EFFECTS OF POLYPHOSPHATE MIXED IN ACRYLIC RESIN ON THE ATTACHMENT AND GROWTH OF ORAL BACTERIA

Acrylic Resin에 혼합된 Polyphosphate가 미생물의 부착 및 성장에 미치는 영향

The purpose of this present study was to develop a new way of self-curing acrylic resin, using commercially available polyphosphate, Calgon, which is known to be antimicrobial and safe. For the study, polyphosphate(polyP) was blended with acrylic powder and devided into four groups as follows: no polyP(control), 1% polyP, 2% polyP, and 3% polyP. For the experiment, Streptococcus mutans GS5, Streptococcus sobrinus 6715, Streptococcus gordonii G9B and Challis, Porphyromonas gingivalis 2561, and Candida albicans ATCC 90027 were used. Resin specimens in each group were tested in vitro for the purpose of investigating the effect of polyP on the microbial attachment, growth and hydrophobicity of the resin surface. The results were as follows. 1. PolyP added to the acrylic resin decreased attachment of S. mutans GS5, S. sobrinus 6715, S. gordonii G9B. The greater binding inhibition was found in acrylic resin polymerized with polyP at higher concentrations. 2. The addition of polyP to acrylic resin failed to significantly affect the growth of the tested microorganisms. 3. The addition of polyP to acrylic resin seemed to reduce hydrophobicity of the acrylic resin. PolyP in acrylic resin does not seem to exert a direct antibacterial activity, but rather inhibit attachment of oral bacteria, especially mutans streptococci to saliva-coated acrylic resin. The acrylic resin reduces attachment of streptococci may be due to the decreased hydrophobicity caused by polyP added to the resin. PolyP may be included to acrylic resin to inhibit dental caries which often occurs when removable acrylic resin appliance is placed.

자가중합형 아크릴릭 레진에 polyp를 혼합하지 않은 대조군, 그리고 레진 분말에 대한 polyP(사슬길이 13과 18의 혼합물인 Calgon)의 무게비를 1%로 혼합한 polyP 1%군, 2% 혼합한 polyP 2%군 및 3% 혼합한 polyP 3%군으로 분류하여 경화시킨 후, 경화된 각각의 레진과 실험균주 S. mutans GS5, S. sobrinus 6715, S. gordonii G9B및 Challis, 그리고 P. gingivalis 2561과 Candida albicans ATCC90027을 대상으로 레진표면에 대한 미생물들의 부착의 정도, 성장 억제효과 및 접촉각의 변화를 관찰하여 그 결과로 미루어 아크릴릭 레진에 포함된 polyP는 구강 미생물에 대해 직접적으로 강한 항균 효과를 나타내지는 않는 것으로 판단되나 미생물의 부착 특히 우식원인균인 mutans streptococci의 부착을 방해하는 것으로 가늠되며, 이는 polyP의 첨가에 의한 아크릴릭 레진 표면에서 일어난 소수성의 변화가 일부 관여하는 것으로 여겨진다. PolyP가 혼합된 아크릴릭 레진의 장착은 일반적인 아크릴릭 레진으로 제작된 가철성 장치를 장착한 후 나타날 수 있는 우식 이환의 가능성을 감소시킬 수 있는 임상적 적용 가능성을 제시하였다고 여겨진다.