• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.156-161
• /
• 2007

To develop array magnetic sensors, specular-type giant magnetoresistive- spin valve (GMR-SV) film of Glass/Ta(5)MiFe(7)/IrMn(10)NiFe(5)/$O_2$/CoFe(5)/Cu(2.6)/CoFe(5)/$O_2$/NiFe(7)/Ta(5)(nm) was deposited by using a high-vacuum sputtering system. One of 15 way sensors in the area of $8{\times}8mm^2$ was Patterned a size of $20{\times}80{\mu}m^2$ in multilayer sample by Photo-lithography. All of 15 sensors with Cu electrodes were measured a uniform magnetic properties by 2-probe method. The highest magnetic sensitivity of MR and output voltage measured nearby an external magnetic field of 5 Oe were MS = 0.5%/Oe and ${\triangle}$V= 3.0 mV, respectively. An easy-axis of top-free layers of $CoFe/O_2/NiFe$ with shape anisotropy was perpendicular to one of bottom-pinned layers $IrMn/NiFe/O_2/CoFe$. When the sensing current increased from 1 mA to 10 mA, the output working voltage uniformly increased and the magnetic sensitivity was almost stable to use the nano-magnetic devices with good sensitive properties.

• Journal of Sensor Science and Technology
• /
• v.9 no.1
• /
• pp.22-27
• /
• 2000

Amorphous FeCoSiB films with high saturation magnetostriction and excellent soft magnetic properties have been studied to evaluate their strain sensitivity. Films were subjected to a strain by bending of their substrates, which caused a change in the magnetic anisotropy of films via magnetoelastic coupling. Films were exhibited a figure of merit $F=({\Delta}{\mu}/{\mu})/{\varepsilon}$ (change in film permeability $\mu$ per unit strain $\varepsilon$) of $1.2{\times}10^5$, which is comparable with that of amorphous ribbons. To make a study of application of magnetostrictive films as strain sensor elements, we have prepared a micro-patterned film by means of the photolithography and ion milling processes. Impedance change in the patterned films, when strain was applied, was measured over the frequency range from 1 MHz to 1 GHz. Reflecting a large value of figure of merit F, a variation of 46% impedance of films was shown at 100 MHz frequency when a strain of $300{\times}10^{-6}$ was applied.

• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.1
• /
• pp.83-90
• /
• 1998

LPCVD를 이용하여 증착한 SiN과 ECR plasma CVD를 이용하여 증착한 SiC의 물 성과 적용가능성을 시험하였다. LPCVD로 증착된 SiN은 열처리 없이 저 응력의 박막형성이 가능했으며 가시광투과도 표면 평활도 역시 우수하였다. 탄성계수 값이 크지 않아 자성센서 의 지지구조로 사용할 경우 자기공명에 의한 진동을 크게 구속하지 않아 유리할것으로 기대 된다. 반면 ECR plasma CVD로 증착된 SiC는 SiN보다는 못하지만 다른 방법에 의해 증착 된 SiC에 비해서는 가시광 투과도 및 표면 평활도가 후수하므로 X-선 조사에 대한 안정성 과 더불어 X-선 마스크용 membrane으로서 사용이 적절할 것으로생각된다.

• Journal of the Korean Magnetics Society
• /
• v.22 no.5
• /
• pp.173-177
• /
• 2012

The multilayer structure of glass/Ta(5.8 nm)/NiFe(5 nm)/Cu(t nm)/NiFe(3 nm)/FeMn(12 nm)/Ta(5.8 nm) as typical GMR-SV (giant magnetoresistance-spin valve) films is prepared by ion beam sputtering deposition (IBD). The coercivity and magnetoresiatance ratio are increased and decreased for the decrease of Cu thickness when the thickness of nonmagnetic Cu layer from is varied 2.2 nm to 3.0 nm. It means that the decrease of non-magntic layer is effected to the interlayer exchange coupling of pinned layer and the spin configuration array of free layer. For experiment of detecting and dropping of magnetic beads we used the GMR-SV sensor with glass/Ta/NiFe/Cu/NiFe/FeMn/Ta structure. From the comparison of before and after for the dropping status of magnetic bead, the variations of MR ratio, $H_{ex}$, and $H_c$ are showed 0.9 %, 3 Oe, and 2 Oe, respectively. The fabrication of GMR-SV sensor was included in the process of film deposition, photo-lithography, ion milling, and MR measurement. Further, GMR-SV device can be easily integrated so that detecting biosensor on a single chip becomes possible.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.1
• /
• pp.81-89
• /
• 1999

