• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.125-131
• /
• 2011

Objectives: The purpose of this study was to evaluate the effect of surface treatment of FRC-Post on bonding strength to resin cements. Materials and Methods: Pre-surface treated LuxaPost (DMG), Rely-X Fiber Post (3M ESPE) and self adhesive resin cement Rely-X Unicem (3M ESPE), conventional resin cement Rely-X ARC (3M ESPE), and Rely-X Ceramic Primer (3M ESPE) were used. After completing the surface treatments of the posts, posts and resin cement were placed in clear molds and photo-activation was performed. The specimens were sectioned perpendicular to the FRC-Post into 2 mm-thick segments, and push-out strength were measured. The results of bond strength value were statistically analyzed using independent samples t-test and oneway ANOVA with multiple comparisons using Scheffe's test. Results: Silanization of posts affect to the bond strength in LuxaPost, and did not affect in Rely-X Fiber Post. Rely-X ARC showed higher value than Rely-X Unicem. Conclusions: Silanization is needed to enhance the bond strength between LuxaPost and resin cements.

• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.153-157
• /
• 2009

The resin matrix in the dental composite is generally composed of 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) as a base resin and triethylene glycol dimethacrylate (TEGDMA) as a diluent for the reduction of viscosity. The applications of dental composite were often limited in dentistry due to the relatively large amounts of volumetric shrinkage during polymerization and water uptake caused by the addition of TEGDMA to the resin matrix. In this study, in order to solve problems stemmed from the TEGDMA by reducing amount of diluent added to resin matrix, diethylene glycol dimethacrylate (DEGDMA) and ethylene glycol dimethacrylate (EGDMA) were explored as new diluents. A decrease in the volumetric shrinkage and an increase in the mechanical strength were observed by replacing TEGDMA in the dental composite to DEGDMA (or EGDMA). Reduction in the mechanical strength of the dental composite containing DEGDMA (or EGDMA), was not serious in comparison with that of the dental composite containing TEGDMA after water uptake.

• Journal of Oral Medicine and Pain
• /
• v.30 no.2
• /
• pp.269-276
• /
• 2005

This in vitro study evaluated the influence of a flowable composite resin on the tensile bond strength of resin to enamel and dentin treated with Er:YAG laser and diamond bur. 96 Buccal enamel and mid-coronal dentin were laser-irradiated using an Er:YAG laser and treated with diamond bur. Each groups(48) were divided two small groups depends on acid-etching procedure. Light-cure flowable resin(Metafil Flo) and self-cure resin(Clearfil FII New Bond) were used in this study. After surface etching with 37% phosphoric acid and the application of an adhesive system, specimens were prepared with a hybrid composite resin. After 24hours storage in distilled water at 37$^{\circ}C$, all samples were submitted to the tensile bond strength evaluation, using a universal testing machine(Z020, Zwick, Germany). The obtained results were as follows: 1. TBS of acid-etching group were higher than those of non-etching group in both enamel and dentin treated with Er:YAG laser and diamond bur. Laser 'conditioning' was clearly less effective than acid-etching. Moreover, acid etching lased enamel and dentin significantly improved the microTBS of M-Flo. 2. In enamel, TBS of laser-irradiated group were lower than those of bur-prepared group. However, in flowable resin subgroup, there were not differed those between two groups in dentin. 3. In laser-treated group, TBS of flowable composite resin were higher than those of self-curing resin in dentin, however, there was no difference in enamel. From this study, we can conclude that the self- and light-cure composite resin bonded significantly less effective to lased than to bur-cut enamel and dentin, and that acid-etch procedure remains mandatory even after laser ablation. We suggest that Er:YAG laser was useful for preparing dentin cavity with flowable resin filling.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.4
• /
• pp.422-428
• /
• 2010

