• The Journal of Engineering Geology
• /
• v.14 no.1
• /
• pp.105-121
• /
• 2004

The purpose of this study is to investigate the relationship between petrographical and engineering properties of granitic rocks, widely used as building and ornamental stones in Korea, at the Namwon are a. This area is one of the most famous area as a domestic dimension stone production. The granitic rocks were examined for grain sizes, modal compositions and then same samples were tested to determine specific gravity, water absorption, porosity, uniaxial compressive strength, tensile strength, abrasive hardness, P-wave velocity, modulus of elasticity and Poisson's ratio. It is suggested that the influence of the grain size on the engineering properties is more important than that of the mode of mineralogical compositions. And quartz contents also significantly influence the engineering properties of granitic rocks.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.111-117
• /
• 1998

원자로 압력용기는 운전기간 동안 중성자 조사에 따른 재료의 기계적 성질이 변화되므로, 용기의 건전성 유지여부를 평가하기 위하여 조사시편을 이용한 주기적인 감시시험이 요구된다. 그러나 감시시편은 방사성 물질로서 일반 환경조건에서 시험이 불가능하다. 따라서 국내의 자력기술로 완공된 조사재시험시설의 핫셀 내에서 감시시험의 주요항목인 온도감시자, 충격, 인장, 파괴인성, 그리고 성분분석 등에 대한 시험을 수행하기 위하여 관련된 규정에 합하도록 장비 및 시험 평가기술을 개발하였다.

• Journal of Korea Foundry Society
• /
• v.28 no.1
• /
• pp.41-44
• /
• 2008

레오다이캐스팅 공정은 용탕상태의 원소재로부터 최종형상에 가장 가까운 정형제품(near-net shape)을 원하는 기계적 성질과 동시에 경제적으로 생산할 수 있는 제조방법으로 개발되어 왔다. 본 논문에서는 전자교반 시스템을 이용하여 결정립이 제어된 반용융 상태의 소재를 수직형 다이캐스팅기를 사용하여 리어파트(rear parts) 자동차 부품을 성형실험 하였다. 성형된 시제품들은 성형조건에 따른 조직 및 인장강도를 관찰하였으며, 시효경화 시간에 따른 T6 최적 열처리 조건을 조사하였다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.72-72
• /
• 2004

대부분의 금속 재료는 제조 공정 중에 인장, 압축, 압연, 압출, 인발 등 소성 변형을 수반하는 가공의 단계를 거치게 된다. 가공 단계에서 가해준 변형률 및 이에 따라 형성된 전위구조 등은 생산재의 기계적 성질에 많은 영향을 미친다. 그리고 소성 변형이 수반되는 또 하나의 과정은 피로, 크리프 손상 등의 소성 변형을 수반하게 되는 기계적 손상이다 이러한 기계적 손상에 의해서도 전위가 도입되며, 전위의 집적부위에서 균열이 생성되기도 한다. 따라서 기계적 손상을 비파괴적으로 평가하는데 있어서도 소성 변형의 영향을 파악하는 것이 하나의 중요한 문제가 된다.(중략)

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.41-42
• /
• 2014

현대 산업에서 철은 매우 중요한 재료이다. 다양한 산업적 요구에 맞게 제철산업에서도 다양한 성질의 강을 개발하고 생산하고 있다. 강의 주요 물성으로는 인장강도, 항복강도, 연신율 등이 있으며 이러한 물성들을 향상시키거나 변경하는데 다양한 첨가원소와 제조 공법들이 적용되어진다. 본 연구에서는 그 중 합금 원소를 첨가하여 강도를 높이는 초고강 강에 대해서 화성처리 특성을 연구하고 그에 영향을 미치는 인자에 대해서 분석하였다. 그리고 화성처리 공정을 개발하여 초고강도강의 인산염특성을 향상 시켰다.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.289-290
• /
• 2003

본 연구는 폴리에스터-나일론 파워 네트 원단의 건열특성을 다룬 것이다. 이 건열특성은 스판덱스(spandex)의 특성에 크게 영향을 받는다. 스판덱스는 통상 활용할 수 있는 신도가 500~600 %에 이른다는 성질 때문에 섬유제품에 많이 응용되고 있다 이는 탄성이 양호하여 스타킹용, 수영복용 등으로 많이 활용하고 있다. 또한 스판덱스는 마모와 마찰강도가 고무보다 우수하고 탄성이 아주 좋고 리 쓰인다. (중략)

