• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.26 no.4
• /
• pp.677-687
• /
• 1999

This study was performed to evaluate the effect of aging and thermal cycling on the tensile strength of six commercially available glass-ionomer materials: two chemically set glass-ionomer materials(Fuji II, Fuji IX), two resin-modified glass-ionomer materials(Fuji II LC, Vitremer), and two polyacid-modified composite resins(Compoglass, Dyract). Rectangular tension test specimens were fabricated in a teflon mold giving 5mm in gauge length and 2mm in thickness. All samples were divided into 3 groups. Group 1 was immersed in a $37^{\circ}C$ distilled water for 1 hour. Group 2 was immersed in a $37^{\circ}C$ distilled water for 30 days. Group 3 was subjected to 10,000 thermal cycles between $5^{\circ}C$ and $55^{\circ}C$, and the immersion time in each bath was 15 seconds per cycle. Tensile testing was carried out at a cross-head speed of 0.5mm/min and fracture surfaces were examined with scanning electron microscope. The results obtained were summarized as follows; 1. The polyacid-modified composite resins were stronger than the resin-modified glass-ionomer materials, which were much stronger than the conventional glass-ionomer materials. 2. Tensile strengths were slightly increased after aging treatments for 30days. 3. Tensile strengths of conventional glass ionomers were significantly increased after thermal cycling treatment(p<0.01). 4. The highest tensile strength value of 45.4MPa was observed in the Dyract group and the lowest value of 13.3MPa was observed in the Fuji II LC group after the thermal cycling test, and the strengths of polyacid-modified composite groups were significantly higher than those of other groups. 5. The highest characteristic strength value of 48.6MPa was obtained in the Dyract group, however the highest Weibull modulus value of 8.9MPa was obtained in the Compoglass group after thermal cycling test.

• Journal of Korean Society of Forest Science
• /
• v.23 no.1
• /
• pp.17-27
• /
• 1974

In order to investigate the variation of nutritive value, fertilizer value, productivity and growth performance by the number of cutting times in Lespedeza bicolor, Lespedeza maximowiczii and Lespedeza japonica var. intermedia, the plots of one, two and four cutting times in a year had been made through 1972 to 1973. The results are summarized as follows. 1. Lespedeza bicolor, Lespedeza maximowiczii and Lespedeza japonicavar. var. intermedia showed increase of growth and productivity in two plots excluding the plots of four time cuttings. 2. Significant differences at 1% level were shown among the species and the number of cutting times in total grass yield. Lespedeza bicolor showed the greatest production, and followed by Lespedeza maximowiczii and Lespedeza japonica var. intermedia. The plots of one cutting time a year produced more dry weight than that of two and four cutting times. The production in plots of fourth cutting showed less growth and yield. 3. The ratios of dry weight to fresh weight and of leaf weight to stem weight were decreased when the number of cutting times increased in Lespedeza bicolor, Lespedeza maximowiczii and Lespedeza japonica var. intermedia. 4. Crude protein was decreased, though crude fiber content was increased when the grasses were growing more and more. Conent of crude fat showed great variation by the number of cutting times and cutting period seoson. 5. Early cut tings of Lespedeza showed higer fertizer value than late cuttings in all the species. 6. It is suggested that two and three time cutting through a year in Lespedeza bicolor and Lespedeza japonica var. intermedia having high nutritive and fertilizer value is good when using the Lespedeza species as a fodder or manuers, and one time cutting a year will be good when using the Lespedeza species as a fuel.

• Journal of the East Asian Society of Dietary Life
• /
• v.17 no.6
• /
• pp.834-839
• /
• 2007

This study was designed to determine the optimal ratio of dropwort powder in castella by adding the powder at levels of 0, 3, 6, 9, and 12% respectively. The properties of the castella were analyzed by specific gravity, specific volume, color determinations, texture properties and sensory evaluation. The Specific gravity increased with increasing amount of dropwort powder. However, the specific volume decreased with increasing dropwort powder. For the color values, as more dropwort powder was added, the L-value decreased. The castella with 9% dropwort powder had a higher hardness, gumminess, and chewiness. A sensory panel perceived that the external and internal color of the castella become darker with the dropwort powder substitution and the grain size decreased with increasing amount dropwort powder, while sweet taste showed no significant difference. The order of overall preference was DP 9>DP 6>DP 12>CON>DP 3. Therefore, the substitution of 9% of wheat flour with dropwort powder was recommended in the production of castella.