Giomer is fluoride-releasing, resin-based dental materials that comprise PRG(pre-reacted glass ionomer) filler. The purpose of this study was to evaluate the shear bond strength of Giomer using self-etching primer systems to bovine dentin. Bovine incisors were mounted in self-curing orthodontic resin and the facial surfaces were wet ground on SIC paper to expose the dentin. Total 100 samples were made and divided randomly into 4 groups, Giomer group(I), Composite resin group(II) and Compomer group(III), Giomer and single bottle adhesive group(IV). The shear bond strengths of 25 samples per each group were measured using universal testing machine. And data were analyzed statistically with One-way ANOVA and Scheffe test. Giomer group(I) showed the significantly higher bond strength than Compomer group(III)(p<0.05). There was no significant difference between Giomer group(I) and Composite resin group(II)(p>0.05). And there is no significant difference between gourp(I) and group(IV). Based on the results of present study, the use of Giomer as an esthetic restorative material for primary teeth might be justified. It is considered that more study about the fluoride releasing ability is needed to evaluate the anticariogenic effect of giomer.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.1
• /
• pp.8-15
• /
• 2010

Purpose: The purpose of this study was to evaluate the effect of various methods of dentin bonding agent application and air abrasion pretreatment on microtensile bond strength between dentin and resin, using a self-etching adhesive system. Material and methods: Thirty freshly extracted human molars were obtained and divided into 6 groups of 5 teeth. A 2-step self etching adhesive system (Clearfil SE Bond) was used for all groups. The control specimens were prepared using a direct immediate bonding technique. The delayed dentin sealing specimens were prepared using an indirect approach without dentin prebonding. The immediate dentin sealing specimens were prepared using dentin prebonding immediately following preparation. Immediate dentin sealing teeth and delayed dentin sealing teeth had provisional restorations using Fermit for two weeks. Then all specimens of each group were divided into two groups of three, depending on air abrasion pretreatment. Composite "crowns" were incrementally built on and specimens were stored in water for 24 hours. All teeth were prepared for a microtensile bond strength test. Bond strength data were analyzed with a one-way ANOVA test, and post hoc comparison was done using the Scheffe's test. Results: The mean microtensile bond strengths of all groups were not statistically different from each other. Conclusion: When preparing teeth for indirect restorations, IDS and DDS with Clearfil SE bond, have no difference on the microtensile bond strength between dentin and resin. Air abrasion pretreatment did not affect the microtensile bond strength when using IDS and DDS with Clearfil SE bond.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.1
• /
• pp.69-79
• /
• 2003

The purpose of this present study was to develop a new way of self-curing acrylic resin, using commercially available polyphosphate, Calgon, which is known to be antimicrobial and safe. For the study, polyphosphate(polyP) was blended with acrylic powder and devided into four groups as follows: no polyP(control), 1% polyP, 2% polyP, and 3% polyP. For the experiment, Streptococcus mutans GS5, Streptococcus sobrinus 6715, Streptococcus gordonii G9B and Challis, Porphyromonas gingivalis 2561, and Candida albicans ATCC 90027 were used. Resin specimens in each group were tested in vitro for the purpose of investigating the effect of polyP on the microbial attachment, growth and hydrophobicity of the resin surface. The results were as follows. 1. PolyP added to the acrylic resin decreased attachment of S. mutans GS5, S. sobrinus 6715, S. gordonii G9B. The greater binding inhibition was found in acrylic resin polymerized with polyP at higher concentrations. 2. The addition of polyP to acrylic resin failed to significantly affect the growth of the tested microorganisms. 3. The addition of polyP to acrylic resin seemed to reduce hydrophobicity of the acrylic resin. PolyP in acrylic resin does not seem to exert a direct antibacterial activity, but rather inhibit attachment of oral bacteria, especially mutans streptococci to saliva-coated acrylic resin. The acrylic resin reduces attachment of streptococci may be due to the decreased hydrophobicity caused by polyP added to the resin. PolyP may be included to acrylic resin to inhibit dental caries which often occurs when removable acrylic resin appliance is placed.

