• The Journal of Korean Academy of Prosthodontics
• /
• v.56 no.3
• /
• pp.199-205
• /
• 2018

Purpose: This study evaluated the effect of nonthermal plasma treatment on the bond strength of autopolymerizing relining resin to the injection molded thermoplastic denture base resins (TDBRs) with different surface treatments. Materials and methods: Acrylic Resin (Acrytone), Polyester (Estheshot-Bright), Polyamide (Valplast) and Polypropylene (Weldenz) were subjected to various surface treatments: No treatment, Nonthermal plasma, Sandblasting, Sandblasting and nonthermal plasma. Specimens were bonded using an autopolymerizing relining resin. Shear bond strength was tested using universal testing machine with crosshead speed of 1 mm/min. Statistical analysis by two-way analysis of variance with Tukey's test post hoc was used. Results: Acrytone showed significantly higher shear bond strength value among other TDBR group while Weldenz had the lowest. The sandblasting and nonthermal plasma condition had significantly higher shear bond strength value in all of the resin groups (P < .05). Conclusion: The use of nonthermal plasma treatment showed limited effect on the shear bond strength between TDBRs and relining resin, and combination of nonthermal plasma and sandblasting improved the shear bond strength between TDBR and reline material.

• The Journal of Korean Academy of Prosthodontics
• /
• v.60 no.3
• /
• pp.231-238
• /
• 2022

Purpose. This study aimed to investigate the effect of different veneering methods on the tensile bond strength between polyetherketoneketone (PEKK) and denture base resins. Materials and methods. A total of 80 PEKK T-shaped specimens were fabricated and the primer (Visio.link) was applied after airborne-particle abrasion with 110 ㎛ alumina oxide powder. According to the veneering method, the specimens were divided into four groups (n = 20) to be veneered with the gingival colored packable photopolymerized composite resin (SR Adoro); flowable photopolymerized composite resin, (Crea.lign); heat-polymerized resin (Vertex); and self-polymerized resin (ProBase Cold). Each group was divided into two subgroups (n = 10) according to the artificial thermal aging. After the tensile bond strength measurement via universal testing machine, the fracture sections of all specimens were observed. Two-way ANOVA and Tukey's HSD post hoc test were used for the statistical analysis (α = .05). Results. The results of the two-way ANOVA showed statistically significant differences in the tensile bond strength according to the veneering method and artificial thermal aging of denture base resins (P<.001). The highest tensile bond strength showed in the packable photopolymerized resin group before and after the artificial thermal aging. The lowest tensile bond strength showed in the heat-polymerized resin group. The mixed and adhesive fracture showed in all groups. Conclusion. The veneering method and artificial thermal aging can influence in the tensile bond strength between the resin and PEKK. The artificial thermal aging can reduce the tensile bond strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.318-324
• /
• 2015

Purpose: This study compared shear bond strengths of five self-adhesive cements with phosphate monomer to zirconium oxide ceramic with and without airborn particle abrasion. Materials and methods: One hundred zirconia samples were air-abraded ($50{\mu}mAl_2O_3$). One hundred composite resin cylinders were fabricated. Composite cylinders were bonded to the zirconia samples with either Permacem 2.0 (P), $Clearfil^{TM}$ SA Luting (C), $Multilink^{(R)}$ Speed (M), $RelyX^{TM}$ U200 Automix (R), G-Cem $LinkAce^{TM}$ (G). All bonded specimens were stored in distilled water ($37^{\circ}C$) for 24 h and half of them were additionally aged by thermocycling ($5^{\circ}C$, $55^{\circ}C$, 5,000 times). The bonded specimens were loaded in shear force until fracture (1 mm/min) by using Universal Testing Machine (Model 4201, Instron Co, Canton, MA, USA). The failure sites were inspected under field-emission scanning electron microscopy. The data was analyzed with ANOVA, Tukey HSD post-hoc test and paired samples t-test ($\alpha$=.05). Results: Before and after thermocycling, $Multilink^{(R)}$ Speed (M) revealed higher shear-bond strength than the other cements. G-Cem $LinkAce^{TM}$ (G) showed significantly lower bond strengths after thermocycling than before treatment (P<.05), but the other groups were not significantly different (P>.05). Conclusion: Most self-adhesive cements with phosphate monomer showed high shear bond strength with zirconia ceramic and weren't influenced by thermocycling, so they seem to valuable to zirconia ceramic bonding.

