The Crystallographic and Magnetic Properties of $Fe_{1-x}Co_x$System ($Fe_{1-x}Co_x$계의 결정구조와 자기적인 성질)

  • 김정기;한경훈;서정철
    • Journal of the Korean Magnetics Society
    • /
    • v.9 no.4
    • /
    • pp.190-195
    • /
    • 1999
  • The crystallographic and magnetic properties of the system of $Fe_{1-x}Co_x$(x=0.2 and 0.4) prepared by microwave arc-melting with the maximum power of 3.5 kW and a iron-foil with thickness of 25 ${\mu}{\textrm}{m}$ have been studied by the methods of X-ray diffraction and the measurement of the magnetic hysteresis using the vibrating sample magnetometer at room temperature. The samples were prepared in three different ways: First, pellet form pressed under the pressure of 9,000 N/$\textrm{cm}^2$. Second, the sheet cold rolled. Third, thin sheet treated with the temperature of 90$0^{\circ}C$. The X-ray diffraction pattern of the sample prepared by the first method shows that the crystal structure of the sample is bcc as same as that of Fe with a good uniformity. The iron-foil has the coercivity of 43 Oe and the initial slope of magnetization of 0.328 emu/gOe. The coervicity and magnetization of the sample prepared by the second method increased as the Co content increased. But the initial slop of the magnetization decreased as the Co content increased. This means that the displacement of domain wall is suppressed by the increases of coercivity as the Co content increased. The saturation magnetization of the samples made by the third method increased. On the other hand, the coercivity of these samples decreased. The increase of saturation magnetization of the samples seems to be related to the changes in X-ray intensity after heat treatment. Also some magnetic parameters of the samples were calculated by using a simple model and compared with other values.

  • PDF

Magnetic Properties of Cr-Doped Inverse Spinel Fe3O4 Thin Films (Cr 치환된 역스피넬 Fe3O4 박막의 자기적 특성)

  • Lee, Hee-Jung;Choi, Seung-Li;Lee, Jung-Han;Kim, Kwang-Joo;Choi, Dong-Hyeok;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.17 no.2
    • /
    • pp.51-54
    • /
    • 2007
  • By substituting Cr in inverse-spinel $Fe_3O_4,\;Cr_xFe_{3-x}O_4$ thin film samples were prepared by sol-gel spin-coating method and their structural electronic, and magnetic properties were analyzed. X-ray diffraction indicates that the lattice constant decrease with increasing Cr composition (x). This result can be explained in terms of occupation of octahedral sites by $Cr^{3+}$ ions with smaller ionic radius than that of $Fe^{3+}$ Vibrating sample magnetometry measurements on the samples at room temperature revealed that saturation magnetization ($M_s$) decrease by Cr substitution, explainable by comparing spin magnetic moment among the related transition-metal ions. A decrease of magnetoresistence effect with x was observed, similar to that of $M_s$. The coercivity of the $Cr_xFe_{3-x}O_4$ films was found to increase with x, attributed to the increase of magnetic anisotropy by the existence of octahedral $Cr^{3+}(d^3)$.

The Physical Properties of Mn-Ferrite According to the Variation of Fe-Mn Composition Ratio (철-망간 화합비 변화에 따르는 망간 페라이트의 물성)

