• Korean Chemical Engineering Research
• /
• v.58 no.1
• /
• pp.84-91
• /
• 2020

The efficiency of the synthetic magnesium silicate used in basic polyols and edible oil purification is evaluated by its purification ability and filtration rate and is affected by the particle size and surface area of magnesium silicate. In this study, it was investigated the change on the particle size of magnesium silicate was influenced by the reaction temperature, injection rate, injection order (Si, Mg) and Mg/Si reaction mole ratio. The synthesized magnesium silicate was compared and analyzed for the synthesis, grinding, and refining processes. In the synthesis process, the reaction temperature and feed rate did not affect the average particle size change of magnesium silicate, while the reaction molar ratio of Mg / Si and the order of injection acted as main factors for the change of average particle size. The average particle size of magnesium silicate increased by 8.7 ㎛ from 54.4 ㎛ to 63.1 ㎛ at Mg injection when Mg molar ratio increased from 0.125 to 0.500, and increased by about 4.8 ㎛ from 47.3 ㎛ to 52.1 ㎛ at Si injection. The average particle size according to the order of injection was 59.1 ㎛ for Mg injection and 48.4 ㎛ for Si injection and the difference was shown 10.7 ㎛, therefore the filtration rate was about 2 times faster under the condition of Mg injection. That is, as the particle size increases, the filtration time is shortened and washing filtration rate can be increased to improve the productivity of magnesium silicate. The cake form of separated magnesium silicate after filtration becomes a solid through drying process and is used as powdery adsorbent through the grinding process. As the physical strength of the dried magnesium silicate increased, the average particle size of the powder increased and it was confirmed that this strength was affected by the reaction molar ratio. As the reaction molar ratio of Mg / Si increased, the physical strength of magnesium silicate decreased and the average particle size after grinding decreased by about 40% compared to the average particle size after synthesis. This reduction of strength resulted in an improvement of the refining ability due to the decrease of the average particle size and the increase of the amount of fine particle after the pulverization, but it resulted in the decrease of the purification filtration rate. While the molar ratio of Mg/Si was increased from 0.125 to 0.5 at Mg injection, the refining ability increased about 1.3 times, but the purification filtration rate decreased about 1.5 times. Therefore, in order to improve the productivity of magnesium silicate, the reaction molar ratio of Mg / Si should be increased, but in order to increase the purification filtration rate of the polyol, the reaction molar ratio should be decreased. In the synthesis parameters of magnesium silicate, the order of injection and the reaction molar ratio of Mg / Si are important factors affecting the changes in average particle size after synthesis and the changes of particle size after grinding due to the changes of compressive strength, therefore the synthetic parameter is an important thing that determines productivity and refining capacity.

• Resources Recycling
• /
• v.27 no.1
• /
• pp.55-63
• /
• 2018

Physical property changes of printed circuit board (PCB) according to heat treatment conditions were investigated. The heat treatment was carried out in air and nitrogen atmosphere at temperature range from $200^{\circ}C$ to $325^{\circ}C$. Thermogravimetric analysis showed that the PCB was pyrolyzed in two steps. The thickness of PCB expanded by 11~28% at about $300^{\circ}C$ in both air and nitrogen atmosphere as layer disintegration occurred. Mechanical strength of PCB decreased from 338.4 MPa to 20.3~40.2 MPa due to the delamination caused by the heat treatment. The heated printed circuit boards were crushed and sieved for analysis of density distribution and liberation degree of copper according to particle size. As a result of the density distribution measurement, non metallic particles and copper particles were concentrated into different size range, respectively. The liberation degree of copper was improved from 9.3% to 100% at size range of $1,400{\sim}2,000{\mu}m$ by heat treatment.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.5
• /
• pp.773-781
• /
• 2004

This research was Performed to raise grade efficiency of Sturtevant type air classifier. to treat powder less than $74\mu\textrm{m}$ particle produced at the crushing process of the dry aggregates manufacturing system or concrete wastes recycling system. The experimental conditions were in the ranges. 0.85 to 5.15 $m^3$/s of primary air flow rate. 0.005 to 0.015 $m^3$/s of secondary air flow rate $30^{\circ}$ to $70^{\circ}$ of auxiliary blades angle. respectively. for 1.7~3.3 kg/min of the powder feed rate. It was found that the grade efficiency of the air classifier was increased as the baffle plate was attached at the expansion region. and the optimal operating conditions of the air flow rates and the blade angle were obtained. The fractional recovery curves from the experiments were well agreement with the theoretical one of Molerus model.

