• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.3 s.40
• /
• pp.1-8
• /
• 2006

Higher density integration and adoption of new materials in advanced electronic package systems result in severe electrochemical reliability issues in microelectronic packaging due to higher electric field under high temperature and humidity conditions. Under these harsh conditions, metal interconnects respond to applied voltages by electrochemical ionization and conductive filament formation, which leads to short-circuit failure of the electronic package. In this work, in-situ water drop test and evaluation of corrosion characteristics for SnPb solder alloys in D.I. water and NaCl solutions were carried out to understand the fundamental electrochemical migration characteristics and to correlate each other. It was revealed that electrochemical migration behavior of SnPb solder alloys was closely related to the corrosion characteristics, and Pb was primarily ionized in both D.I. water and $Cl^{-}$ solutions. The quality of passive film formed at film surface seems to be critical not only for corrosion resistance but also for ECM resistance of solder alloys.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.108-108
• /
• 1998

일반적으로 탄소강은 수용액 중에 노출될 경우 전면부식에 의한 손상을 받는다. 그러나 부식방지를 위하여 부식억제제를 적용할 경우, 탄소강의 부식거동은 현저한 변화를 겪게된다. 이러한 부식거동의 변화는 첨가되는 부식억제제의 종류에 따라 분 류할 수가 있는데, 양극부식억제제, 음극부식억제제 그리고 이들의 혼합부식억제제로 분류할 수가 있다. 현장에 적용된 부식억제제 시스템 중에는 자동차용 부동액과 가스히터용 열전달 매체액이 있다. 이러한 부식억제제가 적용된 시스댐은 정확한 부식억제능의 평가에 의한 그 교체 시기의 결정이 매우 중요하다. 교체 시기가 빠를 경우, 유지비용이 과다하게 소요되는 문제가 있으며, 교체시기가 늦을 경우 설비의 부식을 초래하는 문제 가 있다. 따라서 부식억제제의 정확한 성능 평가법은 매우 중요하며, 이에 대한 다양 한 연구가 진행 중이다. 부식억제제가 함유된 용액의 부식억제성능을 평가하는 방법에는 대표적으로 무게 감량법을 이용하고 있다. 이 방법은 다종의 금속이 적용된 자동차용 부동액을 실제 사용조건과 유사한 실험 조건에서 단기간, 가혹조건에서의 무게 감량에 의해 부식억 제능을 평가하는 방법이다. 그러나 이러한 방법은 특히 국부부식이 진행될 경우 부 식억제능을 정량화 하는데 어려움이 있다. 한편 전기화학적 측정방법으로는 분극곡선법을 이용한 $E_P$(공식개시전위), $E_R$(재부동태 화전위)의 측정법이 있다. 또한 부식억제피막의 안정성을 측정하기 위한 방법으로 인 위적인 양극전류 인가에 의한 피막의 파괴후에 피막이 복원가능 여부 및 그 속도 측 정에 의해 부식억제제의 건전성을 확인할 수가 었다. 본 연구에서는 가스히터의 주구성 재료인 A210 Gr Al의 탄소강을 사용하여, 사용기간이 5년 이상되어 부식억제 기능을 거의 상실한 것으로 여겨지는 열전달 매체액 과 신규 부식억제제가 적용된 시스템 등 객관적으로 확인된 부식억제제 시스랩에 대 하여 다양한 평가 방법을 동원 비교분석하고자 하였다. 실험은 KSM 2142에 의한 무게감량법, 분극곡선 측정에 의한 $E_P$(공식개시전위), $E_R$(재부동태화전위) 측정, 시간에 따른 자연전위 변화 측정 빛 이때의 부식속도(선형분극법), 인위적인 피막 파괴 전,후 의 전위 변화 및 부식속도 측정법에 의한 국부부식 발달 저지능 등을 평가하여 각 실험결과를 비교분석하여 보았다.