• Proceedings of the Korean Society of Fisheries Technology Conference
• /
• 2001.05a
• /
• pp.101-103
• /
• 2001

가식성 및 생분해성 필름은 식품과 외부와의 물질이동을 차단하고, 영양성분, 향기성분, 항 산화제 등의 carrier 역할을 한다. 기존의 플라스틱 고분자 필름은 생분해성 필름에 비해 가격 경쟁력 및 물리적 성질이 우수하기는 하지만, 생분해성 필름은 단백질과 다당류 및 지질을 주원료로 하여 이들의 단독 또는 조합에 의해 만들어지고, 생물학적 분해가 용이하고 식용 가능하여 포장재로 인한 환경오염을 줄일 수 있다는 것이 생분해성 필름의 가장 큰 장점이다. (중략)

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.3
• /
• pp.464-470
• /
• 2001

The purpose of this study was to evaluate the tensile strength of light-cured restorative posterior resin-based composites. Five commercially available light-cured composites(Denfil : DF, P60 : PS, Unifil S : US, Z100 : ZH, Z250 : ZT) were used. Rectangular tension test specimens were fabricated in a teflon mold giving 5mm in gauge length and 2mm in thickness. Specimens were subjected to the 5,000 thermal cycles between $5^{\circ}C$ and $55^{\circ}C$ and the immersion time in each bath was 15 second per cycle. Tensile testing was carried out with Instron at a crosshead speed of 0.5mm/min and fractured surface were observed with scanning electron microscope. The obtained results were summarized as follows; 1. The tensile strength of PS was highest. PS was significantly higher than DF, US and ZH(p<0.05) but in the case of ZT was similar to PS(p>0.05). 2. The tensile strength DF was lowest. DF was significantly lower than PS, US, ZH and ZT(p<0.05). 3. The tensile strength of US and ZH were significantly lower than PS and ZT(p<0.05). but were significantly higher than DF(p<0.05). The tensile strength of US and ZH were similar(p>0.05).

• Korean Journal of Materials Research
• /
• v.2 no.1
• /
• pp.65-75
• /
• 1992

0.4wt%C steel added with V and/or Nb were forged and followed by air cooling. The structure-property relationships were examined and multiple regression analysis was conducted to quantify the magnitudes of effects of microalloying elements on the properties of the steels. All material's tensile strength are greater than $70kg/\textrm{mm}^2$, so they are equal to or superior to Q/T material's(S45C). Their impact energies are less than 40J, so they are 50% of Q/T material's. Increasing the content of V from 0.10 to 0.15 wt% had brought improvement in UTS about 20% but with some sacrifice of impact energy. These were the results from the precipitation strengthening by fine dispersion of VC in ferrite, increment of pearlite volume fraction and decrement of pearlite interlamellar spacings. However, increasing the content of Nb from 0.05 to 0.l0wt % slightly improved UTS and impact energy. NbC precipitates were more effective in suppression of austenite grain coarsening than VC precipitates. Combined additions of V+Nb were more effective to bring impact toughness than sole addition. Optimum combination of strength and toughness was accomplished wish 0.4C-1. 19Mn-0.05S-0.12V-0.07Nb steel.

• Polymer(Korea)
• /
• v.25 no.4
• /
• pp.521-527
• /
• 2001

The miscibility, molecular interaction and tensile properties of the blends of poly (${\varepsilon}$-caprolactone) (PCL) with poly(vinyl chloride) (PVC) have been studied. The measured glass transition temperature values of PCL/PVC blends were found to be well fitted by Fox equation. We found that PCL/PVC blends are amorphous up to 23% PCL content. The blends showed the highest Young's modulus and yield strength at 5% PCL content and the highest tensile strength at 11% PCL content. The blends with low contents of PCL(up to 13%) show increased tensile strength and decreased elongation of PCL/PVC blends. Consequently, the antiplasticization phenomenon is observed in the PCL/PVC blends.