• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.225-231
• /
• 2000

The crystallographic and magnetic properties of the sample F $e_{0.8}$ $Co_{0.18}$(BN)$_{0.02}$ synthesized by microwave arc-melting with the maximum power of 3.5 kW have been studied by the methods of an X-ray diffraction and the measurement of the magnetic hysteresis using the vibrating sample magnetometer at room temperature. The samples were prepared in a form of pellet pressed under the pressure of 9,000 N/c $m^2$, rolled coldly, and treated with the different temperatures. The X-ray diffraction pattern of pelleted sample shows that the crystal structure of the sample is bcc as same as that of Fe with a good uniformity. The X-ray diffraction pattern shows that a residual stress, which exists in the sample, is eliminated by final 90$0^{\circ}C$ annealing. As rolling rate and heat treatment temperature increases, the saturation magnetization and the remanence of the samples increase whereas the coercivity of the samples shows decrease. Also the saturation magnetization and the remanence of the samples were affected by rolling rate and rolling direction than heat treatment temperature, but the coercivity of the samples was affected by rolling rate and direction as well as heat treatment temperature. This means that a domain wall motion is easy due to elimination of a residual stress and an inclusion which exists in the sample by rolling and heat treatment and a local induced-magnetization easy axis was also formed to parallel to the rolling direction due to creation of the like-atom pairs across the slip plane by rolling......

• Journal of the Korean Magnetics Society
• /
• v.13 no.4
• /
• pp.155-159
• /
• 2003

We report on the annealing effect and ferromagnetic characteristics of Zn$_{0.7}$Mn$_{0.3}$O film prepared by sol-gel method on the silicon (100) substrate using field emission-scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), X-ray diffractometry (XRD) and superconducting quantum interference device (SQUID) magnetometry. Magnetic measurements show thatZn$_{0.7}$Mn$_{0.3}$O films exhibit ferromagnetism at 5 K revealing the coercive field of ∼110 Oe for as grown sample and 360, 1035 Oe for samples annealed at 700, 800 $^{\circ}C$, respectively. Our experimental evidence suggests that ferromagnetic precipitates of a manganese oxide may be responsible for the observed ferromagnetic behaviors of the film.he film.

• Journal of the Korean Magnetics Society
• /
• v.16 no.2
• /
• pp.140-143
• /
• 2006

Single crystalline $CoFe_2O_4$ thin films on (100) MgO substrates were fabricated using a rf magnetron sputtering method. The deposited films were investigated for their crystallization by X-ray diffraction, Rutherford back-scattering spectroscopy and field emission scanning electron microscopy. When a cobalt ferrite film was deposited at the substrate temperature of $600^{\circ}C$, squared grains of about 200 nm were uniformly distributed in the film. However, the grains became irregular and their sizes also varied from 30 to 150 nm when the substrate temperature was $700^{\circ}C$. Hysteresis loops of a film deposited at $600^{\circ}C$ showed that the magnetically easy axis of the film was perpendicular to the substrate surface. Except for the squareness ratio, magnetic properties of the cobalt ferrite films grown by the present rf sputtering method were as good as those of the films prepared by a laser ablation method: The in-plane and perpendicular coercivities were 283 and 6800 Oe, respectively. As the thickness of the deposited film increased twice, the saturation magnetization became double but the coercivity remained unchanged. However, deposition of the Co ferrite films with a higher rf powder decreased the squareness ratio and the perpendicular coercivity of the films.

• Journal of the Korean Institute of Telematics and Electronics T
• /
• v.36T no.4
• /
• pp.38-46
• /
• 1999

This paper discusses the repetitive tracking control method for a coarse-fine actuator. The proposed system is composed of a magnetic linear drive as a coarse actuator and a piezoelectric linear positioner as a fine actuator. In particular, nonlinear friction in a magnetic linear drive and hysteresis characteristic of a piezoelectric linear positioner are modeled first. The feedback linearization loop uses these models in tracking position control. The control strategy is then further extended to include a repetitive control algorithm in tracking periodic reference inputs. This repetitive controller is implemented on the existing PID controller augmented with feedback linearization loop. The experimental results show that performance in tracking sinusoidal waveforms is noticeably improved by augmenting a PID controller with feedback linearization loop and a repetitive controller together.