• Proceedings of the KSR Conference
• /
• 2000.11a
• /
• pp.535-542
• /
• 2000

Pure copper, Cu-1.1wt%Cd and ACSR(Aluminum Conductor Steel Reinforced) have been used as Catenary Materials in Electric Railway System. Since these materials may have chance to be exposed to the corrosive environments like polluted air, acid rain and sea water, it is important not only to investigate the corrosion characteristics but also to measure corrosion rates in various corrosive environments. In order to examine corrosion characteristics according to the dissolved oxygen content, pH, chloride ion concentration ion, and the addition of Cd to Cu, a series of tests such as potentiodynamic polarization. a.c impedance spectroscopy and galvanic corrosion tests were carried out in these materials. Results showed that the addition of Cd to Cu and chloride ion in the solution have an adverse effect on the resistance to corrosion. Additionally, Galvanic currents between Al and steel wires of ACSR were confirmed by using ZRA(zero resistance ammeter) method.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.814-821
• /
• 1999

The specific capacitance characteristics of the electric double layer capacitors(ELDC) which were made of phenol based activated carbon fiber(ACF) electrodes. Also the effect of aqueous electrolytes on the cell performance has been investigated with respect to different specific surface areas of electrodes and different kinds of aqueous electrolytes. It has been shown that larger surface area and pore size, higher conductivity of electrodes, and higher ion mobility of electrolytes have better specific capacitances. It has been found that heat treatment at $1200^{\circ}C$ and $CO_2$ post-activation at $900^{\circ}C$ of the electrode are effective to improve the specific capacitance over 145F/g and 165F/g, respectively. The EDLC showed high efficiency and long cycle life over 30000 cycles.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.1-13
• /
• 2022

This study aims to investigate the feasibility of the half-cell potential (HCP) measurements on the concrete surface for evaluation of corrosion rate (or corrosion levels) of reinforcing steel in concrete. A series of experimental study is performed to measure HCP (or corrosion potential, E_corr) and corrosion current density (i_corr) of reinforcing steel in concrete cube specimens, with a side length of 200 mm. Various corrosion levels in a range of 0% to 20% of the test specimens are accelerated by impressing current to the reinforcing steel in concrete immersed in 3.0 % NaCl solution. HCP is measured in accordance with ASTM C876-15, and corrosion current density is determined by using the Stern-Geary equation and measured polarization resistance measured by electrochemical impedance spectroscopy (EIS). As a result, a numerical formula that relates HCP and i_corr in the test specimen is established by a regression analysis of the measured data in this study. It is observed that HCP is linearly correlated with log(i_corr) with a R² greater than 0.87, which is less affected by the experimental variables such as concrete mixture proportion, diameter of reinforcing steel and the amount of applied current in this study. These results exhibit that HCP measurements could be effective for evaluation of corrosion rate (or corrosion levels) of reinforcing steel in concrete in the case of exposed to a certain consistent environment.

• Journal of the Korea Concrete Institute
• /
• v.21 no.6
• /
• pp.689-696
• /
• 2009

In this study, electro-deposition method was applied to heal cracks in various blended concrete. The performance of the method was indirectly monitored by measuring impressed voltage, electrolyte, galvanic current monitoring, linear polarization resistance, and directly by image analysis of the cracks. The indirect and direct monitoring values are compared to develop guidelines for relating the indirect measures to actual crack healing. As a result, It was found that impressed voltage was convergence to 2.9V after 20000 minutes. From the galvanic current test results of artificial crack healing, the corrosion resistance showed that the order of 0.4 $>$ 0.6 $>$ 0.5 water to cement ratio. Furthermore, in view of binder, the corrosion resistance order was calculated OPC $>$ 60%GGBS $>$ 10%SF $>$ 30%PFA. Finally, It was found that 76.47% of healed crack surface calculated from the artificial crack healing technique using electrochemical deposition method.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.83-90
• /
• 2017

The corrosion behavior of a rebar in concrete according to the amount of NaCl and $LiNO_2$ was observed by using Electrochemical Impedance Spectroscopy. The corrosion was accelerated in a short time by using dry/wet cycles method, which is one of the corrosion acceleration methods, and though the value of measured impedance, equivalent circuit can be introduced. It was confirmed that the passive film of a embedded rebar in concrete with NaCl was broken quickly, and when $0.6M\;LiNO_2$ was added, the velocity of ongoing corrosion was declined considerably compared to the amount of NaCl. However, when $1.2M\;LiNO_2$ was added, it was confirmed that the passive film was not broken and its performance remained, compared to the amount of NaCl.