• Journal of Oral Medicine and Pain
• /
• v.37 no.4
• /
• pp.221-225
• /
• 2012

Disc dislocation without reduction, as known as closed lock, is a clinical condition in which the disc is dislocated from the condyle and does not return to normal position during condylar movement When the condition of disc dislocation without reduction is acute, the initial therapy should include an attempt to reduce or recapture the disc by manual manipulation. When patients report a history of being locked for 1 week or less, manual manipulation is usually successful. In patients with a longer history, success rate tends to decrease rapidly. If the disc has been successfully recaptured, placing an anterior positioning appliance is recommended to prevent clenching on the posterior teeth, which would likely redislocated the disc. But it is hard to make an appliance immediately in the clinic because it takes too much time. And making an appliance using self-curing acrylic resin is not very popular because of its discomfort by odor and working time. Also, if the patient has resin allergy or is under orthodontic treatment, or if it is impossible to control behavior of the patient, it has been restricted to make an appliance immediately. Therefore, to supplement this disadvantages, we tried to confirm about successful short term use of temporary anterior positioning splint made by using putty impression material after manual manipulation in this study.

• Polymer(Korea)
• /
• v.28 no.5
• /
• pp.426-432
• /
• 2004

To reduce volumetric shrinkage of the commercially available polymeric dental composite during curing reaction, (2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane) (bis -GMA) derivatives, i.e., (2,2-bis[3-methyl, 4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propan) (DMBis-GMA) and (2,2-his [3,5-dimethyl ,4- (2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane) (TMBis-GMA) were synthesized and then new dental composite resin composed of Bis-GMA derivatives, diluent, spiro orthocarbonate (SOC), and inorganic filler was produced. Among the Bis-GMA derivative/Bis-GMA derivative/diluent mixtures, Bis-GMA/ TMBis-GMA/TEGDMA mixture exhibited the lowest volumetric shrinkage. Volumetric shrinkage of this mixture was further reduced by adding SOC. Volumtric shrinkage of dental composite prepared from commercially available resin monomer mixture was $2.5\%$, while that prepared from resin monomer mixture having minimum volumetric shrinkage was reduced to $0.7\%$. Mechanical strength of this dental composite was nearly the same with that of commercial products but the time required for the curing reaction was retarded.

• Polymer(Korea)
• /
• v.27 no.5
• /
• pp.493-501
• /
• 2003

Poly(methyl methacrylate) (PMMA) particles, denture base resin, were synthesized by suspension polymerization through control of polymerization conditions (stabilizer concentration, co-monomer concentration, and the agitation speed) and evaluated changes in molecular weight and particle size. We also investigated their mechanical properties of compression-molded samples which were from synthesized polymer powder mixed with methyl methacrylate (MMA) solution. under the condition of volumetric ratio as 2:1(PMMA powder and MMA solution). The results shows that the mechanical properties were mainly affected by particle size over 100 ${\mu}$m (in particle size) and by molecular weight under 100 ${\mu}$m (in particle size). From these results, we concluded that the most appropriate particle size of PMMA powder for heat-cured denture base resins is around 100 ${\mu}$m. and its molecular weight is around 300000 (M$\sub$n/).

• Korean journal of food and cookery science
• /
• v.18 no.6
• /
• pp.557-561
• /
• 2002

The changes in some chemical and physical properties of fresh or rancid soybean oil by the treatment with sweet potato, potato, burdock, and carrot were investigated. The results of the study were as follows: The specific gravity of the soybean oil increased by heating and decreased by the addition of sweet potato, burdock and carrot into the oil. The chromaticity of soybean oil increased by heating and treatment with above vegetables having antioxidant activity. To investigate the antioxidant effects of above vegetables during heating, anisidine value (AV) and DPPH (1,1-diphenyl-2-picrylhydrazyl) electron donating ability were measured. The AV of oil decreased by heating with sweet potato in fresh or rancid oil. The DPPH value decreased by heating with sweet potato and carrot, of which the antioxidant activity were similar to that of 0.02 ∼ 0.05 mg of dl-${\alpha}$ -tocopherol.