  • Kim, Yu-Sang;Hwang, Yong-Gil
    • Korean Journal of Materials Research
    • /
    • v.2 no.2
    • /
    • pp.126-132
    • /
    • 1992
  • Experiment has been performed to investigate the thermal and magnetic properties of Mn-ferrite by electrolysis. Using the 0.2%C mild steel as soluble anode and SUS 304 stainless steel as cathode, Mn-ferrite could be made from the sulfuric acid leaching of the wasted manganese dry cell and $MnSO_4$reagent by electrolysis. As the result of X-ray diffraction, thermal analysis and magnetic measurement, Mn-ferrite was the spinel type in $Mn_{x}Fe_{3-x}O_4$ (X=1), the weight loss rate of $Mn_{x}Fe_{3-x}O_4$ were linearly increased up to the $200^{\circ}C$. Ms, Mr and Hc values were decreased with increasing Mn content and heating temperature. When Mn-ferrite was formed by $MnCl_2$reagent electrolysis, Ms values were higher than those formed from the sulfuric acid leaching of the wasted manganese dry cell and $MnSO_4$reagent by electrolysis. In Mn-ferrite, which was formed from the sulfuric acid leaching of the wasted manganese dry cell by electrolysis, Ms and Mr values were higher, Hc values were lower than which was formed by $MnSO_4$ reagent electrolysis at $200^{\circ}C\;and\;300^{\circ}C, while the same values at $100^{\circ}C$. The shape of particles was spherical type, the sizes of them were about $0.1{\mu}m$ sub-micron in $MnSO_4$reagent electrolysis, $0.5{\mu}m$ in the sulfuric acid leaching of the wasted manganese dry cell by electrolysis.

  • PDF

Magneto-electronic Properties of $Si_{ l-x}Mn_x$ Thin Films Grown by MBE (MBE로 성장한 $Si_{ l-x}Mn_x$ 박막의 전자기적 특성 연구)

  • Kim, Jong-Hwan;Ryu, Sang-Su;Kim, Hang-Yeom;Kwon, Dang;Cho, Yeong-Mi;Lim, Yeong-Eun
    • Proceedings of the Materials Research Society of Korea Conference
    • /
    • 2003.03a
    • /
    • pp.100-100
    • /
    • 2003
  • 본 연구에서는 Si에 Mn을 첨가한 Si$_{l-x}$Mn$_{x}$ 박막의 전기적 및 자기적 특성을 조사하였다. Si$_{l-x}$Mn$_{x}$ 박막은 MBE(Molecular Beam Epitaxy)를 이용하여 native oxide층을 제거하지 않은 (100)Si wafer 위에 성장하였다. Substrate 온도는 50$0^{\circ}C$로 하였으며, 첨가한 Mn 농도는 20%에서부터 80%까지였다. 전기적 특성은 Hall, 4-point probe를 통하여 측정하였고, 자기적 특성은 VSM, FMR, SQUID을 이용하여 측정하였다. 상 분석은 XRD, TEM을 이용하여 관찰하였다 Si$_{l-x}$Mn$_{x}$ 박막은 Hall 측정 결과 상온에서 P-type carrier를 가지며, 비저항은 반도체 영역인 7.6$\times$$10^{-4}$~4.2$\times$$10^{-2}$(ohm-cm)의 값을 가진다. 상온 VSM, 측정결과 Mn의 양이 52% 첨가 시 포화 자화 값이 가장 높은 40emu/cc를 가지며, Mn의 양이 증가할수록 포화 자화 값이 증가하다 다시 감소하는 경향을 가진다. FMR, SQUID 측정에서도 이러한 경향을 확인할 수 있었다 특히, SQUID 분석 결과 두 개 이상의 자성 상이 존재하는 것을 관찰할 수 있었다. XRD, TEM 관찰결과, Si$_{l-x}$Mn$_{x}$은 poly crystal로 성장하였으며, Mn 농도에 따라 여러 상들이 관찰되었다.따라 여러 상들이 관찰되었다.

  • PDF

Magnetic and Magneto-Optical Properties of FeCo/Pd Multilayers (FeCo/Pd 초격자 다층박막의 자기 및 자기광학적 특성)

  • 김진홍;신성철
    • Journal of the Korean Magnetics Society
    • /
    • v.3 no.1
    • /
    • pp.56-60
    • /
    • 1993
  • We have investigated the dependence of the magnetization, anisotropy, coercivity, and Kerr rotation on the Fe concentration in FeCo/Pd multilayer thin films, where the Fe concentration in the FeCo sublayer varied between 0 and 100% with maintaining the same sublayer thickness of $2.5\;{\AA}$ FeCo and $10.5\;{\AA}$A Pd. The maximum saturation magnetization was observed at the Fe concentration of about 48at.% in the FeCo sublayer. Perpendicular magnetic anisotropy and coercivity of the FeCo/Pd multilayer thin film decreased monotonically with increasing the Fe con-centration. The Kerr rotation angle also decreased with increasing the Fe concentration and the amount of vari-ation was remarkably changed with decreasing the light wavelength.

