 환경에 따라 방식 성능이 다르므로 실제 도막의 사용환경을 고려하여 도장 사양별 적용 부위에 따른 적정 가속 실험 방법을 선정할 필요가 있다고 사료된다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.3
• /
• pp.294-305
• /
• 1994

The influence of deposition parameter on the electrical, optical andsurface morphology of $SnO_2(:F)$ films prepared by ultrasonic spray deposition using DBDA and $SnCl_4.5H_2O$ as a source material was studied. Resistivity was decreased sharply with increasing F/Sn ratio in solution up to 0.6. Depending on the source material, $SnCl_4.5H_2O$ shows lower resistivity than DBDA. When F/Sn ratio in solution was 1, optical transmittance was higher DBDA than $SnCl_4.5H_2O$.

• Proceedings of the IEEK Conference
• /
• 1999.06a
• /
• pp.283-286
• /
• 1999

Transparent conductive aluminum-doped ZnO(AZO) films Were prepared by a ultrasonic spray pyrolysis method at the substrate temperature below 23$0^{\circ}C$. A vertical type hot wall furnace was used as a reactor in the deposition system. Zinc acetate dissolved in methanol was selected as a precursor. The substrate temperature was varied from 18$0^{\circ}C$to 24$0^{\circ}C$. Aluminum (Al) was doped into ZnO films by incorporating anhydrous aluminum chloride (AlCl$_3$) in the zinc acetate solution. The proportion of the Al in the starting solution was varied from 0 wt % to 3.0 wt %. The crystallographic properties and surface morphologies of the films were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The resistivity of the films was measured by the Van der Pauw method, and the mobility and carrier concentration were obtained through the Hall effect measurements Transmittance was measured in the visible region. The effects of substrate temperature and aluminum content in the starling solution on the structural and electrical properties of the AZO films are discussed

• Journal of ILASS-Korea
• /
• v.27 no.1
• /
• pp.11-17
• /
• 2022

In upcoming Post Stage-V and Tier 5 regulations of construction machineries, nitrogen oxide (NOx) emissions are strictly limited in cold start conditions. In response to this, a method of improving NOx conversion efficiency has been applied by installing an electric heating catalyst (EHC) in front of conventional urea-SCR systems so that the evaporation and thermal decomposition of urea-water solution can be promoted in cold start conditions. In this strategy, the evaporation and thermal decomposition of urea-water solution and corresponding NOx conversion efficiency are governed by temperature conditions inside the EHC. Therefore, characterizing the temperature distribution in the EHC under various operating conditions is crucial for the optimized operation and control of the EHC in Urea-SCR systems. In this study, a 1-D modeling analysis was performed to predict the heater surface temperature distribution in EHC under various operating conditions. The reliability of prediction results was verified by comparing them with measurement results obtained using an infrared (IR) camera. Based on 1-D analysis results, the effects of various EHC operation parameters on the heater surface temperature distribution were analyzed and discussed.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.1509-1514
• /
• 2008

To fabricate microsized poly(methyl methacrylate)(PMMA) beads of uniform size and density on poly(ethylene terephthalate) (PET) fis, we introduce an electro spraying technique that uses a target electrode applied with an ac electric fid. Using the apparatus and various material properties, we could obtain uniform size PMMA beads which were deposited on the thin PET film. The optical properties, transmittance and light diffusivity of the fis electro sprayed with the PMMA were characterized. The results show that the sprayed beads appear to act as a good optical diffuser, like microlenses. To understand the effect of process variables, applied field conditions and rheological properties, the morphological pictures of the deposited particles were investigated through the optical and scanning electron microscope.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.2
• /
• pp.67-73
• /
• 2012

Spherical lithium manganese oxide spinel, $LiMn_{2-x}M_xO_4$ (M = Al, Mg, B) prepared by wet-milling, spray-drying, and sintering process has been investigated as a cathode material for lithium ion batteries. As-prepared powders exhibit various surface morphologies and internal density in terms of boron (B) doping level. It is found that the dopant B drives the growth of the primary particle and minimizes the surface area of the powder. As a result, the dopant enhances the internal density of the particles. Electrochemical tests demonstrated that the capacity of the synthesized material at 5 C could be maintained up to 90% of that at 0.2 C. The cycle performance of the material showed that the initial capacity was retained up to 80% even after 500 cycles under the high temperature of $60^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.48.2-48.2
• /
• 2011

열전재료는 열과 전기에너지의 상호 변환이 가능한 재료로 이를 이용한 응용제품의 개발이 크게 주목을 받고 있으며, 특히 $Bi_2Te_3$계 합금의 경우 상온에서 가장 우수한 성능지수를 가지는 재료로 많은 연구가 진행되고 있다. 그러나 기존의 $Bi_2Te_3$계 합금은 일방향응고법으로 제조되어 많은 시간과 비용을 필요로 하고, 특히 C축의 Van der Waals 결합으로 인해 기계적 강도가 약하다는 단점이 있었다. 최근 분말야금법을 이용하여 기계적강도를 높이고, 격자산란에 의한 열전도도의 감소로 성능지수를 높일수 있는 방법들이 제시되고 있다. 본 연구에서는 급속응고공정인 가스분무법을 이용하여 n-type의 $95%Bi_2Te_3-5%Bi_2Se_3$분말을 제조하였고, 이 재료의 경우 성형조건에 따라 조직이 쉽게 변하기 때문에 이를 제어하기 위해 단시간동안 고압으로 성형가능한 자기펄스압축성형법(Magnetic Pulsed Compaction)을 이용하여 성형체를 제조하였다. 제조된 성형체는 밀도를 증가시키고 결정립성장을 억제시킬수 있는 방전플라즈마소결법(Spark Plasma Sintering)을 이용하여 소결체로 제조되었으며, 각각의 공정이 열전성능에 미치는 영향을 고찰하였다. OM (Optical Microscope) 및 SEM (Scaning Electric Microscope)을 이용하여 미세구조를 관찰하였고 XRD (X-Ray Diffraction)를 이용하여 상의 변화를 분석하였으며, 상온에서 경도를 측정함으로서 공정조건에 따른 기계적강도를 비교하였다. Seebeck계수는 시편의 양단에 온도차를 주어 발생하는 기전압을 측정하여 계산하였고, 전기비저항은 4point probe방법으로 측정하였다. 전하이동도 및 전하농도는 Hall측정으로부터 구하였고 열전도도를 측정하여 종합적인 열전성능을 평가하였다.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.54 no.7
• /
• pp.304-307
• /
• 2005

The $In_2S_3\;and\;In_2S_3:Co^{2+}$ thin films were grown by the spray Pyrolysis method. The thin films crystallized into tetragonal structures. The indirect energy band gap was 2.32ev for $In_2S_3\;and\;1.81eV\;for\;In_2S_3:Co^{2+}$ at 298K. The direct energy band gap was 2.67ev for $In_2S_3:Co^{2+}$ thin films. Impurity optical absorption peaks were observed for the $In_2S_3:Co^{2+}$ thin films. These impurity absorption peaks are assigned, based on the crystal field theory to the electron transitions between the energy levels of the $Co^{2+}$ ion sited in $T_{d}$ symmetry. The electrical conductivity($\sigma$), Hall mobility(${\mu}_H$), and carrier concentration (n) of the $In_2Se_3$ thin film were measured, and their temperature dependence was investigated.