• Journal of Biomedical Engineering Research
• /
• v.23 no.2
• /
• pp.139-145
• /
• 2002

Bis-GMA, 2.2-bis[p(2-hydroxy-3-methacryloyloxypropokyl)phenyl]Propane, is an essential component as a multifunctional methacrylate prepolymer in the light-curable polymeric dental composite resins. Two hydroxyl groups of the Bis-GMA molecule are considered to induce water sorption of the photocured composite resin in a mouth, resulting in gradual long-term deterioration of aesthetics and mechanical properties of the composite resins. In this study, some additives such as light stabilizer and antioxidant were added to composite resins to promote durability and storage stability of the last product. First of all, color change increased as a light stabilizer. Tinuvin P, was added to the composed resins and color stability was improved as an antioxidant, Irganox 245, was added to ones. In addition, when Tinuvin P and Irganox 245 were added together to the composed resins. the color stability was enhanced and mechanical properties such as diametral tensile strength before and after acceleration tests were also not greatly decreased. Therefore, when 0.5 weight Percent of Tinuvin P and 0.1 weight percent of Irganox 245 were added together to dental composite resins. the durability and color stability were enhanced, and furthermore the storage stability was also improved for the composed resins.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.26 no.2
• /
• pp.296-309
• /
• 1999

Autopolymerized resin facilitates a more rapid and easier means for the construction of removable orthodontic appliances than heat cured resin. But many reports reveal that more unreacted monomer is found in autopolymerized resin. It is very important to achieve maximum degree of polymerization because if polymerization is inadequate, high level of unreacted monomer has been shown to adversely affect mechanical and physical properties, and also the question of allergy or toxicity to methylmethacrylate must be considered. The purpose of this study was to compare the degree of polymerization according to curing method and curing time. Five groups were desinged ; Group 1 was polymerizied at room temperature($28^{\circ}C$) ; Group 2 in $28^{\circ}C$ water ; Group 3 in $28^{\circ}C$ water under 30psi pressure ; Group 4 in $43^{\circ}C$ water ; Group 5 in $43^{\circ}C$ water under 30psi pressure for 10 minutes, 1 hour 12 hours, 1 day and 3 days. The degree of polymerization was measured by means of Fourier Transform Infrared spectroscopy. The results were as follows: 1. The degree of polymerization increased constantly in accordance with curing time in all groups and after curing for 10 minutes, Group 1 showed significantly higher degree of polymerization after 12 hours and Group 2, Group 3, Group 4, Group 5 after 1 hour(p<0.05). 2. The degree of polymerization decreased in the order of Group 5, Group 4, Group 3, Group 2, Group 1 except when the curing time was 1 hour and 12 hours(p<0.05). 3. The degree of polymerization of Group 4, Group 5 cured at $43^{\circ}C$ showed significantly higher degree of polymerization than Group 2, Group 3 at $28^{\circ}C$ except when the curing time was 1 day(p<0.05). 4. Among Group 2, Group 3 and Group 4, Group 5, the pressure had no effect on polymerization except when the curing time was 12 hours(p<0.05). 5. Between Group 1 and Group 2, the method of storage had no effect on polymerization except when the curing time was 1 hour(p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.33 no.4
• /
• pp.389-396
• /
• 2008

The purpose of this study was to evaluate the color stability of resin cements with accelerated test. Four dual curing resin cements: Panavia-F (KURARAY). Duolink (BISCO), Variolink-II (Ivoclar Vivadent), and RelyX Unicem (3M ESPE) and 1 self curing resin cement: Resiment CE (j. l. Blosser) were used in this study. In control group, Gradia Anterior (GC) composite resin and Tescera Dentin (Bisco) indirect composite were used. Ten disk shape specimens were made from each resin cement. The specimens were subjected to an accelerated aging process in a refrigerated bath circulator at 60$^{\circ}C$ for 15 and 30 days. Spectrophotometric analyses were made before and after 15 days and 30 days of accelerated aging time. The color characteristics ($L^*,\;a^*,\;b^*$) and the color difference (${\Delta}E^*$) of the specimens before and after immersion were measured and computed. Regardless of type of the resin cements, $L^*$ value was decreased and $a^*$ value was increased, but there were no significant difference. But $b^*$ value was increased significantly (p < 0.05). Tescera inlay showed least color change (p < 0.05), but Gradia showed notable color change after 15 days. After 30 days on accelerated aging, ${\Delta}E^*$ value was increased (Panavia-F < Variolink-II < Resiment CE < Duolink < Unicem) (p < 0.05). but there were no significant difference among Panavia-F, Variolink-II, and Resiment CE groups. After 30 days of accelerated aging, ${\Delta}E^*$ value of all resin cements were greater than 3.0 and could be perceived by the human eye.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.46 no.3
• /
• pp.274-282
• /
• 2019

The purpose of this study was to evaluate effect of saliva decontamination procedures on microtensile bond strength (MTBS) of 1-step self-etching adhesives to dentin of primary posterior teeth. 63 sound primary-posterior teeth were randomly divided into 3 groups according to different kinds of 1-step self-etching adhesives: $Scotchbond^{TM}$ Universal Adhesive (SBU), All-Bond $Universal^{(R)}$ (ABU), and $Tetric^{(R)}$ N Bond Universal (TBU). Each group was randomly categorized into 7 subgroups: (I) application of adhesive without saliva contamination (control); (II - IV) contamination by saliva before photopolymerization; (V - VII) contamination by saliva after photopolymerization; (II, V) decontamination by drying; (III, VI) decontamination by washing and drying; (IV, VII) decontamination by washing, drying, and reapplication of adhesive. All samples were cut into the blocks. At least 15 blocks were tested for each subgroup. For SBU and ABU, the MTBS values of subgroups (I, IV, VII) were significantly higher than those of subgroups (II, III, V, VI). For TBU, the MTBS values of subgroups (I, IV) was significantly higher than those of subgroup (II, III, V, VI). The MTBS of 3 adhesives was reduced by saliva contamination. The adhesive strength on dentin of primary posterior teeth was restored by reapplication of the adhesives after washing and drying.