  • PDF

Effect of Reaction Conditions on the Size and Size Distribution of Magnetite Nanoparticles Coated with Siloxane (반응조건에 따른 실록산으로 코팅된 마그네타이트 나노입자의 크기 및 분포)

  • 윤관한;한창민;장용민
    • Polymer(Korea)
    • /
    • v.28 no.2
    • /
    • pp.170-176
    • /
    • 2004
  • The effect of reaction conditions on the size and size distribution of superparamagnetic iron oxide coated with siloxane was big investigated by using dynamic light scattering. The hydrogen bond between the hydroxyl groups on tile surface of the magnetite and silanol was confirmed by FT-IR. The size of nanoparticles increased with the reaction temperature, but decreased with monomer contents and agitation speeds. There was not a big difference in size of nanoparticles, prepared by different reaction conditions, but its distribution was in the range of 14∼41nm. All samples exhibited the superparamagnetic nature. The magnetic susceptibility of the nanoparticles increased with the reaction temperature while it decreased with the monomer content and agitation speed.

Fabrication and Magnetic Process of 13Cr-1.5Nb-Fe Stainless Sensors (13Cr-1.5Nb-Fe 스텐레스 센서재료의 제조 및 연자기특성)

  • 윤성호;김택기;조용수
    • Journal of the Korean Magnetics Society
    • /
    • v.8 no.3
    • /
    • pp.125-130
    • /
    • 1998
  • 13Cr-1.5Nb-Fe alloy powder was fabricated by water atomization method, and ring-shape specimen of this composition was fabricated by oil press, and then sintered in the vacuum furnace. Powder shape, size distribution, composition (C, N, O, S) analysis and saturation magnetization of as-prepared 13Cr-1.5Nb-Fe alloy powder were investigated. Ac permeability and power loss was measured after forming and sintering process. Saturation magnetization and contents of oxygen of the alloy powder is160 emu/g and about 6000 ppm, respectively. 50 % volume fraction indicate particle size of 70$\mu$m. The ac permeability of sintered specimen increases with increasing sintering temperature and forming pressure. The power loss is 107 W/cc at sintering temperature of 1200 $^{\circ}C$, 12 ton/$\textrm{cm}^2$ forming pressure, and 20 KHz. It is the lowest among the prepared specimen.

  • PDF

Ferromagnetic Resonance Study of an YIG Thin Film Grown by LPE Method (LPE법으로 제조한 YIG 박막에 대한 강자성공명 연구)

  • 이수형;염태호;윤달호;김약연;한기평;이상석
    • Journal of the Korean Magnetics Society
    • /
    • v.9 no.2
    • /
    • pp.85-90
    • /
    • 1999
  • The ferromagnetic resonance study of the magnetostatic wave modes for an YIG thin film, grown by a liquid phase epitaxy method, was performed by an FMR spectrometer at room temperature. The magnetostatic surface wave and backward volume wave modes show periodic excitations in parallel configuration, whereas the complex spectra were observed in perpendicular configuration. The resonance spectra in parallel configuration can be well explained by the Walker and Damon-Eshbach theory. The peak-peak line width of uniform mode was 0.4 Oe. The saturation magnetization $M_s$ of the YIG thin film was calculated as 137 emu/㎤. In order to know the dependence of the magnetostatic modes as a function of the saturation magnetization and the thickness, the (1,1) and (3,1) modes of the magnetostatic backward volume wave were compared and theoretically calculated.

