• Journal of the Korean Applied Science and Technology
• /
• v.33 no.1
• /
• pp.129-135
• /
• 2016

CO oxidation was performed with Cu-Mn and Cu-Zn co-precipitated catalysts as differential precipitant, metal ratio and calcination temperature. The effects of differential metal mole ratio and calcination temperature in mixed metal oxide catalyst were investigated with CO oxidation reaction. Physiochemical properties were studied by XRD, $N_2$ sorption and SEM. 2Cu-1Mn with $Na_2CO_3$ catalyst calcined at $270^{\circ}C$ has a large surface area $43m^2/g$ and the best activity for CO oxidation. $Cu_{0.5}Mn_{2.5}O_4$ in XRD peak shows the lower activity than others. The catalytic activity over the catalyst calcined $270^{\circ}C$ displayed the highest conversion, and it was better activity comparing with Pt catalysts CO conversion.

• Journal of the Korean Chemical Society
• /
• v.29 no.2
• /
• pp.111-120
• /
• 1985

The oxidation reaction of CO on the catalysts 4 mol%, 8 mol%, and 12 mol% Cd-doped ${\alpha}-Fe_2O_3$ is individually investigated. Regardless of Cd doping level, over-all reaction order for the oxidation of CO is 1.5; the first order with respect to CO and the one-half order with respect to $O_2$. Over the temperature range of 350∼$460^{\circ}C$, the activation energy for CO oxidation is 10.10∼11.30Kcal/mol. From the agreement between the kinetic data and conductivity measurements, the reaction mechanism is suggested. Especially from the effect of Cd doping, the fact that catalytic activity of ${\alpha}-Fe_2O_3$ is due to the excitation of electrons which are traped on oxygen vacancy is found, and the adsorption sites for reactant molecules are found.

• Clean Technology
• /
• v.26 no.4
• /
• pp.286-292
• /
• 2020

This study confirmed the effect of the Cu/CeO2-X catalyst on the CO oxidation activity at low temperature through the catalyst's structure and reaction characteristics. The catalyst was prepared by the wet impregnation method. Cu/CeO2_X catalysts were manufactured by loading Cu (active metal) using CeO2 (support) formed at different calcination temperatures (300-600 ℃). Manufactured Cu/CeO2_X catalysts were evaluated for the low-temperature activity of carbon monoxide. The Cu/CeO2_300 catalyst showed an activity of 90% at 125 ℃, but the activity gradually decreased as the calcination temperature of the CeO2-X and Cu/CeO2_600 catalysts showed an activity of 65% at 125 ℃. Raman, XRD, H2-TPR, and XPS analysis confirmed the physicochemical properties of the catalysts. Based on the XPS analysis, the lower the calcination temperature of the CeO2 was, the higher the unstable Ce3+ species (non-stoichiometric species) ratio became. The increased Ce3+ species formed a solid solution bond between Cu and CeO2-X, and it was confirmed by the change of the CeO2 peak in Raman analysis and the reduction peak of the solid solution structure in H2-TPR analysis. According to the result, the formation of the solid solution bond between Cu and Ce has been enhanced by the redox properties of the catalysts and by CO oxidation activity at low temperatures.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.411.2-411.2
• /
• 2016