The fabrication process for miniaturizing the Electronic Article Surveillance (EAS) sensor was studied using micromachining technique. Two types of sensor structure, free standing membrane type and diving beard type, were proposed and researched for establishing the fabrication process. The membrane type structure was easy to change the sensor shape but had the limitation for miniaturizing, because the size of the sensor depends on the silicon substrate thickness. The diving board type structure has the advantage of miniaturization and of free motion. Since the elastic modulus is not trio high, SiN film is expected to be adequate for the supporting membrane of magnetic sensor. The selectivity of $H_2O_2$for sputtered W with respect to Fe-B-Si, which was studded for magnetic sensor materials, was high enough to be removed after using as a protection layer. Therefore, the diving board type process using the silicon nitride film for the supporter of the sensor material and the sputtered W for protection layer is expected to be useful fur miniaturizing the Electronic Article Surveillance (EAS) sensor.

• Journal of the Korean Magnetics Society
• /
• v.23 no.6
• /
• pp.200-204
• /
• 2013

In this study, we have fabricated magnetoresistive sensors of $50{\mu}m{\times}50{\mu}m$ cross type by trilayer structure of antiferromagnetic/nonmagnetic/ferromagnetic. The magnetic signal and magnetic domain of this sensor is measured. The sensor hysteresis loop is not in symmetrical at 0 Oe. This is may be due to the exchange coupling between ferromagnetic layer and anti ferromagnetic layer. This exchange bias value is 20 Oe. The sensor signal is measured at between the applied magnetic field and current. The sensor signal is measured between the applied magnetic field and current at $20^{\circ}$ and $90^{\circ}$ angles. The sensitivity of sensor signals is $20{\mu}V/Oe$ and $7{\mu}V/Oe$ at $20^{\circ}$ and $90^{\circ}$ angles, respectively. In addition, this sensor is also applied for the detection of magnetic bacteria at $20^{\circ}$ angle. From these results, we calculate the stray field of single bacteria is to be $5{\times}10^{-5}$Oe.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.400-400
• /
• 2010

우리는 기본 진공 $10^{-11}\;Torr$의 UHV surface magneto-optical Kerr effect (SMOKE) 시스템을 quarter-wave plate를 사용하였던 기존의 방식에서 PEM (photo elastic modulator)를 사용하는 방식으로 장비의 기능을 향상시켰다. 기존 quarter-wave plate를 사용하는 방식의 경우 Kerr signal을 구하기 위해 편광자와 검광자를 수직으로 두어 광량을 0으로 만들어야 한다. 그러나 금속의 경우 대부분 가시광선 영역에서 큰 반사율 때문에 측정되는 광량이 편광자와 검광자를 거치면서 넓은 각도 범위에서 최소값을 갖기 때문에 정확한 영점을 잡는 데 한계가 있다. 이러한 단점을 해결하기 위하여 우리는 PEM을 이용한 위상변조방식을 사용하였다. 위상변조 방식은 Kerr signal과 관계된 양을 PEM을 이용하여 50 kH ($1{\omega}$)와 100 kH ($2{\omega}$)의 진동 주파수에 공조시키고 이를 Lock-in-amplifier를 사용하여 탐지하기 때문에 좋은 sensitivity를 얻을 수 있을 뿐 아니라 Kerr ellipticity와 Kerr rotation을 동시에 측정할 수 있다. 자화에 필요한 전자석은 순철로 된 코어를 제작하여 챔버에 부착하였고 10 A에서 최대 7 kOe의 고자장을 얻을 수 있어 포화자화가 큰 물질에 대해서도 필요한 자성영역까지 측정이 가능하게 하였다. 또 저온 측정을 위해 SMOKE 샘플 홀더를 개조하여 액체 질소를 이용하여 100 K 근방의 영역에서 온도를 제어할 수 있도록 저온 장치를 구성하였다. 여기에서 샘플 근처에 위차한 e-beam heater가 장착된 고온 부분과 액체 질소 냉각, 온도감지를 위한 센서, cartridge heater가 장착된 저온 부분을 sapphire plate로 분리하여 저온용 cartridge heater의 파손을 최소화하였다. 이러한 SMOKE 시스템을 구성한 후에 우리는 Fe/Cr(001)시스템의 자성특성에 대해 연구하였다. Fe/Cr 시스템은 Fe/Cr/Fe의 exchange coupling이나 bulk Cr의 복잡한 자성 특성 때문에 주목을 받아왔다. 이 연구에서 우리는 저온 및 상온에서 Cr(001) 단결정 위에 증착된 Fe 박막의 자성 특성을 보고한다.