• Resources Recycling
• /
• v.6 no.3
• /
• pp.15-21
• /
• 1997

Flyash from a coal-hed power plan1 is produced approximtcly 3 million tons m 1996 and causes the serious environmentalpmblem due to the disposal in the ash pond. Flyash is an accepted additive in concrete where it adds strength, sulfate ateresistanceand reduced cost, provided acccptablc levcls of unbunrned carbon are mmtmed This papzr describes to investigate thc technicalfeasibility of a dry triboelcctrostatlcp roccss to scparate unburned carbon h m f lyash into economically valuable produck Puliclesof unburned carbon and flyash can be impded positivc and negative surface charzes. rcapeclively. with a copper tniochargcr dueto dirferences in the work function values of thc particles and the tnbacharger. and cm he separated by passing thcm throuph anexternal electic field. A laboratory s d e separation system consists of r sacw feeder for ash supply, a tniocharger, verticalcollecling copper plates, power supplies, a flow meter, and a fan. Separation tests taking into account separahian efficiency and ashrecovery showed that flyash recovery was sh-nngly dependent an thc tnbocharger geomzhy, elect"c ficld strength. flyssh s ~ c a,n dash feeding late. Optimal separation conditions were flyash size less than 125 Fm and electric field shcngrh of 200 kV1m. Ovcr 80%of the flyash with 7% lass on ignition was recovered at wrbon contznts less than 3%bon contznts less than 3%

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.3
• /
• pp.317-324
• /
• 2020

Plastic wastes generated from domestic waste are separated by mixed discharge with foreign substances, and the cost of the separation and screening process increases, so recycling is relatively low. In this study, as a fundamental study for recycling mixed plastic wastes generated from domestic waste into concrete aggregates, changes in concrete properties according to the plastic waste types and the substitution rate were evaluated experimentally. The mixed plastic waste aggregate(MPWA) was found to have a lower density and a higher absorption rate compared to the coarse aggregate with good particle size distribution. On the other hand, the single plastic waste aggregate(SPWA) was composed of particles of uniform size, and both the density and the absorption rate were lower than that of the fin e aggregate. It was found that the MPWA substitution concrete did not cause a material separation phenomenon due to a relatively good particle size distribution even with the largest amount of plastic waste substitution, and the amount of air flow increased little. The compressive strength and flexural strength of the PWA substitution concrete decreased as the amount of substitution of the PWA increased due to the low strength of the PWA, the suppression of the cement hydration reaction due to hydrophobicity, and the low adhesion between the PWA and the cement paste. It was found that the degree of deterioration in compressive strength and flexural strength of concrete substituted with MPWA having good particle size distribution was relatively small.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.131-132
• /
• 2004

원자력연구소에 보관 중인 오염 토양폐기물을 토양 세척법으로 제염하여 비 방사성폐기물화 한다면 그 부피를 10% 이하로 저감시킬 수 있으며 연구소의 고체 방사성폐기물 저장 용량을 크게 늘릴 수 있다. 1988년 발견 당시 오염 토양 폐기물의 주요 방사성 핵종은 Co-60 이었는데 시간경과에 따라 Cs-134, 137 이 주요 방사성 핵종이 되었다. 오염토양 폐기물의 60 % 이상은 방사능 농도가 극히 낮아 물리적으로 입도를 분리하거나 수 세척에 의해 비 방사성폐기물화 할 수 있음을 파악하였다.(중략)

• Journal of the Mineralogical Society of Korea
• /
• v.21 no.4
• /
• pp.383-395
• /
• 2008

