• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.9-13
• /
• 2008

Bismuth-substituted yttrium iron garnet($Bi_{0.5}Y_{2.5}Fe_5O_{12}$) films were deposited with the aerosol deposition method and their magnetic and optical properties were investigated as a function of the aerosol incident angle. The optical transmittance of Bi:YIG increased about 80% with increasing the aerosol incident angle from 0 degree to 30 degree, due to decrease of the defects which were formed from agglutinations of the Bi:YIG particles inside and/or surface of the film. The coercive force also decreased largely with increasing the aerosol incident angle due to the reduction of the collision energy between the particles and the substrate and the decrease of the defects.

• The Journal of the Korea Contents Association
• /
• v.19 no.6
• /
• pp.471-480
• /
• 2019

L-spine 3~4, L-spine 4~5, and L-spine 5~Sacrum 1 intervertebral disc(IVD) angle according to gender, age, body mass index(BMI), lumbar lordosis angle(LLA) were compared and analyzed. The anteriorposterior incidence angle of L-spine 3 ~ 4, L-spine 4 ~ 5 and L-spine 5~Sacrum 1 in body mass index were 5.66, 13.23 and 29.13 degrees in the head direction and L-spine 3 4, L-spine 4 ~ 5, L-spine 5~Sacrum 1 had 6.32 degrees, 16.09 degrees and 35.36 degrees in the head direction. The distortion area ratio comparison was performed with the phantom image using the proposed incidence angle. There was a significant difference in L-spine 4~5 and L-spine 5~Sacrum 1 IVD angle relative to body mass index and LLA(p<0.05), IVD angle and LLA were positively correlated(p<0.05).As a result of evaluating the usefulness of the image by applying the incidence angles of the disc angles according to the phantom angle of deviation to the head direction as 11 degrees for L4 and 26 degrees for L5, the distortion ratio area decreased from 14.90% to 12.11% in L4, And from 15.25% to 13.72% in L5. In anteriorposterior image of the Lumbar spine applying the incidence angle according to the measured disc angle, it is possible to reduce the distortion to purpose L4, L5. And improved the quality and diagnostic information of the target site.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.373-373
• /
• 2016

파푸아뉴기니 열대 우림에 서식하는 극락조의 가슴깃은 독특한 나노 구조를 가지고 있다. 이 독특한 구조에 의해 구조색이 발현된다. 또한 이 구조색은 입사하는 빛의 각도에 따라 색이 변화 하며 아름다운 색을 낸다. 극락조의 가슴깃의 구조는 keratin과 melanin으로 구성 되어 있는데 keratin과 melanin이 한 층씩 교대로 위치하여 multi layer 구조를 가진다. 가슴깃의 단면의 형태는 부메랑 모양의 구조로 되어 있는데 물질은 주로 keratin 으로 이루어져 있고 keratin 내부에 melanin rodlet이 층층이 박혀서 multi layer를 형성한다. 부메랑 모양의 단면에서 keratin 피질의 각도는 약 $30^{\circ}$ 정도로 이루어져 있고 내부의 melanin 기둥이 이루는 층은 약 $11.3^{\circ}$ 정도로 이루어져 있다. 본 연구에서는 극락조 가슴깃의 구조를 도식화 하여 입사하는 빛의 각도에 따라 나타나는 구조색을 FDTD simulation을 통해 계산하였고 실제 구조에 의해 측정된 reflectance spectra와 비교하여 특성이 유사하게 나타남을 확인 하였다. 실제 극락조 가슴깃의 반사 특성은 부메랑 모양 구조의 가운데 부분에서는 파장이 610 nm 정도인 주황빛이 주로 반사가 되고, 부메랑 모양 구조의 양옆 부분에서는 파장이 420 nm 정도인 파란빛이 주로 반사되어 나타난다. 그리고 각도에 따른 구조색의 변화는 보통의 multi layer의 특징과 다르게 나타난다. 입사하는 빛의 각도가 커질수록 reflectance peak가 나타나는 파장이 점점 짧아지는 특징은 일반적인 multi layer와 일치하지만 일반적인 multi layer가 입사 각도가 커질수록 reflectance가 커지는데 반해 극락조 가슴깃의 반사특성은 입사 각도가 커질수록 reflectance는 오히려 작아진다. 우리가 도식화한 구조를 FDTD simulation한 결과는 이러한 특징이 실제 구조의 측정 결과와 일치하게 잘 나타났다. 또한 keratin과 melanin층의 각도 및 두께변화에 따른 reflectance를 FDTD simulation을 통해 계산 해보았고 구조변화에 따른 특징들을 확인해 보았다.