• Journal of Bio-Environment Control
• /
• v.27 no.3
• /
• pp.245-252
• /
• 2018

Yam bean (Pachyrhizus erosus) is a subtropical plant belonging to the Fabaceae family, and is a tuberous vegetable used as various food material with a crisp and juicy taste. This study was conducted to seek optimum sowing time of yam bean in Korea. For this, we surveyed germination properties by the different temperatures and compared the accumulation temperature (AT) and dry matter production (DMP) on growth stages of yam bean by the different sowing times. Two types of varieties cultivated mainly in Korea, Thailand local variety (TLV) and Cheongunmanma cultivar (CGMM), was used. The germination rate of yam bean was 86.0~94.0% at above $18^{\circ}C$, and germination days was longer at lower temperature. The times for flowering and tuber formation of CGMM were later than those of TLV, and the AT required for flowering, tuber formation and hypertrophy of CGMM were higher than those of TLV by $293^{\circ}C$, $280^{\circ}C$ and $108^{\circ}C$, respectively. Also, DMP of shoot and tuber in CGMM were greater than those in TLV. In sowing at April 25, tuber formation was slower than sowing after that time, and harvest index (HI) was relatively low due to delayed formation and hypertrophy of tuber. In sowing after June 9, DMP of shoot was relatively greater in early growth, but tuber was not sufficient to enlarge due to lack of growth days by cold and frost in late October. In sowing May 10 and 25, DMP of tuber and HI were the highest, because the change of day length and temperature gave an advantage to vegetable growth and tuber development. All above suggest that it was suitable to sow seeds on May for increment of tuber productivity in Korea.

• Korean Journal of Plant Resources
• /
• v.15 no.2
• /
• pp.164-171
• /
• 2002

Morphological characteristics and growth pattern of 10 Polygonatum collections indigenous to Korea were examined to select the promising medicinal, edible resources and horticultural crops. Plant heights of I0 collections ranged from 15 to 102cm. Stem type was ascending or erect, and node numbers per a stem was 6.2 to 23.2. Phyllotaxis type was alternate or verticillate, and leaf shape was elliptical or linear. Leave numbers per a stem was 5.2 to 63.4, and bract types were classified into bracteate and nonbracteate. Flowers bloomed from May 7 to May 30, and flowering period was 5 to 13 days. Inflorescence types were classified into racemose, corymbose, and umbellate. Flower numbers per a stem was 1.5 to 125.2, and flower length was 13.1 to 30.2㎜. Perianth shapes were classified into tubular, constrict and urceolate. Surface colors of rhizome were pale yellow, pale brown, brown, and dark brown. As a result of this experiment, P. sibiricum, P. odoratum var. pluriflorum and P. odoratum var. thunbergii were thought to be useful as the medicinal and edible resources plants. On the other hand, P. odoratum var. pluriflorum 'Variegata', and P. odoratum var. maximowiczii, P. lasianthum. P. involucratum, P. desoulavyi, P. humile, and P. inflatum were thought to be useful as horticultural plants.

• Korean Journal of Agricultural Science
• /
• v.22 no.1
• /
• pp.1-10
• /
• 1995

All agricultural crops and products should be cultured, harvested, handled and processed by the proper mechanical methods in the mechanized farming systems. Agricultural crops might be injured or deformed through various working stages due to static or dynamic forces of machines. Mechanical forces had to be applied with proper degrees to the agricultural crops in incoincidence with properties of crops without any damage of crops so as to increase the work efficiency qualitatively. Knowledges of mechanical properties of agricultural materials are essential to prevent of agricultural crops in relation with mechanical farming system. This study was carried out to examine and analyze the creep behavior of the rice stalk on growing and harvesting periods by mechanical model with computer measurement system in radial directional compressive force and bending force. The creep behavior of the rice stalk could be predicted precisely and its results approached closely to the measured values. The creep behaviors were increased greatly with increase of compressive force, namely, the steady state creep behavior occurred at the force less then 25N and the logarithmic creep behavior at the force bigger than 30N. The instantaneous elastic modulus $E_o$ and the retardation time ${\tau}_K$ were increased together with increase of applied forces, meanwhile the retarded elastic modulus $E_r$ and viscosity ${\eta}_v$ were decreased with increase of applied forces in mechanical model being expected the creep behavior in relation with the level of applied forces, which was well explained that the rice stalk might be visvo-elastic material. In the creep test along the stalk portion with compressive force and bending force, the intermediate portion showed greatest values and also the lower portion showed the least values, which implied that the intermediate portions of rice stalk were very weak. The steady state creep behavior occured at the intermediate portion and the upper portion in the rice stalk at the compressive force larger than 25.0N, which showed the possibility of injury due to external forces.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.232-239
• /
• 2009