• Journal of the Korea Concrete Institute
• /
• v.21 no.5
• /
• pp.565-572
• /
• 2009

In this study, corrosion resistance of palm oil fuel ash (POFA) concrete as a blended concrete is evaluated by using electrochemical technique. The POFA is an industrial byproduct obtained from fuel ash after extracting palm oil from palm-tree. In order to obtain basic material characteristics of the POFA concrete, tests on compressive strength, slump, weight loss, bleeding and expansion ratio were carried out the early-aged POFA concrete. On the other hand, durability characteristics, both chloride penetration and carbonation depth test, were also conducted. Finally, corrosion resistance were evaluated by applying electro-chemical artificial crack healing technique, and the tests on the impressed voltage characteristic, galvanic current and linear polarization resistance. From the experimental results, it was found that long-term strength, bleeding, lower slump ratio, expansion ratio, chloride penetration, carbonation and corrosion resistance were improved by using the POFA due to activated pozzolanic reaction. It can be also mentioned that POFA concrete has a potential to be used as a cementitious binder for green-recycling resources.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.83-83
• /
• 2017

생체재료의 표면은 이식과 동시에 생체계면의 역할을 하게 되어, 일련의 생물학적 반응이 시작되고 진행되는 중요한 장소가 된다. 초기에 생체계면에서 일어나는 단백질 흡착이나 염증반응을 비롯한 생물학적 반응들은 궁극적으로 임플란트의 성패를 좌우할 만큼 중요하다. 골융합을 개선하기 위한 다른 방법으로 생체불활성의 타이타늄 (Ti)과 골조직의 능동적인 반응을 이루기 위해 생체활성 표면을 부여함으로서 계면에서의 골형성 반응을 증진시키는 방법이 이용된다. 생체불활성의 Ti과 Ti합금은 골조직과 직접적인 결합을 이루지 못하므로, 골조직과의 반응을 향상하기 위해 여러 종류의 생체활성 재료를 코팅하는 방법이 연구되어 왔고, 이 중 생체의 변화와 가장 유사한 하이드록시아파타이트 코팅이 가장 대중적인 방법으로 사용되었으며 이는 초기 골형성을 촉진하는 것으로 알려졌다. 치과용 임플란트의 표면형상과 화학조성이 골 융합에 영향을 미치는 가장 중요한 인자이므로 최근의 연구동향은 이들 두 가지 표면특성을 결합함으로서 결과적으로 최적의 골세포반응을 유도하고, 골융합 후 골조직과의 micromechanical interlocking에 의해 임플란트의 안정성에 중요한 역할을 하는 마이크론 단위의 표면조도와 표면 구조를 유지하면서, 부가적으로 골 조직 반응을 능동적으로 개선할 수 있는 생체활성 성분을 부여하여 골 융합에 상승효과를 이루기 위한 표면처리법에 관해 많은 연구가 요구되어지고 있다. 따라서 골을 구하는 원소인 망간과 실리콘으로 치환된 하이드록시아파타이트를 플라즈마 전해 산화법으로 코팅하여 세포와 잘 결합할 수 있는 표면을 제공함으로써 골 융합과 치유기간을 단축시킬 수 있을 것으로 사료된다. 실험방법은 시편은 치과 임플란트 제작 합금인 Ti-6Al-4V ELI disk (grade 5, Timet Co., USA; diameter, 10 mm, thickness, 3 mm)이며, calcium acetate monohydrate, calcium glycerophosphate, manganese(II) acetate tetrahydrate, sodium metasilicate을 설계조건에 따라 혼합 제조된 전해질 용액을 이용하여 플라즈마 전해 산화법으로 표면 코팅을 실시하였다. 각 시편의 플라즈마 전해시 전압은 280V로 인가하였고, 전류밀도는 70mA로 정전류를 공급하여 해당 인가전압 도달 후 3분 동안 정전압 방식을 유지하였다. 코팅된 피막 표면을 주사전자현미경과 X-선 회절분석을 통하여 미세구조 및 결정상을 관찰하였다. 또한 코팅된 표면의 생체활성 평가는 정량적으로 평가하기 위해 동전위시험과 AC 임피던스를 통하여 시행하였다. 분극거동을 확인하기 위해 potentiostat (Model PARSTAT 2273, EG&G, USA)을 이용하여 구강 내 환경과 유사한 $36.5{\pm}1^{\circ}C$의 0.9 wt.% NaCl에서 실시하였다. 전기화학적 부식 거동은 potentiodynamic 방법으로 조사하였고 인가전위는 -1500 mV에서 2000 mV까지 분당 1.67 mV/min 의 주사속도로 인가하여 시험을 수행하였다. 임피던스 측정은 potentiostat (Model PARSTAT 2273, EG&G, USA)을 이용하였으며, 측정에 사용한 주파수 영역은 10mHz ~ 100kHz 까지의 범위로 하여 조사하였고 ZSimWin(Princeton applied Research, USA) 소프트웨어를 사용하여 용액의 저항, 분극 저항 값을 산출하였다. 망간의 함량이 증가할수록 불규칙한 기공을 보였으며, 실리콘은 $TiO_2$ 산화막 형성을 저해하는 경향을 확인할 수 있었다. 단독으로 표면을 처리한 경우보다 두 가지 원소를 이용해 복합 표면처리를 시행한 경우가 내식성이 좋아 임플란트과의 골 유착에 긍정적인 영향을 미칠 것으로 사료된다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.164-164
• /
• 2016