• Proceedings of the Optical Society of Korea Conference
• /
• 2000.02a
• /
• pp.180-181
• /
• 2000

일반적으로 광통신이나 고출력 레이저에 사용되는 광학 소자들 중 고반사율의 거울은 특정 파장과 특정 각도에 대해서만 민감하도록 설계되어 있다. 이것을 여러 파장의 빛을 여러 각도로 입사시키더라도 높은 반사율을 얻는다면, 소자의 효율을 향상시키는데 상당한 효과를 볼 수 있다. 은이나 알루미늄의 금속박막으로 제작되는 금속 거울은 제작하기 쉽고 입사파장과 금속의 재질에 관련되어 90 %이상의 반사율을 갖지만, 특정한 각도에서는 빛이 금속 내에 있는 자유 전자들에 의해 상당량 흡수되어 버린다. 따라서 금속 거울은 에너지의 손실이 적어야 하는 광통신이나 고출력 레이저와 같은 응용분야에는 사용될 수 없다. 이러한 흡수가 거의 없는 유전체 거울은 고굴절률과 저굴절률의 층이 λ$_{0}$/4의 광학 두께를 가지고 주기적으로 반복되는 구조를 갖는다. 이러한 λ$_{0}$/4 유전체 다층 박막계는 1-차원 photonic 결정 구조와 동일하게 다룰 수 있는데, 1-차원 photonic 결정 구조가 모든 입사각도에 대해서 전방향 반사를 보인다는 것을 이론과 실험적으로 증명하였다[1-3]. (중략)

• Korean Chemical Engineering Research
• /
• v.44 no.5
• /
• pp.498-504
• /
• 2006

The etch rates of photoresist (PR) and the etch selectivity of $SiO_2$ to PR in a high density $CHF_3$ plasma were investigated at different ion-incident angles and bias voltages. A Faraday cage was employed for the accurate control of ion-incident angles. The ion energy was controlled by changing bias voltages. The etch rate of $SiO_2$ continuously decreased with ion-incident angles but the etch rate of PR remained constant up to the middle angle region and decreased afterwards. The etch rates of $SiO_2$ normalized to those at $0^{\circ}$ incident angle changed with the ion-incident angle following a cosine(${\theta}$) curve. On the other hand, the normalized etch rates of the PR changed showing a drastic over-cosine shape in the middle angle region. The etch selectivity of $SiO_2$ to PR decreased with an increase in the ion-incident angle because the etch yields of PR were enhanced by physical sputtering in the middle angle region compared to the case of $SiO_2$ etching. The etch selectivity of $SiO_2$ to PR decreased with an increase in the bias voltage at nearly all ion-incident angles.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.408-408
• /
• 2011

태양광 발전은 발전 셀의 특성상 태양광의 일사량과 태양과 셀 단면이 이루는 각도에 의하여 발전량에 차이를 가져온다. 태양전지의 표면의 입사각은 고정된 위치에서 태양전지 장치의 각도를 가변함으로서 변경 할 수 있다. 이 입사되는 빛의 각도를 변경하는 것은 효율개선의 한 측정의 방법으로써 사용된다. 본 연구에서는 입사각에 따른 a-Si/${\mu}$-Si 적층 태양전지의 양자 효율의 특성에 대해 분석하였다. 태양전지의 측정을 위하여 스테이지는 제작되었으며, 이 연구에서 양자효율 측정에 대한 유용성을 실험을 통해 입증하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.506-507
• /
• 2011