Statements of the problem: Many denture wearers occasionally use denture adhesives to improve denture retention, stability and chewing efficiency. An ideal denture adhesive is nontoxic, non-irritating, and provides comfort to the oral mucosa. Purpose: The purpose of this study was to evaluate the cytotoxicity and adhesive properties of a selected denture adhesive. Material and methods: To test cytotoxicity of the selected denture adhesive, mouse fibroblast cells were used in MTT testing. Cytotoxicity was examined according to the concentration of the denture adhesive and incubated for 1 to 4 days. To examine adhesive property, a denture base was fabricated on an edentulous dentiform. The adhesive was applied to the denture base, then tensile bond strength was measured, to evaluate the change in retention during 3 days. Results and Conclusion: 1. 1% and 2% concentration denture adhesive cream had no cytotoxicity. 2. The tensile bond strength of the group with both denture adhesive and artificial saliva was significantly higher than that of the group with only denture adhesive(P<.05). The tensile bond strength of the group with denture adhesive was significantly higher than that of with only artificial saliva(P<.05). 3. The tensile bond strength had no significant change during 1 hour, and then gradually decreased. After 1 day, it decrease to half. Within the limitation of this study, the tested denture adhesive had no cytotoxicilty and was effective in improving denture retention. The adhesive strength began to continuously decrease after 1 hour and it decreased to half at 1 day after application.

• The Journal of Korean Academy of Prosthodontics
• /
• v.58 no.3
• /
• pp.177-184
• /
• 2020

Purpose: The purpose of this study was to compare and evaluate the tensile bond strength of chairside reline resin to denture base resin fabricated by different methods (subtractive manufacturing, additive manufacturing, and conventional heat-curing). Materials and methods: Denture base specimens were fabricated as cuboid specimens with a width of 25 mm × length 25 mm × height 3 mm by subtractive manufacturing (VITA VIONIC BASE), additive manufacturing (NextDent Base) and conventional heat-curing (Lucitone 199). After storing the specimens in distilled water at 37℃ for 30 days and drying them, they were relined with polyethyl methacrylate (PEMA) chairside reline resin (REBASE II Normal). The subtractive and additive manufacturing groups were set as the experimental group, and the heat-curing group was set as the control group. Ten specimens were prepared for each group. After storing all bound specimens in distilled water at 37℃ for 24 hours, the tensile bond strength between denture bases and chairside reline resin was measured by a universal testing machine at a crosshead speed of 10 mm/min. The fracture pattern of each specimen was analyzed and classified into adhesive failure, cohesive failure, and mixed failure. Tensile bond strength, according to the fabrication method, was analyzed by 1-way ANOVA and Bonferroni's method (α=.05). Results: Mean tensile bond strength of the heat-curing group (2.45 ± 0.39 MPa) and subtractive manufacturing group (2.33 ± 0.39 MPa) had no significant difference (P>.999). The additive manufacturing group showed significantly lower tensile bond strength (1.23 ± 0.36 MPa) compared to the other groups (P<.001). Most specimens of heat-curing and subtractive manufacturing groups had mixed failure, but mixed failure and adhesive failure showed the same frequency in additive manufacturing group. Conclusion: The mean tensile bond strength of the subtractive manufacturing group was not significantly different from the heat-curing group. The additive manufacturing group showed significantly lower mean tensile bond strength than the other two groups.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.3
• /
• pp.557-568
• /
• 2005

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four esthetic restorative materials in an alkaline solution(0.1N NaOH). The brands studied were MetafilCX(Sun medical, Japan) Solitaire 2(Heraeus Kulzer, USA), Composan LCM(Promedica, Germany), DenFil(Vericom, Korea). The results were as follows: 1. The mass loss of each brand was 0.74~7.94% and highest value in Metafil($7.94{\pm}0.39%$). 2. The sequence of the degree of degradation layer depth was in descending order by Metafil, Solitaire 2, DenFil, Composan LCM. There were significant differences between Metafil and the others(p<0.05). 3. The sequence of the Si loss was in descending order by Metafil, Solitaire 2, Composan LCM, DenFil. There were significant differences among the materials(p<0.05). 4. On SEM, destruction of bonding between matrix and filler and on CLSM, the depth of degradation layer of specimen surface was observed. 5. The sequence of maximum wear depth was in descending order by Metafil, Solitaire 2, Composan LCM and DenFil. There were significant differences among the materials(p<0.05). 6. The correlation coefficient between Si loss and degradation layer depth (r=0.491, p<0.05) and Vicker's hardness number and maximum wear depth (r=-0.942, p<0.05) were relatively high. These results indicate that hydrolytic degradation and wear may consider as a evaluation factors of composite resins.