• Analytical Science and Technology
• /
• v.8 no.2
• /
• pp.195-203
• /
• 1995

Carbon and small amounts of alloying elements were added in Fe-5.7% Al ferromagnetic damping alloy. The specific damping capacities(SDC) of these alloys were investigated in relation to the grain size and the magnetic hysteresis loops. The behavior of carbon was analysed by XRD and EDS. These alloys showed characteristic damping nature of ferromagnetic damping materials. The alloying elements decreased SDC and especially the carbon was remarkable. The SDC was observed to be not related with the grain size but with the magnetic hysteresis loop area. The remarkable decrease of SDC by carbon addition was attributed to the locking migration of $90^{\circ}$ magnetic domain wall by the interstitial carbon in Fe-Al solid solution. However, the carbides also seems to decrease the SDC.

• Polymer(Korea)
• /
• v.30 no.5
• /
• pp.412-416
• /
• 2006

The superparamagnetic nanoparticles were prepared by coprecipitation of $FeCl_3$ and $Na_2SO_3$ with $NH_4OH$ and the surface charge on hydroxyl group by chemisorption was changed depending on pH. We studied correlation between surface charge of magnetite and pH. Using this correlation the properties of poly (acrylic acid) (PAAc) hydrogel embedded with magnetite was studied. The magnetite was characterized by XRD, AFM. and FTIR. The zeta-potential of magnetite was influenced by pH: great positive charge was shown high under the pH 4 and isoelectric point was found at pH 7. The hydrogen bond formed by combining oi PAAc hydrogel and magnetic colloid under pH 4 caused tensile strength to increase, while swelling and elongation at break to decrease. The result confirmed that the magnetic moment was increased proportionally to the content of magnetite.

• Journal of Engineering Education Research
• /
• v.13 no.1
• /
• pp.78-86
• /
• 2010

Training Curriculum Integrated Information Network is allowed to searching the all curriculums and courses related with training but also is a one stop handling integrated learning system to cover a course registration, learning and analysis of learning performance. Through developing and managing the Training Curriculum Integrated Information Network, it is available to get the various curriculum thus it is for trainers able to enforce the self oriented course choice and then high quality of training could be proposed by the diverse training curriculums and competitions. To manage Training Curriculum Integrated Information Network more effectively, active public relations marketing activities, high reliable correct information service and rich contents are required. It is essential to manage the learner and learning contents supplier, stable financial resources, personal security issue and protecting a copyright of training curriculum to be a successful network system.

• Resources Recycling
• /
• v.11 no.5
• /
• pp.34-38
• /
• 2002

To minimize the size of transformer volume, the operating frequency of ferrites cores increasing. The power loss of Mn-Zn ferrites comprises hysteresis loss, eddy current loss and residual loss. In the range more then 500 KHz, the total power loss is mainly due to the residual loss. The power loss increase with the frequency 3rd power. To minimize residual loss as well as eddy current loss, the microstructure should have small grain and high density, It should be noted that as the product of resonance frequency and static permeability increase, the power loss decrease at high frequency region.

• The Journal of the Korea Contents Association
• /
• v.17 no.7
• /
• pp.538-545
• /
• 2017

Moisture evaporates, when concrete is exposed to fire, not only at concrete surface but also at inside the concrete to adjust the equilibrium and transfer properties of moisture. The equilibrium properties of moisture are described by means of water vapor sorption isotherms, which illustrate the hysteretical behavior of materials. In this paper, the prediction method of the moisture distribution inside the concrete members at fire is presented. Finite element method is employed to facilitate the moisture diffusion analysis for any position of member. And the moisture diffusivity model of high strength concrete by high temperature is proposed. To demonstrate the validity of this numerical procedure, the prediction by the proposed algorithm is compared with the test result of other researcher. The proposed algorithm shows a good agreement with the experimental results including the vaporization effect inside the concrete.

• Progress in Superconductivity
• /
• v.6 no.1
• /
• pp.84-88
• /
• 2004

The polycrystalline superconductor $SmBa_2$$Cu_3$$O_{x}$ is fabricated, and intergranular magnetic properties are investigated using the critical state model, from which some useful parameters such as the critical current density and the intergranular volume fraction are obtained. The curve fitting for M-H hysteresis loop shows that the intergranular critical current density of $SmBa_2$$Cu_3$$O_{x}$ / decreases in the form of ($1-T/T_{c}$ )$^{1.5}$ . The intergranular volume fraction is influenced by granular morphology. From SEM image, the grains of $SmBa_2$$Cu_3$$O_{x}$ are found to be randomly shaped. This mean:; that the intergranular volume fraction of $SmBa_2$$Cu_3$$O_{x}$ / should be smaller than those of superconductors, of which grains are plate-shaped such as Tl-based superconductor.