• Restorative Dentistry and Endodontics
• /
• v.35 no.6
• /
• pp.486-491
• /
• 2010

Objectives: This study examined the effect of 2% chlorhexidine on the ${\mu}TBS$ of a direct composite restoration using one-step self-etch adhesives on human dentin. Materials and Methods: Twenty-four extracted permanent molars were used. The teeth were assigned randomly to six groups (n = 10), according to the adhesive system and application of chlorhexidine. With or without the application of chlorhexidine, each adhesive system was applied to the dentin surface. After the bonding procedure, light-cure composite resin buildups were produced. The restored teeth were stored in distilled water at room temperature for 24 hours, and then cut and glued to the jig of the microtensile testing machine. A tensile load was applied until the specimen failed. The failure mode was examined using an operating microscope. The data was analyzed statistically using one-way ANOVA, Student's t-test (p < 0.05) and Scheffet's test. Results: Regardless of the application of chlorhexidine, the Clearfil $S^3$ Bond showed the highest ${\mu}TBS$, followed by G-Bond and Xeno V. Adhesive failure was the main failure mode of the dentin bonding agents tested with some samples showing cohesive failure. Conclusions: The application of 2% chlorhexidine did not affect the ${\mu}TBS$ of the resin composite to the dentin using a one-step self-etch adhesive.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.4
• /
• pp.437-444
• /
• 2009

The purpose of this study was to evaluate the physical properties of different automixing resin cements and the shear bond strength on dentin. For this study, two self-adhesive automixing resin cement(Rely-X Unicem(3M ESPE, St. Paul, USA), Embrace resin cement(Pulpdent, Oakland, USA)) and one chemical polymerizing resin cement(Resiment Ready-Mix(J.L.Blosser Inc., Liberty Missouri, USA)) were used. To evaluate the physical properties, compressive strength, diametral tensile strength and flexural strength were measured. The specimens were fabricated using Teflon mould according to manufacturers' instructions and stored for 24 hours in an atmosphere of 100% humidity. To evaluate the shear bond strength on dentin, each cements were adhered to buccal dentinal surface of extracted human lower molars in 2mm diameter. Physical properties and shear bond strengths were measured using universal testing machine(Z010, Zwick GmbH, Ulm, Germany) at a crosshead speed of 0.5mm/min. The physical properties and shear bond strength of different automixing resin cements were statistically analyzed and compared between groups using One-way ANOVA test and Schffe post-hoc test at the 95% level of confidence. The result shows that chemical polymerizing automixing resin cement represents the relatively higher physical properties and shear bond strength than self-adhesive automixing resin cements.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.29 no.1
• /
• pp.69-79
• /
• 2013

The aim of this study was to evaluate the effect of surface conditioning on the shear bond strength of zirconium-oxide ceramic to resin cement. A total of 120 disk-shaped zirconium-oxide ceramic blocks(3-TZP, Kyoritsu, Tokyo, Japan) were treated as follows: (1) no treatment; (2) sandblasting with 110 ${\mu}m$ aluminum-oxide(Al2O3); (3) particles tribochemical silica coating(RocatecTM, 3M ESPE). Then zirconium-oxide ceramic blocks were divided into six groups(10 for each group) and bonded with resin cement(Rely X U-200, 3M ESPE). (1) No treatment / No treatment (2) No treatment / Sandblasting with 110 ${\mu}m$ aluminum-oxide particles (3) No treatment / Silica coating (4) Sandblasting with 110 ${\mu}m$ aluminum-oxide particles / Sandblasting with 110 ${\mu}m$ aluminum-oxide particles (5) Sandblasting with 110 ${\mu}m$ aluminum-oxide particles / Silica coating (6) Silica coating / Silica coating. Each group was tested in shear bond strengths by UTM. Data analysis included one-way analysis of variance(ANOVA) and the Tukey Honestly Significant Difference test (P=0.05). Group that bonded two silica coated specimen showed a highest bond strength(P<0.05). Two silica coated surface conditioning group and air-abrasion and silica coated surface conditioning group showed significantly difference with other groups(P<0.05). Other groups had no significantly difference each other. Within the limitation of this study, Surface conditioning with Rocatec treatment to each side of specimen provided the highest bond strength.