항만 및 해양 구조물은 육상과는 비교할 수 없을 정도로 가혹한 해수 환경에서 사용되며 계속적으로 부식 손상을 받는다. 따라서 강구조물이 장기적으로 안전하게 사용되기 위해서는 적절한 방식은 물론 철저한 유지관리가 필수적이다. 한편, 현재 해양환경 중 항만, 조선, 해양산업 등에 많이 이용되는 강구조물은 이에 대응하기 위하여 일반적으로 도장방식이나 음극방식이 사용되고 있다. 음극방식은 피방식체를 일정전위로 음극 분극하는 원리로써 외부전원을 인가하거나 비전위의 금속을 희생양극으로 연결하여 방식하는 방법이다. 이와같이 해수 중 음극방식을 실시할 경우 해수 중 용존하는 많은 이온들 중에서 특히 $Ca^{2+}$ 이나 $Mg^{2+}$ 이온이 탄산칼슘, 수산화마그네슘을 주성분으로하는 화합물로 형성된다. 이렇게 생성된 전착막은 산소 확산을 방지하는 물리적 장벽을 형성하고 부식율을 감소시키는 것으로 보고되고 있다. 그러나 전착막은 소지 금속과의 결합력이 불균일 함은 물론 막을 형성하는데 있어서 장시간이 소요된다는 단점이 있다. 따라서 본 연구에서는 해수 중 음극방식 응용 원리에 의해 전착막을 형성하고, 석출속도, 밀착성 및 내식특성을 향상시키기 위해 해수 중 기체를 용해시켜 제작한 막의 특성을 분석-평가하였다. 본 연구에 사용된 기판(substrate)은 일반구조용 강(SS400)을 사용하였으며, 면적은 $70mm{\times}30mm$, 두께는 1 mm로 제작하여 실험을 진행하였다. 외부전원은 정류기(Rectifier, xantrex, XDL 35-5T)를 사용하여 3 및 $5A/m^2$ 의 조건으로 인가하였고, 양극은 Carbon Rod를 사용하였다. 이때 해수에 주입한 이산화탄소의 양은 0.5 NL/min 였다. 각 조건별로 제작된 전착막에 대해 외관관찰, 석출량, 모폴로지, 조성원소 및 결정구조 분석을 실시하였고, 밀착성 및 내식특성을 평가하기 위해 테이핑 테스트(Taping Test, JIS K 5600-5-6)와 3.5 % NaCl 용액에서 전기화학적 양극 분극 시험을 진행하였다. 시간에 따른 전착막의 외관관찰 결과 전류밀도의 증가와 함께 상대적으로 많은 피막이 형성되었고, 용해시킨 기체에 의해 더 치밀하고 두터운 피막이 형성됨을 확인할 수 있었다. 성분 및 결정구조 분석 결과 $Mg(OH)_2$ 성분의 Brucite 및 $CaCO_3$ 성분의 Calcite 구조 및 Aragonite 구조를 확인하였으며, 용해시킨 기체의 영향으로 $CaCO_3$ 성분의 Aragonite 구조가 상대적으로 많이 검출되었다. 이는 해수 중 용해된 이산화탄소의 영향으로 인해 풍부한 ${CO_3}^{2-}$ 이온이 형성되고 용액 pH를 낮게 유지시켜 Ca 화합물 형성이 용이한 환경이 조성되는 것으로 판단된다. 밀착성 및 내식성 평가를 실시한 결과 해수중 용해시킨 기체에 의해 제작한 시편의 경우 견고하고 화학적 친화력이 높은 Aragonite 결정이 표면을 치밀하게 덮어 전해질로부터 산소와 물의 침입을 차단하는 역할을 하여 기체를 용해시키지 않은 $3A/m^2$ 및 $5A/m^2$ 보다 비교적 우수한 밀착성 및 내식 특성을 보이는 것으로 사료된다.