  • PDF

Effects of Sputtering Ar Gas Pressure on Magnetic and Magneto-Optical Properties in Compositonally Modulated Co/Pt Superlattice Thin Films (조성변조 Co/Pt 초격자 박막의 Ar 가스 압력변화에 따른 자기 및 자기광학적 특성)

  • 유천열;김진홍;신성철
    • Journal of the Korean Magnetics Society
    • /
    • v.4 no.1
    • /
    • pp.32-38
    • /
    • 1994
  • We have investigated the effects of sputtering Ar gas pressure on magnetic and magneto-optical properties in compositionally modulated Co/Pt superlattice thin films. The samples were prepared by dc magnetron sputtering. Sputtrering Ar gas pressure was varied from 2 to 30 mTorr. The microstructure of the samples was examined by scanning electron microscope and the x-ray diffractometry. The magnetization, the Kerr rotation angle, and the reflectivity of the samples were measured. The columnar structure was developed, and the coercivity was drasti- cally increased, when the sputtering Ar gas pressure was higher than 20 mTorr. We explained that the variation of the magnetization, the Kerr rotation angle, and the reflectivity was related with the microstructure influenced by the variation of the Ar gas pressure.

  • PDF

A Study on Structure and Magnetic Properties of Fe-N Films with Different Sputtering time (증착 시간에 따른 Fe-N 박막의 구조 및 자성 특성에 관한 연구)

  • Han, Dong-Won;Park, Won-Uk;Gwon, A-Ram
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2017.05a
    • /
    • pp.161.2-161.2
    • /
    • 2017
  • 희토류계 영구자석은 대부분의 전기, 전자 제품의 핵심부품이며 높은 보자력, $BH_{max}$를 가지고 있어 자기기록저장매체, MEMS(엑츄에이터), 소형센서, 소형모터 등의 응용 분야에 적용시키기 위해 다양한 연구들이 진행되고 있다. 그러나 영구자석에 들어가는 희토류계 원소의 수급의 어려움 및 가격의 문제점으로 친환경 자석으로의 전환 및 희토류나 중희토류를 사용하지 않는 비희토류계 영구자석을 제조 및 개발하는데 많은 연구가 이루어지고 있다. 이 중 Fe-N 계 자성물질인 $Fe_{16}N_2$는 포화 자화 값이 현재까지의 비희토류계 자성물질 중 가장 높은 값(240emu/g)을 나타내며 상대적으로 높은 결정자기이방성 상수를 가지고 있어 비희토류계 영구자석 물질 중 하나로 주목받으며 연구되어지고 있다. 본 연구에서는 $Fe_{16}N_2$ 박막을 얻기 위해 DC Magnetron Sputtering 방법을 이용하여 Si wafer 위에 박막을 증착하고 증착시간에 따라 두께를 제어하여 제조한 후 박막의 미세구조, 상 분석, 자성 특성을 관찰을 통해 최적의 공정 조건을 찾고자 하였다. 증착 시간에 따른 박막의 성장 속도는 일정하게 증가하였으며, 증착 시간의 증가에 따라 박막 내 $Fe_{16}N_2$의 상대적인 분율은 감소하였다. 모든 공정 조건에서 $Fe_3N$, $Fe_4N$, $Fe_{16}N_2$ 상들이 섞여 성장하였으며 XRD를 통한 상분석과 더불어 VSM을 통한 자성 특성을 분석해본 결과 $Fe_{16}N_2$의 분율을 가장 높게 성장된 공정 조건은 증착 시간이 10분이며 박막의 두께가 ${\sim}1{\mu}m$ 일 때, 최적의 조건을 얻을 수 있었으며, 이 때의 자성 특성을 분석한 결과 ~2.45T의 포화 자화 값과 ~1.41T의 잔류 자화 값을 얻을 수 있었다.

  • PDF