To enhance the grade and recovery rate of the gold/silver ores which yield at Philippine Mankayan mine, we studied the characteristics which are the geologic and mineralogical features of gold and silver ore, the liberation by crushing and grinding, the separation by sieving and shaking table. Gold/silver ore is composed of the sulfide minerals like pyrite, sphalerite, galena; and the gangue minerals which is quartz, clay. Gold/silver element are mainly contained in a sulfide minerals like pyrite, sphalerite and galena. To increase the liberation rate of sulfide minerals containing gold/silver element, the gold/silver ore has to be grounded under $100{\mu}m$ very finely because the crystal size of sulfide minerals is distributed from $1{\mu}m$ to $100{\mu}m$. The liberation rate of gold/silver ore increases to 92% when the particle size ($d_{90}$) of ore is grounded below $100{\mu}m$ by jaw crusher $\to$ cone crusher $\to$ rod mill by steps. The grade and recovery of sulfide minerals could not be enhanced by sieving separation because those crystal size is distributed homogeneously below $100{\mu}m$. But, when we separated the sieved ore using shaking table, the gold and silver grade increased to 40 ppm and 140 ppm, respectively. Then the recovery rate of gold reach almost 100% but that of silver is no more that 50%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.61-61
• /
• 2010

니켈 니켈 와이어를 증류수 및 에탄올 등의 유기용매 중에서 펄스파워 기술을 이용하여 전기적으로 폭발 시켰다. 폭발에 의하여 생성된 입자들은 직경이 수 마이크로미터 에서 수 십 나노미터에 이르는 넓은 입도분포를 보였다. 본 연구에서는 원심분리기술을 이용하여 입자의 크기별로 분리 회수가 가능함을 증명하였다. 또한 유기용매 중에서 제조된 니켈분말에 탄소가 포함되어 있으며, 열처리를 통하여 제거가 가능함을 실험을 통하여 밝혔다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.3
• /
• pp.312-319
• /
• 2017

For high value-added applications of natural blue diatomite, the physical refining process and synthesis of SiC from refined diatomite were investigated. Approximately 30 percent Fe ($Fe_2O_3$) in raw blue diatomite was removed by a particle sieve separation process; the Fe composition for 325 mesh down powder was approximately 2 percent. Although a wet and/or dry magnetic separation process had some influence on the separation and/or refining of Fe composition, the Fe composition in the non-magnetic by-product was approximately 2 percent. Water leaching separation was effective in removing the Fe composition; approximately 40 percent of the Fe in raw blue diatomite was removed. The synthesis of ${\beta}$-SiC by a carbothermal reduction of the $SiO_2$ in the refined diatomite using carbon (graphite, carbon black), the effects of an acid-treatment on removing the Fe, and the specific surface area for the synthesized powder were also investigated. The impurities were mostly eliminated and the specific surface area was increased to $52.5m^2/g$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.5
• /
• pp.249-255
• /
• 2017

Using a magnetic separation process, pond ash generated in thermoelectric power plants was separated into magnetic materials and nonmagnetic materials in order to make it into a raw material of geopolymers and unburned carbon; screening characteristics according to the particle sizes and magnet strength levels of the pond ash were observed. Based on the results of magnetic separation into fine particle (0.15~0.84 mm) and rough particle (0.84~2.4 mm) pond ash using 3000 G magnets, the weight fraction and ignition loss of nonmagnetic materials were found to be higher than those of magnetic materials, regardless of the particle size. In the case of fine particle pond ash, when the magnet strength was increased from 3000 G to 10000 G, even those materials that were weakly magnetic were separated into magnetic materials, leading to drastic increases in the weight fraction of magnetic materials, such that the ignition loss accounted for 66.9 % (22.8 wt%) of the entire ignition loss of 32.6 wt%, despite of the low ignition loss. Based on the results of measurement of the compressive strength levels of geopolymers made of magnetic-separated rough particle pond ash, the compressive strength of geopolymers made of magnetic materials containing small amounts of unburned carbon was found to be 20 MPa.