직접 메탄올 연료전지 (DMFCs)는 친환경적이고 낮은 작동 온도로 인한 빠른 구동, 높은 에너지 밀도 등 다양한 장점을 가지고 있어 차세대 에너지 변환소자로 많은 관심을 받고 있다. 직접 메탄올 연료전지는 메탄올을 연료로 사용하며, 메탄올이 보유하고 있는 화학적 에너지를 전기 에너지로 변환하는 장치로써 음극에서는 백금 촉매로 인한 메탄올 산화반응, 양극에서는 환원 반응이 일어나며 전기화학적 구동을 하게 된다. 하지만 일산화탄소 피독으로 인한 촉매 활성 저하, 메탄올의 cross over, 백금 촉매 사용으로 인한 고비용 등의 문제점을 가지고 있다. 따라서 많은 연구자들이 백금 사용량을 줄이고 백금 촉매를 고르게 분포하기 위해 값이 저렴하고 넓은 비표면적을 갖는 탄소계 (graphite, graphene, carbon nanotube, carbon nanofiber 등) 지지체 재료를 도입하고 있다. 이 중 탄소나노섬유 (carbon nanofibers, CNFs)는 우수한 전기전도도와 열적/화학적 안정성을 가지고 있으며, 특히 넓은 비표면적을 가지고 있어 백금 촉매의 지지체로서 많은 연구가 진행되고 있다[1]. 따라서 우리는 전기방사법을 활용하여 넓은 비표면적을 보유하는 다공성 탄소나노섬유를 성공적으로 합성하였다. 또한, 이를 백금 촉매의 지지체로 도입하여 직접 메탄올 연료전지를 위한 다공성 탄소나노섬유에 담지된 고분산성 백금 촉매를 제조하였다. 제조한 다공성 탄소나노섬유의 형상 및 구조 분석은 주사전자 현미경 (field-emission scanning electron microscopy)와 투과전자 현미경 (transmission electron microscopy)를 이용하여 분석하였고, 결정구조와 화학적 결합상태는 X-선 회절분석 (X-ray diffraction) 및 X-선 광전자 분광법 (X-ray photoelectron spectroscopy)를 이용하여 규명하였다. 전기화학적 특성은 순환 전압 전류법 (cyclic voltammetry)를 이용하였다. 이러한 실험 결과들을 바탕으로 다공성 탄소나노섬유에 담지된 고분산성 백금 촉매의 자세한 특성을 본 학회에서 다루도록 하겠다.

• Journal of Korean Society for Atmospheric Environment
• /
• v.1 no.1
• /
• pp.43-51
• /
• 1985

This study is concerned with the oxidation of carbon monoxide on platinum and platinum-palladium catalysts. Catalysts were made by the impregnation method and flow reactor was used in the catalytic reaction. As for the mixed gases, carbon monoxide concentration varied from 1 to 4% and that of oxygen from 1 to 4%. $N_2$ was used as carrier gas and GHSV varied from 24, 000 $h^{-1} to 60, h^{-1}$. The temperature range was from 200 to $600^\circ$C. It was also taken into consideration that the heat and mass transfer resistance of our catalysts was negligible in the study. Experimental results showed that platinum-palladium catalyst was about 1.5-3.9% superior to platinum catalyst in conversion yield. When we used platinum-palladium catalyst, we observed that carbon monoxide oxidation was found to be 1 st order with respect to carbon monoxide concentration. Activation energy of the catalyst was 23.5 kcal/mol.

• Journal of Korean Society for Atmospheric Environment
• /
• v.6 no.1
• /
• pp.57-72
• /
• 1990

The oxidation of carbon monoxide on a catalyst, $LaSrNiCoO_3$ was investigatigated with a plug flow system. Kinetic quantities such as reaction-rate, reaction order and Arhenius-parameters at various reactor temperature from 200$^\circ$C to 300$^\circ$C were determined. Also, the optimum condition for the oxidation of carbon monoxide with this catalyst was determined and are as follows. Partial pressure of oxigen ; 428mmHg Partial pressure of carbon monoxide ; 332mmHg Mixed moral ratio of oxigen and Carbon monoxide ; 1.3 : 1 Total gas flow ; 224ml/min Reaction temperature ; 340$^\circ$C The reaction kinetic equation at the optimum condition, temperature range from 200$^\circ$C to 340$^\circ$C, are as follow. $$ $v = Ae^{6.5Kcal/RT} [CO]^{0.93 \sim 0.98} [O_2]^{0.42 \sim 0.50}$ $$ In addition to this, numerical calculation were performed to evaluate the mass and heat transfer effect on this system.