경사코팅 기술(Oblique Angle Deposition; OAD)은 입사 증기가 기판에 수직으로 입사하지 않고 90도 보다 작은 각도로 비스듬히 입사하도록 조절하여 코팅하는 물리증착 기술의 하나로 피막의 조직을 다양하게 제어할 수 있는 방법으로 알려져 있다. 초기의 경사 코팅 기술은 경사각을 가진 정지된 기판 상에 코팅하였으나 최근에는 기판의 각도와 회전을 동시에 조절하여 이루어지는 소위 스침각 증착(Glancing Angle Deposition; GLAD) 기술이 개발되어 다양한 형태의 구조를 제어하는 연구가 활발히 진행되고 있다. 특히, 컴퓨터를 이용하여 입사각과 방위각을 정밀 제어함에 의해 나노 스케일의 Zigzag 및 나선형, 기둥형 조직 등 복잡한 형태의 박막을 제조하는 것이 가능하게 되었다. 현재, GLAD 기술과 다양한 형태의 나노 조직을 이용하여 각종 센서는 물론 태양전지와 같은 에너지 소자, 필터와 같은 광학코팅 등에 응용하기 위한 연구가 세계적으로 폭넓게 진행되고 있다. 본 연구에서는 조직의 치밀도 향상을 통한 특성 향상을 위해 Al 및 TiN 박막을 제조함에 있어서 경사코팅 기술을 응용하여 단층 및 다층 피막(각도를 반대로 하여 여러 층을 제조)을 제조하고 그 특성을 비교하였다. Al 박막은 UBM (Un-Balanced Magnetron) 스퍼터링 소스를 이용하여 타겟 표면과 기판 표면이 이루는 각도 즉, 입사빔과 기판이 이루는 각도를 각각 0, 30, 45, 60 및 90도의 각도에서 강판 및 실리콘 웨이퍼 상에 시편을 제조하되 단층 및 다층으로 시편을 제조하고 치밀도 및 내식성과 반사율 및 조도 등의 특성을 비교하였다. 그 결과 경사각으로 코팅한 시편에서 조도 및 반사율이 향상됨은 물론 치밀도 및 내식성이 향상됨을 확인하였다. 특히, 염수분무에 의한 내식성 시험에서 경사 코팅된 시편의 경우 내식성이 현저히 향상되었는데, 이는 경사 코팅 방법이 박막의 치밀도를 향상시켜 나타난 현상으로 판단된다. TiN 박막은 Cathodic Arc 방식을 이용하되 Al 박막과 동일한 방법으로 코팅을 하고 내식성 및 경도 등의 특성을 비교하였다. TiN 박막은 경사각이 커지면서 경도가 낮아지며 특히 다층막의 경우 경도 감소가 현저함을 알 수 있었다. 다만, 45도에서는 다른 경사각에 비해 약간의 경도 상승이 측정되었다. 경사각 코팅에서의 경도 감소는 피막의 경사에 의해 탐침이 미끄러지거나 또는 우선 방위에 의한 경도 증가 효과가 나타나지 않아 생기는 현상으로 판단되었다. Ferroxyl 시험을 이용한 기공도 시험에서는 경사각 코팅의 경우가 기공이 다소 감소함을 확인하였다.

• Proceedings of the Korean Institute of Communication Sciences Conference
• /
• 1998.06a
• /
• pp.769-772
• /
• 1998

• Proceedings of the Optical Society of Korea Conference
• /
• 1998.08a
• /
• pp.112-112
• /
• 1998

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.1
• /
• pp.27-31
• /
• 2015

The degradation of refractories can be caused by erosion, friction of abrasive particles, as well as by corrosion by molten slag in the gasification reactors. There was little knowledge about the erosion of refractories so far. The castable refractories of which the maximum applying temperature of 1300 and $1500^{\circ}C$ were abraded using SiC particles varying the incidence angles. It was revealed that the maximum abrasion was occurred at the incidence angle of $60{\sim}75^{\circ}$ not at $90^{\circ}$ and thought that the porosity of the refractories was the principle factor.