• Journal of the Korean Magnetics Society
• /
• v.20 no.4
• /
• pp.129-133
• /
• 2010

Two-layered ferromagnetic alloy films (NiFe, CoFe) with a Conetic (NiFeCuMo) intermediately soft magnetic layer of different thickness were investigated to correlate the coercivity values and magnetization process with the strength of saturation field of hard axis. Thickness dependence of the $H_{EC}$ (coercivity of easy axis), $H_{HS}$ (saturation field of hard axis.), and X (susceptibility) of NiFe and NiFeCuMo thin films for the glass/Ta(5 nm)/[CoFe or NiFe(5 nm-t/2)]/NiFeCuMo(t = 0, 4, 6, 8, 10 nm)/[CoFe or NiFe(5 nm-t/2)]/Ta(5 nm) films prepared by the ion beam deposition method was measured. The magnetic properties $H_{EC}$, $H_{HS}$, and X of two-layered ferromagnetic CoFe, NiFe films with a NiFeCuMo intermediately super-soft magnetic layer were strongly depended on the thickness of NiFeCuMo layer. The value of the coercivity and magnetic susceptibility of the NiFeCuMo film decreased by 25% and doubled relative to that of the NiFe film.

• Journal of the Korean Magnetics Society
• /
• v.13 no.5
• /
• pp.193-197
• /
• 2003

To materialize the magnetoelastic devices, such as a highly functional sensor and a signal processing device, using the Fe base amorphous film which has both excellent soft magnetic and magnetostrictive properties, in this study, a new method to control the magnetic anisotropy of a highly magnetostrictive film using bias stress has been proposed and tested. The film pattern, which was stressed by its substrate bending, was subjected to annealing for relieving its stress. Successively, the compressive stress occurred by flattening the substrate was formed in the pattern. With the introduction of the residual compressive stress, the magnetization of the film pattern was aligned in the transverse direction through magnetoelasic coupling. The magnetic domain structure and magnetization curve of the film pattern of which magnetic anisotropy was controlled by the proposed method were presented to verify the availability of the method.

• Journal of the Korean Magnetics Society
• /
• v.8 no.2
• /
• pp.74-78
• /
• 1998

High quality single cystal Bi, Gd : YIG films have been grown on GCMZGG wafers by LPE techniques. The magnetic, magneto-optic and sensor properties of the films have been investigated. The films showed high linearity with almost no hystersis, saturaton Faraday rotation angle of 45$^{\circ}$, saturation field of about 1.1 kOe, Verdet constant of 5.6$^{\circ}$ /(Oe, cm) at room temperature, and temperture coefficient of Verset constant of 0.0056$^{\circ}$ /(Oe, cm, $^{\circ}C$) in the range of 0 $^{\circ}C$~100 $^{\circ}C$. The sensor made out of the film exhibited highly linear signal in the range of 3 A-300 A.