• Journal of Hydrogen and New Energy
• /
• v.17 no.3
• /
• pp.241-247
• /
• 2006

The catalytic performances for CO preferential oxidation in hydrogen-rich fuels were investigated by varying the types of alumina supports, additives excluding platinum, and synthetic methods of impregnation and sol-gel synthesis. The reactions were conducted in the range of $25{\sim}300^{\circ}C$ over Pt, Co, and/or Na impregnated catalysts supported on commercial gamma-alumina, pseudoboehmite, or sol-gel derived xerogels. Catalytic activities were enhanced by cobalt addition due to strong Pt-Co interactions in the bimetallic phase. Additional sodium promoted not only the formation of the Pt-Co bimetallic interphase but also oxygen adsorption capability, giving rise to increase in the CO oxidation rate at lower temperatures. Moreover, chemical interaction between Pt and Co was considerably enhanced by sol-gel synthesis.

• Proceedings of the KAIS Fall Conference
• /
• 2008.11a
• /
• pp.407-410
• /
• 2008

원소분석 결과 평균값은 "화합물 및 화학제품 제조업"의 경우 C 33.06wt%, H 4.34wt%, O 24.81wt%, N 5.18wt%, S 0.72wt%로 나타났으며, "코크스, 석유 정제품 및 핵연료 제조업"의 경우 C 36.58wt%, H 4.74wt%, O 26.79wt%, N 5.09wt%, S 0.49wt%로 나타났다. 열중량분석 결과, B사에서 배출되는 슬러지는 $700^{\circ}C$ 이상에서 그리고 F와 N 사에서 배출되는 슬러지는 $600^{\circ}C$ 정도의 온도에서도 연소가 가능할 것으로 판단된다. 연소테스트 결과, 산화반응과 동시에 열분해 반응이 일어나 고농도의 일산화탄소가 배출된다.

• Clean Technology
• /
• v.16 no.2
• /
• pp.132-139
• /
• 2010

The Cu-Mn mixed oxide catalysts with different molar ratios of Cu/(Cu+Mn) prepared by co-precipitation method have been investigated in CO oxidation at $30^{\circ}C$. The catalysts used in this study were characterized by X-ray Diffraction (XRD), $N_2$ sorption, X-ray photoelectron spectroscopy (XPS), and $H_2$-temperature programmed reduction $(H_2-TPR)$ to correlate with catalytic activities in CO oxidation. The $N_2$ adsorption-desorption isotherms of Cu-Mn mixed oxide catalysts showed a type 4 having pore range of 7-20 nm and BET surface area was increased from 17 to $205\;m^2{\cdot}g^{-1}$ with increasing of Mn content. The XPS analysis showed the surface oxidation state of Cu and Mn represented $Cu^{2+}$and the mixture of $Mn^{3+}$ and $Mn^{4+}$, respectively. Among the catalysts studied here, Cu/(Cu+Mn) = 0.5 catalyst showed the highest activity at $30^{\circ}C$ in CO oxidation and the catalytic activity showed a typical volcano-shape curve with respect to Cu/(Cu+Mn) molar ratios. The water vapor showed a prohibiting effect on the efficiency of the catalyst which is due to the competitive adsorption of carbon monoxide on the active sites of catalyst surface and finally the formation of hydroxyl group with active metals.

• Applied Chemistry for Engineering
• /
• v.1 no.2
• /
• pp.207-214
• /
• 1990

The catalytic reaction between CO and NO on polycrystalline Pt surface, which is very important in the development of catalyst for automobile exhaust gas control, has been studied using thermal desorption spectrometry(TDS) and steady-state experiment under ultra-high vacuum(UHV) conditions. With the pressures of CO and NO of each $1{\times}10^{-7}Torr$, the $CO_2$ formation rate showed a maximum at 560K. At the reaction temperature of 560K and the NO pressure of $1{\times}10^{-7}Torr$, the production of $CO_2$ was first order in $CO_2$ was first order in CO pressure below $1.35{\times}10^{-7}Torr$ of CO pressure whereas at higher CO pressures the rate became minus 0.3 order in CO. But the efforts of reactant pressure on the reaction was understood in consideration of the surface concentrations of adsorbates. With the results, we proposed a new reaction mechanism for this reaction.